Scientific Tools for Conservation IConservation nfrared Spectrosco y in p Science Michele R. Derrick Dusan Stulik James M. Landry T h e G e t y Conservation I n s t i u t e Los Angeles Tevvy Ball, Managing Editor Sylvia Tidwell, Copy Editor Anita Keys, Production Coordinator Hespenheide Design, Designer Printed in the United States of America 10 9 8 7 6 5 4 3 2 1 © 1999 by the J. Paul Getty Trust All rights reserved. Illustration credits: Figures 3.8, 4.27, 4.28, 4.29, 5.16, 5.24, and 6.9: Courtesy of the Journal of the American Institute for Conservation of Historic and Artistic Works. Figures 4.20, 6.1, 6.2, 6.3, 6.10, 6.14, 6.15, 6.20, 6.21, 6.23, and 6.24: From "Infrared Microspectroscopy in the Analysis of Cultural Artifacts," by Michele R. Derrick, in Practical Guide to Infrared Microspectroscopy, ed. Howard Humecki, pp. 287-322 (New York: Marcel Dekker, Inc., 1995). Reproduced by permission. The Getty Conservation Institute The Getty Conservation Institute works internationally to further appreciation and preservation of the world's cultural heritage for the enrichment and use of present and future generations. The Institute is an operating program of the J. Paul Getty Trust. The Institute's Scientific Tools for Conservation series provides practical scientific procedures and methodologies for the practice of conservation. The series is specifically directed to conservation scientists, conservators, and technical experts in related fields. Previously published in the series is Thin-Layer Chromatography F. Library of Congres Cataloging-in-Publication DaIta for Binding Media Analysis (1996), by Mary Striegel and Jo Hill. Derrick, Michele R., 1955- Infrared spectroscopy in conservation science Michele R. Derrick, Dusan Stulik, James M. Landry. p. cm.-(Scientific tools for conservation) Includes bibliographical references and index. ISBN 0-89236-469-6 1. Infrared spectroscopy. I. Stulik, Dusan, 1956N8558.2.153D47 7021.8'8-dc21 2. Art-Expertising-Methodology Case studies. II. Landry. James M. III. Title. IV. Series. 1999 99-37860 CIP Contents Chapter Chapter Chapter 1 2 3 vii Foreword ix Preface xi Acknowledgments 13 44 68 112 11334 1156 12790 22341 256 History of Infrared Spectroscopy Additional Reading Infrared Absorption Theory Electromagnetic Radiation Wave Theory Absorption Theory Molecular Absorptions Degrees of Freedom Selection Rules Group Frequencies Infrared Spectra Infrared Regions Near-Infrared Region Mid-Infrared Region Far-Infrared Region Summary Additional Reading Sample Collection and Preparation Sampling Methodology Sampling Design Sampling Location Sampling Implementation Tools Sample Documentation and Storage Avoidance of Contamination Sample Collection and Preparation Procedures Gases Liquids Sampling with Swabs Chapter Chapter 4 5 238 42 44536 5520 66203 66598 77690 80 8822 88764 99321 5109 1120039 1122154 1297 Solids, Powders, and Particles Fibers Cross Sections Summary Additional Reading Infrared Analysis Methods Infrared Transmission Measurements Infrared Window Materials Transmission Analysis of Gases Transmission Analysis of Liquids Transmission Analysis of Solids Infrared Reflection Measurements Specular Reflection Reflection-Absorption Diffuse Reflection Internal Reflection Infrared Microspectroscopy Microspectrophotometer Design Microspectrophotometer Capabilities Particle and Fiber Analysis Cross Section Analysis Microspectrophotometer Accessories Summary Additional Reading Spectral Interpretation Infrared Spectra Absorption Bands Plotting Format Instrument Configuration Qualitative Analysis Spectral Quality Visual Comparison Computer Libraries Spectral Region Examination Spectra-Structure Correlations Correlation Charts Identification of Materials Used in Art and Art Conservation Natural Organic Materials Synthetic Resins (Polymers) Colorants Mixtures Quantitative Analysis Mathematical Manipulations of Spectra Subtraction Techniques Resolution Enhancement Methods Summary Additional Reading Chapter 6 11330 4138 114418 51592 116731 117728 220015 220370 236 Case Studies Identification and Characterization of Materials Deterioration Studies The Case Studies Case Study Case Study Case Study Case Study Case Study Case Study Case Study Case Study Case Study Case Study 132:: 465: 798:: 10 Ultramarine Pigments Creosote Lac Resin Chumash Indian Paints Varnish on a Desk Reflection versus Transmission Painting Cross Sections Vikane Parylene Cellulose Nitrate Sculptures Dead Sea Scrolls Summary Appendix I: Selected Infrared Spectra Collections and Digitized Libraries Appendix II: Infrared Reference Spectra Glossary Suppliers References Index About the Authors Foreword Since the founding of the conservation field's flagship j ournal, Studies in Conservation, in the early 1 95 0s, the number of museum laboratories has increased remarkably. Where once a single optical microscope may have sat in dusty isolation, today chemists, engineers, physicists, and other scientists make use of a wide range of analytical instruments, often working side by side with conservators and curators. It is clear that those who benefit from this development are people responsible for managing and interpreting vast arrays of collection types, but the public is also a prime recipient of this benefaction. This relatively recent infusion of science into the museum environment has significantly enhanced preservation practices, affording a deepened understanding of materials' properties and degradation processes. The simple optical microscope now coexists with many other instruments, which allow advanced techniques for separation and chemi­ cal identification, high magnification and analysis of microstructure, and imaging using nuclear magnetic resonance, thermal neutrons, and a range of electromagnetic radiation. Today the most widely used method in most museum labora­ tories is infrared (IR) spectroscopy. It is extremely cost-effective, and it has directly contributed to the current enhanced interest in organic mate­ rials in art and archaeology. Recent years have witnessed the develop­ ment of a robust network of IR users, who share spectra and insights on a regular basis. The activities of such a group, informal as it may be, help to refine the method, broaden its utility, and provide a specialized training environment for its novitiates. Many benefit from this-curators, museum directors, collectors, and, of course, the museum-going public. For all these reasons we are proud to include this volume as the second to be published in the Getty Conservation Institute's Scientific Tools for Conservation series, which is designed to present methods and procedures of practical use to conservators, conservation scientists, and others engaged in the preservation of the cultural heritage. viii Foreword We are grateful to the authors, Michele R. Derrick, Dusan Stulik, and James M. Landry, for their dedication in writing this book. With its focus on the practical applications of IR spectroscopy-including a detailed presentation of ten case studies-the present volume hopes to make this important technology more readily available to those who can benefit from it the most. Tim Whalen Director The Getty Conservation Institute Preface The purchase and use of infrared ( IR) spectrometers in art conservation labs have grown more than tenfold in the last decade. This expansion can be traced to decreased instrument costs, enhanced interest in organic materials in art and archaeological obj ects, and increased requests for scientific analyses by conservators and curators. Additionally, the current computer-driven, user-friendly IR instruments make it extremely easy to perform an IR spectral analysis on a sample. But herein lies a problem, since simplification of a method can result in lost intricacies and misin­ formation. Thus, critical evaluation and availability of information on a technique are important in order for pitfalls to be recognized and for any of the technique's significant limitations to be understood. This book fills a gap, since currently there is no available compilation of information that deals directly with the IR analysis of historical and artistic materials. These materials can pose significant problems for analysts, as they tend to be natural products that are often mixtures and are sometimes affected by age. Scientific books and refer­ ence sources rarely provide key information necessary for dealing with such materials. This text provides practical information on the use of IR spectroscopy for the analysis of museum obj ects, disseminating many sample handling and spectral acquisition techniques specifically applica­ ble to their analysis, along with discussions of these techniques' potential problems. This book is meant to be a learning tool as well as an infor­ mation resource. While the present volume provides a comprehensive overview of the technique, individual chapters may be read indepen­ dently for specific information. Chapter 1 defines IR spectroscopy and provides a historical 2 perspective on its development as a modern analytical technique. Chapter provides an overview of the position and relation­ ship of the IR spectral region to the entire electromagnetic spectrum. It also supplies a simplified version of the theory of molecular interactions that produce IR spectral patterns. Included is a basic description of the phenomena that occur in a material to produce a unique IR spectrum. Sample collection and preparation are key steps in the analy­ sis of all materials. Chapter 3 provides basic and widely applicable infor­ mation on sampling methodology and implementation. This chapter is important not j ust for analysts but also for anyone who may be requesting, x Preface collecting, or submitting samples for analysis. Emphasis is placed on the effect of sampling on analytical results. Comparative tables are included that illustrate the capabilities and sample requirements of some common analytical techniques. Once the sample is collected, several options exist for its IR analysis. Chapter 4 reviews the theory and operation of both transmission and reflectance methods, as well as provides references as to how each of the techniques has been used in the analysis of art materials. Many excel­ lent books that provide more detailed information about IR methods and instrumentation are also included in an additional reading list. Chapter 5 focuses on the spectral interpretation of conserva­ tion and artist materials and provides schemes or flowcharts to facilitate the characterization of unknowns. Examples of basic peak identification for the maj or classifications of materials found in works of art are given. Problems relating to material mixtures are discussed, as are several options for the mathematical manipulation of spectra. Chapter 6 incorporates reviews of existing conservation and related literature. Case studies illustrate several types of problems and materials and show approach, utility, and limitations of the techniques. Professionals who are not spectroscopists may find individual sections useful to their understanding of the applications and restrictions of the different procedures. One of the most important factors in IR spectral identifi­ cation is access to reference spectra corresponding to appropriate materi­ als. Appendix I is a list of commercial sources that supply digitized and hard-copy spectral collections. Appendix II provides IR spectra of com­ mon art and conservation materials. There is a list of references, and additional readings on related subjects are provided at the end of each chapter. IR spectroscopy is a useful and fascinating challenge that can provide the answers to many of the problems encountered in the analysis of works of art. It is hoped that the practical information provided in this book will stimulate interest in, and perhaps lay the groundwork for, many future IR applications. Michele R. Derrick Acknowledgments Funds for the preparation of this manuscript were provided in part by a Kress Foundation conservation publication fellowship awarded to Michele Derrick in 1 99 5 . Portions of this book were presented at a workshop held j ointly by the Getty Conservation Institute ( GCI) and Loyola Marymount University, Los Angeles, in 1 9 9 1 . The authors would like t o thank the following organizations and people for providing samples for analysis: the J. Paul Getty Museum, Los Angeles (Andrea Rothe and Brian Considine ) ; the Museum of Modern Art, New York ( Eugena Ordonez and Patricia Houlihan) ; the Fine Arts Museum, Houston ( Christopher Shelton); the Bureau of Land Management, Needles, California (Tom Holcomb and Claire Dean) ; and the Museum of Natural History, New York ( David Thomas) . The authors would also like to thank Miguel Angel Corzo, the former director of the GCI, for his support of the book; Neville Agnew for initiating this series of books; Kevin Thompson for providing several historic books on optics; Eric Hansen, Richard Newman, and Charles Selwitz for their helpful suggestions; Janice Carlson for her extensive and meticulous tech­ nical editing; Tanya Kieslich and Margaret Bolton for preparing some of the drawings in Chapter 4; Herant Khanj ian for photographs in Chapter 4; and the GCI Information Center for obtaining numerous and often obscure offprints. Additionally, Michele Derrick gives her deepest appreciation and gratitude to her family, John, Erin, and Kristin Stacy, for their patience during the lengthy period of manuscript writing and rewriting. Chapter 1 History of Infrared Spectroscopy In simplified terms, one dictionary defines infrared as "those invisible rays just beyond the red end of the visible spectrum . . . [that] have a penetrating heating effect: used in cooking, photography, etc . " ( Guralnik 1 9 8 4 ) . While this may seem obvious, since infrared (IR) is such an inte­ gral part of our lives, it was not until 1 8 00 that IR was recognized as a distinct region of the energy spectrum. This discovery was made by Sir William Herschel, an astronomer, when he measured the heating effect of sunlight (Herschel 1 8 0 0 ) . However, the field of IR spectroscopy-i .e., the study of wavelengths of light in the IR region of the spectrum and their interaction with various materials-did not develop at that time due to difficulties in building suitable detectors to measure IR radiation. Eventually, beginning in 1 903, William W. Coblentz conducted compre­ hensive experiments leading to the accurate measurement of IR spectra for hundreds of inorganic and organic compounds ( Coblentz 1 90 5 ) . Interest increased i n the potential o f I R spectroscopy for analytical chem­ istry when the first prototypes of IR spectrometers were built in the 1 930s. Commercial development of IR spectrometers quickly followed, stimulated by the need for rapid analytical methods in the synthetic rub­ ber industry. This development expanded the acquisition of IR spectra and motivated research into deeper theoretical studies of all features of IR spectra. The next j ump came as advances in electronics during and after World War II furnished the thermocouple detector technology that led to development of stable double beam spectrophotometers (Wright and Hersher 1 947). By the 1 95 Os, IR spectroscopy was established as a key analytical method in academic and industrial labs. Most IR instrumentation used through the 1 970s was based on prism or grating monochromators. A maj or breakthrough in IR technology was the introduction of Fourier transform infrared ( FT-IR) spectrometers. In the late 1 8 00s, Albert Michelson developed the inter­ ferometer for studying the speed of light ( Michelson 1 8 9 1 ) . Two years later, Lord Rayleigh recognized that the output from an interferometer could be converted to a spectrum by a mathematical procedure devel­ oped about seventy years earlier by the French mathematician Fourier ( Rayleigh 1 8 9 1 ) . However, because of the numerical complexities of the Fourier procedure, it was not until 1 949 that Peter Fellgett actually cal­ culated a spectrum from an interferogram ( Fellgett 1 970). Fellgett, an astronomer, used Fourier transform spectroscopy to isolate the weak 2 Chapter 1 signals of distant stars from environmental background noise and in doing so discovered the multiplex advantage, later named in his honor. A few years later, Jacquinot, a French scientist, pointed out the throughput advantage of interferometry (Jacquinot 1 95 4 ) . These advantages for FT-IR over dispersive instruments translated into practical improvements such as high-speed data collection, increased resolution, lower detection limits, and greater energy throughput. Acceptance of FT-IR spectroscopy, however, was slowed by the complexity of the calculations required to transform an interferogram into a spectrum. Then, in 1 964, the discovery of the fast Fourier trans­ form ( FFT) algorithm by James Cooley and John Tukey reduced the time for the computer calculation of the transform from hours to j ust a few seconds ( Cooley and Tukey 1 96 5 ) . Even so, it was still a time-consuming process for spectroscopists to record an interferogram on a paper tape or punched cards, walk it over to the computing center and wait for calculation of the spectrum ( Griffiths and de Haseth 1 9 8 6 ) . The next significant change came in 1 9 69, when the first commercial FT-IR with a dedicated minicomputer was developed and sold by Digilab (see Suppliers). For the first time, spectroscopists were able to see a spectrum plotted shortly after the interferogram was collected; correspondingly, it took less total time to obtain a spectrum using an FT-IR spectrometer than using a dispersive instrument. Since then, further developments in computer technology, together with substantial price decreases, have been responsible for the large number of commercial FT-IR spectrometers on the market and for the wide application of FT-IR spectroscopy in all branches of science and technology. Particularly useful for the field of art conservation was the coupling of the optical microscope with the IR spectrometer. Initial stud­ ies were done at Oxford by Barer, Cole, and Thompson, who used a microscope designed with all-reflecting optics attached to a dispersive IR spectrometer ( Barer, Cole, and Thompson 1 94 9 ) . Although the system performed well, the sensitivity achievable by a microscope in combina­ tion with a wavelength dispersive IR spectrometer was low, and interest in the technique waned. Revival of IR micro spectroscopy was stimulated by the development of FT-IR instrumentation, with its increased energy throughput. In 1 9 8 1 , at McCrone Associates, Robert Z. Muggli success­ fully adapted a microscope to an FT-IR spectrometer ( Palenik 1 992 ) . In 1 9 8 3 Digilab introduced the first commercial microscope designed specifically for FT-IR spectrometers by Spectra-Tech (see Suppliers). Following that time, a number of other instrument companies have developed IR microspectrophotometers and micro accessories for IR spectrometers. Availability of the IR microscopes precipitated a new range of analytical applications, and IR microspectroscopy has become a powerful tool in many branches of basic and applied research. The historical background for IR spectroscopy is shown in Figure 1 . 1 . 3 History of I nfrared Spectroscopy 1 700s-Fourier developed mathematical 1 80G-Herschel discovered transform (FT) method. IR radiation . • • + 1 905--Coblentz's 1 891 -Michelson experiments led to IR published design of spectra of organic and his interferometer. inorganic compounds . . 1 930s-lnterest increased in IR application to 1 949-Fellgett analytical chemistry. discovered multiplexing advantage of FT. •4-J t5--C 1 947-Wright and Hersher developed double beam 1 95 dispersive IR discovered throughput spectrophotometer. advantage of FT. • \ 1 949-Barer and coworkers linked IR spectrometer 1 96 1 969-Digilab with microscope. commercial FT-IR acquinot ooley and Tukey discovered fast Fourier � transform (FFT) algorithm. with dedicated minicomputer. T 1 983-Spectra-Tech and Digilab developed the first commercial FT-IR Figure 1 . 1 microspectrophotometer. f-+ 1 980s-FT-IR combined with personal computers to make widely used, versatile, and cost- Sign ificant events leading to the effective method of analysis. development of cu rrent FT-IR spec­ high-quality microanalysis. Microspectrophotometers provide trometers and m icrospectrometers. Additional Reading Colthup, N. B . , L. H. Daly, and S. E. Wiberly 1990. Introduction to Infrared and Raman Spectroscopy. 3d ed. Boston: Academic Press. Griffiths, P. A., and J . A. de Haseth 1986. Fourier Transform Infrared Spectrometry. New York: Wiley-Interscience. S i lverstein, R. M . , F. C. Bassler, and T_ C. Morri l l 1981. Spectrometric Identification of Organic Compounds. 4th ed. New York: John Wiley and Sons. S m ith, A. L. 1979. Applied Infrared Spectroscopy: Fundamentals, Techniques, and Analytical Problem Solving. Chemical Analysis series, vol. 54. New York: John Wiley and Sons. Chapter 2 Infrared Absorption Theory Electromagnetic Radiation In simplest terms, spectroscopy is defined as the interaction of light with matter. Light, in this context, is the broad spectrum of continuous energy called the electromagnetic spectrum. The maj or regions of the electro­ magnetic spectrum are shown in Figure 2 . 1 . There is no uniform naming system for the spectral regions, as the specific names for each type of radiation-such as visible, X ray, and radio-were assigned when it was discovered. Even so, the designations are commonly known and useful for quick orientation. The same physical properties govern all radiation, regardless of its spectral region. The types of radiation are generally grouped by the kinds of chemical and physical effects they can produce on matter. For example, in a magnetic field, exposure to the low-energy radio frequency radia­ tion only reorients nuclei, while exposure to the slightly higher-energy microwave region changes electron spin states of molecules with unpaired electrons. Microwave radiation can also change the rotational energy of molecules; this effect is used to heat food quickly in a microwave oven. In the middle regions of the electromagnetic spectrum, absorption of IR radiation causes changes in the vibrational energy of molecules. Visible (Vis) and ultraviolet (UV) radiations alter the electron energies of loosely held outer electrons of atoms and molecules. Higher-energy X rays can cause electron transitions between inner electron levels, and gamma radi­ ation produces changes within atomic nuclei. As all compounds absorb radiation in multiple regions of the spectrum, the information on molecu­ lar activity in each region provides complementary data for material characterization. The following overview of the relationship of radiant energy to its effects on matter has a focus on IR absorption theory. For more information, several excellent references are listed at the end of the chap­ ter. In particular, the book by Colthup, Daly, and Wiberley ( 1 990) pro­ vides good, in-depth coverage of IR theory and molecular structure correlations. Wave theory All energies of the electromagnetic spectrum can be considered to be waves that move at the speed of light, with the types of radiation differ- 5 I nfrared Absorption Theory O-H 40.-..360.- 32-0 -28lilt0.. 2.4.,0 20 180 ,. 160 ...140.. ..120 ....10 ... 80 ...-60 FAR-IR •WAEVNERUGMYBINECRINECARSEASE I 1 X <(/)CDrm IIIIIII WAEVNELRNGYTDHECINREASE A, " 111 ' '- 20 Wavenumber (cm- 1 ) Wavenumber (cm-1) I GAMMA RAYS RAYS I I I I MICROWAVE INFRARED (IR) ULTRAVIOLET (UV) I I I Wavelength (f..lm) Figure 2 . 1 II III v, I RADAR, RADIO, TELEVISION WAVES ing only in amplitude, frequency, and wavelength ( Fig. 2 . 2 ) . The ampli­ Spectral regions of electromagnetic tude is the height, or maximum size, of the wave, which corresponds to rad iation, with expansion of IR region . the intensity, or volume, of the signal. The frequency, is the number of oscillations, or waves, per unit time-that is, cycles per second. The wavelength, is the distance between two successive maxima or minima of a wave-that is, the length of one wave. The wavelength of the radia­ tion is inversely proportional to frequency. Thus, high-frequency radia­ tion has short wavelengths. Energy, according to Planck's law, is directly proportional to frequency. Since frequency is inversely proportional to wavelength, it follows that energy of electromagnetic radiation and wavelength are also inversely related. Thus, longer wavelengths have lower energy and fre­ quency, while shorter wavelengths have higher energy. Electromagnetic radiation can also be characterized by the number of waves per unit length. This is termed wavenumber, v 1 A v: Chapter 2 6 A. (wavelength) A "0:Ci«�OJE v = 1.5 z A. I · 1 Bv = z vx = v = = y Figure 2 . 2 Two frequencies o f electromagnetic waves at a 1 second interval. Radiation waves can be characterized by their amplitude (height), wavelength (distance between two maxima), and frequency ( n u m ber of oscillations per u nit ti me). (wavelength) OJ "0 .Ci«€E 4 where: uum (3 / c (cm- 1 ) frequency ( Hz, sec- 1 ) / velocity of light in vac­ 1 01 0 cm/sec ) ; and A wavelength (cm). While wavenumber is usually expressed in cm units [ ( 1 /A cm- 1 ] , it could be expressed in any reciprocal distance units. Because of the simple inverse relationship, wavenumbers can readily be converted to wavelength units when needed. For example, 1 000 wavenumbers (cm - 1 ) is the same as the wavelengths of 0.001 cm or 0 . 0 1 I-Lm or 1 0 nm. Frequency and wavenumber units have two advantages over wavelength units. The first is that they remain constant, regardless of the media traversed by the radiation, whereas the wavelength is reduced when radiation passes through a medium with a refractive index greater than that of a vacuum. This change in wavelength due to refractive index is ignored except for high-accuracy experiments, since the refractive index of air is near unity under normal conditions. The second advantage of the use of frequency and wavenumber units over wavelength is that they are directly proportional to energy. Thus, a transition that requires greater energy will occur at a higher wavenumber. For this reason, wave­ number units are commonly used in IR spectroscopy, as opposed to wavelength units (i.e., nanometers or micrometers ) , which are commonly used in visible and UV spectroscopy. Absorption Theory Toward the end of the nineteenth century, it became increasingly evident that the classical laws of physics describing natural phenomena-such as time, gravity, and momentum-did not successfully account for effects 7 Infrared Absorption Theory observed when light interacted with matter. At the 1 904 St. Louis World's Fair, top scientists debated for and against the existence of atoms. Two years later, modern atomic theory was established when experiments by Ernest Rutherford showed that atoms existed and that each consisted of a positively charged nucleus surrounded by a cloud of negatively charged electrons. Experimentally, the emission spectrum of hydrogen consists of a number of very sharp lines at distinct energies. In order to explain the fact that the hydrogen atom emits only these characteristic frequen­ cies, Niels Bohr postulated in 1 9 1 3 that the electrons of an atom occupy specific energy states or levels that are defined by the radius of the orbit of the electron around the nucleus. He further suggested that to move between different energy states, atoms must absorb or emit energy and that the amount of energy absorbed or emitted must be equal to the difference in energy between the two levels ( Fig. 2 . 3 ) . One photon of energy, hv, is emitted when an electron falls from a higher ( Eh) to a lower ( El) energy state. This is also called the energy of transition, �E. Alternatively, the electron can absorb a photon of light ( energy) and move from a lower to a higher energy state. Each element ( hydrogen, helium, etc . ) has electrons at unique energy levels corresponding to its atomic structure. Even though an ele­ ment is exposed to radiation of all wavelengths, only the wavelengths ( energy photons) that match the levels ( energy states) within that atom can interact. The resultant pattern of energy lines, called a spectrum, coincides with the absorption or emission of the photons specific to that particular element. This phenomenon is responsible for the emission lines produced by excited atoms and molecules, as well as for the absorption bands in all regions of the electromagnetic spectrum. It forms the basis for all atomic and molecular spectroscopy. Nucleus -1-+--, Higher energy level (E h l Lower energy level (E l l Figure 2 . 3 B o h r atomic model f o r hydrogen. B o h r hv hv theorized that energy whose frequency matches the energy difference between - electronic levels can be absorbed or emit­ ted as the electron transitions between the two levels (hv = one photon) . ---....-. Absorption EI ---....I..--Emission EI 8 Chapter 2 Molecular absorptions Scientists expanded and advanced Bohr's theories to include multielectron atoms and molecules. By the end of the 1 930s, detailed models were in place that accounted for the placement of electrons in orbitals. These pro­ vided key links to understanding elemental bonding, molecular structures, and chemical reactions; this new knowledge in turn led to a greater understanding of molecular spectroscopy. Specific wavelengths of energy correspond to all molecular transitions or motions: electronic, translational, rotational, and vibra­ tional. In electronic motion, the electrons change energy levels or direc­ tions of spin. For translational motion, the entire molecule shifts to a new position, while for rotational motion, the molecule rotates around its center of mass. Vibrational energy is required for individual atoms within a molecule to change position relative to one another without moving or rotating the molecule. The energy of IR radiation is too low to affect the electrons within an atom. IR radiation does, however, correspond to the energy required for translational, rotational, and vibrational energy transitions. Since a molecule's movements are unique to its structure, the measure­ ment of these transitions makes IR a powerful tool for compound characterization. The primary transitions in the IR region are vibrational. Rotational and translational transitions are weak and often difficult to measure in the IR region without the aid of high-resolution instruments . One common exception is for water vapor (regions 4000-3 600 and 1 8 00-1400 em- I ) , where the unrestricted motion of some gas-phase mol­ ecules produces sharp rotational absorption bands that can easily be seen ( Fig. 2 . 4 ) . The occurrence of many unresolvable rotational transitions in the IR region is one reason that a single, associated vibrational transition appears as an absorption envelope or band rather than a sharp line, as predicted by theory. Figure 2.5 illustrates the relationship of the vibra­ tional energy levels to rotational energy levels. Degrees of freedom In a molecule, the atoms are constrained by molecular bonds to move together in certain specified ways, called degrees of freedom. When a particular molecular structure is known, its constraints allow prediction of expected molecular transitions. To determine the degrees of freedom for any molecule, first consider the molecule positioned in a three-dimensional Cartesian coordi­ nate system (x, y, and z ) , with its center at the point of origin (0, 0, 0 ) . Then designate each atom b y its coordinates i n space (i.e., atom 1 x ' l Y ' z )· For a molecule with N ( any number) atoms, the total number of l l coordinates (xn, y n' zn) specified will be 3N. These 3N coordinates are = the maximum number of potential transitions possessed by that molecule and are called its degrees of freedom. For example, a molecule with 5 atoms has 15 degrees of freedom. The 3N degrees of freedom can be assigned to the transla­ tional, rotational, and vibrational motions of the molecule ( see Table 2 . 1 9 I nfrared Absorption Theory ---Water- vapor (rotational motion) ... ..___ Liquid water '"::u (vibrational motion) E (/) c '" c '" � "* Figure 2 .4 IR spectrum of water vapor rotational absorption bands versus a spectrum of the major vibrational absorption band for liquid water. 3200 3600 4000 and Fig. 2 . 6 ) . All molecules have three translational degrees of freedom­ that is, the center of mass of the molecule can move in three directions (x, y, and z ) . If the molecule is nonlinear, then it also has three rotational degrees of freedom as it spins around each of the three axes (x, y, and z ) . Linear molecules have only two rotational degrees of freedom, since two rotation directions are equivalent. Thus, the total of translational and - 6, -5 rotational degrees of freedom is 6 ( 5 for linear molecules ) . All remaining motions, 3N are vibrational degrees of freedom (3N � Figure 2.5 Vibrational I evels Energy transition levels for vibrational and rotational transitions. Vibrational transi­ tions produce the primary IR absorption First excited state bands. A fundamental transition occurs when the absorbed photon increases the energy level from the ground state (E o) to the first excited state (E ) . An overtone 1 occurs when the transition covers two transition levels. The very small energy dif­ ference between rotational levels results in very sharp. closely spaced rotational bands in a spectru m . in the case E � �E = hv Ground state } 1 Eo c :;:;gE","'.:§·0w'"'':;:.' LL:::J;Q> - c . c- "0 '" c� c 0"'cu·£;w 0>�"'2-:;.0[" :;::; c t0·w !9LL"'Eeg!0� c :;::; _c c� - "0:;::; c '" :::l� Rotational levels OlWa;>­ c Chapter 2 10 Table 2 . 1 Degrees o f freedom corresponding t o type of motion for any molecule with N atoms. The total nu mber of degrees of freedom for any molecule is 3 N . Motion Degrees of freedom Translation (position of the molecule) 3 3 (nonli near) (li near) Rotation (about the center of the molecule) 2 3N 3N Vibration - 6 (nonli near) - 5 (li near) of linear molecules}. This is an important number, since vibrational tran­ sitions are the strongest and most important in IR spectroscopy. For x = - example, a nonlinear molecule with 3 atoms, such as S0 2' will have 3 fundamental vibrations [ ( 3 -6 -5 3) 6 3 ] , as shown in Figure 2 . 6 . All vibrational motions of the atoms can be described completely in terms of these 3N or 3N fundamental vibrations, which are called the nor­ mal modes of vibration for the molecule. The most common vibrations are stretching, torsional, and bending modes. A stretching vibration increases or decreases the length of the bonds between the atoms. A torsional, or skeletal, vibration Ground state Translational motion Rotational motion Figure 2 . 6 Degrees of freedom for molecular motion of a triatomic molecule such as 502' The molecule at rest is shown at the top. The molecule can move i n three translational motions (x ,y, and z), as well as rotate around the three axes. Of the nine total motions allowed by the degrees of freedom for a triatomic molecule, only three are left for vibrational motion. These are shown as stretching and bending vibrations. Vibrational motion y Infrared Absorption Theory 11 involves the twisting of the backbone of the molecule. A bending vibra­ tion changes the bond angles of the atoms relative to one another or to the remainder of the molecule. Bending vibrations can be further classified as scissoring, rocking, wagging, and twisting. Vibrations are also characterized by their symmetry-that is, they can be symmetric or asymmetric. Selection rules The degrees of freedom specify the maximum number of fundamental vibrations for a molecule. A fundamental vibration-also called a first­ order vibration-corresponds to a change from the molecular ground state to the first energy level. A first-order vibration produces the strongest energy absorptions, but only those that are active in the IR region will be seen as an absorption band in the IR spectrum. Selection rules, based on the symmetry of the molecule, determine whether a given vibration will be seen in the spectrum. The primary selection rule, or requirement, for active IR absorptions is that the vibration must change the dipole moment of the molecule. In a heteronuclear molecule, non­ symmetrical vibrations change the distance between the two nuclei and thus its dipole moment. This vibrating dipole moment creates a dipolar electric field that in turn absorbs a discrete unit of energy unique to that transition. Vibrations in a homonuclear diatomic molecule or symmetri­ cal vibrations in a heteronuclear molecule do not change the dipole moment and thus are not seen in the IR spectrum. In practice, the number of absorption bands observed in an IR spectrum is usually smaller than the number of fundamental frequen­ cies. In addition to the primary selection rule, other factors affecting a reduction in the number of absorption bands are ( 1 ) degeneracy, where two vibrational modes may occur at identical frequencies, (2) overlap­ ping or weak absorptions, or ( 3 ) vibrational modes outside the instru­ ment analysis range. Alternatively, the number of observed bands may be increased by the detection of weak, or so-called forbidden, absorptions, in which the change in the vibrational level is greater than one. These are known as overtones. Two or more fundamental vibrations may also interact to produce discrete absorption bands that occur at a frequency correspond­ ing to the sum or the difference of the individual band frequencies. Such absorptions are known as combination bands. Group frequencies Within any molecule, a given functional group (a combination of atoms such as a carbonyl group or an amide group) is responsible for IR absorp­ tions at or near the same frequency, regardless of the rest of the molecule. The position (i.e., frequency or wavenumber) of an absorption band depends on the mass of the atoms in the absorbing group, along with the strength and angles of the connecting bonds. A mathematical equation for the vibrational frequency of a two-body system ( Hooke's law) can be used to predict the absorption band position for simple molecules ( Smith 1 979). However, only a limited number of small molecules have vibrational 12 Chapter 2 spectra simple enough for complete theoretical analysis and interpretation. The maj ority of IR spectra-structure correlations are empirical, having been determined by the analysis of a large number of compounds. The vibrational frequencies for any particular functional group are characteristic of that group-e .g., most carbonyl stretches occur between 1 650 and 1 750 cm- l , and most carbon-hydrogen stretches occur near 3000 cm -1. These characteristic vibrations are termed group frequencies and are used for the identification of materials and for the determination of structure in an unknown pure compound ( see Chap. 5 on spectral interpretation). Molecules rarely consist of j ust a two-atom pair but, rather, consist of multiple groups of atoms, each involved in its own vibrational transitions. The energy of a vibration and, thus, the position of the band in the IR spectrum are sometimes influenced by the atoms surrounding the vibrational group. A highly electronegative atom (e.g., chlorine) near a functional group can cause shifts in the electron distribution ( inductive effects) that raise the frequency (wavenumber) of vibration. The presence of heavier atoms near a functional group (e.g., nitrogen next to carbonyl in an amide group) will dampen the oscillations (resonance ) and lower the frequency (wavenumber) of vibration. Strong coupling between stretching vibrations occurs only when there is an atom common to the two vibrations. Interaction between bending vibrations requires a com­ mon bond between the vibrating groups. Little or no interaction is observed between groups separated by two or more bonds. Infrared Spectra Figure 2 . 7 I R spectrum of gelatin plotted a s percent An IR spectrum displays detector response as percent transmittance ( % T) transm ittance (% T) on the y-axis, and I R on the y-axis, and IR frequency in terms of wavenumber (cm- 1 ) on the frequency in terms o f wavenu mber (cm - ' ) x-axis, as shown in Figure 2.7. The detector response indicates the extent on t h e x-axis. of interaction of the IR electromagnetic radiation with the sample as it is 4000 3600 3200 2800 2400 2000 1 800 1 600 Wavenumber (cm- ' ) 1 400 1 200 1 000 800 600 400 13 Infrared Absorption Theory proportional to the resultant intensity of IR radiation that reaches the detector after passing through the sample. Two types o f interactions-absorption and transmission-are important in the typical IR experiment. When the molecule in the sample compartment of the spectrometer is exposed to a source of continuous IR radiation, the photons of discrete energy units that are absorbed by the molecule do not reach the detector. The IR spectrum reveals these miss­ ing photons, or absorptions, as a series of well-defined, characteristic, and reproducible absorption bands. Photons that are not absorbed by the sample are transmitted to the detector essentially unaltered. For a given wavelength or frequency of IR radiation striking a sample, these two interactions are inversely related through the follow­ ing equation: A where: A = absorbance and T == log liT transmittance (% T/l 00 ) . Infrared Regions As was seen in Figure 2 . 1 , the IR spectral region of the electromagnetic spectrum extends from the red end of the visible spectrum to the microwave region; it includes radiation with wavenumbers ranging from about 1 4,000 to 20 cm- I , or wavelengths from 0.7 to 500 /-Lm. Because of application and instrumentation reasons, it is convenient to divide the IR region into the near (NIR ) , middle ( IR or mid-IR) , and far ( FIR) sub­ regions. The majority of analytical applications are found in the middle region, extending from 4000 to 500 cm- 1 (2.5 to 20 /-Lm) . Near-infrared region The near-IR (NIR, NIRS) region extends from the visible region at 1 4 ,000 cm- 1 ( 0 . 7 /-Lm) to the mid-IR region at 4000 cm-1 ( 2 . 5 /-Lm) . Because i t i s accessible with quartz optics, near-IR instrumentation is often combined with UV-Vis spectrometers (UV-Vis-NIR). Spectra gener­ ated in the near-IR region consist of many overtones and combinations of the mid-IR region fundamental vibration modes. Since all organic species absorb in the NIR and produce many overlapping bands, single­ band spectroscopy and qualitative band assignments are nearly impos­ sible. NIR is useful for quantitative work, including in situ monitoring of reactions. Mid-infrared region The spectral range of greatest use for chemical analysis is the mid-IR (MIR) region. It covers the frequency range from 4000 to 500 cm-1 (2.5-20 /-Lm ) . This region can be subdivided into the group frequency region, 4000- 1 300 cm - 1 (2.5- 8 . 0 /-Lm) and the fingerprint region, 1 3 00-500 cm- 1 ( 8 . 0-20 /-Lm) . 14 Chapter 2 In the group frequency region, the main absorption bands may be assigned to vibrational modes corresponding to individual func­ tional groups: NH-OH (4000-3000 cm- I ) C-H stretch region ( 3 000-2 800 cm- I ) window region (2800- 1 800 cm- I ) carbonyl region ( 1 800-1 5 00 cm- I ) Both the presence and absence o f these characteristic group frequency bands are useful for characterizing molecular structure. The absorption bands in the fingerprint region of the spec­ trum are the results of single-bond as well as skeletal vibrations of poly­ atomic systems. Multiple absorptions in this region make it difficult to assign individual bands, but the overall combined pattern is very charac­ teristic, reproducible, and useful for material identification when it is matched to reference spectra. Far-infrared region The far-IR ( FIR) region is generally designated as 5 00-20 cm-I (20-500 /-Lm) . In this region, the entire molecule is involved in low­ frequency bending and torsional motions, such as lattice vibrations in crystals. These molecular vibrations are particularly sensitive to changes in the overall structure of the molecule that are difficult to detect in the mid-IR region. For example, the far-IR bands of isomers and long-chain fatty acids can often be differentiated in solid-state materials. FIR is also useful in the identification and differentiation of many minerals and colorants. Summary Light and matter can interact. The examination of this interaction is termed spectroscopy. The interactions are characterized by the energy of the radiation and its effects on materials. IR radiation supplies sufficient energy to produce translational, rotational, and vibrational motion in molecules. The measurement of the characteristic IR energies (photons) that correspond to these transitions results in a spectrum. Based on its atomic structure, each molecule produces a unique and characteristic IR spectrum. The specific number and position of absorption bands for any molecule are governed by its degrees of freedom, its functional groups, and the IR selection rules. A spectral pattern, sometimes called a finger­ print, is used to identify an unknown material when the absorptions in its spectrum are matched with the absorptions in the spectrum of a known material. Additionally, since functional groups (combinations of atoms) produce absorptions at or near the same frequency, regardless of the rest of the molecule, the presence or absence of certain functional groups can be determined by interpretation of the IR spectrum. Infrared Absorption Theory 15 Additional Reading B ri l l , T. B . 1 98 0 . Light: Its Interaction with Art and Antiquities. New York: Plenum Press. Colthup, N. B . , L. H. Daly, and S. E. Wiberley 1 990. Introduction to Infrared and Raman Spectroscopy. 3d ed. Boston: Academic Press. Schutte, C. J. H . 1 976. The Theory of Molecular Spectroscopy. Vol. 1. New York: Elsevier. Si lverste i n , R. M . , F. C. Bassl er, and T. C. Morri l l 1 9 9 1 . Spectrometric Identification o f Organic Compounds. 5th ed. New York: John Wiley and Sons. S m ith, A. L. 1979. Applied Infrared Spectroscopy: Fundamentals, Techniques and Analytical Problem Solving. Chemical Analysis series, vol. 54. New York: John Wiley and Sons. Chapter 3 Sample Col lection and Preparation Much effort has been put forth to optimize instrumentation for material analysis, as well as to maximize the amount of information that can be gleaned from data. The most important step of any analysis, however, is the collection and preparation of a sample. Although numerous software manipulations can sometimes recover useful data from an ill-prepared sample, it is best to concentrate on using good sample handling and experimental technique. The extra time required will be rewarded by the generation of high-quality data. This chapter details collection and preparation procedures for many types of samples. Sampling Methodology Sampling is defined as the process of selecting and collecting the sample for analysis. Analytical chemists receive training in the importance of correct sampling and valid data treatment. For example, Majors states, " Collect the wrong sample, or collect the right sample incorrectly, and you trivialize all that follows, rendering your data worthless" (Majors 1 992). In the ideal situation, the analyst will be involved in and pre­ sent at each sampling step. When this is not practical, the sampler should provide as much information as possible to the analyst. In the analysis of art obj ects, conservators are often the most qualified to remove samples because of their skill and knowledge of the history, problems, and obj ec­ tives related to the sampling. When sampling and analysis functions are shared between more than one person, it is important to keep communi­ cation open . A sampling strategy should be established, based on thor­ ough discussion of analytical questions and experimental choices. When dealing with works of art, the possibility for sampling may be limited; thus, it is important to draft the sampling strategy accordingly ( Reedy and Reedy 1 9 8 8 ) . Sampling consists of two steps: first, the sampling design and, second, the implementation. The purpose of the sampling design step is to determine how to obtain a representa­ tive sample or set of samples related directly to the analysis question. The second sampling step, implementation, involves the actual removal and preparation of the sample or samples, with the goals of avoiding sample loss and contamination. 17 Sample Collection and Preparation Sampling design The design, or planning, step requires intimate knowledge of the obj ect as well as of the reason for analysis. Since cultural obj ects are irreplace­ able and their preservation the ultimate goal in any conservation exami­ nation, samples are removed only when necessary. Nondestructive techniques ( X-ray fluorescence [XRF] , X radiography, IR and ultraviolet [UV] photography, etc . ) should receive priority and are often used to survey obj ects. Physical testing methods-such as measurement of color, hardness, and porosity-may at times be in situ analyses. However, most chemical analysis techniques require sample removal. Table 3 . 1 com­ pares the capabilities of IR spectroscopy to other commonly used chemi­ cal analysis techniques. Each technique has its own advantages, and when techniques are used together, they can supply complementary information on a sample. The range of materials used in art obj ects is nearly universal. Inorganic substances are found as base materials ( stone, metal, glass, ceramic ) , as colorants ( pigments), as thickeners and fillers, as polishers (talc, alum, carbonates), as stabilizers and neutralizers, and as unwanted reaction products (corrosion, weathering crusts, salt deposits ). Organic materials in objects may have either natural or synthetic sources. Both plants and animals generate natural products (cellulose, hair, skin, resin, gum, dye, oil, protein, wax) that are themselves complex mixtures of Tab le 3.1 chemical compounds, even before being prepared for use as art materials. A comparison of com monly used chemical In contrast, synthetic organic materials ( found as fibers, colorants, analysis tech niq ues. binders, adhesives, plasticizers, coatings, backings, supports) are, in Minimum sample size Sample preparation Sensitivity Specificity Tech nique Acronym Description Polarized light microscopy PLM Ide ntification of material based on physical properties 5 fJm easy n/a none I R spectroscopy IR Compositional analysis of organic and inorganic compounds 1 0 fJg easy 10% none X- ray fl uorescence XRF Elemental analysis nondestructive 1 m m spot none 0.1 % elements only (heavier than potassium) Energy dispersive spectroscopy EDS Elemental analysis (sim i lar to XRF but attached to scan n i n g electron microscope) 1 easy 0.1 % elements only (heavier than carbon) X- ray diffraction XRD Compositional analysis of crystalline materials 1 0 fJg easy 5% crystalline materials I n d u ctively coupled plasma ICP Quantitative/qualitative analysis of elements down to trace levels 1 mg slow 0.01 ppm elements only (heavier than nitrogen) fJ m spot Q uantitative/qual itative analysis of organic components Ch romatography Thin- layer liqUid TLC H PLC Gas GC in a mixture (TLC usually only qual itative) High performance liqUid chromatography 1 mg 1 pg slow slow 5% 1 fJg slow 0.01 ppm 0.01 ppm General class of materials in mixture must be known before starting analysis Chapter 18 3 general, originally produced as well-defined, purified materials; they may later be combined for use in commercial products. In most cases, IR spectroscopy, since it is a nondiscriminatory technique, is one of the first analysis methods chosen. Table 3 .2 indicates the general order in which common analytical methods are usually applied. Information on the microscopic characterization of particles, another common first-choice technique, can be found in McCrone and Delly ( 1 973) and Aldrich and Smith ( 1 99 5 ) . I n the analysis of complex materials, such as paints, several analytical methods are usually needed to produce a complete characteri­ zation of a sample's components. Elemental analysis of the inorganic Table 3.2 Common analytical methods and the gen­ eral order i n which they are applied to var­ ious organic and inorganic materials ( l R = infrared spectroscopy [compositional analysis of organ ic/inorganic compounds] ; XRF = X-ray fluorescence [nondestructive elemental analysis]; EDS = energy disper­ sive spectroscopy [same information as XRF but requires sample]; PLM == polarized light microscopy [size, color, shape, crys­ tal l i n ity, refractive index, etc.]; XRD X-ray diffraction [compositional analysis of == == , = = crystalline materials]; I C P ind uctively coupled plasma [quantitative elemental analysis]; UV /Vis ultraviolet/visible spec­ troscopy [precise color measurement]; fluorescence UV-induced fluorescence [both autofluorescent and with reactive dyes]; color sol ubility visual color assessment; Material Fi rst-choice analysis methods Other useful analysis methods Organic Coatings IR sol u bil ity, chromatography, fluorescence sol ubil ity, chromatography, fluorescence sol ubility, chromatography, fluorescence solubility, chromatography, fluorescence solubil ity, chromatography, fluorescence sol ubil ity, ch romatography Adhesives IR Consolidants IR Binders IR Plastics IR Polymer additives Sizes/fi n ishes IR Solvents Air pollutants IR I R , chromatography Synthetic fibers Natural fibers PLM, I R PLM, I R Dyes Wood I R , chromatography, U V/Vis PLM Organic/inorganic Paints IR chem ical reactivity tests conducted on a microscopic scale). (with mordants, also use XRF or E D S) fluorescence XRF(EDS), IR, PLM XRD, solubil ity, chroma­ tography, fluorescence Lacquers XRF(EDS), IR, PLM XRD, sol ubil ity, chroma­ tography, fluorescence Residues XRF(E DS) , I R, PLM Patinas XRF(E DS) , I R , PLM Corrosion products U n knowns XRF(E DS) , I R , PLM, XRD XRF(E DS) , I R , PLM XRD, solubil ity, chroma­ tography, fluorescence XRD, solubility, chroma­ tography, fluorescence ICP XRD, solubil ity, chroma­ tography, fluorescence solvent solubility testi ng; m icrochemical tests solubil ity, ch romatography, fluorescence ch romatography specific compound detectors Inorganic Pigme nts Gems Glass Ceramics Stones Masonry Mortars/plasters Fillers (inorganic) Salts Metals color, XRF(EDS), PLM, I R color, XRF(EDS) XRF(E DS) XRF(E DS) , PLM XRF(EDS) , PLM XRF(E DS) , PLM XRF(E DS) , PLM XRF(EDS) , PLM, I R XRF(E DS) , PLM, XRD XRF(E DS) , metallography XRD, microchemical tests I R , XRD ICP IR, XRD, ICP IR, XRD IR, XRD IR, XRD PLM, XRD IR, microchemical tests ICP Sample Col l ection and Preparation 19 material i n a paint sample can indicate the presence of certain com­ pounds otherwise not obvious from the IR spectrum. Additionally, in an IR spectrum of a multiple-component sample, knowledge of one material simplifies the identification of the remainder. Thus, the complementary use of other analysis techniques ( such as scanning electron microscopy [SEM] , XRF, X-ray diffraction [XRD ] , optical microscopy, etc.) in con­ j unction with IR is very helpful. The data resulting from each method can be fit together as pieces in a puzzle, with the addition of each piece bringing it closer to completion. For further information on the potential and strategy of combining multiple analytical techniques for the charac­ terization of samples from works of art, see Masschelein-Kleiner, Heylen, and Tricot-Marckx ( 1 96 8 ), Schreiner and Grasserbauer ( 1 9 8 5 ) , Roelofs ( 1 9 8 9 ) , Karreman ( 1 9 8 9 ) , and Erhardt and coworkers ( 1 9 8 8 ) . Sampling location When the removal of samples is permitted, the value of the obj ect and its state of deterioration often dictate very specific restrictions on the num­ ber, size, and location of the samples removed. The obj ect's history, pre­ vious analyses, treatments, revarnishing, and retouching are considered in the sampling design. In view of the complexity and variety of possible components in a sample from an art obj ect, the first step for its analysis is to obtain all the background information possible. This measure can substantially reduce the amount of time necessary for sampling and for the later spectral interpretation, as well as minimize the chances for erro­ neous conclusions. Questions, such as the following, should be asked before the sample is taken: •• • • What is the background of the object? What is the reason for analysis? What information is needed ? What is the desired format for results ? Can a sample be removed? If so, how much? Where ? Does the sample have a single component or is it multicomponent? Are all components original to the piece? Has any previous analysis been done ? After background information has been obtained, the obj ect is thoroughly examined in visible and UV light to evaluate its condition and homogeneity, as well as to inspect potential sampling sites. All infor­ mation is recorded. Then, when possible, all involved personnel-conser­ vator, curator, and scientist-discuss the sampling plan and make a j oint decision as to sample numbers, locations, and amounts. In the simplest sampling decision, an unknown contains a single homogeneous component or matrix. Examples include a new sheet of paper, a uniform varnish layer, an adhesive from one location, or a modern ( unaged) sculpture out of a single metal or polymeric resin. In these situa­ tions, a sample can be taken from any location, and the analytical results 20 Chapter 3 will be the same. However, a homogeneous, single-matrix situation is more often found in manufactured objects than in works of art. For an inhomogeneous matrix or set of objects, the ideal sampling protocol is to assign an identifier to each obj ect or sample loca­ tion ( such as with a grid) and to select randomly the objects or sites for analysis. This method will provide a statistical basis for sample selection. If cost, time, or value of an obj ect limits the number of samples that can be taken, then visual classification of the obj ect by color, texture, struc­ ture, UV fluorescence, and so on, can be used to j ustify minimizing the sample number and locations. It is rare that a random and truly representative sample is removed from a valuable obj ect. More often " convenience" samples are selected because of their accessibility or because they can be taken from regions of previous damage. For example, a typical sampling procedure · for a surface finish from a museum furniture object is to remove one or two barely visible samples « 50 fJ..g) from arbitrarily chosen, obscure areas near or under metal mounts, in the rear of the carcass, or on the legs. In such circumstances, the sample may not be truly representative of the obj ect. However, with care and knowledge of the situation, good data can still be obtained and j ustified as valid when combined with background information and visual examination results. Sampling Implementation Sampling implementation is the collection and preparation of the sample for analysis. Once the analyst has removed or received the sample, addi­ tional steps may be taken to prepare it for a specific analytical method. As it is the sample that determines the quality and utility of the results, care is taken in each step of its removal, storage, preparation, and analy­ sis to prevent contamination or loss. Appropriate sampling tools and containers for storage are necessary to keep the sample from changing prior to analysis. Tool s Several types of sampling tools are useful for the mechanical removal of a sample (Fig. 3 . 1 ) . Fine-point forceps are appropriate for samples that are visible to the naked eye. Smaller particles may be manipulated with a tungsten needle with an extremely fine ( 1 fJ..m ) point. A tungsten needle is prepared by heating the tip of a tungsten wire (3 cm of 24 or 26 gage wire attached to a wire holder) to red hot in a burner, then quickly draw­ ing it through sodium nitrite ( McCrone and DeIly 1 9 73; Teetsov 1 977). Another fine-point probe for manipulating small samples can be made from a cat hair or a thick human eyelash that has been adhered to a wooden stick ( Reid 1 972 ) . Also helpful in retrieving small particles is a fine artists' brush (no. 2 or no. 3) or a brush modified to contain only a few bristles. The static electricity in a small sliver of cured silicone, freshly cut from a flexible mold, makes it extremely useful for picking up and transferring small particles. Fine-tip paper points, available from 21 Sample Collection and Preparation �- Disposable scalpel blade in universal metal handle; both pointed- and curved-end blades are useful for sample collection. Disposable1llade prepared from a cut razor blade and a wcoden stick. BC=======� ______________� � L- Disposable eye blade in a 3 inch (7.62 cm) Beaver blade handle; this blade is useful for removing cross sections. ________________________---- ---- �L- �c= An inexpensive artists' brush with all but a few bristles removed; the brush fibers are useful for picking up groups of particles. - D c= A tungsten fine-point needle in a universal metal handle; a fine­ point needle is used for separating and transferring single particles. Figure 3 . 1 Several types of sam pling tools. An eyelash brush prepared by adhering an eyelash or cat hair to a wooden stick; this tool is useful for handling fragile particles or thin sections. microscopy supply companies, may also be used for picking up tiny par­ ticles; dampening a point with a microdrop of distilled water creates a tool that will pick up the most obstinate particle; however, this treatment subsequently makes it difficult to release the particle into a container. Scalpels are used to remove barely visible particles as well as multiple-layer cross section samples. Microsurgical scalpels have sharp, thin blades that work well; of particular note are eye blades. Another option is a microscalpel made by adhering 1 -2 mm broken from a razor blade to a sharpened wooden applicator stick ( Hill 1 9 8 9 ) . With any tool, it is important that the cutting or sampling end is immovably secured to the handle. Sample removal and subsequent sample preparation require a steady hand. The probe or scalpel should be held at a low angle to the working surface (McCrone 1 9 8 2 ) . Optimally, the working hand and arm should be supported on a vibration-free surface. This is rarely possible during the sample removal step, unless an exterior bridge ( boom arm, stool, scaffolding) is available, since the obj ect itself should not be used as a support. The sampler's other hand can be used to steady the work­ ing hand, provided it is not required for holding the sample container. Sample documentation and storage Documentation of samples is crucial for understanding and interpreting the analytical results and relating the sampled area to the conservation 22 Chapter 3 problem. Proper documentation starts with a picture of the object (e.g., a photocopy or a Polaroid) on which the explicit sampling areas and dis­ tinguishing features can be marked. Corresponding labels are placed on sample containers, with the date of sampling and the initials of the sam­ pler noted. All pertinent information is recorded in a sampling notebook. This information includes a complete description of the object, the sam­ pling area, and the sample, along with the reason for sampling and the potential types of analyses. Each sample is placed in its own well-labeled container. Containers can introduce their own sets of problems. Plastic containers (BEEM capsules, Ziploc bags, etc. ) often produce static electricity that hinders the addition and removal of samples. Also, additives in and on plastic containers ( such as slip agents added to plastic bag surfaces to keep them from sticking together) readily contaminate samples. Samples in solution should never be placed in plastic containers because of the potential for leaching of plasticizers or dissolution of containers. Gelatin capsules should also not be used for sample storage, as they may hamper the determination of the presence of proteinaceous materials within the sample. Organic samples are best contained in clean glass containers, such as a depression slide sandwich ( described below) or a vial with a Teflon-lined lid. Aluminum foil is an acceptable alternative. A glass depression slide is ideal for small samples. A standard microscope slide can be placed on top of the depression slide to serve as a lid; tape hinges can be added on one side and a tape latch attached to the other (Fig. 3 . 2 ) . The cover slide provides protection as well as a suitable flat area for the required labeling or coding. The primary advantage of the glass depression slide container is that samples can be examined and pho­ tographed with an optical microscope multiple times without the con­ tainer being opened, so that opportunities for contamination or loss are minimized. When the cover is removed, the sample is readily accessible to scalpels, tungsten needles, cured silicone rubber slivers, or other probes Tape latch, with end folded over for easy lifting Figure 3 . 2 A sample holder made from a single­ Glass cover slide depression glass slide with a standard glass microscope slide as a cover. Single-sided (3 x 1 in. [7.62 x 2.54 cm]) Tape hinges transparent adhesive tape is used to make h i n ges and a latch . The tape latch should be placed on the cover slide and not on the depression slide to m i n im ize the chance that the sample might become attached to the adhesive. 0 Single depression slide (3 x 1 in. [7.62 x 2.54 cm]) Sample Collection and Preparation 23 used to select and transfer a portion for analysis. The slide sandwich also allows the samples to be carried and stored in microscope slide trays. Avoidance of contamination Sample purity is always a primary concern, especially in microanalysis, where contaminants, such as dust particles, can be as large as or larger than the sample. There are numerous means by which a sample may become contaminated, and it is always best to analyze a sample blank as a check. A sample blank should be exposed to all environments and come into contact with the same materials and solvents as the sample itself. The most common sources of contamination are unclean sam­ pling tools, storage containers, and analytical support materials, such as IR windows. Remnants from previous samples can be incorporated into a new sample, producing a deja vu spectrum. Storage containers-such as plastic vials, bags, and lid liners-can pollute the sample with particu­ lates, plasticizers, and processing oils. Glass slides, even though marked "precleaned," may be covered with a thin layer of formic acid, calcium carbonate, sodium sulfate, or silicates ( Sommer and Katon 1 9 8 8 ) . Whenever solvents are used, chromatographic o r spectroscopic grades should be selected to minimize contamination from solvent impurities. Residual impurities in solvents, as well as contaminants, such as sili­ cones, from capillary pipette holders, are readily detected by the exami­ nation of residue left after evaporation of a solvent drop on a glass slide or IR window. Environmental substances can taint a sample before or after it is removed from the obj ect. Fibers (natural, synthetic, and hair) are the most commonly recognized contaminants in nonfiber samples. Inorganic particulates, such as quartz, clay, gypsum, and calcite, are generally soil related; it is difficult, if not impossible, to tell whether the soil source is current contaminant ( nonsignificant) or from the weathered crust of the obj ect (potentially significant) . Organic materials may also be distributed as airborne matter. Activated carbon particles may come from the air­ conditioning and filtration system. Plants, insects, animals, and humans are the sources of oils and protein bits that may produce potentially ambiguous results in the analysis of art materials containing natural products. Work areas and containers should be clean, and sample han­ dling with bare fingers and powdered gloves (containing talc, starch, etc . ) should b e avoided. Optical surfaces should not b e sprayed with com­ pressed air from canisters, as the spraying may leave a fine residue of oil on the surfaces ( Leyshon and Roberts 1 9 8 3 ) . Lang and coworkers have identified a number o f common contaminants that make IR microanalysis very difficult (Lang, Katon, and Bonanno 1 9 8 8 ) . An excellent chapter on the detection and identification of contaminants commonly found in laboratory samples has been pub­ lished by Aldrich and Smith ( 1 9 9 5 ) . Launer provides an extensive list of spurious IR absorption bands that may be due to contaminants (Launer 1 9 6 2 ) . Of particular interest on the list are the bands that are attributed to internal impurities in halide windows (see Table 4.2). 24 Chapter 3 Sample Collection and Preparation Procedures Many, if not most, samples will be analyzed by more than one method. Thus, unless additional samples can be obtained easily, the entire sample must never be used during any single sample preparation step. If a small, irreplaceable sample must be used in totality, it should first be analyzed by a noncontaminating, nondestructive method, such as optical micros­ copy or IR micro spectroscopic analysis-after which it can be retrieved and stored for further testing. Good laboratory practices are important. Sample documen­ tation, which began during the collection phase, is continued, with all preparation steps recorded in a lab notebook. Photomicrographs are obtained on the sample whenever possible. If not, drawings and visual observations are recorded. This procedure helps to distinguish the physi­ cal characteristics of the sample. Subsamples, such as solubility fractions or isolated inhomogeneous particles, are always labeled accordingly, along with identification of the parent sample. The following describes a possible sample preparation proce­ dure for a multilayer paint sample after its arrival in the lab. The sample is examined under a stereomicroscope, and a drawing or photograph­ with colors and relative sizes noted-is made of the visually discernible layers. Particles are removed for further characterization and identifi­ cation by polarized light microscopy, if this has not already been done. Then a small portion of the sample (no more than half) is embedded. After polymerization of the mounting medium, the embedded sample is microtomed. This method achieves two goals: First, thin sections are pro­ duced for analysis by IR transmitted light. Second, a flat, even surface is obtained on the remainder of the embedded cross section, so that the effort required for polishing the surface is minimized. At this point, photomicrographs, in visible and UV light, are taken of the cut surface, preferably adj acent to the thin section layer removed for IR analysis. Later, if desired, the embedded residual sample can be used for IR reflectance mapping studies, SEM, and fluorescent staining. The compiled data set from these analyses should give a clear image of the structural composition of the paint sample . The unembedded portion of the sample is retained for later chromatographic studies or for additional embed­ ments, if problems arise from the first sample. In the interrelated sampling scheme, the steps required for sample collection and preparation depend not only on the analysis meth­ ods but also on the type of sample (Table 3 . 3 ) . The following sections discuss a variety of sample collection and preparation procedures that apply to IR analysis, as well as to other analytical methods. The IR­ specific techniques mentioned in this section are described in chapter 4 . Gases IR analysis is rarely used to monitor pollutant levels within museums and display cases because these are relatively clean environments, with low­ level contaminants that are better measured by quantitative techniques such as chromatography. IR analysis can, however, be used to perform 25 Sample Collection and Preparation Sample type Examples Potential collection methods Potential preparation methods Potential analysis methods I n situ nondestructive analysis surface studies none none (possible precleaning) Photography ( I R , UV, etc . ) ; XRF Gas pollution measurements; h u m idity studies none; syringe; flow­ through cells; pump; sorbent tube none; desorption; derivitization; preconcentration IR; G C ; H PLC; colorime­ try; visual indicator Liquid residue; exudates; pre­ polymer components syringe; capillary tubes; swab; sorbent none; solvent evapora­ tion ; derivitization I R ; GC; H PLC; TLC Solid Solvent-soluble coati ng; adhesive solvent-soaked swab extraction; solvent evaporation; derivitization I R ; GC; H PLC; TLC Solid Particles corrosion layer; stone; pigment; coating; alloy; adhesive scraping; scalpel; for­ ceps; probe; silicone sliver mounting; physical sep­ aration; grinding; flattening; dissolution; derivitization I R; G C ; H P LC; TLC; SEM/EDS; PLM; fluores­ cent microscopy; chemi­ cal microscopy; XRD Solid Cross section painting; alloy; weath­ ered crust scalpel; needle; drill mounting; physical sep­ aratio n ; grinding; embedding; microtom­ ing; derivitization I R ; GC; H PLC; TLC; SEM/EDS; PLM; fluores­ cent microscopy; chemi­ cal m icroscopy; XRD Solid Fibrous textile; contaminant; basket forceps; probe none; mounting; embedding; flattening; cutting; extract dye IR; PLM; S EM/EDS; UV!Vis Table 3.3 Sample types and related sample collec­ = gas chromatography; H PLC = high tion, preparation , and analysis methods (GC = polarized light microscopy; SEMI = scan n i n g electron microscopy with energy d ispersive spectroscopy; TLC = thin -layer chromatography; UV!Vis = u ltraviolet/visible spectroscopy; XRD = X-ray diffraction; XRF = X-ray fluorescence). comparative studies of environments, evaluate changes in atmospheres, and identify some offgassing materials. Koestler demonstrated that IR spectroscopy could be used to detect the by-products of insect activity in an inert atmosphere (Koestler 1 99 3 ) . A later example in this book shows performance liquid chromatography; the effectiveness of gas-phase IR measurements in the evaluation of the PLM interaction of a reactive gas ( Vikane) with different types of materials EDS ( chap. 6, case study 7). When a gaseous environment is to be analyzed, a sample may be collected by ( 1 ) opening an evacuated gas container in the area of interest, (2) pulling an air sample into a gas syringe, or ( 3 ) using a pump to make the air flow over a sorbent that will specifically trap the compo­ nents to be analyzed. Due to its volatility, a collected gas sample should be stored at cool temperatures and analyzed as soon as possible. Alternatively, the IR gas cell may be used as a collection device for an in situ experiment, where the analyte gas is produced from a sample within the gas cell via some process, such as a chemical reaction or heat. In this case, the sample is kept out of the beam path, so that only the atmosphere in the cell is measured. Outside the laboratory, portable long-path length IR monitors are available for the measurement of gaseous environments ( see Suppliers, Midac Corp . ) . Liquids Liquid samples encbuntered in the analyses of art materials are usually in the form of solvents, uncured materials ( coatings, adhesives, etc . ) , or exudates on the surface of obj ects. In any case, a liquid sample should be collected and stored in a well-sealed glass vial with a Teflon-lined lid. 26 Chapter 3 Small droplets of a liquid can be collected with a capillary tube that is used to draw up the liquid. The capillary can be placed in a glass vial for labeling. A scalpel may occasionally be used to collect a small vis­ cous drop and to place it in a glass depression slide. Teetsov describes the use of a small, 0.2-0.4 mm polyester filter square to collect a very small volume of nonvolatile liquid from the surface of an obj ect (Teetsov 1 99 5 ) . Alternatively, a swab may be used to collect the liquid sample ( see below for cautions regarding the use of swabs ) . However, with either of the last two procedures, it may be difficult to extract the liquid from the swab or filter later, if the liquid (or a portion of it) is insoluble in common solvents. Liquids generally require very little sample preparation. For IR analysis, volatile liquids can be analyzed directly by use of a commer­ cial liquid cell or simply by sandwiching a drop between two salt plates. A liquid sample that is nonvolatile or of low volatility can be analyzed by a procedure of spreading one drop on a single salt plate or other transparent surface, such as a single surface of a diamond cell (two diamonds should not be put together, or the liquid will be displaced ) . Alternatively, a few drops o f the liquid may b e dripped onto a bed o f powdered potassium bromide (KBr) for analysis b y diffuse reflection. Liquids may also be analyzed with an internal reflection cell. This tech­ nique works particularly well with liquids that contain water. Sampling with swabs Solvent-dipped swabs are used to conduct solubility studies and to collect samples when the analysis pertains to a solvent-soluble surface of an object, such as a patina or coating on a bronze sculpture. The sampling area can range from a few millimeters to a centimeter in diameter, depend­ ing on the size of the swab and the prominence of the area in question. Commercially purchased cotton swabs or applicators should not be used for this type of sampling because the cotton is typically adhered to the stick by an adhesive, such as poly(vinyl acetate } . Instead, swabs for analysis should be prepared by winding a small piece of cotton fiber, gauze, nylon, polyester, or additive-free clean-room wipe onto the end of a wooden stick ( Fig. 3 . 3 ) . The smaller the point of the wooden stick, the smaller the swab. Selected fibers, wipes, and sticks should be tested before sampling to ensure that they will not be a source of conta­ mination. A sharp, pointed stick, such as an uncoated toothpick, is needed to prepare a tiny swab. The sampling end of the stick and the swab should be handled only with tweezers to prevent contamination from skin cells and oils. After preparation, the swabs may be wrapped in coating-free aluminum foil for storage. When sampling preparations are complete, the selected area on the obj ect is lightly swept with a sable artists' brush to remove any loose particles or dust. A drop of an appropriate solvent (water, ethanol, acetone, chloroform, hexane, etc.) is put on the swab, which is then rubbed over the small area on the object. Multiple samples taken with swabs treated with different solvents may be collected from the same sampling area. After collection, each sampling swab is placed in a clean 27 Sample Collection and Preparation � Forceps Wood," ""k Rotate clockWise Cotton fibers Swab �� Aluminum foil ��========== ==== ::== :::J Wrapped swab (may be stored until use) Rotate clockwise Place solvent drop on swab, then place swab on object, hold at a low angle, and rotate swab to collect sample. Figure 3 .3 I n - house fabrication of a cotton swab and collection of a solve nt-soluble sample from After sample collection, place swab in clean vial, break end of stick, seal vial, and label. the surface of an object. An alternative proced u re is to use small squares of clean­ room wipes for swabbing; they should be held with forceps for sample collection, then placed in a vial for storage. glass vial; either the stick is removed or its end is broken off; and the vial is sealed and labeled. Samples obtained by solvent-dipped swabs or filter squares contain the evaporation residue of the solvent-soluble portion removed from the sampled area on the object. For analysis, the residue is extracted from the swab with the same solvent that was originally used to acquire the sample. A corresponding blank should be prepared to check for conta­ mination from solvents, capillaries, or other contact sources. Swab sampling is not recommended when any other choice is available. While the solvent swab removes the soluble portion of a sam­ pled area, it may be difficult to determine whether the swab sample con­ tains only the surface coating or whether it also contains some leachate from lower layers. Additionally, particles may be removed by abrasion. Thus, this selective but nonspecific removal can create confusion in the analysis scheme. When possible, it is better to remove a scraping and perform solvent solubility tests under the microscope. 28 Chapter 3 Solids, powders, and particles Samples consisting of fine powders or crystalline particles are often collected when the analysis question pertains to pigments, stone sur­ faces, corrosion products, adhesives, or coatings. Loose samples can be acquired with a fine-tip brush. Single particles can be picked up with a tungsten needle or a cat-hair probe. In cases in which particles must be scraped from a surface, a scalpel is used. The scalpel blade is held at a low angle, and the blade is pulled backward or away from the cutting edge ( Fig. 3 . 4 ) . This technique a brades only the very top surface and minimizes the chance of accidental damage ( from slicing or gouging) to the obj ect. The particles will often cling to the scalpel; this tendency aids in the transfer of particles from the object's surface to a glass slide. When the sample surface is not horizontal, it is best to hold (or have someone else hold) the slide directly below the sample area to prevent possible loss of valuable particles that fall as they are loosened. It is advisable to wear gloves ( cotton, latex, or other gloves appropriate to the object) to protect the obj ect, sample, and future samples from contamination. The preparation procedure selected for solid materials depends on the form and homogeneity of the sample. For IR analysis, a homogeneous sample can be ground or filed to form fine particles, then analyzed by either KBr pellet, KBr micropellet, diffuse reflection, internal reflection, diamond cell, or microscope. Although inhomogeneous samples, such as mixtures and multilayered paints, can be analyzed directly, the characterization of each component is simplified by the use of a physical or chemical preseparation step prior to analysis . Drag scalpel away from the cutting edge to lightly abrade the surface. of movement Figure 3 . 4 The proper u s e o f a scalpel t o remove particles from the surface of an object for analysis. Alternative procedu res involve a fine brush for gathering loose particles or a tungsten needle for removing a single particle. to the surface of the object. Static from the abrasion usually causes the particles to cling to the scalpel. 29 Sample Collection and Preparation Mixture separation by solvent extractions Similar to separation experiments described by Gettens, solvent extrac­ tions can be performed on multiple-component particles to identify indi­ vidual components ( Gettens 1 95 9 ) . For this procedure, a sequence of solvents is used to selectively remove one or more components in a mix­ ture; after each extraction step, IR spectra are collected from the soluble and insoluble portions of the analyte. A secondary benefit is that the sol­ ubility information from the extraction can also aid in the identification of components. This method is especially useful when the IR spectrum of a bulk sample of a coating or consolidant is difficult to identify because of the presence of other components, particularly inorganic fillers or pig­ ments. Figure 3 . 5 is a solubility schematic for many natural and syn­ thetic materials. For solute extraction of macrosamples (e.g., a swab sample xf.11). or a particle large enough to be seen with the naked eye), the sample is placed in a micro test tube (5 of solvent (about 1 0- 1 00 35 mm), then covered with a few drops The test tube can sit for about an hour or can be briefly agitated in an ultrasonic bath. A micro drop ( 1-5 f.1l) of the extract is removed with a capillary tube or micropipette; the microdrop is then placed on an inert IR window ( such as barium fluoride, BaF2 ) for IR microspectroscopy analysis, or it is dripped onto KBr powder for pressing a salt pellet or for diffuse reflection analysis. The solvent is then Figure 3 . 5 A so lubility schematic for many natural allowed to evaporate. The drop procedure may be repeated to concen­ and synthetic materials. trate the amount of sample for analysis . Sample + Soluble in hexane? (organic solvent-low polarity) yes ! Polyethylene (partial) Hydrocarbon waxes and oils Paraffin Mineral oil Ceresine wax Carnauba wax Beeswax (usually) Some plasticizers and slip agents �I Soluble in ethyl acetate? (organic solvenl-high polarity) yes ! Insoluble in chloroform Cellulose acetate Cellulose nitrate Methyl cellulose Ethyl cellulose Polyvinyl chloride Epoxy (uncured) Urethanes (some) Soluble in chloroform The following solvents may be substituted: Acetone for ethyl acetate Methylene chloride for chloroform Toluene for benzene Formic acid for cresylic acid Polystyrene Polyvinyl butyral Poly(vinyl acetate) Acrylics Cellulose acetate butyrate Silicones Natural resins ABS rubbers Alkyds Plasticizers Beeswax Soluble in chloroform but insoluble in ethyl acetate Polyesters Cellulose triacetate no Soluble in benzene? no � Soluble in water? (organic solvent-aromatic) yes ! yes ! Crystalline residue Polyvinyl chloride Natural resins Elastomers Polystyrene Polyethylene (hOI) Polypropylene (hot) Indene resins Rubber (natural) Polybutadiene Polyisoprene Cellulose esters Polyesters (some) Salts Amorphous residue Proteins (hot) Sugar, pectin, gums Starch, dextrin (hot) Polyvinyl alcohol Methyl cellulose Acid-sensitive minerals Nylon Drying oils Formvar (baked) Alkyds (baked) Polyester (baked) Insoluble Minerals, pigments Proteins (egg) Urethanes Teflon Epoxy (cured) T no yes Soluble in cresylic acid? (organic solvent-acid) � 30 Chapter 3 For smaller samples, a micro drop ( 1-5 fLl) of solvent is placed directly on a sample that is on an inert window or glass micro­ scope slide ( care must be taken that the drop cover only the sample of interest and does not spread over other samples, and that the solvent chosen does not react with the substrate ) . Any soluble portion of the sample will dissolve and be deposited away from the insoluble material as the solvent evaporates. Depending on the solvent and the solute, the deposition may appear as a solid film, as droplets in a ring at the former Uniform film layer. sometimes thicker at the edges edge of the solvent, or as a dried puddle ( Fig. 3 . 6 ) . The most highly soluble materials-such as waxes, synthetic resins, gums, and inorganic nitrates-will form a solid film that often has a more concentrated region at the exterior rim. Such analytes as nondrying oils, waxes, and natural resins tend to form a ring of droplets. " Before" and " after" photos for a mixture of natural resins extracted with chloroform are shown in Figure 3 . 7 . In the analysis of many art materials, water-soluble proteins have been found to occur most often as dried, wrinkled puddles near or under the original sample. To identify these new puddles, it is desirable to have a good visual memory or a photograph of the sample prior to the solvent Ring of droplets at the former edge of the solvent drop drop . Because multiple components might have been extracted and deposited in different areas, it is also important to collect IR spectra from all visually different areas after each extraction. Multiple extractions and analyses can be done sequentially on the same sample. The selection of solvents for a series of microextrac­ tions depends on the components expected to be in the sample . For a sample thought to be composed of natural products, a typical solvent series would start with a drop of hexane to extract nonpolar components such as mineral waxes. After the drop has evaporated and the spectrum collected, a second solvent is selected-typically either ethyl acetate or chloroform-to check for the presence of other waxes, natural resins, Dried puddles of solute that may appear shriveled and may exist in addition to a ring Figure 3.6 Possible deposition patterns for sol u ble components extracted from a sample with a d rop of solvent. With IR m icrospec­ troscopy. a spectrum can be collected of the solvent-so l u ble and solvent- i nsol u ble fractions. nondrying oils, and many synthetic resins. If multiple components are extracted at this point, then ethanol or acetone is used for further sepa­ ration. The final solvent is usually a drop of water to check for the pres­ ence of carbohydrates or soluble proteins. After the drop of water is placed on the sample, the pellet is positioned under a warm light to heat the water; this procedure increases the solubility of many proteins while also hastening the evaporation of the droplet. After each drop dries, spectra are collected at several positions around the deposition ring. Once the solvent series is completed, the insoluble residue of the sample is analyzed. It is also important to analyze a blank for each solvent. The same extraction procedures can also be done on a gold mirrored surface; the IR spectra are then collected by reflection measure­ ments. Because of the nonreactive surface of gold, acids and bases may be used to further characterize the sample components. A sample with a high content of drying oil can be treated with a 5 % solution of sodium hydroxide to saponify the oil and separate it from the pigment particles ( Gettens 1 95 9 ) . Alternatively, a drop of concentrated nitric acid placed on the sample and warmed to dryness will solubilize most oil and resin media. A drop of concentrated sulfuric acid will extract many colorants from dyed fibers (Saltzman and Keay 1 9 72 ) . The acids and bases will Sample Col l ection and Preparation 31 Figure 3 . 7 The separation of components of a carved resin sculpture by solvent extraction. The top photograph shows a sample placed on a BaF2 window for I R microanalysis. The lower photograph shows the same sample after a microdrop of chloroform was placed on the sample, then allowed to evaporate. Two d istinct components were separated. The chloroform -soluble compo­ nent, later characterized as a pine res i n , primarily collected i n a r i n g a t t h e former edge of the droplet. A chloroform­ insoluble portion , later characterized as copal, was concentrated as a residue i n t h e center. I R spectra were collected o n t h e b u l k sample, a s well a s from several regions of the extract and residue. also react with some pigments and thereby provide additional informa­ tion on the sample ( Gettens 1 95 9 ) . Disposable glass capillaries used for thin-layer chromatogra­ phy can be employed to dispense the microdrops of solvent required for this procedure. However, because some capillaries have been found to be a source of contamination, it is recommended that each capillary be rinsed inside and out with a drop of solvent prior to use. An alternative to glass capillaries are the polypropylene tips for the Eppendorf GELoader (available from any scientific supply company) , as recommended by Teetsov ( 1 99 5 ) . While they must also be rinsed, the tips can be bent with heat to provide an improved pipette for easier control of the drops. Mixture separation by pyrolysis Pyrolysis is useful for the separation of small amounts of insoluble organic materials from an inorganic matrix, such as a glass-filled epoxy resin, a low-binder oil paint, or a polyurethane-consolidated stone. For manual pyrolysis, it is best to have at least 1 mg of sample, as the proce­ dure becomes easier as the sample size increases. Smaller samples can be analyzed manually with careful manipulation ( Humecki 1 9 95a) or with temperature-controlled, commercially available pyrolysis equipment. To pyrolyze a sample manually, it is placed as pulverized chunks or as a pile of powder inside a glass capillary tube or disposable glass pipette with an inner diameter of approximately 1-8 mm. The sample should be at least 1 inch (2.54 cm) from the end of the tube. With the tube held horizontally with forceps or pliers, the sample area only is placed in the hot spot of a flame from a Bunsen burner or a butane lighter ( Fig. 3 . 8 ) . After the sample produces smoke, the tube is 32 Chapter 3 Pyrolysate droplets /� Sample Figure 3 . 8 The manual pyrolysis technique useful for the separation of nonsoluble organic com­ pounds from an inorganic matrix. A por­ tion of the sample is compactly placed inside a glass pi pette, then heated. After the sample smokes, the tube is cooled, and the pyrolysate that collects as droplets in the cooler regions of the tube is col­ lected and analyzed. removed from the flame and cooled. The volatiles in the smoke will pri­ marily condense and collect as droplets in the regions of the tube not heated by the flame. These droplets can be sampled with a metal probe and placed on an IR transparent pellet for analysis. While in most cases, the spectra of pyrolysates will correspond to the parent compounds, it is best to prepare pyrolysate references for comparison. Fibers For micro spectroscopic analysis, fiber samples may be collected from paper, textiles, and ethnographic obj ects with fine-tip forceps. A single fiber can be grasped and pulled loose from its thread or mat. Some small bristles or lint particles embedded in or attached to painted or coated surfaces may require a scalpel for removal. When a larger fiber sample is needed for macro IR analysis, a sharp scalpel can be used to cut the thread while it is held in position with forceps. Since this maneuver often requires three hands, this job is best performed by two people. Some forensic examiners have used adhesive tape to collect loose fibers and particles from a surface ( Ryland 1 99 5 ) . The adhesive from the tape can, however, contaminate the surface of the sample . Fiber, hair, and brush samples require little sample prepara­ tion. They may sometimes even be analyzed "as is" by taping the ends of a single fiber to hold it across a hole in a metal disk, or by simply laying it on an IR window (Tungol, Bartick, and Montaser 1 99 5 ) . However, the fiber is often too thick and absorbs too strongly for direct transmission. In such a case, one alternative is to use a reflection method, such as dif­ fuse reflection or internal reflection. When a large sample, such as a length of yarn or a piece of textile, is available, internal reflection is a very good nondestructive method. A second alternative is to make the fiber thinner. The advan­ tages to flattening a fiber are twofold. First, the horizontal area of the fiber is increased. Second, the surface is now planar. The use of the Sample Col l ection and Preparation 33 diamond cell is a quick and easy method for flattening fibers. Another method is to press the sample between two IR transparent windows in a compression cell. A final option is to use a scalpel to slice a thin section from the end or side of the fiber. This method is sometimes preferred for the examination of the fiber structure, since flattening destroys its physi­ cal shape and may change its crystalline orientation. Cross sections When the surface of an object, such as a painting or a folk art carving, has a complex structure with multiple layers, a cross section sample is taken that incorporates this stratigraphy to facilitate the study of the sample. Paint cross sections have been used for the examination of paintings for over eighty years ( Laurie 1 9 14; Gettens 1 932). The technique of embed­ ding paint cross sections was revived in the 1 950s; it quickly became a standard method for the study of painting techniques (Plesters 1 95 6 ) . With the use of a stereomicroscope, a cross section sample i s removed b y cutting with a scalpel from the top down t o the bottom sub­ strate. When possible, a sample is taken from the edge of the painting or near a preexisting crack, provided that the sampling area has not under­ gone previous restoration ( Plesters 1 95 4 ) . Alternate methods for cross section removal have been tried but have not proved to be as successful as skillful extraction with a scalpel. Laurie used a hypodermic needle, and Gettens constructed a workable, although complex, apparatus (Laurie 1 9 1 4; Gettens 1 93 6 ) . While these tools are useful with some paintings, crumbling can occur with brittle paints . Once removed, the resultant cross section sample is often too small to be picked up with forceps and may not have enough static charge to cling to the scalpel. In these cases, an artists' brush modified to contain only a few bristles is used to pick up the particle and transfer it to a glass depression slide. Occasionally, for a few obstinate samples, a short breath of air on the brush ( directed away from the sample) will supply enough moisture to the bristles to adhere the particle temporarily for transfer. However, when a very sensitive analytical technique, such as gas or liquid chromatography, is used, it is important to minimize the potential for pro­ tein contamination. In these cases, the brush may instead be moistened with a mist of distilled water (Johnson and Packard 1 97 1 ) . Before I R micro spectroscopy was commonly used a s a n ana­ lytical technique in conservation, the two usual IR sampling techniques for the analysis of paint cross sections consisted either of examining the entire chip or of selectively removing visually different sections for analy­ sis. Both methods can misrepresent the composition of the paint. In the first method, when an entire multilayer chip is ground into a homoge­ neous mixture, usually with KBr salt to make a pellet, any stratigraphic or layering information about the sample is lost. In the second method, physical separation of layers is time-consuming and difficult unless the layer is large. Small layers may be missed altogether. To obtain meaningful analyses of multilayer media, it is important to work with a high-quality cross section of the sample. IR micro spectroscopic analysis can be done on cross sections with reflected Chapter 34 3 or transmitted light. Cross section samples from paintings contain many materials, such as binders and pigments, with various particle sizes. These variations can produce a reflectance spectrum that, even after mathematical corrections, looks different from the spectra collected by transmission from the same components because of the dissimilar reflection and absorption characteristics of each material. For the analy­ sis of binders, which generally absorb IR radiation better than they reflect it, transmission FT-IR is usually more successful. To produce good-quality IR transmission spectra, most paint samples need to be 1 - 1 0 !Lm thick. Microtoming is normally used to prepare a thin section of a multiple-layer sample, and an embedding medium is needed for the support of small and fragile paint samples during microtoming. Audrey Glauert provides an excellent reference on embedding and microtoming procedures ( Glauert 1 9 72 ) . Embedding media and procedures Polyester resins have been commonly used in art conservation since the 1 950s for embedding paint cross sections prior to microscopic and analyt­ ical studies ( Plesters 1 954 ) . Indeed, polyester resins have many desirable properties for embedding resins, and they are nearly ideal embedding media for most samples found in fine-art paintings (Table 3 . 4 ) . Polyester resins are clear and colorless and easy to section; they cure at room tem­ perature and do not react with most samples. A polyester resin may, how­ ever, dissolve some compounds, such as some waxes on furniture-finish cross sections ( Godla 1 990), organic dyes on inorganic carriers in modern (post- 1 8 50) pigments ( Stodulski 1 994), and fresh natural-resin layers ( Derrick et al. 1 9 9 2 ) . Additionally, Derrick found that polyester resins infiltrate porous samples ( Derrick, Souza et al. 1 994 ) . Embedding with Polyester Resin. To embed a typical paint sample in polyester media ( brand names are noted in Table 3 .4; see also Table 3.4 Suppliers ) , six drops of catalyst ( methyl ethyl ketone ether) are mixed Types and brand names of selected media thoroughly with 10 ml of liquid polyester resin in styrene solvent. The tested for embedding and m icrotoming of transparent resin is initially light blue; it turns yellow when the catalyst paint cross sections. is well mixed, and then it quickly becomes colorless as the reaction pro- Type Brands Source Comments Paraffin Paraplast Ladd Research I nd ustries Opaque; m i n imal shrinkage; soft; cuts well; elevated temperatures req uired for preparati o n . Epoxy Epon 8 1 2 LX- 1 1 2 Maraglas 655 SPURR Ted Pella, I nc. Ladd Research I ndustries Ladd Research I ndustries Ted Pella, I n c . Generally needs elevated temperatures to cure; transparent though sometimes yellow; forms very hard block that is difficult to slice at 1 fJm thicknesses. Quetol 523M L R White Butylmethyl-methacrylate Exothermic cure reactions; transparent; shrinks more than polyesters; cuts well; may infiltrate some samples; dissolves lipids; toxic. Krazy Glue (cyanoacrylate) Ted Pella, I n c . Ladd Research I nd ustries Ladd Research I nd ustries Borden, Inc. Caroplastic Bio-Plastic Castolite Carolina Biological Supply Ward 's Natural Science Casto lite Co. Cures at room temperature; transparent; cuts well; minimal shrinkage; may infiltrate some samples. Acrylic Polyester > Sample Col l ection and Preparation 35 ceeds (Ward's Natural Science 1 99 0 ) . Excess catalyst, while it will speed up the curing process, will also make the final mount more brittle and difficult to microtome. A mold is initially half filled with the well-mixed embedding medium and cured at room temperature for 3-6 hours. A rep­ resentative portion of the sample containing all the layers is transferred to the hardened base layer in the mold with forceps or a probe and posi­ tioned in the desired orientation. A label is placed on the opposite end of the mold, then both the label and the sample are covered slowly with freshly prepared polyester embedding medium. The embedment is cured and nontacky within 24 hours. For microtoming of the sample for IR microanalysis, the best results are obtained by allowing the embedment to set 3 6-4 8 hours before slicing. The medium continues to cure slowly over time ( Demmler 1 9 8 0 ) . After one month, the microtoming becomes noticeably more difficult, and the samples tend to crumble . The bottom and top halves of the block should be prepared within a few days of each other to prevent a hardness differential between halves that interferes with microtoming. Silicone molds, ice cube trays, and peel-away molds are all useful for preparing embedments; some examples are shown in Figure 3 . 9 . Because the presence of excess medium around the sample produces stress during microtoming, most of the plastic around the sample has to be trimmed away to reduce the area of contact with the microtome blade. Trimming time can be minimized by the use of small Pelco silicone rubber molds for embedding ( see Suppliers, Ted Pella, Inc . ) . These molds produce embedments with trapezoidal tips that only require minimal trimming prior to slicing. While small embedments are good for microtoming, they are difficult to hold in a level position for the polishing of samples. Infiltration. Paints are porous when the amount of binder is low enough that it does not fill the void spaces around the pigment particles ( Hansen, Lowinger, and Sadoff 1 994 ) . The embedding resin can then seep into the sample, fill these spaces, and, by doing so, coat the particles. This is termed infiltration. Infiltration can occur with matte or porous paints and glue gessoes . If analysis of the binder or organic com­ ponents in the sample is needed, infiltration may be undesirable, and in Figure 3.9 Molds and embedding media blocks used for the preparatio n of embedded cross sections. 36 Chapter 3 some cases, steps should be taken to prevent infiltration from occurring ( Derrick, Souza et al. 1 9 94). In other cases, sample infiltration is benefi­ cial. It consolidates the sample to produce a smooth block that is readily polished or sliced in preparation for analysis. If several samples of a porous material are to be embedded for analytical studies of the media, it is prudent to embed only one sample initially to see if infiltration occurs and, more important, whether it inter­ feres with analysis. Depending on the type of analysis, it is possible that infiltration will not cause a problem, but it is important that the analyst recognize that resin may be in the sample, taking that into account in any spectral interpretation. IR spectroscopy is more sensitive to the presence of the infiltrated resin than is visual or microscopic examination; thus, when IR is used, it may be important to prevent infiltration. Visual examination of a paint cross section can often detect infiltration of the embedding resin from the discoloration or darkening of the sample. This is particularly noticeable for white paints and grounds. Samples that visually appear very white and opaque before embedding can take on a darker, transparent appearance after resin penetration. Because of the presence of embedding resin inside and outside of the sample, there is less contrast at the sample edges, and the edges may seem poorly defined. For example, two small portions of a sample from a polychrome sculpture were embedded separately-one in an acrylic medium and one in polyester ( Figs. 3 . 1 0, 3 . 1 1 ) . The sample in the poly­ ester medium ( Fig. 3 . 1 1 ) shows infiltration of the resin, while the sample embedded in the acrylic ( Fig. 3 . 1 0 ) does not. The acrylic-embedded sample has very well defined edges, and the opaque white ground remains white after embedding. The polyester-embedded sample visually appears to have a more transparent, darker ground layer. The IR spectrum of an infiltrated sample will contain absorp­ tion bands for the sample components, as well as for the polyester resin . • Figure 3 . 1 0 A paint cross section from a painted sculp­ ture i n a church i n Minas Gerais, Brazil, embedded i n acrylic med i u m . Sample Collection a n d Preparation 37 Figure 3 . 1 1 A cross section from the same paint chip as shown in Figure 3 . 1 0, embedded in polyester med i u m . The polyester resin produces numerous strong absorption bands. Theoretically, the absorption bands for the polyester could be subtracted, but the subtraction process can distort the remaining bands in the spec­ trum, thus limiting the detection of other components. Many binding media are present in low concentrations and have absorption bands at wavenumbers similar to those of polyester, making the binder especially difficult to detect. Since infiltration of polymer severely inhibits the IR analysis of the sample, several methods for preventing this occurrence were examined ( Derrick, Souza et al. 1 9 94). The most successful method discovered for inhibiting the infiltration is to precoat the sample with a thin layer of acrylic emulsion ( Rhoplex AC-3 3 ; see Suppliers, Conser­ vation Materials) thickened with fumed silica to form a gel. A thin layer of this gel dries quickly to encapsulate very porous samples, even plaster, thereby preventing polyester infiltration without inhibiting the optimal slicing properties of the polyester. Microtoming procedures Rotary microtomes were first developed in the 1 950s. They are available with manual and motorized cutting arms. The cutting arm moves the clamped sample past a sharpened knife or blade to produce a thin section of the sample. Detailed information on micro tomes and microtoming techniques is available in Reid ( 1 972 ) . Four types o f knives ( steel, tungsten carbide, glass, and dia­ mond) are readily available for use with any type of rotary microtome ( Figs. 3 . 1 2, 3 . 1 3 ) . The steel blade is an all-purpose, inexpensive micro­ tome blade that can routinely provide slices 1 5-30 J.lm thick. However, depending on the absorption of the sample, this may be too thick for IR analysis. Both the tungsten and the glass knives routinely produce good, clean slices 1 - 1 0 f.Lm thick. The diamond knife is typically used for ultramicrotomy of sections, since it should only be used to cut sections 3 38 Chapter Figure 3 .1 2 thinner than 1 /-Lm. A general dictum is that harder samples require A motorized rotary microtome with a harder knives. Of the four blades, glass knives are the easiest to use. Glass stereobinocular m icroscope for viewing and positioning the sample. knives are made by scoring and breaking a 2.54 em ( 1 inch) square of Figure 3 . 1 3 glass to create two triangular pieces, each with a very sharp edge ( Figs. A selection o f m icrotoming blades: dia­ 3 . 1 4 , 3 . 1 5 ) . This procedure produces a 45° angle on the blade. The angle mond (in the box at the upper left) , glass may be increased for cutting harder materials and decreased for cutting (lower left) , tungsten (lower right), and softer materials ( Malis and Steele 1 99 0 ) . The glass knives section best on stainless steel (in the blade holder at the polyester-embedded paint samples containing finely ground pigments; in upper right) . such instances they produce transparent, cellophane-like thin sections. Small samples are easier to microtome because smaller cutting­ surface areas require less force. Cutting-surface areas that are too large may produce sections that curl or cause layers to debond. Thus, to reduce the size of the cutting surface, self-supporting, strong, hard sam­ ples-such as polymers, laminates, and metals-should be trimmed to a sharp point. Harder samples require finer points . The facet point for a self-supporting polymer should be less than 0 . 5 mm; for aluminum it • Figure 3 . 1 4 A glass k n ife maker for t h e accu rate scor­ ing and breaking of microtome blades. Sample Collection and Preparation 39 Figure 3 . 1 5 A glass knife positioned i n the rotary microtome. The sample is held in the chuck and slowly moved past the station­ ary knife. should be less than 0 . 1 mm; and for ceramics, the facet should be only a few microns (Malis and Steele 1 99 0 ) . Delicate, small, or soft samples, such as paints, waxes, papers, or textiles, should be cut into a pie shape and positioned in a mold for embedding, such that the point is cut first ( Fig. 3 . 1 6 ) . An embedded sample should have all excess medium trimmed from the embedment so that only a trapezoidal facet with 1 -2 mm of medium outside the sample at the cutting surface is left ( Fig. 3 . 1 7 ) . A trapezoidal shape of plastic around the sample helps in later microtoming by providing a pointed region to initiate and end the cutting stroke. Unexpected thickness variations and j agged cutting surfaces are often due to vibrations or movement of the sample block during microtoming. Thus, the embedment or sample block should be fastened tightly in the microtome chuck, and the fastening should be checked reg­ ularly, since some materials, such as polymers, can creep under pressure. Moreover, positioning the majority of the sample block within the clamp, such that only the cutting tip extends, will increase stability. Orientation of the sample to the knife edge can affect the quality of the section. In the following description, a multilayer sample is considered as a series of parallel lines that can be placed either vertically or horizontally in a rotatable vise of a microtome with a horizontal knife edge ( Fig. 3 . 1 8 ) . For most samples, the initial cut is best made with the sample rotated 1 0 0 from vertical, with the most important layer closest to the knife. Additionally, a corner of the trapezoid, rather than a flat edge, should be cut first; this order minimizes stress on the block. Exact vertical orientation of the layers can increase section curling and particle loss, while exact horizontal orientation can result in the compression of Figure 3 . 1 6 the sample. Depending on the sample and how it behaves during cutting, An optimal embedment for microtoming, the orientation may need to be changed. with a small triangular sample positioned at the tip of an embedment cone. The standard procedure is to cut the multilayer sample with the layers orthogonal to the knife edge . However, other orientations are 40 Chapter 3 /' /' Sample embedment First trimming step -- Figure 3 . 1 7 The precise tri m m i n g angles required to produce a trapezoidal tip for optimal Second trimming step; rotate 1 05° Third trimming step; rotate 1 05 ° microtoming. The trapezoidal shape is placed i n the microtome vise, with the parallel sides vertical (as shown) or / rotated slightly to the left, so that the cutting blade, when stri king the block from the botto m , will first cut into a small corner, then progress to the rest of the sample. This proced ure min imizes stress on the knife as it cuts into the hard polymer block. Fourth trimming step; rotate 85° Close-up o f sample in trapezoidal cut media possible. Cartwright and coworkers placed the sample with the layers parallel to the cut edge and produced slices of individual layers that were then placed in a micro diamond cell for analysis ( Cartwright, Cartwright, and Rodgers 1 977). Oblique sectioning is another method used in the case of thin layers to increase their analysis width effectively ( Reffner and Martoglio 1 99 5 ) . In this method, the sample is oriented such that the layers are at an angle to the cutting edge ( Fig. 3 . 1 9 ) . As shown in Reffner and Martoglio, an angle of 1 0° will increase the free width of a 1 0 /-Lm layer to nearly 53 /-Lm. Figure 3 .20 shows a sample from the var. nish layer of an eighteenth-century gilded table. The analysis question was to determine the adhesive under the gilding. Since this layer was Figure 3 . 1 8 The orientation o f sample layers and the trapezoidal-trimmed tip for optimal micro­ toming. The cut direction is from the bot­ tom to the top, with the imaginary knife edge aligned parallel to the bottom edge of the page. Horizontal: creates compression Vertical: causes curl ing; the sample may pop out Angle offset: optimum Sample Col l ection and Preparation R * I II ", RI "I ', ,,'�=::7Z.==27::=*=::7Z.=::"""'7 only about 1 0 /-Lm thick, the cross section was cut at an oblique angle to increase the width for analysis. The optimal sample thickness for IR transmission analysis is 1 - 1 0 /-Lm (Derrick, Landry, and Stulik 1 99 1 ) . Sections thicker than 1 5 /-Lm usually absorb IR radiation too strongly to allow for analysis. Moreover, an attempt to cut thick sections can result in a sample pop­ ping out of the slice, in chattering of the knife, or in damaged knife edges. When a microtoming problem occurs, it can often be solved by slicing thinner sections ( 1 11m ) , then returning to slice a thicker section (5-10 /-Lm) . All cuts should be smooth, slow, and executed with a motor­ Figure 3 . 1 9 Two possible cuts for a m u lti layered sam ple. Cutting a sample at an oblique = angle will in crease the effective analysis width of the layer ( R 41 IR beam direction). ized microtome, if available, set at speeds of 0. 1 -3 . 0 mm/sec. Cutting speeds that are variable or too fast can cause particle loss and curling of the thin section. The optimum environment for microtoming is a small room with no foot traffic, drafts, or temperature and humidity fluctuations. The microtome should sit on a sturdy, vibration-free table. When cutting problems occur, all sources of heat are suspect and should be modified when possible. These heat sources include lighting, hand temperature, and the human breath. If a motorized microtome is used, the microtome and its bench should not be touched during the cutting stroke. As the section is being cut, it can be encouraged to cling to the knife. This technique can be performed with a small, stiff bristle artists' brush ( size 000) that can be used to hold the initial cut edge of the section to the knife surface without the sample region being Figure 3.20 touched . An eyelash brush or a cat-hair brush will also work well. Static A finish cross section from a gilded table charge should keep the section on the knife. After the section is cut, it sam ple. The photograph on the left shows can be easily and delicately picked up from the glass surface with the a thin section that was microtomed with paintbrush. For IR analysis, sections are taken directly from the micro­ the cut edge perpendicular to the top sur­ tome, placed on an appropriate IR window, and transferred to the face of the sample. The photograph on sample stage of the IR microspectrometer. If necessary, folds or wrinkles the right shows a thin section from the in the section can be removed by the placement of another transparent same sample that was cut at an oblique window on top of the section. Alternatively, ethanol or heat may be angle (45°) . The width of the top coating used to relax the polymer, provided that the sample will not be layer was increased significantly. adversely affected. 42 Chapter 3 Summary The ultimate goal of any analysis is to produce useful and reliable infor­ mation about the sample. Critical steps toward that goal are the selec­ tion, collection, and preparation of the sample. Errors at any point in this process-such as selection of a sample that poorly represents the obj ect or contamination of the sample through placement in a poor stor­ age container-can produce analytical results that are, at best, recognized as meaningless or, at worse, misdiagnose the object and its condition and lead to inappropiate treatment decisions. Additional Reading Chal mers, J . M . , and M. W. Mackenzie 1 9 8 8 . Solid sampling techniques. In Advances in Applied Fourier Infrared Spectroscopy, ed. M. W. Mackenzie. New York: John Wiley and Sons. H umecki , H . , ed. 1 995. Practical Guide to Infrared Microspectroscopy. New York: Marcel Dekker. Kri s h n a n , K . , and S. L. H i l l 1 990. FT-IR microsampling techniques. In Practical Fourier Transform Infrared Spectroscopy, ed. J. Ferraro and K. Krishnan. New York: Academic Press. Perkins, W. D. 1 99 3 . Sample handling in infrared spectroscopy-An overview. In Practical Sampling Techniques for Infrared Analysis. Boca Raton, Fla.: CRC Press. Chapter 4 Infrared Analysis Methods Proper instrumentation-that is, a well-functioning spectrometer-is the first step toward producing good IR spectra. The design, operation, and maintenance of IR spectrometers, however, is beyond the scope of this book. Resources for information on IR instrumentation are listed in the additional readings at the end of this chapter. In particular, Low and Baer clearly describe the interferometer design, along with the advantages Fourier transform infrared ( FT-IR) spectrometers have over dispersive instruments ( Low and Baer 1 977). The second step toward the production of good spectra is the selection of a suitable technique for presenting the sample to the spec­ trometer. There are a wide variety of methods using accessories that fit into the sample compartments of most spectrometers. The selection of an appropriate analysis method depends on the type, form, and amount of sample to be analyzed. No one method can meet the analysis needs of all samples. Theoretically, one material should give one, unique IR spec­ trum that relates to its chemical composition. However, the physical state of the sample, its preparation, and the analysis method chosen have an effect on the resulting spectrum and can shift band positions, as well as change band shapes and relative intensities. Figure 4 . 1 shows spectra for Acryloid B-72 ( methyl acrylate-ethyl methacrylate copolymer) obtained by four different analysis methods. Slight, but recognizable, spectral vari­ ations are seen in these four spectra, because of their different analysis techniques. Thus, while spectra are reproducible within each method, caution must be used when spectra acquired from one technique are compared to reference spectra collected through a different method. This chapter focuses on the equipment, sample requirements, spectral variations, and limitations of several of the most common analy­ sis techniques. Transmission methods-in which the beam passes through the sample-are used for the analysis of gases, liquids, and solids. Reflec­ tion methods measure changes in the IR beam as it is reflected by the sample; these methods are generally used for solid samples. Microspec­ troscopy, often the best method for the analysis of small samples taken from works of art, will be discussed in detail. Additionally, micro scale versions of each method will be presented for use with limited amounts of sample when an IR micro spectrophotometer is not available. Table 4 . 1 presents analysis methods described i n this chapter and their relationship 44 Chapter 4 Transmission Attenuated total reflection (ATR) Diffuse reflection (DRI FTS) Figure 4.1 IR spectra of Acryloid 8-72 collected by fou r different analysis methods. The over­ all spectral pattern is similar, but slight variations in band position and intensity 4000 3600 3200 2800 2400 2000 1 800 1600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) can be related to the analysis method. to different sample types. In-depth information on the techniques presented here, as well as on other techniques ( chromatographic, ther­ mal, photoacoustic, and emission ) , can be found in the Additional Reading section. 45 I nfrared Analysis Methods Examples Potential analysis methods poll utant, fum igant transmission gas cell oil, paste, gel, curing adhesive, plasticizer fi l m on transparent window o r diamond cell, horizontal reflection­ absorption, liquid i nternal reflectance cell Nonviscous solvent liqUid ceil/liquid internal reflectance cel l , film on transparent win­ dow, horizontal reflection -absorption Solution e m u lsion , varnish, paint, consolidant (before curing) diffuse reflectance , pressed pellet (dried residue), cast fi l m on window o r reflective su bstrate, diamond cell, internal reflectance plastic, glass external reflection, grind for K B r pellet, section for transmission o r reflection-absorpti o n , f i l m o n transparent window o r diamond cell Hard (rough) ceramic, sto ne, corroded metal diffuse reflectance, grind for KBr pellet, section for transmission or reflection-absorption, fi l m on transparent window or diamond cell Soft flexible polymer, adhesive, paper, parch ment dissolve in solvent and recast as thin fi l m , internal reflectance, fi lm o n transparent window o r diamond cel l , reflection -absorption Sample form Gases Non reactive gas, gas mixture, trace atmospheric components Liqu ids Viscous Solids Hard (smooth) o n mi rrored su bstrate Thin film plastic fi l m dissolve in solvent and recast as thin fi l m , internal reflectance, film on transparent window o r diamond cell, reflection-absorption on m i rrored su bstrate Coating coated paper, coated metal, adhesive dissolve in solvent and recast as thin film internal reflectance, film on transparent window o r diamond cel l , external reflectance Fiber fabric, fur, carpet, polymer, wood diffuse reflectance, internal reflectance, film on transparent w i n ­ d o w o r diamond cell Powder m i neral, colorant, clay, stone, corrosion product diffuse reflectance, grind for KBr pellet, internal reflectance, film on transparent window o r d iamond cell Table 4.1 Infrared Transmi ssion Measurements I R analysis methods for various types of samples. Each tech n i q ue may also be per­ Until thirty-five years ago, transmission measurement was the only formed on microsamples. method of IR analysis. Because of its versatility, IR transmission was used for both qualitative and quantitative analysis of gas, liquid, and solid samples. Large libraries of spectra from IR transmission analyses were produced. Thus, IR transmission spectra became a standard that is still used today and against which spectra generated from other analysis methods are compared. One advantage of transmission analysis is that the total sample absorption is proportional to the thickness of the sample (pathlength) and its concentration. This correlation establishes a simple relationship for quantitative calculations. Also, because of high energy throughput, trans­ mission analysis methods have greater sensitivity than reflection analysis. The character of a transmission spectrum is dependent on sample preparation, particle size, and absorptivity. For example, spectral distortions, such as band broadening, occur when the transmitted beam is partially reflected or refracted ( Fig. 4 .2 ) . Additionally, whenever another material is added to the sample, either to dilute it or to support Chapter 46 4 it, there is an added risk of contamination, which can result in spurious Transmission absorption bands. Some common spectral anomalies and solvent bands seen with transmission spectra are listed in Table 4.2. Many of the dilu­ ents mentioned in this table are no longer common in IR analysis labs; however, they may still be encountered in published reference spectra because of their previous high incidence of use. Infrared window materials For transmission analysis, the sample can be placed freestanding in the IR beam, or it may be held in place by a supporting material. Ideally, the supporting material would not, in itself, absorb any of the IR radiation. Refraction While many materials come close to this ideal, each has its own limita­ tions regarding frequency range and chemical compatibility. The selection of the support material is dictated by the character of the sample and analysis method. Table 4.3 lists the common types of support materials used, their useful frequency ranges, refractive indices, and chemical compatibilities. While glass is a good support for the visual examination of samples, it absorbs strongly over most of the mid-IR region. Figure 4 . 3 shows the IR spectrum of a standard glass microscope slide, as well a s the characteristic spectra of two materials, potassium bromide ( KBr) and barium fluoride (BaF2 ) , commonly used as IR windows in the mid-IR region. The glass slide essentially absorbs all the IR radiation from 2200 to 400 cm-1. Since the main property desired for IR window Reflection material is its transparency to the IR radiation emitted by the source, glass is not used as a support material for IR analysis. Many IR transparent materials are available for use as IR window materials; each one has certain advantages and disadvantages, and it is up to the analyst to select the material most suited for a particu­ lar experiment. The relatively inexpensive KBr and sodium chloride (NaCl) windows are commonly used. The KBr and NaCI windows are Figure 4.2 A radiant beam path when the beam is transmitted, refracted, and reflected by a sample and/or substrate ( n A = refractive index of air; n s = refractive index of the material). useful over the entire mid-IR region, but are moisture sensitive and will dissolve in water. Thus, the use of aqueous solutions must be avoided. Moreover, KBr and NaCI pellets, if left in humid air, will fog and become pitted. These windows are, therefore, typically kept in a desiccator. Also, NaCl and KBr windows are easily scratched and gouged, so that the requirement for routine cleaning and polishing makes it hard to maintain the original level of transparency. Poor window surface quality and trans­ parency are particular problems in microspectroscopy-both during the process of aperture positioning as well as at the photodocumentation step. BaF2 windows are not attacked by water. Therefore, they can be stored in the open, and aqueous solutions can come in contact with the material without dissolution. Also, because the windows are very clear, they provide high-quality imaging for light microscopy and photodocumentation. However, BaF2 windows are roughly four times as expensive as KBr windows. While they can be readily cleaned and pol­ ished for reuse, they are also very fragile and will break when dropped even a few inches. Finally, these windows have a cutoff at 700 cm- 1 and 47 I nfrared Analysis Methods Sample preparation method Problems and causes Remedies Free film interference fringes from shiny sample surfaces abrade the sample surface o r analyze by another method bands totally absorbing from a too-thick sample make sample thinner by flattening o r cutting bands totally absorbing from a too-thick sample make sample thin ner by flatten i n g o r cutting curved or slanting baseline due to n onflat sample surface flatten sample o r place i n a compression cell; avoid particle edges Dissolved in carbon tetrachloride (CCI4) interfering bands at 700-800, 980, 1 2 50, 1 550 cm- 1 due to solvent use only for 4000-1 350 cm-1 range Dissolved in carbon disulfide (CS2) interfering bands at 1 400-1 650, 2 1 50 , 2300 cm-1 due to solvent use only for 1 3 50-650 cm- 1 range Diluted with N ujol (mineral oil) interfering C-H bands (2850-2960, 1 460, 1 3 80, 720 cm-1 ) due to dil uent use only for 1 3 00-200 cm- 1 range Dil uted with Fluorolube (fluorocarbon oil) interfering bands at 1 080-1 200, 965, 900 cm-1 due to diluent use only for 4000-1 300 cm-1 range Grou nd and diluted with KBr, Csl, AgCl, then pressed into pellet salts are hygroscopic; may absorb water with interfering bands at 3400, 1 640 cm-1 grind and mix sample and salt in dry atmosphere and/or under heat lam p Film, liquid, or particles placed on a support may contain sharp N0 3 at 1 3 84 cm- 1 = band use only fresh salt supply and store in dark contai ner Table 4.2 thus may not be appropriate for the identification of some inorganic Possible spectral anomalies d ue to the materials with characteristic absorptions that occur at lower energies, Silver chloride (Agel) windows are also water insoluble. They sample preparation method. have good transmission properties from 4000-400 cm- I, are relatively inexpensive ( only twice the cost of KBr) , and are fairly durable. These windows, however, are sensitive to light and will darken upon exposure to short wavelength visible light-therefore, they must be kept in the = dark. For IR microspectroscopic analyses, their relatively high refractive index (n 2.00) may affect focusing and sample isolation. While the most commonly used window size for an IR salt x plate is a 13 mm diameter disk of 2 mm thickness, some instruments x have sample holders specifically designed for small (6 (32 1 mm) or large 2 mm) salt plates. Windows can be found in a 4 mm thickness, but these tend to decrease the available energy in the low-wavenumber end of the usable window region and may actually cut off 5 0- 1 0 0 cm- 1 higher than the 2 mm window. Windows of 1 mm thickness can be specially ordered. These will have better transmission properties than the 2 mm thick variety and therefore may be desirable for some situations. They are likely to be more expensive, though, and are substantially more frag­ ile than the 2 mm thick windows. In normal use, IR windows may become fogged or scratched or accumulate insoluble deposits. When this happens, the surface can be reconditioned by being polished with fine-grain emery paper. The coarse­ ness of grit selected for the initial polishing depends on the extent of the damage. Polishing kits from many of the IR supply companies have a Chapter 48 4 Material Range (cm - ' ) Refractive index Compatibility Glass 55,000-3000 1 .45 water insoluble, attacked by hydrofluoric acid Quartz 40,000-2500 1 . 54 water insoluble, attacked by hydrofluoric acid Sapphire 20,000-1 780 1 .7 good strength, no cleavage Diamond 40,000-200 except 2500-1 800 2 .42 insolu ble, inert, hard, expensive Calcium fluoride 70,000-1 1 1 0 1 .43 water insoluble, does not fog, incom patible with ammon i u m salt solutions Barium fluoride 1 . 47 65, 000-700 water insoluble, does not fog, breaks easily, incompatible with ammonium salt solutions Zinc selenide ( i rtran IV) 2 .49 1 0 ,000-550 water insoluble, resistant to most solvents, brittle, sli ghtly soluble in acids Sod ium chloride 40,000-625 1 . 54 hygroscopic, fogs slowly, easy to polish, low cost, water soluble Silver chloride 25,000-400 2 .07 water insolu ble, very soft, sensitive to light Potassium chloride 40,000-500 1 .49 hygroscopic, fogs slowly, easy to polish, water soluble Potassi u m bromide 40, 000-400 1 . 56 hygroscopic, fogs with moisture slightly faster than NaCI; softer than NaCI KRS-5 (Thallium iodidebromide, TI 2 I B r) 1 5 ,000-250 2.38 water insoluble, toxic, soft, soluble i n bases Cesi u m bromide 1 0,000-250 1 . 66 hygrosco pic, soft Cesium iodide 1 0,000-200 1 . 79 hygroscopic, soft, fogs slowly Teflon (th in film) 5000-500, except 1 200-900 1 .5 1 inert, u naffected b y any solvent, avai lable a s disposable cards Polyethylene (thin fil m ) 4000-30, except 3000-2800, 1 4601 3 80 and 730-720 1 . 53 water insoluble, resistant to most solvents, very soft, difficult to clean, available as disposable cards Table 4.3 good selection of fine-grain papers, generally ranging from 400 to 1 200 I R transmission ch aracteristics of support grit. The grinding process is performed with emery paper wetted with materials. alcohol and moved in a figure eight motion. The figure eight is necessary to prevent the flat crystal from becoming convex. It is usually necessary to use only one or two strokes with each grade of paper. For final polish­ ing, a cloth-lap procedure is used ( Chicago Society for Paint Technology 1 9 8 0 ) . For this technique, a soft, lint-free cloth is stretched tightly and fastened over a thick flat surface, such as a piece of glass. A small amount of very fine polishing agent ( 0 . 5 !-Lm or less) is placed on one area of the cloth and wetted with a little solvent ( or, for salt plates, with alcohol ) . The crystal to be polished is swept in the figure eight motion until it appears clear and smooth. Then the crystal is placed on a clean, dry area of the cloth and slid across in a straight motion to gently dry and clean its surface. To determine whether the crystal is still flat, it may be placed on an optically flat piece of glass and illuminated with a sodium vapor lamp to be examined for fringes: fewer fringes indicate a flatter crystal. Plastic gloves should be worn during the polishing process to keep finger oils and moisture from affecting the window and to pro­ tect the polisher's hands from hazardous materials. ( For more polishing methods, see Smith 1 979: 1 1 5-1 7; for polishing methods for micro size KBr pellets, see Teetsov 1 99 5 . ) 49 I nfrared Analysis Methods Glass microscope slide Q)'"() .=if. c <1l E C/l c <1l 4000 3200 3600 2800 2400 2000 1 800 1 600 1 400 1 200 �.=if.()E 1 000 800 600 800 600 Q) c KBr C/l c <1l 3600 4000 , ,, ,••, , Q)'"() .=if. C <1l E C/l C <1l Figure 4.3 I R spectra of glass (1 m m thick), potas­ sium bromide, and barium fluoride sub­ strate materials. The I R tran smission range 3200 4000 • 3600 2800 2400 2000 2800 2400 1 600 1 400 1 200 1 000 ,•·, ,, ,•, ,• ,, , , • • , • · ,, • • ,,•· ,•, ,• ·•, ,, •, •,• •, • ,•, ·•• ,,• •,·• •,•, ,•, •, •,, •,• ,• , , , , ,. 3200 1 800 · BaF2 • 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) is shown. Most IR windows should be stored in a dry atmosphere to protect them from moisture. Desiccators and low-temperature ovens are available for this purpose. When limited amounts of sample are avail­ able, it is sometimes prudent to save the sample on or in a pellet for later reanalysis. Sample holders can be used to label and store pellets for later use. 50 Chapter 4 Transmission analysis of gases Materials that are in the gas phase at room temperature may be analyzed as a gas or condensed in a cold trap with liquid nitrogen and analyzed as a liquid or solid. Gas-phase molecules rotate freely, producing very sharp rotational absorption bands that are not seen in the liquid or solid-phase spectra for the same sample (as shown in Fig. 2 . 4 ) . These bands are very characteristic, though, and are often used for the identification and quan­ titation of components in a gaseous mixture. For quantitative analysis of a gas, its absorbance is proportional not only to its concentration and to the IR path length but also to its pressure. High pressures can, however, result in absorption band broadening. A gas cell consists of a glass or metal cylinder fitted at each end with a transparent, nonreactive IR window ( Fig. 4 . 4 ) . The cell has two stopcocks for evacuation and filling. The windows must be well sealed during assembly to prevent leakage. The typical cell is single pass and 10 cm long, though other pathlengths are available. A multiple­ pass cell contains mirrors on its ends to reflect the beam back and forth through the sample several times before passing it on to the detector. This increases the effective optical pathlength and thus increases the absorbance and sensitivity of the measurement, allowing the detection of concentrations in the parts-per-million range. Gas cells with reflections of 40- 1 0 0 times, producing pathlengths up to 1 2 0 m, are available. Miniature, variable-temperature, flow-through gas cells can be used to identify the small amounts of a gas-phase material obtained from the effluent of a gas chromatograph ( GC ) or thermal analyzer. Alternatively, a unique GC-IR interface, in which the gas-phase effluent from the GC is frozen onto an IR transparent window cooled to liquid nitrogen temperatures, was developed by Fuoco, Shafer, and Griffiths ( 1 9 8 6 ) . The window is then rotated into the IR beam to obtain spectra of the condensate fractions. Transmission analysis of l iquids Solution spectroscopy-that is, spectroscopy of liquids or solids in solu­ tion-has the advantage of being highly reproducible. Problems and spec- Figure 4.4 A single-pass, I R gas cell ( 1 0 em). I R transparent windows at each end of the cell allow the passage of IR rad iation beams. I nfrared Analysis Methods 51 tral artifacts due to sample preparation (heat, pressure, and particle size) are rarely encountered. Liquids generally require very little sample preparation. A nonvolatile liquid sample can be spread as one drop on a single salt plate ( BaF2 is nonreactive to most liquids) or other transparent surface, such as a single surface of a diamond cell. However, unless they are applied to the support as very thin films, most liquids absorb too strongly; the result is spectra with some absorption bands having less than 1 0 % trans­ mittance. If this is the case, the sample must be diluted with a solvent. Carbon tetrachloride and carbon disulfide solvents were commonly used as diluents in IR spectroscopy because they themselves have few interfer­ ing IR absorptions. These diluents are rarely used today because of their toxicity and because of the availability of alternate IR analysis methods. Volatile liquids can be analyzed by use of a commercial liquid cell or simply by sandwiching a drop between two salt plates. Commercial liquid cells consist of two IR transparent windows wedged together in a metal frame. The cavity for holding the solution is either a drilled space in one of the windows or a space created by a gasket of known thickness between the two windows. The spacers are typically made of Teflon or lead; the spacer thickness controls the pathlength and capacity. For quan­ titative analysis of a liquid, absorbance is proportional to both concentra­ tion and cell pathlength. Sealed and unsealed liquid cells are available ( Fig. 4 . 5 ) . For cleaning, a permanently sealed liquid cell is flushed thoroughly with sol­ vent, then dried with a stream of nitrogen or clean, dry air. Nonsealed, or demountable, liquid cells can be cleaned after disassembly. The demountable cells provide flexibility in changing the IR windows as they become clouded or scratched. However, since these demountable cells have the potential to leak, they are best used for viscous liquids or mulls. Micro liquid cells are available for the analysis of small sample volumes ( 0 . 5-50 f..LI ). Other specialty cells, such as variable-temperature, variable­ thickness, and flow-through cells, are also sold. Liquids can also be ana­ lyzed by some reflection methods, such as diffuse reflection (DRIFTS) and internal reflection (IRS ) . Figure 4.5 Single-reflection and micro liquid I R cells. For both types of holder, the cell is sealed , and then the liquid is injected with a syringe. The cells can be d isassembled for cleaning. 52 Chapter 4 Transmission analysis of solids Several methods can be used for the IR transmission analysis of solid samples. In the most commonly known method, the samples are pow­ dered, then mixed with an IR transparent material, such as KBr, and pressed into a clear pellet for analysis . In other methods, samples are analyzed as free, or unsupported, films or as thin films flattened or deposited on a transparent window. The deposition of films on a support is a highly versatile technique that has become the primary method used for samples analyzed with IR microspectrophotometers. Even hard and tough materials can be compressed by use of a diamond cell for transmis­ sion studies. Examples of materials that may be analyzed by these IR methods are viscous or nonvolatile liquids ( oils, adhesives), films dried from a solution (varnishes, paints, emulsions), and flattened, solid samples (particles, pigments, fibers, scrapings ) . A disadvantage to the transmis­ sion analysis of solid materials is that grinding, dissolution, melting, or flattening is usually required. Any of these procedures can produce changes in sample orientation or in crystalline structure; the result is a slightly altered spectrum. Pellets and micropellets The pressed-pellet technique for IR analysis was first introduced in 1 952, and it was used as the primary method for the analysis of solids for over two decades ( Stimson and O'Donnell 1 9 5 2 ) . It is still a commonly used technique because it requires no expensive instrument accessories, it allows for control of analyte concentration, and it results in a sample that may be conveniently stored for later reanalysis. Butz's text on IR absorption analysis of powdered samples is recommended as a good basic reference, since it gives detailed information on the preparation and problems of preparing salt pellets (Butz 1 96 0 ) . The analysis of small samples with KBr micro pellets has been successfully applied to early microphotographic emulsions (Newman and Stevens 1 9 77), artist paint materials (Newman 1 9 80; Meilunas, Bentsen, and Steinberg 1 99 0 ) , and furniture finishes ( Derrick 1 9 8 9 ) . The standard pellet size for commercial dies i s 1 3 mm. Micropellet dies can produce disks of 0.5 or 1 .5 mm in diameter. For analysis, a sample pellet is placed in a pellet holder and inserted directly into the sample compartment of the IR spectrometer. A background scan is usually taken with no pellet in the IR beam path. Micropellets require a beam condenser unit that focuses the energy of the beam to the x4 correct size and position of the sample. Figures 4 . 6-4 .9 show pellet dies and holders for both the normal and the micropellets, along with a beam condenser. Beam condensers allow micrograms of samples to be ana­ lyzed, because they focus the radiation to a smaller diameter, thereby maximizing the amount of the energy in a minimum size area. The beam condenser must be aligned when placed in the sample chamber with both the pellet holder and empty pellet in place, to ensure that the beam will pass through the pellet area. Most instruments have a white light source that can be used for the rough alignment of the mirrors in sampling I nfrared Analysis Methods 53 accessories when needed. Turning out the room lights increases the visi­ bility of the alignment beam. A white card or piece of paper can be inserted at each position to locate the beam and to ensure that the focal point occurs at the pellet position. Final alignment is done by optimizing the IR beam intensity at the detector. The pellet and its holder must be Figure 4.6 A 1 3 m m pellet die (top center) and hold­ ers. A sample is ground into fine particles and mixed with an alkali halide salt i n the mortar and pestle, then transferred to the pellet die and pressed into a transparent pellet. Figure 4.7 A standard sample holder with accessories for 1 3 mm pellets and thin fi lms. The stan­ dard holder fits into the sample compart­ ment of the IR spectrometer. Figure 4.8 A micropellet die (1 . 5 mm) and holder. Sample preparation for micropellet analysis requires small tools and an extra-small mortar and pestle. 54 Chapter 4 Figure 4.9 A beam condenser (x4) shown with a micropellet at the center focal point. The beam condenser may also be used with the internal reflection holder and the micro liquid cel l . repositioned in exactly the same manner each time, with the entrance face always oriented in the same direction. It is important to recheck alignment with the sample in place, since the sample itself may slightly change the focal length of the beam. If a spectrum with a low signal-to­ noise ratio is obtained, the first thing to check is the position of the beam relative to the pellet. To prepare a pellet, a small amount of sample is first placed in a clean agate mortar and ground with a pestle to produce particles that are smaller than the wavelength of IR radiation (5 fLm ) . To deter­ mine when the sample is ground finely enough, use the pestle to form a smear on the mortar; the sample should feel slippery, should have no grit, and should spread out in a waxy film. For pulverizing large numbers of samples, a stainless steel ball mill or vibrator-grinder ( see Suppliers, Wig-L-Bug, Crescent Dental Manufacturing Co. ) can minimize the tedium. Heat and pressure produced by excess grinding, however, can cause changes in some samples. As with the mortar and pestle, all grind­ ing containers should be thoroughly cleaned between samples to prevent cross contamination. Some tough, hard samples-such as epoxy resins, paper, parchment, and rub ber-are very difficult to grind. Adding a few drops of liquid nitrogen to the sample will freeze it before crushing, thus making it brittle and easier to grind. After the sample is ground, it is uniformly mixed with a pow­ dered matrix, such as an alkali halide salt, that has a broad window of transparency in the mid-IR region. While potassium chloride (KCI), KBr, cesium bromide, cesium iodide, AgCl, and polyethylene have all been used to press pellets, KBr is the most commonly used. When KBr is used, it is important to mix quickly, as KBr is hygroscopic and will pick up water for the atmosphere that will appear in the resultant spectrum as broad bands at 3450 and 1 65 0 cm- 1 • Preparing the samples under a strong incandescent light or heat lamp can slow water absorption. The mixed matrix is transferred to a pellet die and spread evenly. Then the plunger portion of the die is inserted, twisted, and lightly tapped against the sample to ensure that the sample is distributed I nfrared Analysis Methods 55 evenly within the die. An uneven distribution of the salt matrix will pro­ duce a pellet with cloudy areas. The surfaces of the stainless steel dies are highly polished mirrors that produce transparent faces on the pellet and thereby minimize scattering effects. It is important that the die surfaces are clean and not scratched. They should not be touched with fingers and should be cleaned thoroughly between samples and before storage to minimize chances for corrosion. After loading with the sample, the die is usually attached to a vacuum line and evacuated for a few minutes with a high vacuum pump. This procedure removes water, solvents, and air from the mixture and results in a clearer and longer-lasting pellet. The die is then compressed under several thousand pounds of pressure, either by hand or by a hydraulic press. After the pressure is released, the die is opened, and the sample pellet is carefully removed with plastic forceps. The sample should be immediately transferred to a pellet holder in the instrument for analysis. For analysis at a later time, the pellet must be stored in a water­ free environment, such as a desiccator, a low-temperature oven, or a purged IR bench. A pellet may also be prepared from a sample dissolved in a volatile solvent: a few drops of the solution can be placed on some pow­ dered salt; once the solvent has evaporated, the solute is mixed with the salt powder, then pressed into a pellet. Any residual solvent, however, will hinder the production of a clear pellet. Microsamples dissolved in a solvent can be drawn up and concentrated into the tip of a KBr cone commercially available as a Wick-Stick ( see Suppliers, Perkin-Elmer Corp . ) . The tip of the cone is broken off, ground, and pressed into a micropellet. A solvent blank pellet should be run alongside any sample to check for potential contamination and impurities. Micropellets containing only a few micrograms of sample may also be prepared. With small samples, extraneous absorptions due to contaminants can appear aS' strong as absorptions from the sample. Therefore, it is critical to ensure that clean techniques are used. One method for preparing tiny, irreplaceable samples is to do all grinding, mixing, and transferring inside a glove bag that is slowly purged with dry air or nitrogen. This method will minimize moisture pickup, as well as other sources of environmental contamination. Most solid samples can be analyzed as pellets, but some problems may result. Nonhomogeneous samples, such as a paint cross section, will be homogeneous after grinding. Since individual components of multicomponent mixtures can be difficult to identify from an IR spec­ trum, a preseparation method should be used when feasible. Grinding some samples can cause changes in crystallinity. When particles are not ground finely enough in a pellet, some scattering of the beam may occur, resulting in energy loss and a broadening of the absorption bands. The sample spectrum should always be examined for potential absorption bands due to the pellet matrix, such as water absorption, contaminants, or even reaction products ( for example, some organic acids can react with alkali halides). 56 Chapter 4 Unsupported films Self-supporting materials, such as films, fibers, and tapes, can sometimes be mounted directly in the path of the IR beam without the aid of a sup­ porting material; in this way problems of contamination and interfering bands are avoided. The only sample preparation is mounting the sample. A holder should maintain the sample at the focal point of the beam with­ out blocking the beam. Commercially available magnetic film holders easily hold a large sample. Other sample mounts, such as pellet holders, can often be converted for use by stretching the sample across the empty pellet opening and holding it in place with tape. While easily prepared and analyzed, freestanding samples can be difficult to analyze. A sample that is sturdy enough to be self­ supporting is often too thick and absorbs too strongly, producing satu­ rated spectral bands. Samples that are not flat, such as fibers, can cause the radiant beam to scatter. Scattering can be reduced by applying min­ eral oil to the sample (if the hydrocarbon band region is not critical) or by flattening the sample. Free film samples can produce interference fringes. Inter­ ference fringes are the result of internal reflections of the IR beam inside the sample. Interference fringes are seen as a sinusoidal wave superim­ posed on the sample's molecular absorption pattern ( Fig. 4 . 1 0 ) . The intensity of the wave is a function of the refractive index of the sample and the glossiness of its surface. The frequency of the wave is dependent on the wavelength of the radiation, as well as on the thickness of the sample film. In fact, counting the fringes is an accurate method for the calculation of film thickness; the equation shown in Figure 4 . 1 0 is used (Harrick 1 9 7 1 ) . The fringes can be minimized by abrading the sample surface, by using polarized incident light along with an off-axis entry angle of the beam, by sandwiching the sample between two pellets or diamond surfaces, by coating the sample with an oil, or simply by ana­ lyzing the sample by another method, such as internal reflection. Films on transparent supports Most solid samples can be cast, melted, pressed, or spread into thin films for transmission analysis, but they require a supporting surface in order to place and maintain them in the path of the IR beam. The support is typically an IR-transparent material or window, such as a halide salt pel­ let. Another type of support, disposable IR cards ( see Suppliers, Spectra­ Tech, Inc., 3M films ) , has recently been introduced. These cards contain a thin polymer film ( either Teflon or polyethylene) stretched on a card­ board holder. The analysis of a thin film of solid material on an IR window is one common method used for IR microanalysis. This method has the advantage that the sample can be prepared in a horizontal orientation on the support material and can then be moved onto the sample stage with­ out further disruption or transfer. Films may be prepared from samples in many forms-that is, solutions, powders, or chunks. Solutions of solid samples in volatile solvents (e.g., emul­ sions, varnishes, and paints) , as well as some viscous liquids (e.g., oils ) , 57 I nfrared Analysis Methods Ql o c Figure 4 . 1 0 An interference fringe pattern obtained from a free film of polystyrene. The equation t = --- .�E'"'" <n c � <fI. 1 0n 2 R I (V -V2) 1 may be used to calculate the thickn ess of the fi lm (n = n u mber of oscillations; v = 1 starting waven umber [cm - 1 ] ; v2 = ending waven umber [cm - 1 ] ; t = fi lm thickness in m m ; and RI = refractive i ndex) . 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) can be cast or spread onto the surface of a transparent window and dried into a thin film. The liquid is drawn up into a capillary pipette and dripped onto the surface of the window. Thick liquids may need to be spread thinly and evenly over the surface by use of the pipette horizon­ tally as a draw-down edge or by pressing another pellet on the sample and compressing. The ideal sample should have a uniform thickness over the analysis area. For macrosamples, the area of analysis may cover the x entire salt pellet, while for samples to be analyzed on a microspectrom­ eter, the area of analysis may be only 1 1 mm or less. Thus, when a 1 3 mm window for microanalysis is used, multiple samples may be placed on one window. It is important, however, that the liquid samples not overlap and mix. The viscosity and surface tension (flow) of each liquid sample may be checked by observing a drop of the sample on a microscope slide prior to placing a microdrop on the sample window. Dispersion of particles in an oil mull is a method that has been used for years in IR analysis. Particles are ground finely as for pel­ lets, then mixed with either a mineral oil (Nuj ol) or a fluorinated oil ( Fluorolube ) . Since these oils absorb in separate portions of the IR spec­ tral regions, a sample is usually split into two portions, and half is mixed with each type of oil. The mull is spread as a thin film on a salt pellet for analysis. The mineral oil mixture gives a spectrum of the fingerprint region, while the fluorinated oil mixture provides a spectrum for the functional group region. Because this method is time-consuming and does not have any clear advantage, it is now rarely used, and alternate meth­ ods of analysis are preferentially selected. Some polymers and waxes may be melted and then spread as thin films on IR windows. The sample is placed on a glass slide, metal plate, or tip of a metal spatula, then heated gently on a hot plate. The melted sample is spread quickly on the window in a thin, even film and 58 Chapter 4 allowed to cool. Another method melts and cools the sample on a metal plate, then analyzes it by reflection-absorption ( Fischer and Bader 1 99 4 ) . Particles a n d fibers may b e flattened o r pressed t o form a thin film. The sample is placed on a hard surface, such as a reflective metal or IR window. It is compressed with a flat surface, a metal probe, or a metal roller. A sample flattened directly on a transparent window can be analyzed by transmission, and a sample flattened on a metal surface can be analyzed by reflection-absorption. Soft samples flatten readily and retain their shape. More difficult samples-such as fibers, adhesives, or elastomers-may be placed between two transparent windows, flattened, and held in place by a compression cell. The presence of windows on each side of the sample will decrease any scattering effects resulting from a nonflat sample surface. However, an increase in the total thickness of an IR window ( caused by the two windows) will decrease the energy reaching the detector. If this is a problem, two 1 mm thick windows can used instead of the normal 2 mm windows. An alternative procedure is to mix the sample with a small amount of a nonabsorbing matrix mater­ ial ( such as KBr) and then to flatten the mixture as described above ( Reffner and Martoglio 1 99 5 ) . This procedure essentially forms a minia­ ture pellet that increases the sampling area, minimizes scattering, and makes the sample easier to transfer with a metal probe or razor blade. Films on diamond cells Salt windows can break and scratch when the samples are hard or non­ compressible (e.g., minerals, epoxies) . In 1 95 9 the diamond anvil cell was first introduced by Weir and coworkers ( 1 96 0 ) . The high pressure, hard surface, and inertness of the diamond cell allowed reactive, opaque, hard, or rubbery samples to be converted to thin films for IR analysis. It also eliminated the potential for contamination due to an added matrix and allowed the sample to be retrieved for additional analyses. The use­ fulness of the diamond cell for the analysis of small art and archaeologi­ cal samples was demonstrated in the 1 970s by scientists at the Canadian Conservation Institute (McCawley 1 9 75; Laver and Williams 1 97 8 ) . Forensic spectroscopists have also applied diamond cells t o the analysis of tiny paint chips ( Rodgers et al. 1 976 ) . The diamond anvil cell consists of two industrial-grade dia­ monds, each with a flat, polished face, that are carefully aligned in a steel compression cell. The diamonds serve as windows, on which the sample is placed and through which the IR beam travels. The sample, preferably a homogeneous particle, is placed on the clean diamond facet, the oppos­ ing diamond is positioned on top, the cell is closed, and pressure is applied to flatten the sample. The original high-pressure diamond anvil cell is generally used with a x4 or x 6 beam condenser in which the whole device-diamonds with compressed sample-is placed in the sample compartment for IR analysis. The newer, low-pressure, miniature diamond anvil cell ( see Suppliers, High Pressure Diamond Optics, Inc.; Fig. 4 . 1 1 ) and the micro diamond compression cell ( see Suppliers, Spectra-Tech, Inc . ) are micros amp ling devices that can either be placed directly on the stage of 59 Infrared Analysis Methods Figure 4 . 1 1 A m i n iature diamond com pression cell. Samples are compressed between the 1 .5 mm diamond surfaces. Samples may be analyzed with the cell halves together or separate. an IR micro spectrophotometer or used with a beam condenser. Commonly, the two halves of the cell are separated after sample com­ pression, and one facet containing the flattened sample is placed directly on the analysis stage. Soft or thin samples can be placed directly on a single facet and analyzed with or without the compression step. Liquids may be analyzed on a single surface of the cell but should not be com­ pressed, as they are readily displaced. After analysis, the sample may be removed from the diamond facet with a cotton swab or even with a scalpel, since there is no danger of scratching the diamond. However, solvents should not be used to clean the diamond, since the diamonds are held in place with an adhe­ sive. Solvents may loosen the adhesive, resulting in misalignment or loss of the diamond. If misaligned, a diamond face may scratch or break its opposing surface. As noted in Table 4 . 3 , diamonds are not transparent over the entire mid-IR region. However, the main region of absorption is from 2500 to 1 8 00 cm- I , where few IR absorption bands occur. Also, com­ plete absorption does not occur with the thinner diamonds used in the smaller microsample diamond cells; thus the normal ratioing of a back­ ground spectrum to the sample spectrum will eliminate the diamond absorption bands. High pressures applied to the sample with a diamond cell may induce pressure- and temperature-dependent phase transitions in the sample ( Lippincott et al. 1 96 0 ) . However, it has been pointed out that only minimal pressures are usually needed to spread the sample evenly between the diamond faces, thus minimizing potential spectral alterations ( Ferraro and Basile 1 9 79 ) . Fibers IR spectroscopy is very useful for the characterization of natural and synthetic fibers. It is a standard analysis method used in the textile indus­ try (Wannemacher 1 9 80; Berni and Morris 1 9 84 ) , as well as for the analysis of leather, wood, and cellulose (Hergert 1 9 7 1 ; Liang 1 9 72 ) . x Internal reflection techniques work well for the analysis of larger samples, such as fabrics (20 45 mm), yarns, or fibers ( at least 20 mm) (Wilks and Iszard 1 9 6 5 ) . Very small samples of archaeological fibers and dyes have been analyzed by IR microspectroscopy ( Lang et al. 1 9 8 6 ; 60 Chapter 4 Matsuda and Miyoshi 1 9 89; Jakes, Katon, and Martoglio 1 990; Martoglio et al. 1 990; Jakes, Sibley, and Yerkes 1 99 4 ) . IR micro spec­ troscopy is also standard for the identification of trace fiber evidence in forensic examinations ( Cook and Paterson 1 97 8 ; Bartick 1 9 8 7; Tungol, Bartick, and Montaser 1 9 9 1 , 1 99 5 ) . Fiber, hair, and brush samples require little sample prepara­ tion. Such a sample may sometimes even be analyzed "as is" by taping the ends of a single fiber to hold it across a hole in a metal disk or sim­ ply by laying it on an IR window (Tungol, Bartick, and Montaser 1 99 5 ) . However, the fiber is often too thick and absorbs too strongly for direct transmission. In this case, one alternative is to use a reflection method, such as diffuse reflection or internal reflection. A second alternative is to make the fiber thinner. The advan­ tages to flattening a fiber are twofold. First, the horizontal measurement area of the fiber is increased. Second, its surface becomes planar. The use of the diamond cell is a quick and easy method for flattening fibers . Another method is to press the sample between two IR transparent win­ dows in a compression cell. A final option is to use a scalpel to slice a thin section from the end or side of the fiber. This method is sometimes preferred for the examination of the fiber structure, since flattening destroys its physical shape and may change its crystalline orientation. I nfrared Reflection Measurements In 1 95 9 spectroscopists began exploring reflection techniques for IR analysis. Francis and Ellison investigated films on mirrored surfaces, but their technique of external reflectance did not become widespread until the 1 970s ( Francis and Ellison 1 95 9 ) . The technique of internal reflection spectroscopy ( IRS), also called attenuated total reflection (ATR), was introduced in the early 1 9 60s and quickly became popular, since almost any material-solid, powder, or liquid-could be easily and nondestruc­ tively analyzed. Diffuse reflection spectroscopy (DRIFTS) methods pro­ duced so little reflected IR radiation that they were not widely used until the development of FT-IRs. Figure 4 . 1 2 illustrates the beam reflection paths used by dif­ ferent types of IR reflection devices. In external reflectance measure­ ments, the angle of reflection is equal to the incident angle of the beam, as found in mirrorlike reflections. For this method, the IR beam may be Internal reflected either by the sample surface ( specular ) or by a mirror surface reflection under a thin layer of sample (reflection-absorption) . DRIFTS occurs with High-refractive-index crystal a rough, porous, or powder sample, where the light is reflected at numer­ ous angles that are not equal to the incident angle. IRS occurs when the incident beam is internally reflected in a high-refractive-index material placed in contact with the sample. Leyden and Murthy and Morris pro­ Figure 4 . 1 2 Three different reflection types vide good comparisons of each of these reflection methods ( Leyden and (n A Murthy 1 9 8 6 ; Morris 1 99 1 ) . nB = refractive index of air; = ex = refractive index of the reflecting material; angle of incidence). Each o f these types o f analysis methods can cause slight shifts in absorption band position, as well as changes in relative band intensi- 61 Infrared Analysis Methods Analysis method Correction program Difference from transmission spectra I nternal reflection none band intensities stronger than normal at low wave n u m bers, weaker than normal at high waven u m bers ( I RS) Diffuse reflection ( D R I FTS) K u belka- M u n k some slight band shifting and i ntensi­ fication of weak bands artifiCially flat basel i nes Table 4 .4 Spectral alterations due to reflection analy­ Specular reflection Kramers-Kronig shifting i n position of bands, derivative band shapes Reflection-absorption (R-A) none may contain interference fringes and a specular component, if the surface of the sample is shiny sis methods, as compared to transmission spectra. ties. Table 4.4 provides a summary of some of the changes that are seen in reflectance spectra as compared to spectra collected by transmission methods. Also, an expansion of the carbonyl region of the spectra from Figure 4 . 1 is shown in Figure 4 . 1 3 , to illustrate the changes in peak shape and position. '":='"g(I) Transmission E <f) c t= if. Attenuated total reflection ( ATR) �a:1i5u(I) 1il Diffuse reflection ( DRIFTS) if. Figure 4 . 1 3 Partial I R spectra showing a n expanded carbonyl region of Acryloid 8-72 obtained from four analysis methods. While the overall spectral pattern is sim ilar for the four methods, slight differences in band Specular reflection position and intensities warrant caution when spectra analyzed by different meth­ ods are compared. (The full spectra are shown in Fig. 4 . 1 .) 1 800 1 700 Wavenumber (cm - 1 ) 62 Chapter 4 Specular reflection One type of external reflection, called specular reflection, occurs when the shiny surface of the sample reflects the IR beam at an angle equal to the angle of incidence. The specular reflection technique is used on samples of all sizes. Accessories for either fixed- or variable-angle reflection of the incident beam are available that fit into the IR bench sample compart­ ment. Figure 4 . 1 4 shows a variable-angle external reflection unit. The angle of incidence is adj usted to obtain optimum beam penetration on a sample-and thus optimum sensitivity. Usually a high angle of incidence ( 70°-8 9 ° ) is best ( Harrick 1 979). Larger top-loading external reflection attachments are available for the horizontal placement of samples; they can accommodate any large, flat surface placed face down. Specular reflection spectroscopy is a nondestructive technique in that the analyzed sample does not need to be removed for analysis. However, for high-quality spectra, the sample should be highly reflective and thus may require polishing prior to analysis. In a vertical reflection holder, the sample is generally clamped in place. The large number of polished paint cross sections already in existence in museum labs is an ideal resource for specular reflection microanalysis. Applications presented in Chapter 6 illustrate the combi­ nation of specular reflection analysis and computer-controlled stage movement to perform linear- and area-concentration maps on polished cross sections. Relative variations in paint layer composition can be determined by specular reflection, but identification of components in the samples may require supplemental analysis by other techniques. In specular reflection, strong absorption bands appear as derivative-shaped curves because of dispersion of the radiation. The derivative-shaped bands are referred to as Reststrahlen (residual ray) bands. This effect is dependent on the wavelength, angle of incidence, intensity of absorption, and refractive index of the sample material. Specular reflectance spectra can be converted to transmittance-like spec- Figure 4 . 1 4 A variable-angle external reflection acces­ sory. The sample is placed horizontally on the holder over the angled m i rror. An additional sample holder (shown at left) is available to orient the sample in a vertical positio n . I nfrared Analysis Methods 63 tra with a Kramers-Kronig transformation, which calculates refractive and absorption indices from the specular data . Most IR data processing programs can perform Kramers-Kronig transformations. Such a transfor­ mation works well when the spectrum results only from specular reflec­ tion; however, other types of reflections, refractions, and scattering can occur, such that bands of different shape and position are produced. For further information on specular reflection, refer to Kortum ( 1 96 9 ) . Reflection-absorption A second type of external reflection, called reflection-absorption ( R-A), occurs when the IR beam passes through a thin film of sample and is reflected from a nonabsorbing substrate. When the incident radiation enters the film at a near-normal angle ( 9 0 ° ) , the method is essentially a double-pass transmission experiment. Spectra generated in this man­ ner resemble those obtained in transmission . Reflection-absorption experiments can also be conducted at a greater angle of incidence ( 6 5°-8 5 ° ) , thereby increasing the effective pathlength of the sample. This is called grazing-angle spectroscopy and is used to detect and analyze very thin films. Front-surface aluminum or gold mirrors are used as reflective surfaces for thin films in a reflection-absorption experiment. The sample­ liquid, polymer, particle, or fiber-is smeared, melted, or flattened onto the mirror to form a thin, smooth, and level film. The mirror with sample is then placed in a specular reflection apparatus or on a microspectrom­ eter stage for reflection analysis. Specular reflection is the most common spectral distortion in a reflection-absorption experiment. It occurs when the sample is shiny and some of the radiation is reflected from the surface of the sample rather than from the mirror. To eliminate the specular component, the sample surface may be abraded, or a nonabsorbing material (e.g., salt plate) may be placed on the surface of the sample ( Reffner and Martoglio 1 99 5 ) . A salt plate must be held tightly against the sample surface to pre­ vent interference fringes from occurring. A compression cell can be used for this purpose . Diffuse reflection For a non-mirrorlike surface, light is reflected diffusely, or in all direc­ tions. When all specular contributions are eliminated, DRIFTS can be related to the concentration in the sample by use of the Kubelka-Munk equation ( Kubelka 1 94 8 ) . This conversion makes the spectra analogous to absorbance plots for transmission spectra. DRIFTS has been used in the visible region for many years for the quantitative analysis of colorants ( Billmeyer and Saltzman 1 96 6 ) . For IR analysis, DRIFTS was tried as early a s 1 9 1 3 b y Coblentz, and it was later used for the examination of powdered samples ( Clark 1 964; White 1 964; Vincent and Hunt 1 96 8 ) . It gained popularity in the late 1 970s when an efficient collector designed for diffuse radiation was used in combination with the high-energy throughput of an FT-IR ( Fuller and Griffiths 1 978a, 1 9 78b, 1 9 8 0; Griffiths and Fuller 1 9 8 2 ) . 64 Chapter 4 In the field of art conservation, Meilunas used DRIFTS to examine the surface of paint films and inks ( Meilunas 1 9 8 6 ) . He found that while many pigments could be identified, specular reflection inhib­ ited the identification of binders. Shearer used silicon carbide paper both as a sampling tool and as a DRIFTS substrate for the analysis of archae­ ological organic residues ( Shearer 1 9 8 7) . Using DRIFTS as a nondestruc­ tive tool, Hedley and coworkers ( 1 990) analyzed surfaces of paintings before and after solvent cleanings; Perron ( 1 9 8 9 ) characterized emulsions on photographs; Poslusny and Daugherty ( 1 9 8 8 ) identified the adhesives on stamps; and Faraone ( 1 9 8 7 ) examined the weathering surfaces of stones. McGovern and Michel used DRIFTS in combination with other techniques to determine the composition of royal purple dye, while Dauphin applied it to the quantitative analysis of protein residues found in archaeological bones (McGovern and Michel 1 990; Dauphin 1 99 3 ) . DRIFTS attachments are designed to fi t i n the standard sample compartments of most spectrometers ( Fig. 4 . 1 5 ) . The light reflected from the sample is collimated by an ellipsoidal mirror, then directed to the detector. The sample is held in a small cup on a sliding metal strip that serves to position the sample reproducibly. Some commercial DRIFTS accessories are designed to block the collection of the beam reflected at the angle equal to the incident angle-that is, the specular reflection com­ ponent. This feature eliminates one problem source in DRIFTS. Powder samples are prepared in a manner similar to that for Figure 4 . 1 5 KBr pellets. First, the sample is finely ground and mixed with KBr ( or A DRI FTS u n it with normal and m icro KCl) powder. Since the resolution of the spectrum is dependent on the (custom- machined) sample cups. Samples particle size, it is critical to grind the sample as finely as possible. are held i n a four-position holder that Distorted absorption bands will appear if particle sizes are larger than slides into position for analysis. the wavelength of radiation. The mixed sample matrix is then scooped into a sample cup and packed gently with a tamper. The prepared sample must be level and uniformly packed to produce a good-quality spectrum. The IR beam penetrates only the top 0. 5-2 mm of the sample. Thus, for small samples, it is possible to fill the bottom half of the cup with pure KBr powder, then put the sample matrix in the top half of the cup, to produce a more concentrated sample. Also, microsamples may be ana­ lyzed in microcup sample holders that are smaller in diameter and shal­ lower than the regular cups. Solutions may be analyzed by dripping a few microdrops on a prefilled analysis cup of KBr and allowing the solvent to evaporate. If the drops disrupt the surface of the salt bed, it may be possible to smooth the dried surface by gently tamping it, either directly or by first adding a few sprinkles of KBr powder on top. For nondestructive analysis of solid samples, any matte sur­ face, such as dyed textiles or papers, may be placed at the focal point of the IR beam in the DRIFTS apparatus (Harrick Scientific Corp . 1 9 8 7 ) . Shiny o r smooth surfaces may need t o be roughened with emery paper to diffusely reflect the incident beam. Also, a sample may be collected from a solid by gentle abrasion with a small circle of silicon carbide paper; the sample on the silicon carbide substrate is then mounted on a holder and placed in a DRIFTS accessory for analysis ( Shearer 1 9 87; Pretzel 1 99 4 ) . I nfrared Analysis Methods 65 In this manner, small amounts of sample can be taken from surfaces with minimal damage. The thin layer of sample on the reflective silicon car­ bide substrate essentially produces a reflection-absorption experiment with a spectrum similar to that obtained in transmission. The spectrum should not need the Kubelka-Munk correction used for other diffuse reflectance spectra. Typically, all DRIFTS samples should be diluted to less than 30 w/w% concentration in a nonabsorbing matrix. On solid samples, this dilution can be done by sprinkling a thin layer of nonabsorbing material (e.g., KBr) over the surface of the sample. The powder layer minimizes band broadening and poor resolution effects resulting from saturation or specular reflection problems; additionally, the sensitivity of the measure­ ment is improved by an increase in the depth of penetration of the beam. Spots on thin-layer chromatography plates may be successfully analyzed in this manner ( Zuber et al. 1 9 8 4 ) . The diffuse reflectance spectrum depends on sample density and refractive index, as well as on particle size and morphology. For quantitative analysis, the Kubelka-Munk function is used to relate the absorption coefficients to the material's concentration. This function tends to enhance the strong absorption bands and decrease the weaker bands in comparison to transmission spectra. Additionally, the baseline may be artificially flattened. For nonquantitative work, the diffuse reflectance spectra may be displayed without any correction function. The maj or problem that can occur with diffuse reflectance spectra is the inclusion of a strong specular reflection component that produces slight band distortions. Internal reflection Internal reflection was first noted in 1 7 1 7 by Isaac Newton in his studies of total reflection at the interface of two different media. The phenome­ non is observed in a clear glass of water, where one sees total reflection by viewing the water's surface from slightly below the water level (Harrick 1 9 79 ) . Total reflection is destroyed when another material, such as a finger, is placed in optical (air-free ) , or intimate, contact with the glass. In optical contact, the ridges on the finger surface can be clearly seen-but not the valleys, where no contact is made. In 1 947 Goos and Hanchen described the interactions between light and the two materials as total internal reflection, and the interactions were subsequently used for record­ ing optical spectra ( Goos and Hanchen 1 947). Internal reflection was applied to IR spectroscopy by Harrick ( 1 959) and Fahrenfort ( 1 962). While Fahrenfort coined the name attenuated total reflection (ATR) , the American Society for Testing Materials has since limited the scope of the term ATR and has instead designated the overall technique as internal reflection spectroscopy ( IRS) (ASTM 1 9 8 1 ) . IRS works well with coatings, adhesives, fibers, foams, fab­ rics, plastics, and films, and it is the technique of choice for many opaque and intractable samples. Internal reflectance spectra of films do not exhibit any of the interference fringes that can occur in transmission spectra. In a development significant to the field of art conservation, 66 Chapter 4 Paralusz did an extensive study using IRS of adhesive tapes ( Paralusz 1 974 ) . This paper included studies on resin aging, delamination, and resin-plasticizer migration. An interesting paper by Wilks showed varied applications of ATR, from the analysis of skin to gas chromatography fractions (Wilks 1 96 7 ) . In 1 9 8 5 Cain and Kalasinsky used several analyt­ ical methods to examine the degradation products on nineteenth-century paper ( Cain and Kalasinsky 1 9 8 5 ) . They found that IRS was useful for the determination of gelatin size in the paper samples. More recently, IRS has been used as a nondestructive method to examine eighth-century Japanese fabrics ( Matsuda and Miyoshi 1 9 8 9 ) and to identify synthetic fabrics ( Cardamone 1 9 8 8 ) . In IRS, the incoming radiation enters a high-refractive-index From source material ( hence called an IRS element) and is internally reflected, usually multiple times ( Fig. 4 . 1 6 ) . Based on the fact that internally reflected IR radiation will penetrate a short distance into a lower-refractive-index medium, a sample in optical contact with the surface of the IRS element To detector Figure 4 . 1 6 Multiple internal reflections i n a n I RS ele­ ment. When the I RS element has a higher refractive index than the sample, the IR rad iation will penetrate slightly into a sample if it is in optical contact with the element. will be exposed to IR radiation. The sample can then absorb the radia­ tion and produce a spectrum. Only the surface of the sample is analyzed, since the beam penetrates j ust a few micrometers into the sample. The depth of penetration is proportional to wavelength, and therefore, an increasing depth of penetration is observed at higher wavelengths ( lower wavenumbers ) . The intensity of absorbed radiation is dependent on the amount of sample in contact with the surface of the IRS element and the number of contact points that the radiation has with the sample-element interface. Thus, increasing the number of reflections increases the inten­ sity of the IR absorptions. Varying the angle of incidence can change the number of reflections and their position within the IRS element. For IRS to occur, the IRS element must have a refractive index higher than the sample to be analyzed ( see Table 4.3 for refractive index values). The IRS element material must also be clean, have a high surface polish, and be transparent to IR radiation. Silicon, germanium, thallium bromoiodide ( KRS-5 ), AgCI, and zinc selenide ( ZnSe) are typically used as IRS elements. Germanium and silicon are hard and brittle. They do not scratch easily; they are, however, subject to breaking. They may be cleaned in water, solvents, and dilute acids. KRS-5 elements, the most commonly used, tend to be soft and can retain the imprint of nonflat samples that are pressed into them. They can be cleaned with hydro­ carbon solvents, acetone, or alcohol. AgCl, while softer and more flexible than KRS-5, is light sensitive and inexpensive enough to be discarded when damaged. ZnSe is expensive and brittle but hard and insoluble. It is important not to scratch the optical surfaces of the IRS elements, and all handling should be minimized. Many samples, includ­ ing powders, may be removed from the elements with pressure-sensitive adhesive tape. Thin films and residues may be cleaned with a wash bottle or, if necessary, an ultrasonic bath. Rubbing of the surfaces of IRS ele­ ments should be avoided. Polishing can often refurbish damaged or scratched IRS elements, but because of their toxic nature, it is often best to return the IRS elements to the manufacturer for reconditioning. Pressure plates should be wrapped in an uncoated variety of aluminum Infrared Analysis Methods 67 foil th �t may be discarded after each analysis to prevent cross contamina­ tion between samples. Sample preparation for IRS analysis is relatively simple. The sample is placed on an IRS element (preferably on both sides ) , then the IRS element is positioned in its holder between two pressure plates that are uniformly compressed to place the sample in contact with the IRS ele­ ment (Fig. 4 . 1 7) . As the pressure is raised, the amount of sample in optical contact with the IRS element is increased, thereby enhancing the absorp­ tion intensity. For quantitative or comparative work, a torque wrench is recommended to reproducibly tighten the holder for each sample. Samples, such as films, may need to be cut so that they do not exceed the length of the optical element and interfere with the beam path. Long fibers may be wound around the IRS element to produce an even sample surface. Fibers may also be placed on the bias to prevent orientation effects. To do this, small strips of the fiber are cut, then placed diagonally, adj acent to one another and completely covering a strip of tacky adhesive. The tape is then placed in a manner such that only the fibers, not the adhesive, touch the IRS element. Powders may be evenly spread on an IRS element, or they may be dispersed in a liquid for deposition on the IRS element. For hard samples, the pressure plates can be lined with a thin foam or thick adhesive and then covered with uncoated aluminum foil. This procedure will minimize deformation to the IRS element's surface. Liquids, gels, pastes, and even aqueous solu­ tions can be cast onto an IRS element or run in a cylindrical internal reflection cell ( CIRCLE; see Suppliers, Spectra-Tech, Inc . ) . A long ATR probe, originally developed by Wilks Scientific, can be immersed in liq­ uids and solids for analysis outside of the instrument sample compart­ ment ( needle probe; see Suppliers, Spectra-Tech, Inc . ) . The IRS element holder typically fits into a beam condenser unit in the sample compartment. For optimum performance, it is critical that the beam condenser be aligned to provide maximum IR beam inten­ sity at the detector. The beam condenser should be aligned initially with­ out a sample, after which point a background scan can be obtained. The alignment should be rechecked with every single sample that is analyzed, because the position of the element can vary with the thickness and posi­ tion of the sample, as well as with the placement of the IRS element. Figure 4 . 1 7 An IRS holder, elements, a n d torq ue wrench. The sample is placed adjacent to an I RS element, then positioned between the two pressure plates (covered in alu­ minum foil) of the holder. A torq ue wrench is used for even tightening of the screws that hold the pressure plates around the sample. 68 Chapter 4 Otherwise, the energy losses due to poor alignment will cause significant deterioration of spectral quality. The instrument usually contains a white light source for the rough alignment. Turning out the room lights will aid in the process. When the IRS element is properly positioned in the beam, it will glow. In fact, in a dark room, it is possible to see the points of contact of the beam with the sample-element interface. This feature is useful for the analysis of small bits of sample. These points can be marked on the top surface of the pressure plate; the holder can be removed from the instru­ ment and disassembled; and the sample bits or fibers can be positioned in these places for optimum beam contact. Theoretically, there should be no " dead spots" for angles of incidence :s 4 5 ° . In practice, however, there do seem to be regions that are more sensitive than others. In IRS, the quality of the spectrum depends upon the angle of incidence, the depth of penetration, the number of reflections, and the rel­ ative refractive index difference between the sample and the IRS element. The spectra of thin films are virtually identical to spectra collected by transmission methods. For thicker samples, however, absorption bands at smaller wavenumbers are more intense, since the depth of penetration into the sample increases with wavelength. Poor spectra are obtained when the sample is not in intimate contact with the IRS element. Infrared Microspectroscopy The coupling of a microscope to the IR spectrophotometer produces a system capable of doing IR microspectroscopy. The resulting apparatus, called an IR microspectrophotometer, was first made commercially in the 1 950s ( Cole and Jones 1 95 2 ) . Although the design of the microspec­ trophotometer was satisfactory even by today's standards, the system proved to be costly and was limited by the low energy throughput and corresponding low signal-to-noise ratios. Therefore, the introduction of the FT-IR, with its inherent advantages, as well as advances in IR detec­ tor technology, fueled the reemergence, in 1 9 8 3 , of the IR micro spec­ trophotometer. The recent success in application of this instrumentation to many areas of research ( semiconductors, polymers, and pharmaceuti­ cals ) , as well as forensic investigation, has established the technique of IR micro spectroscopy as a powerful tool in the analysis of small samples. For more information on the history, design, and operation of IR microspectrophotometers, see Roush 1 9 8 7; Messerschmidt and Harthcock 1 9 8 8 ; Katon, Sommers, and Lang 1 9 8 9-90; Katon and Sommers 1 9 92; Reffner 1 9 93; and Humecki 1 995b. Researchers quickly saw the applications of IR microspec­ troscopy to the analysis of tiny samples from works of art. The first published application of IR micro spectroscopy was for the analysis of painting materials, done with a dispersive spectrometer by van't Hul­ Ehrnreich ( 1 970). Later, the attachment of microscopes to FT-IRs stimu­ lated numerous applications for the analysis of paint layers, binding media, varnishes, waxes, dyes, and other materials ( Shearer et al. 1 9 8 3 ; I nfrared Analysis Methods 69 Baker et al. 1 9 8 8 ; van Zelst, von Endt, and Baker 1 9 8 8 ; Orna et al. 1 9 8 9 ; Jakes, Katon, and Martoglio 1 9 90; Martoglio et al. 1 990; Derrick, Landry, and Stulik 1 9 9 1 ; Tsang and Cunningham 1 9 9 1 ; Derrick et al. 1 9 92; Lang et al. 1 992; Derrick 1 9 9 5 ) . Microspectrophotometer design The first IR microscopes were positioned in the sample compartment of the IR spectrophotometer. The microscope contained all the necessary transfer optics to direct the IR beam from the spectrometer source to the sample positioned on the stage of the microscope. In a transmission exper­ iment, after it passed through the sample, the IR radiation was collected and directed back into the spectrophotometer and onto the detector. The optics used in IR microspectrophotometers are reflecting optics. Since both glass and quartz absorb IR light over much of the region of interest, the IR microspectrophotometers are unable to employ standard, visible-light refracting (lens) optics but rather must use reflecting (mirror) optics. Although other detectors were used, the detector of choice was, and continues to be, the mercury-cadmium-telluride ( MCT) detec­ tor. The MCT detector element is cryogenically cooled to liquid nitrogen temperature, thus providing high sensitivity and signal-to-noise values necessary for the low energy levels and small sampling areas found in IR microspectroscopy. As the microscope designs gradually changed, a major improvement in signal-to-noise levels was achieved when the MCT detector was repositioned from the spectrophotometer bench to the microscope apparatus, in order to minimize the IR beam path after inter­ action with the sample. The next wave of improvements came when IR spectropho­ tometers were built with the ability to direct the IR source beam external to the instrument. This flexibility allowed modifications, redesign, and production of new spectrometers with optimal geometry for coupling to IR microscopes. Since the IR microscope had its own onboard detector, it was a complete system, minus the IR source and data processing/com­ puter system. With this new design, the microscope no longer occupied the sample compartment of the spectrophotometer, so that conventional methods could still be used to analyze macro samples. Finally, another design has produced what may be considered the first true IR micro spectrophotometer. In this system, the IR spec­ trophotometer and microscope are no longer separate entities but are, instead, one unified body ( IRf.LS; see Suppliers, Spectra-Tech, Inc .; Fig. 4 . 1 8 ) . This apparatus is not capable of macrosampling but, rather, has been designed to maximize the information and sensitivity obtainable on microscale samples. Samples can be examined with polarized light and digital imaging techniques, in addition to IR microspectroscopy. Microspectrophotometer capabilities All IR microspectrophotometers have some type of visible-light imaging available. Indeed, this aspect is one of three that separates the IR micro­ spectrophotometer from the IR beam condenser accessory. Imaging capa­ bilities range from stereomicroscope viewing to that of a research-grade 70 Chapter 4 Figure 4 . 1 8 An I Rf.LS I R microspectrophotometer (Spectra-Tech , I n c . ) . The instrumentation contains a source, interferometer, computer-controlled sample stage, and detector i n one u n ified body, shown on the left. Also shown are a video camera, monitor, and data processing computer. optical microscope. In addition, most IR micro spectrometers provide photomicroscopy and/or videomicroscopy. A second characteristic of the IR micro spectrometer is the ability to isolate a particular area of the sample optically by the use of movable apertures. Apertures may be a fixed-diameter-circle or a variable-circle iris, or an adj ustable, knife-edge rectangle. For hetero­ geneous samples, this capability means the IR microspectrometer is able to achieve both sample isolation and component identification. Finally, all IR microspectrophotometers have the ability to collect IR reflectance spectra. Reflection IR is useful for highly absorbing samples that do not transmit IR well, as well as for providing informa­ tion on the surface composition of a material. The resulting spectrum is often a complex mixture of specular and diffuse reflection components and must be interpreted with care. The ability to perform reflection analysis increases the versatility of the IR microspectrophotometer. Particle and fiber analysis Many of the techniques previously described in this chapter can be applied to IR microspectroscopy, and, as with macroanalysis, the selec­ tion of the technique depends on the characteristics of the analyte. Most materials are heterogeneous; however, to facilitate examination of typical analytical variables, this discussion will be limited to simple samples with homogeneous analysis areas. The most common analyses performed by the IR micro spec­ trophotometer involve the determination of particle and fiber composi­ tion. In the field of IR microspectroscopy, a particle is simply defined as a piece of material of suitable size for IR micro spectroscopic analysis. The size suitable for analysis includes pieces as small as 1 0 !Lm in diameter, up to sizes on the order of 1-2 mm. The initial examination and manipulation of a particle is done under a stereomicroscope, usually with the sample on a glass microscope slide. A necessary component of any IR microspectroscopic I nfrared Analysis Methods 71 x 1 0- x S O laboratory, the stereomicroscope should have variable-magnification capability, such as magnification. A stereomicroscope with the head mounted to a boom arm is a valuable tool that provides flexibility for a wide variety of samples. For transmission analysis, the first step is to place the par­ ticle on the IR window material, such as a salt plate or a diamond cell ( Fig. 4 . 1 9 ) . Corresponding procedures can also be used for reflection­ absorption measurements if the particle is placed on a polished metal plate. The most important tools for particle manipulation are the probe Figure 4 . 1 9 Typical I R alkali halide pellets in I R microspectrometer holders a n d a com pres­ sion cel l . and the forceps. Each of these tools is available in a variety of shapes and sizes from a host of suppliers. The selection of the appropriate probe or forceps is a matter of taste. Some IR microspectroscopists suggest very fine tools for the manipulation of small particles. However, if the probe is too fine, it can damage the particle. A particle can be transferred by touching it with the probe while observing it under the stereomicroscope. The probe is lifted slightly, and with the free hand, the IR window is brought into view under the stereomicroscope. The probe is lowered until it touches the surface of the window, then gently turned to release the particle. If the probe and particle are kept under the microscope, there is less chance that a valuable sample will be lost. Once the sample is on the analysis window, it is usually flattened with a probe, roller, or another window (e.g., a diamond cell ) . For efficiency, multiple samples can b e prepared o n one salt plate for IR transmission analysis. To prevent confusion, detailed draw­ ings of each sample's position and shape should be made before the pellet is transferred to the IR microspectrophotometer. A label can be scratched into the salt pellet next to each sample. One good method is to prepare the samples as if they were on a clock face. Another system was devel­ oped by Hill; in this method, a numbered grid is scratched into the pellet ( Fig. 4.20), and a sample is placed within a square (Hill 1 99 3 ) . With this procedure, the samples' positions can be easily recorded in the notebook; the position numbers are readily discernible under the IR microspectro­ photometer, and chaos is not introduced if the pellet is rotated when transferred to the analysis stage. Once prepared, the IR window with sample is placed on the analysis stage of the IR micro spectrophotometer. Although the details of instrument adj ustments and alignments vary depending on the manufac­ turer, certain operations are carried out in all IR microspectroscopic analyses. First, using the visible-light capability of the microscope, the Figure 4.20 A photom icrograph ( x 20) of a labeled grid particle is brought into focus and centered in the field of view. After this, scratched into an NaCI pellet. This method the condenser should be checked to ensure that it is at the correct focal helps locate multiple samples placed on point for that particular sample and its substrate material. These focus­ one window. ing and centering steps are critical for accurate spectral results. Apertures are used to isolate the particle, as shown in Figure 4 .2 1 . Rectangular, knife-edge apertures are the most common. When pos­ sible, the edges of the samples should not be included in the analysis area, since the curved edge of the sample can act as a lens and cause dif­ fraction of the beam; this effect is significant in single-aperture micro­ scopes (Messerschmidt 1 9 8 8 ) . Once isolated, the sample stage is moved 72 Chapter 4 Flattened particle Fiber Cross section Figure 4.21 Rectangular aperture selection for a homo­ geneous particle, a fiber, and a cross sec­ tion layer. Each of four knife-edge apertures is positioned to block the I R radiation from regions not selected for analysis. to expose a portion of the IR window where no sample is present. A background single-beam spectrum is collected ( Fig. 4.22). The stage is then moved back until the sample is brought back into view. The sample is scanned and ratioed to the background spectrum, and a transmittance ( % T) versus cm- 1 IR spectrum is produced. The isolation and analysis steps may be repeated for the analysis of various particles loaded on a single IR window. If the size of the aperture is changed from one particle to another, or if the particles are located far away from one another on the window, it is advisable to collect a new background single-beam spectrum before scanning the next particle. Fiber analysis is handled in much the same manner. The transfer of the fiber to the window can be achieved with either the probe or forceps. Knife-edge apertures can also be used to isolate the fiber, as shown in Figure 4 .2 1 . Since many fibers are less than 40 /-Lm in width, the aperture is usually elongated along the axis of the fiber. This elonga­ tion yields a greater sampling area, which in turn produces a better signal-to-noise ratio in the measurement. As the size of the aperture in the sample stage ( x-y) plane increases, the higher energy throughput for analysis of the sample is 73 I nfrared Analysis Methods Background Q)t'()'"'" �if!. .�if!.�()'"cE c E (f) c 4000 3600 600 3200 Polystyrene Q) Ul c 4000 3600 3200 Ratioed polystyrene spectrum Figure 4.22 A single-beam background spectru m , a single-beam polystyrene spectru m , and the resultant ratioed polystyrene spectru m . 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) reflected in the magnitude of the signal seen at the detector. Figure 4.23 illustrates this effect. The top spectrum is the result of measuring a 20 f.1m width of a sample 1 00 f.1m in length. Below is the spectrum for the same sample analyzed with a larger aperture measuring 100 x 1 00 �m. A larger aperture area yields a spectrum with less nOise for the same resolution and sampling time. Diffraction effects become particularly important when aper­ tures are employed. If light is passed through a small slit, the light rays may bend, as shown in Figure 4.24. This process is referred to as diffrac­ tion. The top drawing shows the diffraction effect for the case in which the slit size, x-y, is much greater than the wavelength of the radiation, A. Chapter 74 4 OJ U C :e.=<ft.'"'" E <fl C 4000 3600 3200 2800 2400 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 2000 1 800 1 600 1 400 1 200 1 000 Figure 4.23 Two spectra showing the effects of a vary­ ing aperture area for the same sample, x x wh ich is greater than 1 00 1 00 !-1m. The top spectrum was collected with an aper­ ture of 2 0 1 00 !-1 m . The bottom spec­ trum was collected with an aperture of 1 00 x 1 00 fLm . Note the difference i n noise . I t is best t o use t h e largest apertu re that the sample and instrument will allow. 800 600 Wavenumber (cm- 1 ) Note that the diffraction is small. But as the slit size approaches the wavelength of the radiation, as in the bottom drawing, the diffraction becomes more pronounced. Thus, diffraction is a limiting factor that relates to the minimum aperture size used in the IR micro spectroscopic experiment. The longest wavelengths of IR light used in the typical mid­ IR experiment are on the order of 10 ,..,.,m . Therefore, this figure repre­ sents the resolution limit achievable in IR microspectroscopy. Apertures smaller than this will yield sample information from outside the region of interest, even though such areas are not visible through the aperture. Recent experiments at the Getty Conservation Institute found that a bet­ ter rule of thumb is to employ apertures no smaller than 20 ,..,.,m in width. This guideline ensures good quality in the resulting IR spectrum. It is important to differentiate between the width of a sample, as described above, and its thickness. The thickness of the sample (z direction) is one factor that determines the absorbance of the material. Figure 4.25 shows two spectra of the same sample at two different thick­ nesses but measured with the same parameters. The top spectrum is for the sample when it is too thick. Because some bands are totally absorb­ ing, the usefulness of the IR spectrum is reduced, and it is a poor can­ didate for any mathematical routine, such as spectral searching or 75 I nfrared Analysis Methods I�"''' "' --, " subtraction. The bottom spectrum was collected after the sample was thinned. This time, all absorption bands are on scale. A good rule of thumb is that the % T for the most intense band should not be less than 1 0 % T ( or greater than 1 . 0 absorbance units ) . Appropriate sample thick­ �- nesses for use in IR analysis range from 1 f1m to 20 f1m, depending on the molar absorptivity of the compound of interest . .. In terms of particle and fiber analysis, flattening of the sample may be required to obtain the desired sample thickness. Several options are available. First, the sample can be flattened with a metal y ..I -..L. .J .J J probe or roller blade. Flattening can be done on a glass or metal surface prior to placement of the sample on the window; however, this procedure can make the sample fragile and difficult to transfer. The sample can also be flattened directly on the window or diamond cell. The advantage of pressing the sample directly on the window is that the sample is more likely to lay flat on the surface. For a good spectrum, it is important that the sample be flat and in focus; there should also be no air between the sample and its substrate. A second method of flattening the sample is to place another transparent window on top. Commercially available compression cells Figure 4.24 The effects of aperture slit size on diffrac­ tion. The top illustration shows that dif­ fraction is minor when the aperture slit (x-y) is wide. The lower ill ustration shows () OJ c co i:' E '" c co F if. that when the aperture slit (x-y) is narrow, near the wavelength of radiation (A), dif­ fraction is sign ificant. 4000 3600 3200 2800 2400 2000 1 400 1 200 1 000 800 600 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 Wavenumber (cm- 1 ) 1 200 1 000 800 600 1 800 1 600 () OJ Figure 4.25 Two spectra showi ng the effects of sample thickness. The top spectrum is of a sample c co i:' E '" c co F if. of glue that is too thick; some absorption bands are totally absorbi ng. The bottom spectrum was collected from a thinner area of the same sample; all absorption bands are on scale. 76 Chapter 4 with alkali halide plates or diamond windows can be used to carry out this operation with good results. A nice by-product of compressing the sample is the corresponding increase in sample area. Placing a window on top of the sample is also an important step if the sample-such as a fiber-is not flat; a curved upper surface will bend the light and decrease the energy transmitted to the detector. When two IR windows are used, however, the increase in total thickness will also decrease the energy reaching the detector and may change the low-wavenumber cutoff point for the experiment. If this is a problem, two 1 mm windows, instead of the normal 2 mm windows, may be used. Alternatively, once compressed, a sample, unless it is elastomeric, will normally remain flat. Therefore, the upper compression window can be removed from the cell and the analysis done with the sample on a single window. In either the compression cell or the diamond cell, a back­ ground spectrum is collected in an area adj acent to the sample, with the beam passing through the upper and lower windows. Because of the thickness of the sample, these windows typically have a small air space between them that can produce interference fringes in the background (Sommer and Katon 1 9 8 8 ; Reffner and Martoglio 1 9 95; see also Fig. 4 . 1 0 ) . To eliminate these fringes, a small cube of salt (NaCI, KBr, BaF2, etc . ) is placed next to the sample prior to compression. The background spectrum is then collected through the pressed-salt region, and the air gap and its ensuing fringes are eliminated. For heterogeneous particles and fibers, visually different regions of the sample can be isolated and analyzed. This approach pro­ vides a convenient separation technique without the need for additional sample preparation steps requiring time and energy. Cross section analysis Many samples encountered in art conservation are composed of multiple layers. The obvious example is a paint chip from a painting. One approach to handling this type of sample involves manual separation of the layers for analysis. The sample is placed under the stereomicroscope. After some observation and identification of the structure, the analyst picks off representative particles from each of the layers. The particles removed are then analyzed as described above . This technique works well with samples that have easily identifiable layers. The major draw­ backs to this technique include the time and care needed to perform the separation. In addition, removal of a single particle, particularly from hard samples, may be difficult. An alternative approach is to embed the sample in an appro­ priate medium and then to microtome it into thin cross sections. Once the mold, containing sample and medium, has hardened, it can be mounted in a microtome and sliced into thin sections for sequential analysis of layers under the IR microspectrophotometer. The analysis of the thin cross section is very similar to that of particles and fibers, in that apertures are used to isolate the area of inter­ est. In the case of a multilayer sample, the apertures are used to isolate a single layer within the sample. This procedure is illustrated in Figure 77 I nfrared Analysis Methods 4 .2 1 . After the IR spectrum for one layer is collected, another layer can be isolated and its spectrum collected. In this way, the composition of each layer can be determined. Mapping studies Molecular mapping, also known as functional group imaging, involves t«OJ'sQ. •6 •7 •9 1•0 the systematic study of the structure of a material of interest; molecular mapping can be done in either transmission or reflection microspec­ troscopy ( Harthcock and Atkin 1 9 8 8 ; Reffner 1 9 89; Krishnan, Powell, and Hill 1 99 5 ) . Molecular mapping with an IR micro spectrophotometer is a technique complementary to elemental mapping as achieved in a scanning electron microscope, and it may often be performed on the same sample. Band In its simplest form, linear mapping is conducted as follows: 1 ( 1 ) An aperture of an appropriate size is made, and a background spec­ trum is collected in a nonsample area. (2) With the sample stage, the edge of the cross section is brought into view through the aperture, and the spectrum is collected. ( 3 ) The sample stage is then moved in one direction by a given amount to reveal an adj acent area through the aper­ ture; once again, the spectrum is obtained. (4) The process is repeated until the entire cross section has been analyzed. This procedure, known 2 6 Position number 4 8 as IR linear mapping microspectroscopy, is illustrated in Figure 4.26. On many instruments, this routine can be automated by the use of a map­ Figure 4.26 ping stage that is operated either by a controller box or by software from The I R l i near mapping tech n i q ue . The the spectrometer computer. Commercially available mapping stage acces­ top i l l ustration shows a set of spectral sories fit many IR microspectrometers. Commercial software is available collection positions selected for the li near to help display the information obtained from such an experiment (see mapping of a m u ltilayer material. The Suppliers, Galactic Industries Corp.; Spectra-Tech, Inc.; Bio-Rad Digila b ) . resolution of the map is affected by the A n area mapping experiment i s done t o yield information density of the collection sites and the size about an area of interest; it may be done as a transmitted light experi­ of the aperture. For this example, ten ment on thin sections or as a reflected light experiment on embedded, spectra were collected. After the spectra polished paint cross sections. In either case the sample is placed on the x = are examined, a few specific absorption sample stage of the IR microspectrophotometer, and an analysis grid bands are selected, and their intensity is containing several hundred points (e.g., 20 30 grid 600 points) is plotted versus their collection position on selected for the area of interest on the sample. An array of spectra is pro­ the sample to produce a line map, such duced by the collection of a single spectrum as the aperture moves to as the bottom figure. Of the absorption each point on the grid ( Figs . 4.27, 4 . 2 8 ) . The effective resolution of the bands plotted , only band 2 has an components in the sample is determined by the size of the analysis aper­ in creased intensity from a component ture and the density of the grid. The size of the aperture for the spectra in the first layer. Both absorption bands in Figure 4 . 2 8 was 40 x 20 11m (x-, y-axes, respectively) . The selection of 1 and 2 appear in the spectrum for the appropriate step size and aperture size involves a trade-off between reso­ second sample layer, while none of the lution, energy throughput, and the length of the experiment. In this case, plotted absorption bands occur in the a step size of approximately 20 11m gives an overlap of the windows in spectrum for layer 3. The last and fourth the x direction. Overlapping apertures, while not necessary for complete layer contains absorption bands 2 and 3 sample imaging, do provide an effective increase in the resolution of the in its spectru m . components. The collection and processing of the 50 scan spectrum at each grid point requires about 1 minute. Therefore, a mapping experi­ ment with 1 5 0 grid points, such as shown in Figure 4.27, would require about 2.5 hours. 78 Figure 4.27 4• • • Chapter ••••• An example of grid selection for an IR area map. The dots designate x-y stage loca­ tions for the center of an analysis aperture co Analysis apert ure (example on right) . The resolution of the components i n the sample is directly related to the size of the aperture window and to the density of the grid. 5 4 3 2 Q) .0<{()ccoo(/) 160.0 140.0 i? 120.0 100.0 80.0 ":JQ <;:-<oU,s§v r/; Figure 4.28 A series of spectra collected by computer from an area grid, such as shown in Figure 4.27. The computer stores the collection position of each spectrum to use later for contour plots. 3500 3000 2500 2000 Wavenumber (cm- 1 ) 1500 1000 From the array of spectra, contour maps may be produced that provide information on the concentration and location of com­ pounds related to various functional groups in the sample ( Fig. 4.29 ) . This i s done b y selecting a n absorption band o f interest, such a s a hydrocarbon band, and plotting its intensity versus its position in the grid where it was collected. This procedure produces an area map of the intensities of that specific band plotted as a contour map, where lines connect the areas of similar value. In these plots, line thickness has been used to represent the changes in intensity of the absorption bands. The thickest lines correspond to the areas of strongest band intensity-that is, the highest concentration in the sample-and the thinnest lines repre­ sent the lowest intensities. The intensities are relative to one another, and the background intensity may not be zero, depending on the base­ line in the region. The method of IR mapping shows potential for the determi­ nation of materials and their locations within a cross section sample. The technique is complementary to elemental mapping with an electron 79 Infrared Analysis Methods 2 1 06 2063 Figure 4.29 A contour map showing the intensity of the spectral carbonate band ( 1 424 cm-1) i n relation to its position on the grid where it was collected. To plot the data as a con­ tour map, areas of similar absorbance �� >c o o a. en .� 201 9 1� -===::�:=: � ����� - � � 1 976 1 933 1 890 intensity are con nected with a line. The heavier the line, the higher the concentra­ tion. (Paint cross section from A llegory of Fortune by Dosso Dossi, J. Paul Getty C=�L-�- 1 803 4846 4885 4924 4963 5002 5041 5080 5 1 1 9 5 1 57 5 1 96 5235 5274 531 3 5352 5391 Museum [x67J . ) X-axis position (11m) microscope and may be done on the same sample. At this point, the method has two maj or limitations. The first is its dependence on the use of specular reflection as an analysis method; this dependence places a minimum size of 20 x 20 J.lm on the analysis window because of energy restrictions. Specular reflection can also result in band distortions and shifts, for which it is difficult to compensate. The second limitation is that a material cannot be reliably identified based on one IR absorption band. Thus, additional analyses are required to supplement the map and provide interpretation. Future computer programs should allow the cre­ ation of a map based on the selection of multiple absorption bands that can help identify specific compounds. Microspectrophotometer accessories Several accessories are available for IR micro spectrometers ( Reffner, Wihlborg, and Strand 1 99 1 ) . One is the grazing-angle obj ective ( see Suppliers, Spectra-Tech, Inc . ) , which is used for low-angle reflection measurements of very thin films on polished metal surfaces, as well as for the detection of monomolecular surface films. Another useful acces­ sory is the ATR obj ective ( see Suppliers, Spectra-Tech, Inc.; Bio-Rad Digilab; Nicolet Instrument Corp.; Bruker Instruments; Graseby Specac; Bomem International) , which may be used for internal reflection micro­ spectroscopy to examine small areas of nonreflective materials nonde­ structively ( Fig. 4 . 3 0 ) . Chess provides a good paper on the use of these two obj ectives ( Chess 1 99 5 ) . ATR microspectroscopy, a s with the macro version, i s a sur­ face analysis technique that requires little to no sample preparation. It has been shown to be very useful for the analysis of single fibers, hair and hair coatings, ink on paper, and paint chips ( Bartick, Tungol, and Reffner 1 994 ) . Different crystals ( internal reflection elements) may be selected, depending on the type of sample, its hardness, and its refractive index. ZnSe, germanium, silicon, and diamond elements are available. 80 Chapter 4 Figure 4.30 A Cassegrain reflective optics objective (left) and a micro ATR objective (right) for use on an IR microspectrophotometer. Summary One of the most versatile and important aspects of IR spectroscopy is that samples of any form or composition can be analyzed. Selecting the optimum method for the analysis, however, is not always easy; many sample preparation methods exist, and the analysis technique chosen often impacts the spectral results. Transmission analysis methods have become the de facto standard, because they were the earliest and most widely used techniques. Most reference spectra are generated by trans­ mission methods. While there is no one technique appropriate for the analysis of every sample, some methods can be used for most sample types. Many can be prepared as thin or compressed films on transparent windows, especially with the aid of a compression cell that uses alkali halide or diamond windows. The use of a beam condenser or microscope is also very beneficial to the analysis of the small samples often encountered in the art conservation field. Sample analysis techniques for IR micro spec­ troscopy include mapping experiments used to characterize the composi­ tion and position of constituents in nonhomogeneous samples. Additional Reading Infrared instrumentation Ferraro, J . R., and L. J . Basile 1 978, 1 979, 1 982, 1 9 8 5 . Fourier Transform Infrared Spectroscopy. Vols. 1-4. New York: Academic Press. Griffiths, P. R., and J . A. de Haseth 1 98 6 . Fourier Transform Infrared Spectrometry. New York: John Wiley and Sons. Koenig, J . L. 1 992. Spectroscopy of Polymers. Washington, D.C.: American Chemical Society. Low, M . J . D . , and N. S. Baer 1 977. Application of infrared Fourier transform spectroscopy to problems in conser­ vation. Studies in Conservation 22: 1 1 6 . I nfrared Analysis Methods 81 Reffner, J. A., J . P. Coates, and R. G . Messersch m i d t 1 9 8 7. Chemical microscopy with FTIR microspectrometry. American Laboratory (April) : 8 6 . S m ith, A . l. 1 9 79. Applied Infrared Spectroscopy: Fundamentals, Techniques, and Analytical Problem Solving. New York: John Wiley and Sons. W i l lard, H. H . , l. l. Merritt, J r. , and J . A. Dean 1 9 84. Instrumental Methods of Analysis. New York: D. Van Nostrand Co. Analysis methods ASTM C o m m ittee 1 9 79. Manual on Practices in Molecular Spectroscopy. Philadelphia: American Society for Testing Materials. C h i cago Society for Coating Techn ology 1 9 80. Infrared Spectroscopy Atlas for the Coatings Industry. Philadelphia: Federation of Societies for Coating Technology. Griffiths, P. R., and J . A . de Haseth 1 9 8 6. Fourier Transform Infrared Spectrometry. New York: John Wiley and Sons. Harrick, N. J . 1 9 79. Internal Reflection Spectroscopy. Ossining, N.Y.: Harrick Scientific Corp. Harrick Scientifi c Corp. 1 9 87. Optical Spectroscopy: Sampling Techniques Manual. Ossining, N.Y.: Harrick Scientific Corp. H u mecki, H. J . , ed. 1 9 95. Practical Guide to Infrared Microspectroscopy. New York: Marcel Dekker. Kortu m , G . 1 969. Reflectance Spectroscopy. New York: Springer-Verlag. Messers c h m idt, R. G., and M. A. Harthcock, eds. 1 9 8 8 . Infrared Microspectroscopy: Theory and Applications. New York: Marcel Dekker. Roush, P. B . , ed. 1 9 87. The Design, Sample Handling, and Applications of Infrared Microscopes. Philadelphia: American Society for Testing Materials. S m ith, A. l. 1 9 79. Applied Infrared Spectroscopy: Fundamentals, Techniques, and Analytical Problem Solving. New York: John Wiley and Sons. Wendlandt, W. W., and H. G. Hecht 1 969. Reflectance Spectroscopy. New York: Wiley-Interscience. Wilks, P. A . 1 9 65. Internal Reflection Spectroscopy. Norwalk, Conn.: Wilks Scientific Corp. Chapter 5 Spectral Interpretation Qualitative IR spectroscopy is a valuable analytical tool that allows for the identification of organic and inorganic materials. Each compound's IR spectrum contains a substantial amount of information. This informa­ tion, along with some patience, skill, and knowledge about a sample's background, can be used to determine molecular structures successfully, as well as to characterize unknown materials. This chapter covers general methods for spectral interpreta­ tion and then concentrates on specifics that apply to natural organic materials, colorants, and mixtures often found in works of art. Spectra are discussed in terms of their important features. Also included are fac­ tors that may affect the interpretation of an IR spectrum, such as its generation, presentation, and processing. Some special considerations, cautions, and limitations of IR analysis will be presented in terms of spectral interpretation. Infrared Spectra An IR spectrum displays detector response and is usually plotted in % transmittance (% T) or absorbance (A, which is the base 10 log of the reciprocal of T) versus IR frequency ( in wavenumbers [cm - 1 ] ) . A fre­ quency of radiation that interacts with the sample produces an absorp­ tion band that is characteristic of the energy required for a particular molecular group transition ( usually a vibrational motion). The collective position and pattern of these absorption bands designate the combina­ tion of molecular groups found in any specific compound. Absorption bands The absorption bands in a recorded IR spectrum exhibit three important parameters: frequency, shape, and intensity. These band attributes are unique for each individual molecule or material. Band frequency The band positions, or frequencies, indicate the presence of certain func­ tional groups in a material. Band assignment in the functional group region ( 4000-1 500 cm - 1 ) is usually straightforward, while assigning a Spectral I n terpretation 83 band to a specific functional group in the fingerprint region ( 1 500-500 cm- 1 ) may be difficult, since many types of functional groups absorb at similar wave numbers in this region. Identification of a material using the fingerprint region is based on the correlation between the peak pattern of the sample and the peak pattern of a standard material of known chemical composition. Many aids, some of which are discussed in this chapter, assist the spectroscopist in the determination of molecular structures based on band frequencies. Band shape The shapes of absorption bands provide information concerning the group functionality as well as the material purity. All single absorption bands are, by nature, symmetrical in shape, resembling a normal bell curve, with a peak maximum and equal wings on each side. Deviations in band symmetry, such as a slight shoulder or an unusual tail, indicate the presence of an overlapping band. In a complex molecule, deviations in band shape may be related to similar functional groups that exist in dif­ ferent molecular environments. The presence of asymmetric bands can also indicate that a sample is a mixture or has been modified, such as by oxidation. Theoretically, a normal band shape is very sharp. The width of a band can be increased by inter- and intramolecular interactions, as well as by overlapping bands. Broad bands, such as those due to hydro­ gen bonding or ionic functional groups, are very characteristic. Doublet bands, often produced by crystalline lattice effects, are also useful in characterizing a material. Band intensity The relative intensity of a band, in comparison to the other bands in the spectrum, provides information on the amount and type of a specific functional group present in a molecule. Functional groups that are responsible for a large change in the dipole moment of a molecule­ carbonyl groups, for example, will produce very intense absorption bands. Of the three band attributes, band intensities are most likely to show deviations related to sample preparation. These three attributes define each band in a spectrum. Any two identical samples prepared under identical conditions will produce identical spectra. Any deviation-in band frequency, shape, or inten­ sity-between the two spectra indicates a difference between the two samples. While differences may be due to sample composition, they may also be due to sample preparation, spectral plotting format, or instru­ ment parameters. While the last three factors do not change the molecu­ lar vibrations in the sample, they can cause superficial changes in the character of the spectra that need to be accounted for in the spectrum interpretation. Every good spectrum, especially a reference spectrum, should include information on conditions of analysis and instrumental parameters; this information allows the spectroscopist to make a knowl­ edgeable comparison. 84 Chapter 5 Plotting format The interpretation of an IR spectrum is based directly on visual inspec­ tion of the spectrum, on recognition of characteristic features, and on comparison of the spectrum with reference spectra. Visual cuing is directly dependent on the plot of the spectrum. Several types of spectral presentation formats may be found in j ournal articles, reference books, and spectral libraries. To the novice spectroscopist, these may seem con­ fusing and not comparable. But in fact, the spectra are consistent and reliable and, with a little practice and an understanding of the various plotting formats, they can be visually compared. Examination of the axis labels will quickly provide the mode and scales of the plot selected in any particular case. Figure 5 . 1 displays the same IR spectrum of linseed oil in four commonly used plotting formats. Close examination of each plot may be needed in order to understand that, indeed, these are all plots of the same material. The most noticeable difference among these four spectra is that, in some instances, the bands or peaks descend (transmit- Linseed oil ( X 2 expansion) 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 � V v,,;'V :-0� ��Q) � ,�� � 1/01 T �t'�<J)� 90 80 70 A 60 == -B b II c + r1 D c--- �I VI ·tr------ c--I'-.-.. J'-./-- ! -'" . -� 3400 3000 Linseed o i l (linear) 1800 2200 2600 -. --- 1000 1 400 �<J) 50 40 Wavenumber (em ' ) 3800 600 90 f 80 -- 6 8 Linseed oil 12 10 50 40 16 14 �m Linseed oil (X2 expansion) 4000 Figure 5.1 The same spectrum of linseed oil shown in four different plot formats. The format of plot A is generally considered standard. The format in plot C is no longer com­ monly used. 3600 3200 2800 -" .-- _. it! 2400 2000 1 800 1 600 1400 1 200 -.- :1\ Wavenumber (em- ' ) -- 0.40 0.30 ----- - 1 000 800 Q) () 70 E 60 Wavenumber (em- ' ) 4 () 600 0.20 0.10 .0<t:� Q) () £ Spectral Interpretation 85 tance, Fig. 5 . 1 , spectra A-C ) , and in some they ascend (absorbance, Fig. 5 . 1 , spectrum D ) . The absorbance mode i s used for quantitative analysis and other mathematical processing. According to Beer's law, the intensity of each band is directly proportional to the concentration of the absorbing species-such that there is a linear relationship between band intensity and concentration. This linear relationship applies only to spectra in absorbance mode; in transmittance mode, there is a logarithmic relation­ ship between band intensity and species concentration. Besides quan­ titative analysis, other computer spectral manipulation methods-such as subtractions, transformations ( Kubelka-Munk, Kramers-Kronig), deconvolutions, and spectral searches-are done with the spectra in absorbance . This may be a hidden process, since computers can instanta­ neously switch between absorbance and transmittance. When one mode of display, such as transmittance, is selected for the spectrum, the com­ puter will perform any conversion necessary as part of the processing and quickly return the processed spectrum to the screen in its original mode (i.e., transmittance) . Spectra plotted i n transmittance are shown i n Figure 5 . 1 (A-C ) . This mode has been historically used for IR spectra a n d i s still the most commonly seen format for reference spectra. A transmittance spec­ trum is the ratio of the radiant power transmitted by a sample to the amount of incident radiation on the sample. Prior to the use of Fourier transform IR spectrometers ( FT-IRs ) , this was the value read directly from the detectors and plotted. Transmittance mode has an advantage for the viewing and comparison of spectra, because the logarithmic scale amplifies the intensity of the weak bands while keeping the highly absorbing bands on scale. With the advent of the FT-IR and its integral computer, the operator may select any mode for viewing, plotting, and calculation. The computer can quickly and easily convert from one format to another. Since it will often be necessary to compare the hard copy (printed form) of spectra in different formats, however, it is important to become famil­ iar with the visual and mental gymnastics required to convert between absorbance and transmittance. The scales should always be checked, because there are some spectra that have been plotted in transmission but then inverted, with the bands ascending; conversely, some spectra are plotted in absorbance units, with the peaks descending. This incorrect and confusing practice occasionally appears in publications. Varying abscissa scales are also seen in IR spectral plots . Visible light, when measured in wavelengths, is typically reported in microns ( /-Lm ) . For IR spectra, the corresponding use of the linear scale of wavelengths in microns ( 2 .5-1 6 . 6 /-Lm; see Fig. 5 . 1 , spectrum C) is a simple representation and easily related to the other familiar spectral measurements, such as UVNis, that are used in spectroscopy. Older, prism-type dispersive instruments produced plots with linear wave­ lengths; this practice is now considered obsolete. The surge in the generation of IR spectral libraries occurred with the grating-type dispersive spectrophotometer (without computer ) . 86 Chapter 5 The output of this dispersive spectrophotometer was linear in wavenum­ bers or frequency (cm- l ; see Fig. 5 . 1 , spectrum B ) . Wavenumbers are reciprocally related to wavelength (e.g., 1 000 cm- l = 1 0 /Lm) and are considered more accurate for spectral presentation, since the energy of a vibrational mode is a function of frequency and not of wavelength. In a linear wavenumber representation, however, the finger­ print region of the spectrum ( 2000-500 cm- l ) is compressed and difficult to see. Thus, it became a standard procedure to switch the speed of the chart recorder at 2000 cm-l to a slower setting; this practice resulted in a x 2 scale expansion of the fingerprint region. Thus, the plots have a lin­ ear scale between 4000 and 2000 cm-t and a double-size linear scale between 2000 and 500 em- I , as shown in Figure 5 . 1 , spectra A and D . Plots that use a x 4 scale expansion may occasionally b e found. Because of the large number of reference spectra generated in the format shown in Figure 5 . 1 , spectrum A (i.e., most published libraries and reference books ) , this format has been termed standard. The spectrum is plotted in transmittance, with a linear wavenumber ( cm - l ) scale containing a x 2 expansion i n the region o f 2000-500 cm- l . Instrument configuration Several possible options for instrument configurations exist. While these options do not change molecular absorption bands, they may change the appearance of the spectra. IR mercury-cadmium-telluride (MeT) detec­ tors are available in narrow, medium, and wide ranges. The choice of the detector affects the sensitivity and the spectral range of a given spectrom­ eter, with the narrow-range detector providing the highest sensitivity. Thus, the scale of a spectrum may range from 4000 to 700 em- I , or from 4000 to 500 em- I , depending on the type of detector deployed. The resolution, or number of data points per spectrum, is selectable on FT-IR instruments. A higher-resolution spectrum will con­ tain more data points and will thereby provide better representation and separation of the true absorption bands. To collect a higher-resolution spectrum, the instrument resolution setting must be changed to a lower wavenumber, since this parameter indicates the interval for data collec­ tion. For example, an instrument set at a resolution of 1 cm- l will col­ lect a data point every 1 cm - t . Thus, for a spectrum collected over the range of 4000 to 800 em-I, there will be a total of 3200 data points. An instrument set at 4 cm-l will only collect one-fourth as many, or 800 data points. Therefore, a resolution of 1 cm- l is higher than a reso­ lution of 4 cm- t . A commonly used resolution i s 4 cm- t • However, most instru­ ments are capable of at least 1 cm-t resolution, while many digitized library spectra were collected at 8 cm- t . Spectra produced at the finer resolutions (i.e., 1 em- l or below) may contain a distinct band in an area that only appears as a shoulder in a spectrum collected at a lower resolu­ tion. Interest in studying the fine spectral details is one reason for using the higher resolutions, but a possible effect on the character of the spec­ trum should be kept in mind when spectra recorded at different resolu­ tions are compared. Additionally, higher-resolution spectra require more 87 Spectral Interpretation time for data collection, and since their files are larger, they also require more disk storage space. Most search routines recommend that the reso­ lution of the search spectrum stay within a factor of 2 of the resolution of the library spectra. Qualitative Analysis There is no one set of procedures for the identification of unknown mate­ rials by IR spectroscopy. Nor is it possible to identify every material by IR spectroscopy alone. However, with a good-quality spectrum, it is pos­ sible to screen a sample and to obtain the general classification of a mate­ rial by its major functional groups. Additionally, and sometimes most important, it is possible to rule out several types of materials based on the absence of major functional groups. Thus, it is essential to understand the analytical question framed for each sample prior to spending a significant amount of time on the interpretation of a spectrum. In general, the interpretation of a spectrum of an unknown material requires the identification of functional groups in the spectrum, along with direct comparison to reference spectra. Several useful tools (correlation charts, flow diagrams, computer search routines, etc . ) are Figure 5.2 available to speed up the process. One possible, stepwise approach for An identification scheme for the systematic the identification of an unknown spectrum is presented in Figure 5 . 2 . interpretation of I R spectra. Many aids are A simple spectrum may be identified within a few steps, while a complex avai lable to assist in interpretation. The mixture may require multiple passes through the procedure. final step for identification is always visual comparison of the sample spectrum to Spectral quality known reference spectra. The first step in spectral interpretation is the determination of spectral quality. Many hours can be wasted interpreting a poor-quality spectrum C ::> that misrepresents the true absorption band positions, shapes, and inten­ Begin sities. Table 5 . 1 lists some requirements for a good IR spectrum. Most Visual comparison with collections of reference spectra (match)? 10 material class? (a) Functional group analysis (b) Correlation charts (c) Flow diagrams Summary yes (a) Does match correspond to information known about piece? (b) Can discrepancies be justified? (c) Are possible errors eliminated? (d) Has the initial analysis question been answered? yes no no Alternate analysis method 88 Chapter 5 Table 5 . 1 Req u i rements for a good -quality I R spectru m . Specifi cations of a good-qual ity spectrum Parameter flat and level, positioned near 1 00 % transm ittance Baseline (0.0 absorbance) Possible problems res u lting in deviations from specifications sample is poorly ground; sample surface is not flat; background does not match sample spectrum Noise maximum noise level no greater than 1 % of strongest band sample too small; i nsufficient nu mber of scans collected I ntensity signal no stronger than 1 0 % transm ittance ( 1 . 0 absorbance) sample too concentrated ; sample too thick Extraneous bands water vapor and carbon dioxide should be less than 2% transm ittance (0.1 absorbance) background does not m atch sample spectru m ; instrument is poorly purged poor spectra are the result of improper sample preparation techniques that may be corrected by preparing the sample again. Occasionally an alternate analysis method, such as reflection versus transmission, may be required to eliminate a problem. In cases in which the sample cannot be reanalyzed, computer routines may be used to manipulate spectra into a better form. Any alteration of spectra must be performed with cau­ tion-and only done as a last resort, as it has the potential to produce misleading results. Examination of the spectrum baseline-that is, the portion that has no absorption bands-can provide information on spectral qual­ ity. One quality check for the spectrum is whether the baseline is flat, level, and positioned near 1 0 0 % T ( 0 . 0 absorbance). Shifting of the base­ line above or below the proper position occurs when the intensity of the background spectrum does not correspond to the sample spectrum. With IR microspectrophotometers, this shifting may occur if the aperture size for the background is different from that of the sample. The baseline can also be shifted when a sample is black, since all wavelengths will be strongly absorbed. A sloping baseline is usually an indication that the radiation has been diffracted andlor scattered as it passed through the sample. This problem can occur if the particles in a potassium bromide (KBr) pellet are not ground finely enough or if the sample surface of a thin film on a window is not flat. Figure 5 . 3 shows a spectrum with a sloping baseline before and after the application of a computerized baseline correction routine. Such routines attempt to level the baseline to 1 00 % T (0.0 absorbance ) . Linear and multiple-point correction curves are available. Any spectral alteration of the digitized data by baseline correction should be carefully examined for changes in the relative intensities of the absorption bands. Examination of baseline noise level is also used as a quality check. The signal-to-noise ratio of a spectrum is calculated by comparing the intensity of the noise level at the baseline to the intensity of the 89 Spectral I nterpretation 1 00 Sloping baseline 90 Q) u c (1j :t:if.�: 80 , E (/) c (1j 70 ' �"'''k 60 ' 3500 1 05 2000 2500 Wavenumber (cm- 1 ) 3000 1 500 1 000 Baseline corrected �c \�\4r'r4 .��E �tt.� 1 00 95 Figure 5 . 3 An I R transm ittance spectrum for a protein before and after baseline correction . A sloped basel ine is often caused by diffraction of light when it passes through the sam ple. Baseline correction routines attempt to level the baseline at 1 00 % transm ittance. Relative absorption band intensities may be altered by baseline correction. (I Q) u c(/) (1j if. 90 85 80 75 70 , 3500 3000 2000 2500 Wavenumber (cm- 1 ) 1 500 1 000 strongest absorption band. This calculation is termed the signal-to-noise ratio. The higher the signal-to-noise ratio, the better the quality of the spectrum. A very small sample will often produce a spectrum with high noise levels. The best ways to minimize high noise levels are to run a larger sample or to collect and average more scans. If this is not feasible, a smoothing routine may be applied to decrease noise levels. Figure 5 .4 shows an IR spectrum before and after smoothing to a 5 0 % level. Smoothing effectively decreases the resolution of the spectrum, however, and minor absorption bands or shoulders may disappear. The most intense absorption band in the spectrum should be between 1 0 %T and 6 5 % T ( 1 .0-0 .2 absorbance). The purpose of an intensity check is to ensure that the sample concentration or thickness is optimum. When a sample is too thick, the strongest absorption bands with a transmittance greater than 1 0 % T ( 1 .0 absorbance) will " bottom out," and information regarding band position, shape, and relative intensity will be lost. For accurate quantitative work, such as spectral 90 Chapter 5 Un smoothed subtraction, the optimum absorption range is smaller, with an absorption maximum no greater than 20% T ( 0 . 7 absorbance; see " Subtraction tech­ niques, " p. 1 24 ) . When the strongest absorption band is less than 6 5 % T, the concentration of the sample is low, and some weak bands may not be easily recognized. When comparing the spectrum of a weak sample with a reference spectrum, a spectroscopist can compensate for the feeble bands, but a computer search routine may have difficulty. Another important consideration is whether the instrument and its sample compartment are purged with dry, carbon dioxide ( C02 )-free air. Vapor-phase water (H2 0 ) produces small, sharp absorp­ tion bands in the regions from 4000 to 3000 and 1 8 00 to 1 600 cm- 1 , while the predominant CO 2 absorption band occurs a s a doublet at 2340 cm-1 ( Fig. 5 . 5 ) . Purged instruments will eliminate, or at least diminish, the appearance of these bands. Spectra from nonpurged instru- 91 Spectral Interpretation Water Water vapor vapor ()� oR. OJ c co t: E UJ c co Figure 5.5 An IR transm ittance spectrum of room air containing water vapor and carbon diox­ co ide. Most instruments are purged with dry, CO2-free air to m i n imize contributions due 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) to these absorption bands. ments will show small CO 2 and H2 0 bands if the atmosphere for the background spectrum and the sample spectrum are similar. However, if the room air changes between the background and sample spectral runs because of drafts or human presence, the spectrum may exhibit stronger atmospheric bands. While usually open to the atmosphere, the sample stage area of most FT-IR microspectrophotometers can also be partially purged with the use of a removable shroud placed on the objective lens. Visual comparison Visual examination of the spectrum involves the direct human compari­ son of a sample spectrum to reference spectra of known materials. The visual pattern recognition procedure, while simple, is very important, because it provides definite identification. It is also very time-consuming, since well over 200,000 published reference spectra are available for comparison. Further, differences between spectra of similar compounds are often quite small. Time needed for interpretation can be substantially reduced by narrowing the examined number of spectra based on the sample's physical characteristics, as well as on identification of major functional groups present in the spectrum. The experienced spectro­ scopist will occasionally be able immediately to recognize a spectrum of a material previously encountered. In any case, the visual comparison of the unknown spectrum to a reference spectrum is always the last step toward verification of an unknown material. Appendix I lists several significant books, articles, and digi­ tized databases containing IR spectra collections. These reference collec­ tions are very comprehensive for modern materials. However, they include few spectra of natural materials, such as those used historically in artist materials. In an attempt to fill this void, more than twenty museum and conservation laboratories j oined together to combine their 92 Chapter 5 collections of spectra into a single IR spectral library of artists' materials ( see Appendix I, Infrared Users' Group 1 99 5 ) . Additional compilations of reference spectra prepared specifically for use in conservation are the Gettens Collection ( see Appendix I, Snodgrass and Price 1 99 3 ) and Infrared Spectra of Naturally Occurring Minerals ( see Appendix I, Price and Carlson, forthcoming) . Many of the compilations are available in digitized form on computer disk, for convenient addition to the digital spectral library of any FT-IR. Computer libraries The coupling of high-performance computers with IR spectrophotometers allows for the rapid processing of spectra together with the storage of large numbers of IR reference spectra. Many IR operating programs also provide spectrum-structure correlations, automatic spectral interpreta­ tion, and searching of large stored libraries of IR spectra. This greatly reduces the time needed for the visual comparison of an unknown spec­ trum to reference spectra. Computer library search programs are typically based on cal. culation of the difference in peak position and intensity in the unknown spectrum versus those of known spectra. Most software library programs have an option for more than one search algorithm for distinguishing similarities between spectra. Each algorithm performs the calculations slightly differently. In order to determine the variations between these programs and the significance of the match (hit) quality, a known mate­ rial may be analyzed and its spectrum searched in the library multiple times with different search options or parameters. No matter how good the software is, it can never replace the j udgment and visual skills of a well-trained analytical chemist. The list of hits from the library search is, at best, only a starting point for the visual comparison of the unknown sample's spectrum with reference spectra. Generally, a high hit index means that the spectra match well, but this is not always the case. In some programs the hit with the best match qual­ ity is 1 00, while for other programs it would be 0.000. For example, a hit index of 0.0 7 1 6 would be an excellent match if obtained on a scale where 0.0000 is a perfect match, and a typical match of 0.2000 is con­ sidered a good fit. A computer program may find a hit that has similar bands except for one or two. If these are significant bands, then the spec­ troscopist can eliminate that hit as a possible choice. A computer may also be misled by sample or reference spectra with sloping baselines or with extraneous bands from contamination. A j udgment call by an expe­ rienced spectroscopist is needed to determine the importance of spectral features and deviations. The quality of the spectra in the library, as well as the spectrum of the unknown sample, are critical to obtaining credible results. Spectral history-such as analysis method, run parameters, and use of correction routines-should be known for both the unknown spec­ trum and those in the computer library. Characterization of the sample type (polymer, mineral, sol­ vent, etc. ) helps in the selection of the computer libraries to be searched. Spectral Interpretation 93 Since numerous libraries are available, search time may be minimized by limiting the number of libraries. When a library does not contain refer­ ence materials in the same chemical class as the unknown sample, it is not likely that the computer will obtain a good or even a reasonable match. In particular, search programs are very ineffective at characterizing material mixtures, because most libraries are composed of pure materials. The results of a computer search routine are totally dependent on the searched spectral library. The best library is often one that con­ tains reference spectra generated on one's own instrument. These spectra tend to match better, because the reference materials were prepared and analyzed in a manner consistent with the unknown sample. They are also more likely to contain materials related to the sample . It is time­ consuming, however, to generate the large number of spectra required to compile a comprehensive library. Thus, an active exchange of IR data and spectral libraries between labs that are conducting similar experiments is the second-best choice for developing useful spectral libraries. For the most part, IR spectra do not vary significantly from instrument to instrument. This is particularly true for FT-IRs, since they have the advantage of internal wavelength calibration. IR data exchange has been facilitated by the development of a universal data format by the Joint Committee on Atomic and Molecular Physical Data Exchange; the format is known by the committee's acronym JCAMP.DX ( McDonald and Wilks 1 9 8 8 ) . Most IR manufacturers supply programs that use this standard form for external data exchange. Additionally, some stand­ alone computer programs, such as Lab-Calc ( see Suppliers, Galactic Industries Corp . ) , are available for conversion of spectra to and from the JCAMP.DX format. One commercial lab offers spectral searches on digitized spectra ( see Suppliers, Photometries Ltd . ) . Spectral region examination Since the functional groups for a sample are usually not known, interpre­ tation is best started by dividing the spectrum into several frequency regions. The presence and absence of absorption bands in each region are then used to characterize the sample ( Smith 1 9 79). Thus, starting with the frequency regions at the high-wavenumber end, an unknown spec­ trum may be divided as follows: OH-NH region (4000-2600 em-I) Hydroxyl groups generally produce a broad-envelope-type band centered around 3400 cm- l . This band can be misleading, because absorbed water on the sample or on the alkali salt substrate will also produce an O-H band. Hydrogen bonding can change the band position and shape. The O-H band for carboxylic acids is very broad and centered about 3400 em-I, while the water of hydration for clay produces very sharp bands at 3700-3500 cm- l . N-H stretching bands also occur in this region, with their center near 3350 cm- l . N-H bands are usually sharper than O-H bands. For a natural product sample, the absence of bands in this region shows that the sample does not contain any carbohydrates or proteins. 94 Chapter 5 C-H stretching region (3200-2800 em- I) C-H stretches from aromatic and vinyl hydrocarbons occur at 3 1 00-3 000 cm- I . C-H stretches for methylene groups occur near 2925 (asymmetric) and 2 8 5 0 ( symmetric) cm-I, with the corresponding C-H stretches for methyl groups near 2962 and 2 8 72 cm- I . Thus, with 3000 cm-I as an imaginary dividing line, the hydrocarbon stretches for unsaturated carbon groups occur at higher wavenumbers, and the C-H stretches for saturated carbon groups occur at lower wavenumbers. Waxes, oils, and natural resins, for example, have strong hydrocarbon stretches. Window region (2800-1 800 em-I) This is usually a baseline region where few absorption bands occur. The most common band is for atmospheric carbon dioxide ( doublet at 2340 cm- I ) . Other bands that occur in this region are a carbon triple bond near 2 1 20 cm- I , nitrile stretch near 2240 cm-I, isocyanate stretch near 2265 cm- I , and thiocyanate near 2 1 60 cm- I . Prussian blue, ferric ferrocyanide, has a strong absorption band in this region. Carbon double bond region (1 800-1500 em-I) The highly polar carbonyl bond produces a strong absorption band at 1 8 50-1 650 cm-I that varies with carbonyl type-for example, 1 740 cm-I for ester, 1 7 1 0 cm-I for ketone. The carbonyl band for the amide I group is shifted down to about 1 650 cm-I, with corresponding amide II ( 1 5 50 cm- I ) and amide III ( 1 450 cm- I ) bands occurring in stair-step-type intensities. In carboxylic acid salts, the asymmetric stretch for the carbon­ oxygen bonds occurs near 1 650-1 540 cm- I . A carbon double bond stretch occurs about 1 640 cm- I . Aromatic carbon-carbon stretching vibrations occur at 1 600-1 5 8 5 and 1 500-1400 cm- I . Fingerprint region (1 500-500 em- I) Most functional groups also have bands in the fingerprint region. The fingerprint bands, when taken in combination with the group frequency bands, can confirm an assignment. The absorption pattern in the finger­ print region is frequently complex, with interacting vibrations and over­ lapping bands. It is, however, unique for each material and thus most valuable for specific identifications made by direct comparison to refer­ ence spectra. Negative interpretation Just as the presence of functional group bands can be used to select potential matches, the absence of a functional group band is used to eliminate potential groups of materials. Entire chemical classes of materi­ als can be ruled out j ust on the absence of one or more basic group fre­ quencies, such as hydroxyl, hydrocarbon, carbonyl, and amide. This key factor should not be underestimated. The positive identification of a material can never be based on the presence of j ust a single band, because multiple materials can produce similar bands. However, the absence of an absorption band is unambiguous: if one absorption band is not present, then that material is not present. For example, if the spec- Spectral Interpretation 95 trum for a paint binder does not have a carbonyl band between 1 75 0 and 1 650 cm- I , then it does not have any measurable amounts of oil, egg yolk, glue, natural resin, acrylic, alkyd, or any number of other synthetic resins that contain a carbonyl group. This result, in itself, may be sufficient to answer the analytical question about the sample, thus freeing important analysis time for other samples. Spectra-structure correlations An essential part of the spectral identification process is the examination of absorption band frequency to determine corresponding functional groups. Table 5 .2 provides a list of molecular functional groups and their corresponding absorption band frequencies. Hydrocarbons: Aliphatic Commonly found in spectra of most organic materials, the C-H stretch­ ing vibrations occur in the region of 3000-2 8 00 cm- t . As seen in Figure 5 . 6 , a spectrum of paraffin, the methyl group ( CH3 ) vibration produces two small bands at 2 9 62 and 2 8 72 cm-I, because of the asymmetric and symmetric stretching modes. The methylene groups ( CH2 ) produce sharp asymmetric and symmetric stretching vibrations at 2926 and 2 8 5 0 cm- t . Table 5.2 The bending vibrations for the CH3 groups are found at 1 4 5 0 and 1 3 8 0 cm-t for asymmetric and symmetric, respectively. The Some im portant group frequencies. in-plane bending or scissoring band for CH2 is found at 1 465 cm- t . In Functional group Formula Associated absorption band frequencies Hyd roxyl -OH Hyd roxyl groups generally produce a broad-envelope-type band centered at 3400 cm- 1 . Hyd rogen bonding can change position and shape. U n satu rated CH - H -<j>C - H -C=C- CH stretches from aromatic hydrocarbons occur at 3 1 00-3000 cm-1 . C H stretches from a carbon double bond occur about 3030 cm-1 . Ali phatic CH- methylene CH stretches for methylene groups occur near 2925 (asymmetric) and 2850 (symmetric) cm - 1 . The vibrations for bending occur near 1 465 cm-l , for rocking, ca. 730 cm- 1 (only for CH2 sequences greater than 4 and may be split in solids) . Ali phatic CH- methyl -CH 3 CH stretches for methyl groups occur near 2962 (asymmetric) and 2872 (symmetric) cm-1 . The vibrations for CH bending occur near 1 450 and 1 3 80 cm-1 . Carbon-carbon m u ltiple bonds -C=C-C = C- A carbon dou ble bond stretch occurs ca. 1 640 cm- 1 and a carbon triple bond near 2 1 20 cm- 1 . Aromatic carbon stretching vibrations occur near 1 600 and 1 500 cm-1 . Out-of­ plane bending mode vibrations may produce strong sharp bands at 1 000-650 cm-l , depend­ ing on the pattern of su bstitutio n . Carbon-n itrogen -C=N - N =C=O -S-C=N A nitrile stretch occurs near 2240 cm-1 , an isocyanate stretch near 2265 cm- 1 , and a thiocyanate near 2 1 60 cm- 1 . Carbonyl - c =o -c-o- The highly polar carbonyl bond produces a strong absorption at 1 850-1 650 cm- 1 that varies with carbonyl type-e .g., 1 740 for ester, 1 7 1 0 for ketone. Amide -CON H - N-H stretch about 3350 cm-1 . Amide I occurs near 1 650 cm - l , amide II near 1 550 cm -l , and amide I I I near 1 450 cm-1 in stair-step-type intensities. Acid salts -C02- Asymmetric stretch for the carbon-oxygen bonds occurs near 1 650-1 540 cm - l , depen ding on structure. Carbonate -C0 3 = Broad stretching band near 1 450 cm-1 with sharp bands at 900-700 cm-l , depending on cation. Carbon -oxy gen C-O stretch occurs at 1 200-1 000 cm- 1 ; varies with hydrogen bonding and molecular structure. 96 Chapter 5 .J . / CH3 bending CH2 rocking C H2 bending 7 4000 3600 3200 C H2 stretching 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 400 Wavenumber (cm- 1 ) Figure 5.6 long-chain hydrocarbons, with more than four methylene groups, there is An I R transmittance spectrum of paraffi n . also an in-plane rocking band that is found near 730 cm- l . In solid semi­ crystalline materials, such as paraffin and beeswax, the absorptions appear sharper, with characteristic peak splitting forming doublets at the methylene absorption positions. Other weaker methylene bands are observed in the 1 3 50-1 1 5 0 cm- l region. Hydrocarbons: Aromatic Aromatic C-H stretching bands occur between 3 1 00 and 3000 cm- l . The strongest, and sometimes most informative, bands in the spectra of aro­ matic compounds occur in the low-wavenumber range between 1 000 and 655 cm- l . These strong absorption bands result from the out-of-plane bending vibrations of the ring C-H bonds. The absence of any major bands in this region generally shows that the material is nonaromatic. Skeletal vibrations from the C-C interactions in the ring absorb in the 1 600-1 5 8 5 and 1 5 00-1 400 cm- l regions. A spectrum of polystyrene, seen in Figure 5 . 7, illustrates these absorptions. Alcohols and hydroxyl absorptions c-o The characteristic bands observed in the spectra of alcohols result from O-H and stretching vibrations. These functionalities are susceptible to hydrogen bonding, which produces broad IR absorption bands. The O-H stretch generally occurs from 3600 to 3200 cm-l. The C-O absorption in alcohols occurs from 1 2 6 0 to 1 000 cm- l . Other weaker, c-o O-H bending vibrations may be seen at 1 420 to 1 3 3 0 cm- l . Figure 5 . 8 shows a spectrum o f honey, a complex sugar containing multiple and O-H stretches. Carbonyls: Aldehydes, ketones, and esters Ketones, aldehydes, acids, esters, anhydrides, and ami des show a strong carbonyl ( C = O ) stretching absorption in the region of 1 8 70-1 640 cm- l . The carbonyl band has a relatively constant position and high intensity, 97 Spectral Interpretation I nterference fringes Q) t='.=oR.()c'"'" '"c E Overtones Aromatic C-H stretching 3600 4000 � .> 2800 3200 Ring deformation Aliphatic C-H stretching 2400 Aromatic ring C=C stretching 2000 1 800 � 1 600 / C-H bends 1 400 1 200 1 000 800 400 600 Wavenumber (cm- ' ) Figure 5.7 which makes it one of the easiest bands to recognize in the IR spectrum. An IR transm ittance spectrum of The exact position of the C = O stretch is determined by its environment in polystyrene. the molecule. A carbonyl in a ketone usually occurs at 1 720-1 690 cm-I, while a carbonyl band in an ester usually occurs at 1 750-1 730 cm- t . The carbonyl groups in aldehydes absorb near 1 740-1 720 cm- t . The adjacent C-O stretching vibrations found in esters and aldehydes occur between 1 400 and 1 000 cm- t . Ketones also have weak backbone stretching and bending vibrations in this region. Figure 5.9 shows a spectrum of polyester. Carbonyls: Amides The spectra for primary and secondary amides contain a strong carbonyl absorption band in the region of 1 65 0 cm-I, called the amide I band. Figure 5.8 Secondary amides display an additional band near 1 5 5 0 cm- I , called the An IR transmittance spectrum of honey. amide II band, that is a combination of C-N and N-H vibrations. A C-H c Q)��()'"E'"c t- C-H stretching oR. \ CoO stretch 4000 3600 3200 2800 2400 2000 1 800 1 600 Wavenumber (cm- ' ) 1 400 1 200 1 000 800 600 400 98 Chapter 5 Aromatic C=C Q) u c co ""I-�ift Aliphatic C-H stretching E (J) c v C-H bending � c=o stretching 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 C-O stretching 1 000 800 600 400 Wavenumber (cm- 1 ) Figure 5.9 An I R transmittance spectrum of polyester. bending vibration occurring near 1 450 cm-1 has sometimes been called the amide III band. The relative intensities of the amide I, II, and III bands in polyamides (protein, nylon, etc.) occur in a stair-step pattern. The asymmetrical and symmetrical N-H stretching vibrations occur near 3350 and 3 1 80 cm- I , respectively. Hydrogen bonding may broaden the bands, giving the appearance of one band, although they are usually sharper than O-H bands. Often a stronger O-H band overlaps this region, and the N-H stretches appear as shoulders or peaks on the broader O-H band. Figure 5 . 1 0 shows a spectrum of gelatin, which exhibits the typical primary and secondary amide patterns seen in proteins. Figure 5 . 1 0 An I R transm ittance spectrum o f gelatin. Q) u c co ""�ift E f/) c co " __ 4000 3600 3200 Aliphatic C-H stretching N-H stretching 2800 2400 2000 1 800 1 600 Wavenumber (cm- 1 ) N-H bend with C-N stretch (amide I I ) 1 400 1 200 1 000 800 600 400 99 Spectral Interpretation Correlation charts Over the years, many researchers have done extensive studies to deter­ mine the absorption band ranges of specific functional groups. This information has been compiled into correlation charts, several of which may be found in the literature. A simplified version of a correlation chart is shown in Figure 5 . 1 1 . The lines for each functional group indicate the most probable range for the absorption band. The precise wavenumber at which a specific group absorbs is dependent on its molecular environ­ ment and its physical state. One limiting factor to correlation charts is that they represent only the strongest, most characteristic bands. Other important informa­ tion used to identify an unknown spectrum, such as band shape and intensity, is not incorporated in the chart. The correlation chart is best used to classify the functional groups in a compound structure for only the major absorption bands, since minor bands may be due to vibrations not shown on the chart. 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 Hydroxyl Hydrocarbons Aliphatic CH2 Aliphatic CH3 Aromatic CH Vinyl CH Carbon-carbon C=C C=C Carbonyl, C=O Ketones Aldehydes Esters Acids Carbon-oxygen Alcohols Ethers Amides Primary Secondary Figure 5.1 1 The general range of major absorption bands for specific functional groups. This chart can help i n the selection of groups of materials for further examination by Amines Primary Secondary Organic salts Formates Acetates direct spectral comparison. Since the figure Oxalates does not depict exact band position or Stearates intensity and does not include minor Cyanides bands, it cannot be used as a sole means of identification (s = strong; m = med i u m ; b = broad ) . ,b I! I, I"jI I bI_ iI, 'I Ii _I ,I, I I :I , - - _ .... , II, ,, , 1 , , , b -, ,-: I'-� ,' I -I t-'I, ,' I. b_ :,, II I: I Ii �I I - I I�t I ! : I I I I _ s 1 m - r­ I I , :I , , 'I - , , _ " 600 Ii I III II I 800 � IT 4000 3600 3200 2800 2400 2000 1 800 1 600 1400 Wavenumber (cm- 1 ) I I' 1 200 1 000 800 600 1 00 Chapter 5 Identi fication of Material s U sed in Art and Art Conservation A variety of natural and synthetic materials have been used in creating works of art. Though ranging from acrylics to polysaccharides and from carbonates to oxides, the classification, if not the specific identification, of these materials in their pure form, as well as in simple mixtures, is well within the realm of IR spectroscopy. Appendix II provides reference IR spectra for many materials used in art and art conservation. Natural organic material s Natural products, derived from plants and animals, are rarely pure materials; rather, they are mixtures of many components ( maj or, minor, and impurities), because of the number of reactions that occur simulta­ neously in biological systems. The components may range in complexity from simple molecules to multicomponent mixtures of organic and inor­ ganic compounds. A mixture containing slight variations of many com­ ponents produces an IR spectrum with some broad, ill-defined, and overlapping bands, especially in the fingerprint region. The presence of ill-defined bands indicates that a material is a mixture and possibly a natural product. Flowchart for natural organic materials For identification purposes, natural products encountered by analytical chemists working in the art conservation field may be grouped into the following classes that contain similar IR active functional groups: resins (tree ) , resins ( insect, shellac ) , oils, gums, waxes, and proteins . Figure 5 . 1 2 gives examples of spectra for these categories. More information on vibrational group assignments for these natural materials may be found elsewhere ( Bellamy 1 9 80; Omecinsky and Carriveau 1 9 8 2 ) . Classification o f spectra for these general classes o f natural organic materials can be simplified based on the position, intensity, and shape of the carbonyl and hydrocarbon absorption bands. Figure 5 . 1 3 i s a flowchart that separates each material based on the presence or absence of characteristic bands. The schematic trail is followed until one of the final blocks is reached. Positive identification of a material should always be made by final, direct visual comparison of the unknown spectrum to reference spectra. However, there are only a few good reference spectral collec­ tions, books, and digitized spectra available for natural products. Appendix I lists some of these ( see Infrared Users' Group 1 995; Hummel and Scholl 1 9 8 1 ; and Snodgrass and Price 1 9 9 3 ) . Waxes Waxes are long-chain hydrocarbon materials that can be produced by either plants or animals. Waxes are very stable, not changing significantly as they age (Mills and White 1 994 ) . Kuhn provided a basis for the identification of waxes in works of art using IR spectroscopy ( Kuhn 1 9 6 0 ) . More recently, Besaninou presented a thorough history of waxes and their methods of analysis ( Besaninou 1 9 8 4 ) . Parra and Serrano used 1 01 Spectral Interpretation Wax (beeswax) Oil (linseed oil) Resin (mastic) Q) <.) c te.=*-'"'" E (f) c Resin (shellac) Protein (hide glue) Gum (gum arabic) Figure 5 . 1 2 I R transm ittance spectra for several types of u naged natural organic materials. 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- ' ) IR spectroscopy and other techniques to examine wax seals and their attached textile remnants ( Parra and Serrano 1 99 0 ) . Other authors have used IR spectroscopy to identify beeswax in Egyptian paints ( Birstein and Tul' Chinskii 1 97 9 ) , on a column of a German church ( Bleck and Ziessler 1 96 7 ) , and in samples excavated in Sudan ( Delbourgo and Gay 1 9 6 8 ) . I n a wax spectrum, the many CH2 groups (methylenes) i n the chain produce the characteristic and predominant stretches at 2926 and 1 02 Chapter 5 Carbonyl band ( 1 630-1 750 cm-') 1 520-1560 1450 1 240 1 080 3300 C-H stretches (2850-2960 cm-') ( 1 630-1 680 cm-' ) Protein ( 1 695-1 7 1 5 cm-' ) Tree resin ( 1 740-1 750 cm-') 2930-2958 (s) 2865-2875 (s) 1 448-1467 1 382-1387 2955-2957 3400 (s) 291 8-2920 (s) 1 6 1 6-1 645 1 235-1 250 2920-2934 (s) 2926-2928 (s) 1 1 78-1 1 84 2855-2860 (s) 2855-2557 (s) 2949-2851 (s) 1423- 1 440 1 078-1092 1 636 1 46 1 -1 464 (1 736-1 742)* 1 385 1 028-1038 1 466 1 238-1 244 1 472-1 475 1 220-1 240 887-897 1 4 1 0-1 416 1 1 59-1 1 67 1 464-1466 1 068-1 1 00 (s) 1 377-1 381 1 097-1099 ( 1 1 7 1-1 1 84)' 1 250- 1 254 721-727 729-731 71 9-721 1 1 61-1 1 76 1 1 1 2-1 1 1 3 945 928-932 Figure 5 . 1 3 2 8 5 0 cm-I ( see Figs. 5 . 6 and 5 . 1 2 for paraffin and beeswax, respec­ A flowchart to aid in characterization of tively) . Confirmatory bands for waxes are small, sharp doublets at several classes of natural organic materials * based on their IR absorption band posi­ tions and intensities (s = = strong; sent only i n ester-containing waxes). pre­ 1 466/1462 cm- I and 730/720 cm- I . The splitting of the bands near 730 cm- I into a doublet indicates that there are at least four methylene groups in the chain. The appearance of the doublets indicates the semi­ crystalline structure of the wax ( Ludwig 1 96 5 ) . Any pure, long-chain hydrocarbon will have CH2 chains with CH3 methyl end groups and pre­ sent a spectrum similar to paraffin wax. Most natural waxes also contain esters of higher fatty acids with fatty alcohols. Beeswax is composed of about 70% higher aliphatic esters, with 1 3 % free wax acids and only c=o about 12 % hydrocarbons ( Fig. 5 . 1 2 ) . The ester groups account for the weak stretching band at 1 740 cm-I and for the C-O bands in the 1 1 75 cm-I region. Oils Oils, vegetable and animal, consist of glycerol esters of higher fatty acids with even carbon numbers; their diversity lies in the type and composi­ tion of the fatty acids (Mills and White 1 99 4 ) . Oils and fats are ubiqui­ tous and have been used in many contexts; in art objects they are commonly found as binding media in paintings and as residues in archae­ ological samples. While chromatographic procedures are required for the specific differentiation of the fatty acid components in oils, IR can readily identify this class of materials ( Shreve et al. 1 950; Barclay 1 9 8 9; Kosek and Green 1 992 ) . In addition, IR spectroscopy has been successfully used to study the drying of linseed oil ( Baer and Indictor 1 976) and its changes 1 03 Spectral I n terpretation with UV radiation ( Low and Baer 1 977), as well as its aging characteris­ tics when mixed with pigments ( Meilunas, Bentsen, and Steinberg 1 9 90 ) . Hedley and coworkers used I R spectroscopy t o evaluate changes i n the dried oil film after cleaning treatments (Hedley et al. 1 9 9 0 ) . Shown i n Figure 5 . 1 2 is a n example o f a typical oil spectrum illustrating the significant CH2 stretches. However, due to the polar mol­ ecular environment, the methylene bands, at 2926 and 2 8 5 5 cm- I , are at slightly higher wavenumbers than those of the waxes. In addition, there is a weak-to-medium olefinic C = C-H stretching band that occurs at 3020 cm- t • The intensity of this band depends on the state of dryness of the oil, and in well-dried oils, this band will be very small. Oil spectra contain a strong, sharp carbonyl band at 1 75 0- 1 740 cm- I , because of the ester group. It is the only natural organic material of these five classes that has an intense carbonyl band in this region. This is a clear characteristic of oil. However, in mixtures with some pigments, the carbonyl band may be shifted to slightly lower wavenumbers. Other c-o c - o bands characteristic of the oils are aliphatic C-H bands at 1 464, 1 3 79, and 725 cm-t and the three bands at 1 240, 1 1 65 , and 1 1 03 cm- t • The bands occur in a characteristic maple leaf pattern, for which the band at 1 1 65 cm- t is the strongest. Resins (tree) Natural tree resins are primarily composed of aliphatic three-ring struc­ tures called resin acids. The softer resins, mastic and balsam, have been used as adhesives and varnishes, and the harder resins, such as copal and amber, have been used for decorative beads and sculpture. Tree resins fall into three main categories: ( 1 ) aromatic (e.g., benzoin, styrax ) , (2) diter­ penoid (e.g., balsam, copal), and ( 3 ) triterpenoid (e.g., dammar, mastic) (Mills and White 1 977). These resins vary in their degree of stability, and some are susceptible to oxidation ( Mills and White 1 994). Gianno and coworkers used IR to analyze over one hundred southeast Asian natural resins and gums; those references served as a base to identify coatings and adhesives found on ethnographic objects ( Gianno et al. 1 9 8 7 ) . Mastic and dammar resins, commonly used as painting varnishes, have been spectrally characterized by Feller ( 1 954, 1 95 9 ) . IR spectroscopy was one method used by Burnstock and Learner ( 1 992) to monitor changes in mastic varnishes after they were cleaned with alkaline reagents. IR spectroscopy was also used to study historic varnishes (Korte and Staat 1 9 89; McCormick-Goodhart 1 9 8 9 ) , coatings on African ceramics (Hexter and Hopwood 1 99 2 ) , and archaeological residues ( Shearer 1 9 8 7) . Derrick ( 1 9 8 9 ) provided a schematic to differen­ tiate five un aged resins found in furniture finishes using IR absorption band positions. Tar and pitches have been used since early times as putties, paints, and waterproofing agents. Hadzi and Cvek ( 1 97 8 ) used IR to iden­ tify "grave resins" found on urns in excavated graves as birch bark pitch. First analyzed with JR, then confirmed with chromatographic methods, pine pitches were found on an Etruscan shipwreck ( Robinson et al. 1 9 8 7) and in Mediterranean transport amphoras (Beck, Smart, and Ossenkop 1 04 Chapter 5 1 9 8 9 ) . Asphalts and bituminous resins used as brown colorants in paint media have been characterized with IR by Wolbers ( 1 9 8 4 ) . Early I R studies showed that various sources of amber, a fossilized resin, could be differentiated by their IR spectra ( Schwochau, Haevernick, and Ankner 1 96 3 ; Beck, Wilbur, and Meret 1 964; Beck et al. 1 965; Langenheim and Beck 1 9 6 5 ) . Reference sets of amber spectra were collected (Langenheim and Beck 1 9 6 8 ) and later used to identify amber sources in Greek artifacts (Beck et al. 1 9 7 1 ) , in imported archaeological artifacts (Beck 1 972 ) , in Etruscan j ewelry (Follette 1 9 8 5 ) , in samples from Japanese tombs ( Fuj inaga, Takenaka, and Muroga 1 976), and in objects from other archaeological sites (Todd et al. 1 976; Beck et al. 1 9 7 8 ) . Williams, Waddington, and Fenn ( 1 990) used IR spectroscopy to examine the changes in amber after exposure to air pollutants. Grimaldi noted that the routine use of IR spectroscopy for the characterization of amber has significantly helped curators with the classification of artifacts ( Grimaldi 1 99 3 ) . Oriental lacquer, o r urushi, is another significant plant resin used in art objects that has been well studied by IR spectroscopy ( Masschelein-Kleiner and Heylen 1 96 8 ; Fujinaga, Takenaka, and Muroga 1 9 76; Kenjo 1 97 8 ; Carriveau 1 9 8 4 ) . Kenjo used IR to study the effects of pH on the hardening of lacquer films (Kenj o 1 976 ) . More recently, Derrick and coworkers showed that IR spectroscopy can be used to distinguish between lacquer on Japanese furniture and the natural resin-based imitation coatings developed in Europe in the eighteenth century (Derrick, Druzik, and Preusser 1 9 8 8 ) . The various types o f natural resins exhibit several important spectral features. The cyclic ring structure of tree resin (mastic) gives a spectrum with strong C-H stretching vibrations at even higher wave­ numbers than those in the oils ( Fig. 5 . 1 2 ) . These are generally found at 295 8-2930 and 2 8 75-2 8 6 5 cm- I . Because there is a variety of molecular environments for the methylene groups within the compounds in any given resin and because there are several methyl (CH3 ) end groups, the C-H stretches are not as sharp and as well separated as those previously seen in the waxes and oils. Resins may be distinguished from the other groups by two bands. The first band, which is usually weak and broad, occurs at 2700-2500 cm-I and is due to the O-H vibrations of a dimer­ ized carboxyl group. The second distinguishing band that all tree resins contain is a strong carbonyl ( C = O ) stretch at 1 7 1 5- 1 6 9 5 cm- I . This band broadens with resin degradation and oxidation, but the band maxi­ mum remains within this wavenumber region ( see, for example, spectra of light-aged mastic in Fig. 5 . 1 4 ) . Bands i n the fingerprint region are characteristic for each particular tree resin and may be used to distinguish among them. Figure 5 . 1 5 shows exemplary IR absorbance spectra for five commonly used, unaged natural resins in furniture finishes. Figure 5 . 1 6 is an IR absorp­ tion band identification key for these resins; included are family names and major components (Derrick 1 9 8 9 ) . Once a natural material has been classified as a natural resin by use of the information in the nat­ ural products identification flowchart ( Fig. 5 . 1 3 ) , then the type of resin 105 Spectral Interpretation Mastic 2.0 Q) .D«()'"0if) c 1 .0 0.2 +- ----------------�--------------------------�--� � 900.0 1 000.0 1 800.0 1 500.0 Wavenumber (cm- 1 ) 2.0 Sandarac Q) .D«()'"0if) c 1 .0 Figure 5 . 1 4 I R absorbance spectra (1 800-900 cm-1 ) for th ree sets of fresh and deteriorated �:d natu ral resins (mastic, sandarac, and shellac). Each plot is a spectral overlay of 0.2 1 800.0 samples that were exposed to 0 , 37, 75, 1 500.0 1 000.0 900.0 1 000.0 900.0 Wavenumber (cm-1 ) and 1 5 1 kilojoules of en ergy from a xenon arc lamp i n a temperature- and humidityShellac controlled environment. At the longest exposure time, all samples exh i bited d iscoloration and cracking. Note that the absorption band position maxima remain stable, w h i le the band shapes and relative intensities change. The most significant .D«()c'"0if) Q) 0.5 changes are seen in the shapes and relative intensities of the carbonyl bands for \,,"�"""'--", mastic and shellac; for each of these carbonyl bands, the shortest band corresponds to the fresh resin sample, and the tallest band corresponds to the most dete- 0.0 1 800.0 1 500.0 Wavenumber (cm- l ) riorated resin sample. may be distinguished with the aid of the additional information pro­ vided in Figure 5 . 1 6 . This schematic provides a simplified structure for the easy identification of the presence of a resin in a spectrum by a list of its 1 06 Chapter 5 Rosin Copal Mastic Shellac Figure 5 . 1 5 Exemplary I R transm ittance spectra for five types of unaged natural resins. 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm- 1 ) absorption band positions. The strongest bands in the resin spectra are generally the carbonyl and hydrocarbon stretching frequencies. These bands, listed at the top of the key, can provide a distinction for four of the resins. Sandarac and copal are chemically and spectrally very similar and may be distinguished only by some smaller bands in the fingerprint region (2000-500 cm- 1 ) . The presence of at least half of the listed bands 1 07 Spectral Interpretation Source= Tree / Carbonyl bands C-H stretches Vinyl stretches and bends Characteristic fingerprint region bands Figure 5.1 6 A flowch art to aid in characterization of Resin five types of natural resins based on their I R absorption band positions (absorption FamilyA,B bands are represented as wavenumbers [:t2 . 4 cm-1 ] ; A = = Mills 1 977; B Mattiello 1 941 ) . (For more i nformation, see Derrick 1 989 .) Major componentsA, B :......" Source=lnsect ;7 � 1 7 5 1 7 2 1 6 9 0 1 7 0 1 7 001 7 5 3 0 3 8 L"'" 22646-98372-06654 22984739 29847 2983570 1166I927 311406I67943 14518-65-10460 116436 1143296375591 /125193-21952'""63 111026455861 1 61132-579102176 19381007 1142395637 18254098 85307 1190465421 86720532 980527632 79 7320 7 8 9 7 9 2 rPinoascine Cusparensdaarccea Arauccoaprialcea Anacmardstiaiccea Lsaecsrihefetlradlcabcya abietcadsien pscimonamdr dauinceiondcpaimaccidirdss scaonmdarucniodcpaimcaidrsic comftprilexrpmeinxtusre lashceoliclactoidnse '" 7 I I in an unknown sample spectrum is a strong indication that a particular resin is present. Final confirmation comes through visual comparison of the sample spectrum with a reference spectrum of a known material. Resins (insect) Shellac is a resin excretion from the lac beetle. Chemically, shellac resin is a complicated mixture of lactones, esters, and ethers of aliphatic and aromatic polyhydroxy acids. The C-H stretching bands ( Figs. 5 . 1 2 , 5 . 1 5 ) fall i n positions similar t o those o f oils, at 2934-2920 and at 2 8 5 7 em- I . The carbonyl band in fresh shellac i s a characteristic doublet from the c-o ester ( 1 735 em- I ) and from the acid ( 1 7 1 5 em- I ) . A small olefinic band occurs at 1 6 35 em- I . Several bands are present, most noticeably at 1 240, 1 1 63 , and 1 040 em- I ; they are due to the ester, acid, and alcohol groups. A double band at 73 01720 cm-I ( from partially crystalline long­ chain hydrocarbons) occurs in many shellacs and is probably due to accompanying shellac wax. Shellac is included in the resin identification schematic presented in Figure 5 . 1 6 . 1 08 Chapter 5 Proteins Proteins are polymeric substances composed of amino acid monomeric units . The proteins present in living organisms consist of various com­ binations and proportions of twenty naturally occurring amino acids. Proteinaceous materials used in art objects may be from animal tissues (parchment, leather, hair, ivory) or from their by-products (glue, egg, casein, albumin, blood ) . All types of proteins, as a general material class, are readily identifiable by their IR spectra ( Perron 1 9 8 9 ) . Close examina­ tion of absorption band position and intensities can show the denatura­ tion of collagen to gelatin (Birstein and Tul'Chinskii 1 9 8 1 ; Payne and Veis 1 9 8 8 ; Derrick 1 9 9 1 ) . FT-IR analysis has also been used to differenti­ ate between modern elephant ivory and ivory from other sources, such as walrus, hippopotamus, or ancient mastodon ( Lee 1 9 9 1 ) . Protein spectra form a consistent recognizable pattern of absorption peaks ( Fig. 5 . 1 2 ) . Proteins are characterized by the presence of amide I and amide II bands near 1 650 and 1 5 5 0 cm- I , respectively. These two bands along with another, occasionally referred to as an amide III, found near 1 450 cm- I , form a consistent stair-step pattern. Additionally, the presence of an amide may be confirmed by the N-H stretching band near 3350 cm- 1 . While IR is very useful for identifying the presence of a protein, few spectral differences are seen between various protein types, including materials as different in amino acid composition as fish glue and albumin. Thus, a secondary method, such as liquid or gas chromato­ graphy, must be used to determine the exact amino acid composition. Gums Carbohydrates are natural polysaccharides composed of various propor­ tions of several monosaccharide units. They are typically water soluble. Some common examples are sugar, starch, cellulose, and plant gums. An excellent review of plant gums and their use as art materials was given by Twilley ( 1 98 4 ) . Birstein used IR spectroscopy to identify natural gums as binders in central Asian wall paintings ( 1 975 ) and as protective coatings in late antique and early-middle-age Egyptian tombs (Birstein and Tul'Chinskii 1 9 77). Masschelein-Kleiner and Tricot-Marckx detail method­ ology for the IR analysis of gums and illustrate spectra obtained neat and after acid hydrolysis (Masschelein-Kleiner and Tricot-Marckx 1 96 5 ) . Gums a n d cellulose are long-chain polymers o f sugars (poly­ saccharides). Sugars have a high proportion of O-H groups bound to the carbons. This structure produces a very characteristic IR pattern for the c-o polysaccharides ( Fig. 5 . 1 2 ) , which have two strong, broad bands: one at about 1 0 8 0 cm-1 due to and the other at about 3 3 00 cm- 1 due to the O-H groups. These bands are typically about equal in intensity. The C-H stretches tend to be weak and poorly resolved. All polysaccharides also contain a moderately strong band at 1 620 cm- 1 that is partially associated with intramolecularly bound water and partially due to the presence of a carboxyl group. Some gums, such as gum tragacanth, also contain a weak-to-moderate band at 1 73 5 cm- I , which is associated with an ester-containing component. Spectral I nterpretation 1 09 Synthetic resins (polymers) Over forty years ago, many industrial labs purchased IR spectrometers for the analysis of rubbers. As applications for other polymers grew, so did the breadth of samples analyzed by IR. Unlike natural materials, which are complex mixtures of many components, synthetic resins tend to be pure, specific molecular structures that provide sharp, well­ defined IR absorptions. These very specific, recognizable IR patterns make IR spectroscopy the method of choice for the identification of polymers. IR analysis has been used successfully to analyze polymers in objects of art and in art conservation practice ( Freeman 1 979; Martin 1 9 8 8 ; Pratt 1 9 9 1 ; Shearer and Doyal 1 9 9 1 ) . The capabilities and limita­ tions of IR were examined for analyzing acrylic ( Stringari and Pratt 1 99 3 ) and alkyd (Hodson and Lander 1 9 8 7) paint media. In poly(vinyl acetate) films prepared with different solvents, IR spectroscopy showed conformational variations in the polymer ( Hansen et aI. 1 9 9 1 ) . Figure 5 . 1 7 shows spectra o f several important polymers selected as synthetic equivalents to the natural products shown in Figure 5 . 1 2 . Polyethylene is a long-chain hydrocarbon, similar to nat­ ural waxes such as paraffin. Many types of polyester resins, such as alkyds and acrylics, are used as modern artist materials and as conser­ vation materials. Some polycyclohexanones, such as MS2A and Laropol K-80, have been proposed as substitutes for natural resin varnishes. Nylon, a synthetic polyamide, is a chemically resistant material used in fabrics and liners. The spectrum of a water-soluble, modified cellulose, Klucel F, is also shown. More information on vibrational group assign­ ments for many synthetic resins may be found in these Appendix I references: Bellamy 1 9 75; Kagarise and Weinberger 1 9 54; Stimler and Kagarise 1 9 6 6 ; Zeller and Pattacini 1 9 73 ; Chicago Society for Coating Technology 1 9 8 0 . Flowchart for synthetic resins An identification flowchart for classes of synthetic materials is pre­ sented in Figure 5 . 1 8 . It is similar in design and use to the chart pre­ sented for natural materials. This schematic method aids in identifying the type or class of material present. The presence of plasticizers and fillers can complicate the identification of the base polymer. However, since the spectrum is the sum of its components, it is usually possible to find sufficient unobscured bands to characterize the main polymeric component. Positive identification of a material should always be made by final, visual comparison of the unknown spectrum to those in reference spectral collections. Several good reference spectral collections, books, and digitized spectra-such as Sadder Research Laboratories, Hummel and Scholl ( 1 9 8 1 ) , and Chicago Society for Coating Technology ( 1 9 8 0)­ are available for polymers and additives ( see Appendix I). The Gettens Collection contains reference spectra for several early polymers from the 1 930s and 1 940s (Appendix I, Snodgrass and Price 1 9 9 3 ) . 110 Chapter 5 Polyethylene (bubble wrap) OJ o c te�?f!.'"'" E (/) c Polycyclohexanone (Laropol K-80) Polyamide (nylon- 1 1 ) Cellulosic (Klucel F) Figure 5 . 1 7 Exemplary I R transmittance spectra for five classes of u naged synthetic materials. 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm-1) Characterization process for polymers Polymers are usually composed of long chains of two or three primary functional groups. The following discussion uses the wavelength regions, mentioned earlier in this chapter, to classify several types of synthetic polymers based on the presence and absence of major functional groups in their IR spectra. All regions of the spectra should be examined and cross-checked. The goal of functional group analysis is to focus on one or more classes of materials for in-depth visual comparison. 111 Spectral Interpretation weak or absent strong weak or absent Aliphatic hydrocarbons Figure 5.1 8 A flowchart for the ch aracterization of ethers several classes of synthetic polymers based on their I R absorption band positions and intensities. OH-NH region (4000-2600 em- i ) . The absence of broad envelope O-H and N-H bands in this spectral region indicates that the sample does not contain amines, amides, alcohols, or organic acids. This rules out materials such as polyamide (e.g., nylon), phenolic resins (e.g., Bakelite ) , polyurethanes, polyethylene glycols (e.g., PEG- I OO ) , and polyvinyl alcohols (e.g., Elvanol ) , as well as some cellulose esters, alkyds, and epoxies. Note, however, that if the sample was prepared using a hygroscopic alkali salt, such as KBr, the presence of an O-H band in this region may derive from absorbed water rather than from the sample structure. Hydrocarbon stretching region ( 3 2 00-2800 em-i ) . Absorption bands between 3 1 00 and 3000 cm- i correspond to an aro­ matic or vinyl C-H group and may indicate compounds such as poly­ styrene, phenolic resins, some polyurethanes, epoxies, or phthalate plasticizers. A sharp band at 2 9 8 0 cm- may indicate silicone resin or oil. i Strong sharp, methylene absorption bands (2925 and 2 8 5 0 cm - t ) with no carbonyl band ( see next section) indicate the presence o f a long-chain hydrocarbon polymer, such as polyethylene, polypropylene, butadiene, or natural rubber. The spectra for some polyethylenes are only slightly different from the spectra for paraffin waxes. Numerous aliphatic esters, such as polyesters, have moderate to strong methyl and methylene stretching bands. However, if the spec­ trum has weak or absent C-H vibrations, then compounds such as fluoro­ carbons (e.g., Teflon), polyimides (e.g., Kapton), poly(vinyl acetates) (e.g., AYAA ) , epoxies (e.g., Epon), or regenerated celluloses (e.g., cello­ phane, rayon) should be examined. Window region (2800-1 800 em - i ) . This region is associated with adjacent double and triple bonds. In polymers, compounds containing isocyanate or nitrile groups will absorb in this region about 2 1 00 cm- t . Examples o f nitrile-containing polymers are acrylonitrile-butadiene-styrene 112 Chapter 5 (ABS rubber), acrylonitriles (e.g., Orlon, Saran F-120), and some poly­ urethanes (e.g., Adiprene L- 1 00). Overtone and combination vibrations for a monosubstituted aromatic will occur as small, regularly spaced bands from 1 950 to 1 650 em- I . These bands, when seen in the spectrum for a polymer, may indicate that polystyrene or phenolic resin is a sample component. Carbon double bond region ( 1 800- 1 5 00 em- I ) . Because the carbonyl band ( 1 850-1 650 em- I ) is one of the most important and usu­ ally one of the strongest, this region is sometimes the first examined. While it can be difficult to assign an exact type of carbonyl (i.e., ester, aldehyde, ketone, etc . ) in every case, the presence or absence of any car­ bonyl band is a key feature of a spectrum. Polymers with a strong carbonyl band in the region of 1 750- 1 700 cm- I are polyesters (e.g., Mylar), acrylics (e.g., Acryloid), alkyds (e.g., Glyptal), poly( vinyl acetates) (e.g., AYAA ) , plasticized polyvinyl chlorides (e.g., vinyl storage sleeves), polyurethanes (e.g., Adiprene L- 1 00 ) , and cellulose esters (e.g., cellulose acetate) . A carbonyl band shifted down to about 1 650 cm- I may indicate that polyamines (e.g., Melmac), polyamides (e.g., nylon), or cellulose nitrates (e.g., Duco, collodion) are present. Examples of polymer classes that have weak or absent car­ bonyl bands in the region of 1 750-1 650 cm-I are polyolefins (e.g., poly­ ethylene, polypropylene, etc . ) , polystyrenes (e.g., Styrofoam, Fom-cor), fluorocarbons (e.g., Teflon), phenolic resins (e.g., Bakelite ) , unplasticized polyvinyl chlorides (e.g., Geon ) , polyvinyl alcohols (e.g., Elvanol) , acry­ lonitriles (e.g., Orlon, Saran F-120), regenerated celluloses (e.g., cello­ phane, rayon), cellulose ethers (e.g., methyl cellulose, Ethylcel ) , silicone resins, and some epoxies (e.g., Araldite ) . Epoxies that are a mixture o f epichlorohydrin and Bisphenol A consistently produce spectra with a strong absorption band near 1 5 1 0 cm-I and a weaker but sharp band at 1 6 1 0 em- I . Esterified epoxies and plasticized epoxies will show a carbonyl band near 1 720 em- I . Phthalates are plasticizers that produce a strong carbonyl band at 1 735 cm-I and small but distinct doublet bands at 1 600-1 5 8 5 em- I . They are often combined with cellulose nitrates, polyvinyl chlorides, alkyd resins, or polyesters. Organic acids and acid salts, such as stearates, are also common additives. They usually have one or two sharp absorption bands near 1 5 8 5-1545 em- I . Absorbed water, i n the sample or i n a n accompanying alkali halide salt plate, will produce a weak, broad absorption band near 1 65 0 em- I . Fingerprint region ( 1 5 00-5 00 em- I ) . The fingerprint region is most useful when the sample spectrum is directly compared to reference spectra. When two spectra are overlaid, any missing or absent bands in either spectrum show that the compositions of the two materials are dif­ ferent, even if the functional group bands are the same. A strong, broad absorption in the range of 1 1 00-1 000 em-I may indicate regenerated celluloses (e.g., cellophane, rayon), cellulose ethers (e.g., methyl cellulose, Ethylcel ) , silicone resins, or inorganic addi- Spectral Interpretation 113 tives. Silicone resins have very characteristic sharp bands at 1 260 and 800 cm- I , one on each side of the broad band. Aromatic compounds have sharp, strong bands i n the region of 1 000-650 cm- i . The presence of sharp bands in this region may indi­ cate compounds such as polystyrene, epoxies, phenolic resins, some polyurethanes, or phthalate plasticizers. Colorants Minerals, clays, and other inorganic materials are commonly used as colorants and fillers in paints . Many of these materials may be readily identified by IR spectroscopy as well as by several analytical methods, such as scanning electron microscopy with energy dispersive spec­ troscopy, X-ray diffraction, X-ray fluorescence, and polarized light microscopy. These other methods, which generally provide elemental analysis or crystal structure, are complementary to the molecular species information obtained from IR. An advantage for IR is that it supplies information on both the organic and inorganic components in a paint. An excellent source for reference spectra on artists' colorants is the Artists' Pigments handbook series, volumes 1, 2, and 3, which pro­ vide in-depth chapters on the characterization of numerous specific pig­ ments, each of which provides corresponding IR spectra ( Feller 1 9 8 6 ; Roy 1 993; West-FitzHugh 1 997). Additionally, a review article by Newman on IR spectroscopy for the analysis of painting materials provides interesting applications and comparative spectra, as well as an extensive bibliography ( Newman 1 9 8 0 ) . He cites several articles on the IR spectral identification of pigments, including Riederer 1 969; Kuhn 1 9 70; Gettens, West­ FitzHugh, and Feller 1 974; Gettens and West-FitzHugh 1 9 74; Riederer 1 974; and Siesmayer et al. 1 975 . More-recent articles use IR as one method to identify pigments in paints ( Lear 1 9 8 1 ; Guineau 1 9 8 3 ), in grounds ( Schulz and Kropp 1 9 9 3 ) , and in inks on medieval manuscripts ( Orna et al. 1 9 8 9 ) . IR spectroscopy was also used in the following tech­ nological studies of pigment and paint sets: Winslow Homer's watercolor box was analyzed by Newman, Weston, and Farrell ( 1 9 8 0 ) ; the Hafkenscheid collection of 1 3 9 pigments and painting materials dating from the early nineteenth century was analyzed by Pey ( 1 9 8 7 ) ; and a col­ lection of pigments used in a 1 929 diorama at the Missiemuseum at Steyl­ Tegelen was analyzed by de Keijzer and Karreman ( 1 9 8 9 ) . I R spectroscopy i s also useful i n the identification o f organic colorants and dyes, particularly when they occur as pure materials. For example, phthalocyanine blues and greens produce very distinctive sharp bands from 1 700 to 700 cm- i (Newman 1 9 8 0 ) . Other studies also used IR to identify synthetic organic pigments ( Venkataraman 1 977; Strauss 1 9 84; Gillard et al. 1 994 ) . When organic colorants or dyes have been mordanted on a fiber or particle, IR analysis of the combined material produces a strong spectrum for the fiber or particle overlaid on the col­ orant absorption bands. This hinders the colorant's identification by IR spectroscopy, particularly if it is present in low concentrations (Kirby and White 1 99 6 ) . McGovern and Michel ( 1 990) used IR, as one of several techniques, for the confirmation of royal purple dye in an 114 Chapter 5 archaeological vessel. Low and Baer ( 1 97 8 ) studied alizarin complexes prepared on an alumina lake. Colorants in fragile historic and prehistoric colored fabrics were characterized by IR micro spectroscopy (Martoglio et al. 1 9 90; Jakes, Katon, and Martoglio 1 99 0 ) . Martoglio and coworkers also showed that IR characterization of colorants can be assisted by the use of UV/Vis micro spectroscopy on in situ material (Martoglio et al. 1 99 0 ) . Another analytical method for the identification of colorants is first to extract the colorant from the substrate with acid or base and then to use IR, UVNis, or thin-layer chromatography for characterization ( Schweppe 1 9 79, Schweppe 1 9 8 9 ; Saltzman, Keay, and Christensen 1 96 3 ; Saltzman 1 992; Hansen, Wallert, a n d Derrick 1 99 5 ) . Typically, chro­ matographic analysis methods are preferred for the analysis of dyes. McClure, Thomson, and Tannahill ( 1 96 8 ) provide ninety-six reference IR spectra for organic colorants. Digitized spectral collections of organic dyes and colorants are distributed by Bio-Rad Sadder and Aldrich­ Nicolet ( Appendix I ) . See the above references for more information on the identification of dyes, as further details are not given in this text. Characterization process for pigments Six exemplary IR spectra for inorganic materials used as pigments or fillers are shown in Figure 5 . 1 9 . In general, absorption bands for inor­ ganic materials are broader, are fewer in number, and occur at lower wave numbers than absorption bands for organic materials. This is due to their external ion structure (i.e., solid, sometimes crystalline matrix), as well as to their internal ion composition (i.e., functional groups) . This section will examine the basic characterization of absorption bands for inorganic materials. Additional information on vibrational group assign­ ments of minerals and inorganic materials may be found in the following references ( see Appendix I ) : Farmer 1 9 74; Bellamy 1 975; Gadsen 1 9 75; Zeller and Juszli 1 975. External i o n structure. Pigments, minerals, and clays used in works of art are solids at room temperature. With the exception of amorphous silica, the repeating set of molecular units (-A-B-A-B-A-B-) exists as a semirigid matrix in a layered, or three-dimensional, crystalline structure called a lattice. The lattice structure restricts many molecular transitions: translational, rotational, and even some vibrational motions. In some cases, each functional group (A, for example) may not have an environment identical, or equivalent, to other A functional groups. Depending on their position in the overall pattern of molecules, some A functional groups may freely vibrate, while other A functional groups may have vibrational motion limited by space or direction. This situation could result in a split, or degenerate, vibrational band that appears as two or more adj acent bands. Alternatively, the restricted motion can broaden absorption bands. Vibrational transitions of the lattice structure, or lattice vibra­ tions, usually occur at low wavenumbers in the far-IR region. Thus, this region is particularly useful for detailed studies of a mineral's structure. Internal ion composition. A simple inorganic compound, such as table salt ( sodium chloride, NaCI ) , has one cation, sodium (Na + ) , and 115 Spectral Interpretation Chalk (calcite) (CaC03) Malachite (CuC03· Cu[OHb) Barite (BaS04) Plaster (2CaS04· H20) Silica (amorphous Si02) Clay (kaolin) Figure 5 . 1 9 Exemplary I R transmittance spectra for six inorganic pigments and fillers. 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (em-') one anion, chloride ( Cl - ) , and thus, it can be classified as a simple anionic compound. Most simple anionic compounds will not produce any vibrations in the mid-IR range, and their lattice vibrations occur in the far-IR region. Because of this lack of absorption bands in the mid-IR region, many materials with simple anions (e.g., NaCl, KBr, zinc selenide [ZnSe] , silver chloride [AgCl] , etc . ) are used as IR transparent windows. A more complex inorganic compound, such as chalk ( calcium 2 carbonate, calcite, CaC0 3 ) , has calcium ( Ca + ) as the cation and carbon- 116 Chapter 5) ate ( C0 3 = as the anion. Carbonate can be classified as a complex anion, because the anion is itself a functional group. The covalent bonds in the carbonate tightly hold the anion together. Molecular vibrations within the anion functional group are termed internal vibrations. Complex anions produce characteristic absorption bands that are very useful for charac­ terizing inorganics (Table 5 . 3 ) . The attached cation, whether it is calcium, magnesium, or lead, will have only a slight effect on the position of the absorption bands for the complex anion. In general, heavier cations will shift the band to a lower frequency (Nyquist 1 96 8 ) . The effect is most prominent in the lower-wavenumber bending vibrations. Water of hydration. Water adsorbed on the surface of a sample or incorporated in an amorphous structure will produce broad O-H stretches ( 3400 and 1 65 0 cm- l ) , such as were noted in organic compounds. Water molecules incorporated in the lattice structure of a crystalline molecule, however, will produce specific, sharp, characteristic absorption bands in the regions of 3 8 00-3200 and 1 700-1 600 cm- l . The environmental symmetry seen by each hydroxyl group determines whether the band is single or split. The unique patterns of the hydroxyl absorption bands near 3 8 00-3200 cm- l are very important for character­ izing the composition of hydrated inorganics. Hydrated layered silicates (e.g., kaolinite, talc) resemble a double-deck sandwich with the water molecules positioned in sheets between the silicate anions and interlayer cations. This lattice confor­ mation restricts the direction in which the O-H groups can vibrate. Fortunately, fine distinct absorption bands are produced that are a sensi­ tive indicator of the material. For example, O-H stretches for talc occur as one sharp band at 3676 em-I, with a smaller band at 3660 cm- l . The hydroxyl stretches for kaolinite show as two sharp bands at 3 700 and 3620 cm-l with two slightly smaller bands between 3 6 70 and 3652 cm-l (Appendix I, Farmer 1 9 74 ) . Carbonates. Carbonates, such as calcite ( CaC03), cerussite c-o ( PbC03 ) , azurite ( 2CuC0 3 ·Cu(OH2 ) ) , or malachite ( CuC03 ·Cu(OH2 ) ) , show a t least one strong absorption band from stretching i n the l region of 1 5 50- 1 3 5 0 cm- ( Fig. 5 . 1 9 ) . In anhydrous compounds, such as calcite, the band is smooth, symmetrical, and broad. In hydrated carbon­ ates, such as malachite, this absorption band is split. Table 5.3 Vibrational frequencies for selected com­ plex anionic groups. Stretch (cm- 1 ) Anion = Water of hyd ration ( · H 2 0) 3800-3200 1 700-1 600 1 550-1 350 900-650 Nitrate ( N 0 3-) 1 500-1 250 850-700 Sulfate (SO )4 ) ) Carbonate (C0 3 = 1 200-1 050 680-600 Phosphate (PO 4�) 1 300-900 600-550 Silicate (Si0 3 1 200-800 800-400 = Formates, acetates, and oxalates 1 700-1 300 Cyanates, cyanides, and thiocyanates 2200-2000 1 050-700 117 Spectral I nterpretation Carbonate bending vibrations produce sharp bands i n the region of 900-650 cm- l . These bands show measurable frequency devia­ tions corresponding to the attached cation. For example, the out-of-plane bending vibration for calcium carbonate ( calcite) occurs at 8 72 cm- I , while the same vibration occurs a t 8 4 1 cm- l for cerussite ( lead carbon­ ate ) and at 820 cm-l for malachite ( basic copper carbonate) (Newman 1 9 8 0 ) . Because few organic compounds have strong absorptions in this region, these sharp bands are very useful for confirmation and identification of carbonates in a spectrum. Hydrated carbonates-hydrocerussite (PbC03 ·Pb ( OH 2 ) ) , azurite ( 2 CuC0 3 · C u ( OH2 ) ) , o r malachite ( CuC0 3 · Cu ( O H2 ) )-have absorption bands due to hydration at 3 5 3 5 , 3425, and 3 40013 320 ( split) cm-I, respectively ( Appendix I, Farmer 1 9 74 ) . Additionally, small, sharp O-H bending vibrations occur at 1 1 00-1000 cm- l for the hydrated carbonates. Sulfates. Sulfates, such as gypsum ( CaS04 ·2H2 0 ) , anhydrite ( CaS04) , and barite ( BaS04), show a strong S-O stretching vibration s - o s-o band in the region of 1 200- 1 0 5 0 cm- l (Fig. 5 . 1 9 ) . This band is split i f each o f the bonds i n the tetrahedral sulfate anion sees a different environment, as in the barite. Another small band occurs near 1 000 cm-l, because of an bending vibration, along with sharp, slightly stronger bands at 700-600 cm- l . Changes i n the state of hydration make noticeable differences in spectra. For example, plaster ( 2CaS04·H2 0 ) and gypsum ( CaS04·2H2 0) can be readily distinguished by the hydroxyl absorption bands near 3 5 00 and 1 600 cm- l . Specifically, plaster has hydroxyl bands at 3 6 1 5 , 3465, and 1 630 cm- I , while gypsum has bands at 3555 and 1 690 cm- l . Souza and Derrick used IR spectra to quantitatively deter­ mine the proportions of plaster and gypsum in gesso sottile and gesso grosso layers (Souza and Derrick 1 99 5 ) . Silica and silicates. Amorphous silica produces a strong Si-O stretching band near 1 0 5 0 cm- l that has a recognizable asymmetric shape from a shoulder near 1 200 cm-l ( Fig 5 . 1 9 ) . Nearly all types o f glass (including smalt) produce an absorption band that i s similar in appearance, even though glass is composed of a wide range and mixture of materials. The similar IR spectra occur because the basic glass struc­ ture contains an Si-O backbone . Since IR spectroscopy cannot differenti­ ate glass types, it is not the method of choice for characterizing glass constituents. While the crystalline silica mineral quartz has the same pri­ mary absorption band near 1 1 00 cm- I , it also has a unique, but small, doublet band near 790 cm-l that is very characteristic. Silicates have a fully ordered crystalline lattice structure. This produces a well-defined Si-O absorption band at 1 200-800 cm- l . In lay­ ered silicates, such as kaolin, the band is split into two or more peaks, since some of the Si-O bonds are held perpendicular to the layers, while other vibrate in-plane with the layers. In three-dimensional silicates, such as ultramarine ( lazurite) , the Si-O absorption band is smoother, and split­ ting, when it occurs, is less defined. Bending vibrations for Si-O usually occur below 600 cm- l . Chapter 118 5 The hydration absorption bands for layered silicates, men­ tioned earlier, are uniquely distinctive. Because of restricted molecular motion of the water molecules, these absorptions occur as sharp, well­ defined bands in the region of 3 700 cm - 1 . Excellent reference spectra for these silicate hydration absorption bands are provided in Farmer ( 1 9 74; see Appendix I). These bands are useful for identifying silicate species, even in instances where X-ray diffraction has failed. In the production of ceramics, clay undergoes thermal trans­ formations in its lattice structure. At 400-600 °C, clay dehydrates, losing all water molecules. An IR spectrum collected on a clay heated to this temperature will not have any hydroxyl absorptions. When clay is heated to higher temperatures, 970 °C for kaolinite, the lattice structure col­ lapses, producing an amorphous, glasslike material. Accordingly, its IR spectrum will resemble glass, with a single broad absorption band at 1 200-800 cm- 1 . Often the I R spectra for ochres o r earth pigments, found in both ancient and modern paintings, correspond to spectra for silica and silicates (Newman 1 9 9 6 ) . As the natural earth pigments were simply dug out of the ground, they contain a mixture of minerals, including clay and quartz. The clay and quartz are readily identified by their absorp­ tion bands, while the compounds responsible for the pigment color rarely have any absorption bands in the mid-IR range. The color of red ochre is due to anhydrous iron oxide ( hematite ) ; that of yellow ochre is due to hydrated iron oxides (most often goethite ) ; and brown earth pig­ ments, such as umbers, contain manganese oxides. Of these colored compounds, only the absorption bands near 8 5 0 cm-1 for goethite appear in the mid-IR region. Infrared spectral characterization of pigments With a typical mid-IR FT-IR instrument, most inorganic compounds that contain complex anions ( carbonates, sulfates, silicates, etc . ) can be identified. Inorganic compounds that contain simple anions ( oxides, sulfides, etc . ) often cannot be identified. Since many inorganic pigments and fillers contain complex ions, they are amenable to identification by mid-IR region analysis . Table 5 . 4 lists selected pigments with their for­ mulas and mid-IR absorption band regions. Identification of a spectrum should always be made by final, direct comparison of the unknown spectrum to those in reference spectral collections. However, with pigments and minerals, it is important to eval­ Table 5.4 (opposite page) Pigme nts and fillers correlated with I R uate information known about the sample and reference, especially when absorption band ranges. Most pigme nts commercial pigments are used as references. Some commercial sources with complex anions absorb in the mid- I R may label pigments on the basis of their color rather than their composi­ region. A l l pigments have absorption tion. Additionally, many pigments sold in the nineteenth and twentieth bands in the far- I R region (below centuries are actually mixtures of different compounds, such as a colored 700 cm-' ) . The freq uency range is marked compound with one or more fillers (Newman 1 99 6 ) . Since some compo­ for pigments that are active in the nents in a pigment mixture may have absorption bands in the mid-IR mid - I R region. More than one band may region while others do not, the IR spectrum of the mixture may not rep­ = = = occur within each region (s m med i u m ; w weak). strong; resent the total composition of the material. For example, titanium diox­ ide does not have any absorption bands in the mid-IR region, but a 119 Spectral I nterpretation Mid-IR bands? Formula" Pigment White (with extenders) Aluminum hyd rate Anhydrite Barium su lfate Chalk (calcite) Clay (kaolin ite) Gypsum Lithopone yes yes yes yes yes yes yes yes yes yes no yes AI(OH)3 CaS04 BaS04 CaC0 3 AI203 0 2Si02 0 2 H2O CaS04 02H2O BaS04, ZnS Si02 Si02 3 Mg004Si02 0 H P Quartz Silica (amorphous) Talc Titan ium dioxide White lead (basic carbonate) Ti02 PbC0 3 0 Pb(OH)2 PbS04 0 pbO yes ZnO no CdS, CdSe CdS, CdSe, BaS04 no yes PbOo PbCr04 AS2S2 Pb3 04 HgS yes no no no Yellow Barium yellow Cadmium yellow Chrome yellow Massicot (litharge) Lead tin yellow Strontium yellow BaCr04 CdS PbC r04 PbO Pb2Sn04 SrCr04 yes no yes no no yes Green Chromium oxide Chrysocolla Cobalt green Green earth Malachite Verd igris Viridian Cr2 0 3 CuSi0 3 0nH2O CoO onZnO K,AI, Fe,Mg, hydrosilicate CuC0 3 °Cu(OH2) Cu(CH 3 COO)2 °2Cu(OH)2 Cr20 3 0 2 H2O no yes no yes yes yes yes Blue Azurite Cerulean blue Cobalt blue Egyptian blue Phthalocyan ine blue Prussian blue Smalt Ultramarine (Iazurite) 2CuC0 3 °Cu(OH2) CoOonS n02 CoOoAI2 03 CaO °Cu004Si02 C3 2 H 6 N 8 Cu 1 Fe4(Fe(CN) 6 )3 potash glass Si02, A120 3 , Na20, S yes no no yes yes yes yes yes Brown and black Asphaltum (bitumen) Black oxide Bone black (apatite) Charcoal organic Fe20 3 Ca3 (P04)2 ' carbon carbon yes no yes no I ron oxide pigments Yellow (goethite) Red (hematite) Fe20 3 02H2O Fe20 3 yes no White lead (basic su lfate) Zinc oxide Red and orange Cad m i u m red Cadmium red (Iithopone) Chrome orange Realgar Red lead Verm ilion "From Gettens and Stout ( 1 96 ) and Afremow and Vandeberg ( 1 96 )0 3 8003200 cm - 1 22002000 cm -1 1 7001 2 00 cm - 1 1 2001 000 cm - 1 1 000700 cm -1 m w m m m w m s s w w w w w w m s m w m m w w w w m w w m m w m m w m m w w 120 Chapter 5 commercial formulation containing fillers, such as clay or barium sulfate, would produce a characteristic spectrum. In this instance, the recorded spectrum would indicate the fillers and not the actual pigment. Several reference spectral collections, books, and digitized spectra ( listed in Appendix I) are available for minerals and pigments; these are Sadtler Research Laboratories, Sprouse Scientific Systems, Inc., Nyquist and Kagel ( 1 97 1 ) , Afremow and Vandeberg ( 1 96 6 ) , Boldyrev ( 1 976), Nakamoto ( 1 9 7 8 ) , and Price and Carlson ( forthcoming). Mixtures Most conservation-related samples submitted for IR analysis are mixtures. Their IR spectra contain the superimposed spectra of each component present. The intensities of each component's bands are directly propor­ tional to the concentration of that component. The resulting spectrum may be complex, with overlapping bands that obscure those needed for individual material identification. Thus, the interpretation of a spectrum from an unsuspected mixture may lead to erroneous conclusions. How­ ever, it is often possible to identify at least one component directly, and then eliminate its absorptions from further consideration. The pattern of other components, if not initially recognized, may then become clearer. In paints, pigments are dispersed in an organic binder. This usually does not hinder the determination of the pigment, but it may make it difficult to determine the binder if it is present in low concentra­ tions. Figure 5.20 illustrates the IR spectrum obtained from a 5 0150 w/w% mixture of calcium carbonate and rabbit-skin glue. Even though the weight proportion of the two components is equivalent, the relative intensities of the strongest absorption bands for each component are not the same, because the absorptivity of each functional group depends on its dipole moment, bond strength, and molecular environment. For the analysis of paints, it is helpful if the pigment compo­ nent is identified and spectrally subtracted, thus providing a better indica­ tion of any binder absorption bands that may have been obscured by the overlapping pigment absorptions. When the inorganic component cannot be identified or when the subtraction does not work well, solvent extrac­ tions may be useful to physically separate the binder from pigments before each fraction is reanalyzed ( for technique, see chap. 3 ) . Figure 5 . 2 1 illustrates the IR spectrum obtained for a neat sample of red paint. The sharp absorptions bands due to a synthetic organic pigment over­ lapped the absorption bands for the binder, making it difficult to identify. After a drop of acetone was placed on the sample and allowed to evapo­ rate, the dried residue of the acetone-soluble portion of the paint was analyzed. The absorption bands created by the red colorant were no longer noticeable. This spectrum corresponds well with an ethyl acrylate reference spectrum. The average detection limit for most materials in a mixture is 5 % . It may range from below 1 % to 3 0 % , however, depending on the absorptivity of the material and on the number of components in the mixture. The sensitivity to minor components may be enhanced by the use of techniques of spectral subtraction, deconvolution, and derivatiza- 121 Spectral I nterpretation III I Rabbit-skin glue Calcium carbonate Figure 5.20 I R transm ittance spectra of pure rabbit­ skin glue, pure calcium carbonate (calcite) , and a mixture contai ning 50% w/w% of each. The absorption bands for both indi­ 50/50 w/w% vidual compounds are present i n the spec­ rabbit-skin glue and calcium carbonate trum for the mixture, and their respective absorption band intensities correspond to the proportion of that material in the m ixture. In material mi xtures for which absorption bands overlap, it can be 4000 3600 3200 2800 2400 2000 1 800 1 600 1 400 1 200 1 000 800 600 Wavenumber (cm - 1 ) difficult to identify some components. tion, as well as solvent extractions. More details about these spectral manipulation methods are given later in this chapter. Quantitative Analysis The intensities of spectral bands are used for quantitative ( :!: 1 % ) and semiquantitative ( :!:l O % ) IR analysis. Because of potential spectral inter­ ferences, sample preparation variations, and sensitivity limitations, it is difficult to obtain highly accurate quantitative results with IR spec­ troscopy. Quantitative analysis of organic compounds is much more reliably achieved with chromatographic methods. Often, however, semi­ quantitative analysis is sufficient to answer the analysis question. In this case, IR has an advantage, because it can readily supply qualitative and 122 Chapter 1 10 5 Red paint 1 00 90 Q) <.) c: <U :t:: E <JJ 80 70 c: <U � 60 ?f!. 50 40 30 1 10 Acetone extract 1 00 Figure 5.21 90 I R transm ittance spectra for a neat red paint sample (top) and for the acetonesoluble portion of the sample (bottom). The absorption bands from the organic colorant h i nder the identification of the bind er. A solvent extraction separates Q) <.) c: <U :t:: 80 E <JJ c: <U � ?f!. 70 60 some of the binder from the pigment, allowing for a " cleaner" spectrum to be collected. The spectrum for the acetone extract corresponds to an ethyl acrylate 50 40 3000 3500 2500 2000 1 500 1 000 Wavenumber (cm- 1 ) reference spectru m . semiquantitative analysis results. In order for quantitative calculations to be performed, however, the material must first be identified. The capacity of any component to absorb IR radiation is con­ stant. This capacity is termed its molar absorptivity. Additionally, the intensity of any specific absorption band in relation to another is con­ stant, because the intensity of an absorption band is directly proportional to the rate of change in the dipole moment of that particular vibration. A large change in the dipole moment of the atoms during a vibration will produce an intense band. Thus, very polar functional groups, such as those containing halogens, will exhibit intense absorption bands. An intense absorption band can also be produced by the presence of multiple functional groups within the molecule, such as CH2 groups in paraffin wax, that each have the same vibrational energy, such that an additive effect is created. There is a linear quantitative relationship between absorbance and concentration of absorbing molecules: A b c =E = - log ( liT) 123 Spectral Interpretation where: A absorbance; molar absorptivity ( a constant for the = = E= = molecule); b sample pathlength; c concentration; and T = transmit­ tance ( % T/1 00 ) . This equation i s called the Beer-Lambert law-or simply Beer's law-and it is used to determine a relationship between measured absorptivity, band intensity, and concentration of IR-active functional groups in the sample. The linear range for the relationship holds for spectra with a maximum absorption band between 20 and 6 5 % T ( 0 . 7-0.2 absorbance). The equation shows that there is a one-to-one rela­ tionship between the height, or intensity (in absorbance units ) , of an absorption band and the concentration of that molecule. Note that the linear relationship holds for absorbance and not for transmittance, which has a logarithmic relationship. Thus, for quantitative work, spectra should be plotted in absorbance units. All quantitative IR analyses are done by comparing the intensity of a specific absorption band, in a bsorbance units, of the unknown material with the absorbance, or band height, of the same material in a standard of known concentration. In a mixture of materi­ als, the a bsorbances are additive; thus, the total absorbance at any given wavelength is the sum of the absorptions of the individual com­ ponents . Therefore, for quantitative analysis of a material, it is advan­ tageous to select an a bsorption band that not only is characteristic of that material but also is isolated from absorption bands due to other materials in the sample. Beer's law shows that sample pathlength is also a factor in the measurement. For one quantitative method, direct calculation of con­ centration, the path length must be either known or fixed. Thus, direct measurement is normally limited to liquids or solutions that can be ana­ lyzed in a fixed-pathlength liquid cell. In this method, the unknown con­ centration of an identified single component can be calculated from a calibration curve. The calibration curve is prepared by analysis of the same component in solutions, or mixtures, of at least four different con­ centrations. An absorption band is selected that is characteristic of the component of interest and that is free from interferences. Then a plot is made of the absorbance value for that band versus the concentration of the component in each solution. The concentration of the sample is determined by comparing the intensity of that particular band in its spec­ trum with the calibration curve. The intensity of the band is measured as the absorbance difference from its maximum to its baseline. The baseline is drawn where the pen tracing would go if the band were not present ( Smith 1 979 ) . Integrated, or total-area, measurements of the absorption band are rarely needed, since intensity measurements can be made more reproducibly and accurately ( Smith 1 979 ) . Because the pathlength cannot be determined precisely, this method is not used for films and pellets. The absorbance ratio method is used when the pathlength of the sample cannot be readily determined. The method works well for films, pellets, and diffuse or internal reflection measurements. For this method, at least two components (A and B) must be in the sample matrix, and each must have an absorbance band that exhibits minimum 124 Chapter 5 interference. Because the components are present in the same sample, the pathlength is the same and is no longer a variable. The calibration curve is generated from at least four spectra obtained from mixtures of the components in different proportions. The ratio of the intensities of the two bands of interest ( IA/IB ) is plotted versus the ratio of their concentra­ tions ( CA/CB ) . Once the curve is generated, the ratio of the concentration of the components in the unknown sample can be determined, since the sum of their concentrations equals unity, or 1 00 % . Thus, the specific concentrations for each component can be easily calculated. The absorbance ratio method was applied to the study of archaeological wood deterioration by Kirillov and Mikolajchuk ( 1 9 9 0 ) . Ferrus, Pages, a n d Diez ( 1 9 8 1 ) used quantitative analysis for the exami­ nation of kaolin-casein coatings on papers. Other methods, such as the internal standard method used by Biscontin and Volpin for the analysis of calcium oxalate films ( 1 9 8 9 ) , are also available. For other methods of quantitative analysis, see the IR spectroscopy atlas published by the Chicago Society for Paint Technology ( 1 9 8 0:53-5 8 ) and Smith ( 1 979:2 1 9-6 8 ) . Mathematical Manipulations of Spectra The linear proportionality of a material's concentration to its absorbance band intensity ( Beer's law) is the basis for many of the IR data processing algorithms, such as spectral subtraction, spectral searching, and factor analysis. Other routines, such as Fourier self-deconvolution, can aid in the resolution of bands. Subtraction techniques Computer spectral subtraction methods are used to separate spectra of components in a mixture, to remove bands due to impurities, to confirm the identity of a sample, and to detect small changes in a sample . When one component is identified, its pure spectrum ( in absorbance units) is then multiplied by a scaling factor and subtracted out, and the remaining spectral bands are examined for any differences. This is known as scaled absorbance subtraction. Typically, an Autoscale subtraction computer routine esti­ mates a scaling factor based on the integrated areas of several peaks. While this may be a good estimate, the best method for spectral subtrac­ tion is to select visually a single band of the component to be removed in both spectra, then null out that band ( Griffiths and de Haseth 1 9 8 6 ) . The resultant difference spectrum should be evaluated closely to see which bands still exist and to determine if there are other potential components not initially considered. When subtraction is used to confirm the identity of a mate­ rial, its reference spectrum is subtracted from the sample spectrum; if the difference is zero, then it is clear that the two spectra are of the same compound. This is one method used by search routines to check varia­ tions between an unknown spectrum and the reference spectra. Spectral Interpretation 1 25 Difference spectra, resulting from spectral subtraction, are useful for the evaluation of changes in a material due to chemical reac­ tions or aging. The difference spectrum will show only the regions of changing absorption, while the molecular features that remain constant are removed by the subtraction operation. For optimum subtraction results, the two initial spectra should be recorded from samples prepared and analyzed in the same manner. Their maximum absorption bands should be no more than 0 . 7 absorbance units ( n o less than 20% T). This guideline ensures that the components' concentrations are within the linear range covered by Beer's law. Slight changes in band positions or shapes can result in derivative­ like bands or positive residuals occurring in the difference spectrum. These artifacts may be incorrectly attributed to the presence of minor components. For more information on the limitations of spectral subtrac­ tion and its applications, see Koenig ( 1 992) and Bartick, Corbett, and McClure ( 1 9 8 2 ) . Figure 5 .22 illustrates the use of spectral subtraction for the identification of a minor component. The spectrum on top (A) is shellac plus a small amount of an unknown material, indicated by the bands at 1 8 00 and 8 70 cm- l . The middle spectrum ( B ) of pure shellac was spec­ trally subtracted from the top spectrum, and the resultant spectrum ( C ) , which corresponds t o calcium carbonate, is shown a t the bottom. Resolution enhancement methods IR absorption bands are relatively broad and may overlap one another. This is particularly true for the spectra of mixtures. Resolution enhance­ ment methods can artificially narrow the width of the bands and thus minimize overlap. Various mathematical methods, such as derivative spectroscopy and Fourier self-deconvolution, are iterative optimization processes performed on the interferogram. The operator selects band shape and bandwidth parameters; the maximum amount of bandwidth reduction is determined by the initial resolution at which the spectrum was measured. In derivative spectroscopy, the measured absorbance spectrum is first transformed back into an interferogram. Then the computer multi­ plies it by a function to compute the nth derivative. While any order of derivative may be calculated, the even-order functions (2, 4, etc. ) provide the better resultant spectra. The second derivative is the most commonly used. The resultant spectrum will have sharper bands than those of the original spectrum. Drawbacks are that strong bands will have side lobes and that spectrum noise is increased. Figure 5 .23 illustrates the use of derivative spectroscopy to increase the resolution of overlapping hydro­ carbon bands. A deconvolution program may also help elucidate information in a spectrum. It operates on two or more overlapping bands to reduce the line width of the individual components and therefore to improve the resolution of each band up to three times ( Kauppinen et al. 1 9 8 1 ; Koenig 1 992). Convolution is a broadening function that occurs in the produc­ tion of a spectrum and changes the intrinsic line shape of the absorption 126 Chapter 5 2000 1 800 1 600 1 400 1 200 1 000 700 1 000 700 1 000 700 Wavenumber (cm- 1 ) .�'"E'" B Q) u c rn c J!= � 2000 1 800 1 600 1 400 1 200 Wavenumber (cm-1 ) Figure 5.22 = C) for the identification of a A n example of spectral su btraction (A - B minor component. Slight d ifferences between the top spectrum (A) of a shellac and calcium carbonate mixture, and the middle spectrum (B) of shellac were noted. The middle spectrum (B) was su btracted from the top spectru m ; the resultant spec­ trum (C) corresponds to reference spectra for calcareous materials. 2000 1 800 1 600 1 400 1 200 Wavenumber (cm - 1 ) into peaks ( bands ) . Deconvolution is designed to correct for the broaden­ ing function and thus narrow the bands. The optimum use of deconvolu­ tion requires information about the true width of the absorption band, which is usually not known. If the spectrum is under-deconvoluted, little improvement in resolution will result. If the spectrum is over­ deconvoluted, extraneous side lobes, as well as distortions in band intensities, will be produced. Since the different IR bands have different 127 Spectral Interpretation Original spectrum Figure 5.23 An example of derivatization , one method used to increase the effective resolution of a spectrum. The overlapping hydrocarbon bands for a silicone oil and hyd rocarbon Second derivative oil mixture are shown (3050-2800 c m - ' ) for the original transm ittance spectru m , the first derivative, and the second deriva­ tive. The second derivative is most often used, since the absorption band maxima are near their original positions. Derivati­ zation changes the relative intensities of the bands, as well as increases the noise 3040 3020 3000 2980 2960 2940 2920 2900 2880 2860 2840 2820 2800 Wavenumber (cm- 1 ) level of the spectru m . inherent bandwidths, it is impossible to optimally deconvolute all bands. Thus, since the same deconvolution width is used for the entire spectrum, some bands may be overprocessed, while others are underprocessed. Negative bands may appear, and the signal-to-noise ratio is decreased. An example of deconvolution is shown in Figure 5 .24. A sample of a mastic-oil film from the Gettens and Stout Collection, dated 1 934 (prepared on a glass plate as a dried film made from 5 cc oil in 1 00 cc ethanol, with 33 g mastic ) , was analyzed. Even though the com­ ponents of the sample were known, because of the low amount of oil, the bands specific for oil were only slightly recognizable after deconvolution was performed. Summary Characterization of a material class for a pure sample is well within the realm of IR analysis. This chapter, as an introduction to skills and meth­ ods important in spectral interpretation, includes graphs, tables, and dis­ cussion aimed at facilitating spectral analysis. Initial examination of 128 Chapter 5 .,- 0.30 Figure 5.24 An example of deconvolution, another method used to increase the effective res­ olution of a spectru m . The original (top) Q).0<{<.)ceno(f) and deconvoluted (bottom) absorbance Deconvoluted spectra are shown for a sample contai n i n g jJ� +- a mixture o f oil in mastic. Resolved bands due to the oil are marked with asterisks. However, because of the low concentra­ tion of oil in the sample, its absorption bands are poorly defi ned, even after 0.29 1 800 1 000 700 Wavenumber (cm- 1 ) deconvolution. spectra quality is followed by a discussion of information gleaned from the spectral regions and spectra-structure correlations. In-depth informa­ tion is then presented for the interpretation of IR spectra for natural products, synthetic resins, and colorants that are often found in samples from art materials and conservation treatments. Samples from works of art, however, may be complex mix­ tures of components that are difficult to completely identify by IR spec­ troscopy alone. However, IR spectral analysis can characterize the material class (es} present within the sample and thus supply a basis for the selection of a secondary analysis method for further separation of sample components and their identification. For example, knowledge of a sample's component classes ( oil, protein, carbohydrate, etc . ) is fundamen­ tal to the selection of an appropriate chromatographic analysis protocol. Positive identification by IR spectroscopy is often limited by the availability of relevant reference spectra. It is important to have a spectra collection that simulates the probable set of unknown materials. This is especially true for complex samples and mixtures. For the field of art conservation, it is also desirable to have a spectral collection of aged reference materials. Thus, an extensive set of relevant citations are presented. While IR spectroscopy is a valuable method for the identification of an unknown, the spectra and the method of analysis must be examined critically before any conclusions are made. Computer spectral search routines can be very helpful, but the computer can never make the final decision. Instead, the analyst applies j udgment to draw conclusions based on information derived from sampling, analysis, and interpretation. Spectral Interpretation 1 29 Additional Reading Al len, R. 0., and P. Sanderson 1 9 8 8 . Characterization of epoxy glues with FTIR. Applied Spectroscopy Reviews 2 4 : 1 75-87. American Society for Testing Materi als (ASTM) 1 99 1 . Standard Practice for General Techniques of Infrared Quantitative Analysis. ASTM E 1 68 - 8 8 . Annual Book of ASTM Standards, vol. 1 4-0. Philadelphia: ASTM. Bellamy, L. J . 1 975. Advances in Infrared Group Frequencies. London: Chapman and Hall. 1 980. The Infrared Spectra of Complex Molecules. 2d ed. London: Chapman and Hall. Chicago Society for Coating Technology 1 98 0 . An Infrared Spectroscopy Atlas for the Coatings Industry. Philadelphia: Federation of Societies for Paint Technology. Colthup, N. B., L. H . Daly, and S. E. Wiberley 1 990. Introduction to Infrared and Raman Spectroscopy. 3d ed. Boston: Academic Press. Farmer, V. c., ed. 1 974. The Infrared Spectra of Minerals. Mineralogical Society Monograph 4. Surrey, U.K.: Adlard and Son. S i lverstein, R. M., G. C. Bassler, and T. C. Morri l l 1 9 9 1 . Spectrometric Identification of Organic Compounds. 5th ed. New York: John Wiley and Sons. Chapter 6 Case Studies Over thirty years ago, Jacqueline Olin stated that " infrared spectropho­ tometry is becoming an increasingly important method in the analysis, authentication, and preservation of paintings and ancient artifacts " ( Olin 1 96 6 ) . Since that time, IR spectroscopy has been employed in several significant studies of museum materials, and it is now the leading choice for analysis of most organic, and of many inorganic, materials in art con­ servation research. IR spectroscopy enjoys such standing because it can be used for the analysis of small amounts of nearly any substance, thus encompassing the broad range of materials and restrictive sample sizes encountered in artifact analysis. The applications of IR are multifaceted, covering not only the identification of materials but also the evaluation of condition and the monitoring of chemical reactions. Identification and Characterization of Material s IR spectroscopy has long been a primary tool for the identification of art and archaeological materials. When Gettens promoted the technical examination of art in 1 952, IR spectroscopy was included as a technique for the analysis of artifacts and paintings ( Gettens 1 952). In 1 96 8 Masschelein-Kleiner and coworkers selected I R analysis as one method i n a scheme for the identification o f binding media, varnishes, a n d adhesives (Masschelein-Kleiner, Heylen, and Tricot-Marckx 1 96 8 ) . In 1 969 Olin and coworkers reviewed favorably the emerging use of IR spectroscopy for the analysis of art obj ects ( Olin, Salmon, and Olin 1 96 9 ) . Then, in 1 977, Low and Baer showed the increased sensitivity of Fourier transform infrared ( FT-IR) spectroscopy for the analysis of many natural organic materials ( Low and Baer 1 977). In 1 9 8 9 Roelofs presented an analytical schematic for the identification of varnishes, media, and dyestuffs, using IR in a combination of modern techniques (Roelofs 1 9 8 9 ) . One important application for I R spectroscopy is the deter­ mination of components in paint samples. Birstein used IR in several studies to determine the binders and pigments in Asian wall paintings and Egyptian tomb paintings, as well as to examine the aging character­ istics of gelatin ( Birstein 1 9 75, 1 97 8 ; Birstein and Tul'Chinskii 1 9 77). Delbourgo used IR to analyze fresco painting cross sections (Delbourgo 131 Case Studies 1 9 72 ) . Both egg tempera a n d drying oils were found as media in Gothic panel paintings that were part of the main altar in the church of Tingelstad, Norway (Plahter, Skug, and Plahter 1 974 ) . Riederer used IR to examine the techniques and materials of early medieval mural paint­ ings in Turkistan ( Riederer 1 977) . Kobus describes the use of both IR and scanning electron microscopy with energy dispersive spectroscopy ( SEM-EDS ) for the microanalysis of small paint samples ( Kobus 1 9 8 7 ) . A technical examination of Gerard Dou's The Young Mother used I R and gas chromatography ( GC ) ; results indicated the presence of bitumen (van der Loeff and Groen 1 9 9 3 ) . Reference spectra of ethnographic materials are often gener­ ated as part of a corresponding technological study, since commercial libraries do not contain spectra of these materials. To examine the introduction of rice to the Pacific islands, Hill matched the extract of an archaeological specimen from Borneo to reference spectra of rice extracts ( Hill 1 9 8 3-8 4 ) . As part of an investigation in the use of veg­ etable resins on Congo ceramics, a series of reference spectra for native resins were collected and compared to samples from decorative coatings on the ceramics ( Hexter and Hopwood 1 9 9 2 ) . Pigments and media from 1 ,346 samples of historic Native obj ects were analyzed by the Canadian Conservation Institute to form a database characterizing material usage by tribes, regions, and time periods ( Miller, Moffatt, and Sirois 1 9 9 0 ) . Several technical studies have used I R spectroscopy i n con­ j unction with other techniques to examine archaeological obj ects. Delbourgo and Gay analyzed organic remains found in archaeological excavations in Sudan ( Delbourgo and Gay 1 9 6 8 ) . IR spectroscopy was used by Maniatis and coworkers to determine the hydration state of clays in low-fired terra-cotta statues from Greece (Maniatis, Katsanos, and Caskey 1 9 8 2 ) . Duraiswamy and coworkers later used this technique to determine the firing temperature of clays from excavations in India (Duraiswamy, Ramaswamy, and Venkatachalapathy 1 99 2 ) . X-ray fluorescence, atomic absorption, and IR studies were performed on tile and wall fragments from ancient Roman settlements ( Blasius et al. 1 9 8 3 ) . IR was used for the initial examination of cosmetics from a Thracian tomb in Bulgaria; that examination was followed by chro­ matography for the final identification of individual components ( Zolotovich and Popov 1 9 6 9 ) . I R spectroscopy is ideal for the identification o f synthetic resins used as coatings and binders. Jayme and Traser collected reference spectra for paper coatings and fillers and used them for the identification of coated papers (Jayme and Traser 1 97 1 ) . Cellulose nitrate has been identified as an emulsion used on early microphotographs (Newman and Stevens 1 9 77). Stringari characterized acrylics used in artist paints ( Stringari and Pratt 1 99 3 ) . Sharpless used IR to identify the plastics and their additives when he extensively characterized the effects of storage materials and cleaning products on the deterioration of coins in museum collections ( Sharpless 1 9 8 0 ) . 1 32 Chapter 6 IR spectroscopy can also help in the identification of some organic colorants and dyes (Masschelein-Kleiner and Maes 1 97 8 ) . Berberine, a traditional yellow Japanese dye, has been well characterized by fluorescent and IR studies ( Matsuda 1 9 8 6 ) . Garrido used IR to differ­ entiate between Maya blue ( indigo on clay) and malachite for multiple blue painted Mayan obj ects ( Garrido 1 96 9 ) . IR was also used as one method in the identification of royal purple dye, an indigo colorant used in antiquity found in the interior of jars in a thirteenth-centurY-B.c.E. Lebanese archaeological site ( McGovern and Michel 1 99 0 ) . Roelofs and coworkers di scussed IR in their comprehensive study of the advantages and disadvantages of several analytical methods for the identification of dyestuffs ( Roelofs et al. 1 9 8 7 ) . Very small samples of archaeological fibers and dyes have been analyzed by IR microspectroscopy ( Lang et al. 1 9 8 6 ; Matsuda and Miyoshi 1 9 89; Jakes, Katon, and Martoglio 1 990; Martoglio et al. 1 990; Jakes, Sibley, and Yerkes 1 994). Corrosion and patinas on metal surfaces are often a mixture of materials that can be characterized by IR. Tennent and Antonio used IR to characterize bronze disease and its products (Tennent and Antonio 1 9 8 1 ) . Giangrande presented in a paper a selection of reference spectra for bronze corrosion products ( Giangrande 1 9 8 8 ) . IR was one method used by Jakes and Howard to characterize the mineralization of textiles found encrusted on bronze implements from the Chinese Shang dynasty (Jakes and Howard 1 9 6 8 ) . Schrenk found corrosion below protective coatings on Benin bronzes ( Schrenk 1 9 9 1 ) . Koltai used IR to determine corrosion products on a Roman silver fibula ( Koltai 1 9 8 4 ) . Another study used IR to examine the corrosion products of lead exposed both to controlled conditions and to an outdoor environment (Tranter 1 9 76 ) . Corrosion processes occurring on stained-glass windows have also been examined with IR spectroscopy ( Bettembourg 1 9 8 8 ; Fuchs, Romich, and Schmidt 1 99 0 ) . IR spectroscopy has been used to investigate the corro­ sion inhibition capabilities of metal coatings (Tobe et al. 1 9 74; Ito and Takahashi 1 9 8 5 ) . Efflorescence on mollusk shells was characterized by Tennent and Baird, who used IR, X-ray diffraction ( XRD ) , thermal analysis, and nuclear magnetic resonance ( Tennent and Baird 1 9 8 5 ) . IR spectral imaging i s a special technique useful i n the IR spectroscopic analysis of materials. Imaging technologies use multi­ dimensional spectroscopic processing to create compositional maps of samples. Familiar examples are elemental imaging on an electron microscope and magnetic resonance imaging for medical diagnoses. Characterization of materials with IR mapping micro spectroscopy ( also known as functional group mapping) has been developed for several years (for history and more information, see Harthcock and Atkin 1 9 8 8 ) . Derrick and coworkers illustrated the application of IR spectral imaging to the characterization of paint cross sections (Derrick 1 99 5 ) . IR map­ ping combines the analytical capabilities of an IR microscope with a computer-controlled, motorized stage and appropriate software pro­ grams, in order to identify, as well as locate, various types of compo­ nents, anomalies, and defects in materials. 1 33 Case Studies Deterioration Studies While it is easy to think of IR spectroscopy as a tool for the identifi­ cation of materials, it is often used for other studies, such as the moni­ toring of chemical reactions, the determination of chemical changes and degradation, the ascertaining of damage from specific conditions, and the evaluation of material stability. Common exposure conditions (ultra­ violet [UV] radiation, elevated temperatures, oxygen, high humidity, reactive vapor, and dirt) cause deterioration and damage to some materi­ als. However, not all materials react to any one parameter in the same fashion. IR spectroscopy can be used to increase understanding of degradation processes, causes, and rates of change; this knowledge can, in turn, aid in the development of conservation strategies to extend the lifetime of an obj ect. Feller examined the Fade-Ometer-induced alterations occur­ ring in the IR absorption spectra of natural resins and afterward con­ cluded that it is necessary to have reference spectra of aged resins for comparison of samples from aged obj ects ( Feller 1 95 9 ) . In another accel­ erated aging study, Kenj o, who used IR spectrometry to examine the effects of increased temperature and UV light on Japanese lacquer, found that the outer surface of lacquer-covered obj ects exhibited measurable oxidation (Kenjo 1 9 76 ) . The mechanism by which soluble nylon becomes insoluble has been studied: the change in solubility was found to be due in part to photooxidation and hydrolysis (Bockoff et al. 1 9 84; Fromageot 1 9 90; Fromageot and Lemaire 1 9 9 1 ) . Oosterbroek and coworkers used IR to relate chemical and mechanical changes (crack formation and stress development) in organic coatings ( Oosterbroek et al. 1 9 9 1 ) . Both IR and UV/visible (UVNis) spectroscopies were used to study the effect of heat and light aging on three formulations of Paraloid B-72 adhesives (Butler 1 9 8 8 ) . In some wood degradation studies, the ratio of cellulose to lignin was measured by IR (Kosik, Luzakova, and Reiser 1 9 72; Pecina and Kommert 1 9 85; Mikolajchuk et al. 1 9 87; Kirillov and Mikolajchuk 1 9 9 0 ) . Hon used IR spectroscopy to study the degradation of paper documents ( Hon 1 9 8 9 ) . IR has also been used to study the structural stability of hair samples from Egyptian mummies (Lubec et al. 1 9 8 7 ) . The weathering o f stone due t o the outdoor environment and to pollutants has been well studied with IR analysis. Reflection IR mea­ surements were used to examine the effects of temperature, relative humidity, and pollutants on marble ( Sramek 1 9 7 8 ; Faraone 1 9 87; Rao 1 9 82, 1 9 8 4 ) . The effects of sulfur dioxide pollutants and the resulting stone deterioration were further assessed ( Eastes and Salisbury 1 9 8 6 ; Zappia e t a l . 1 992; Connor and Girardet 1 992 ) . Accretions, salt deposits, and weathered surfaces on stone sculptures and buildings were identified with IR spectroscopy ( Frediani and Matteoli 1 9 78; Bradley 1 9 8 7; Abd EI-Hady 1 9 8 8 ; Domaslowski and Kesy-Lewandowska 1 9 8 8 ; Shoeib, Roznerska, and Boryk-Jozefowicz 1 9 90; Blanco et al. 1 99 1 ) . Calcium oxalate has been investigated as a weathering product formed by the action of lichens on stone ( Gorgoni, Lazzarini, and Salvadori 1 99 2 ) . Other studies have quantitatively measured calcium oxalate 1 34 Chapter 6 (Biscontin and Volpin 1 9 8 9 ) and examined the stability of calcium oxalate hydration states (White and Ai 1 99 2 ) , as well as determined its potential for protecting underlying stone (Matteini, Moles, and Giovannoni 1 994). In the study of the reversibility of fluoropolymer treatments of stone, Camaiti and coworkers used IR spectroscopy to determine the extent of polymer removal ( Camaiti et al. 1 9 9 1 ) . The Case Studies Ten case studies are presented below. Note that for Case Studies 1 -6, IR is used to characterize unknown samples. Case Studies 7-1 0 show how IR can be used to monitor changes and examine degradation in several types of materials. Case Study 1: U ltramarine pigments The most common method for the identification of an IR spectrum of an unknown sample is its direct comparison to a reference material spec­ trum. When the materials are the same, the intensity and position of all absorption bands will correspond. If the unknown spectrum is missing bands that the reference contains, then that reference can be unequivo­ cally eliminated. However, if the two spectra correspond except for the addition of one or more bands in the sample spectrum, then the interpre­ tation becomes complex. As shown in this case study, the analyst must determine whether these additional bands are due to a different material, to an added component, or to a contaminant. Background Ultramarine blues are composed of complex sodium aluminum sulfosili­ cates and are one of the oldest blue pigments (Moser 1 9 7 3 ) . Natural ultramarine is an expensive blue pigment produced from the semi­ precious stone lapis lazuli. The colorant can be separated from extrane­ ous minerals in the stone by a time-consuming process. As described by Cennino Cennini in the fifteenth century, the powdered lapis was mixed with a wax-oil-resin mixture and kneaded in a weak lye solution ( Cennini 1 9 6 0 ) . The dough retained the extraneous particles, and the blue particles settled out. In the 1 820s, a commercial process for syn­ thetic ultramarine was developed that produced a very pure, deeply col­ ored, fine-particle material. Optical microscopy is used to distinguish between the natural and synthetic ultramarine particles based on the size and shape of the particles. Other analysis methods (X-ray fluorescence, SEM-EDS, XRD ) commonly used for the identification of pigments can­ not readily differentiate between natural and synthetic ultramarine. During routine IR microanalysis of pigments and binders from a sixteenth-century Italian painting ( Venus and Adonis by Titian, J. Paul Getty Museum, Los Angeles ), it was noted that the IR spectrum obtained from a natural ultramarine blue particle corresponded to a reference spec- 135 Case Studies trum for natural ultramarine, with the exception of an unexpected addi­ tional absorption band at 2340 cm- t . Further analyses showed that all the blue particles in that sample and in paint samples from two other paint­ ings (Presentation in the Temple by Mantegna, Staatliches Museen, Berlin, and Madonna with Child by Mantegna, Accademia Carrara, Bergamo, Italy) contained this absorption band (Fig. 6 . 1 ) . Since this region of the IR spectrum contains rarely found functional groups ( e.g., cyano and carbon­ carbon triple bonds ) , the first concern after the unusual absorption band was observed was that Prussian blue ( ferric ferrocyanide, Fe4[Fe( CN) b 6 developed in the eighteenth century) was in the sample. Analysis question What material is producing the absorption band at 2340 em- I , and is it normally found in spectra for natural ultramarine blue particles? Method IR microanalysis was used for this study. The size of the individual blue particles ranged from approximately 10 to 40 ,....,m in diameter after flatten­ ing. Thus, each individual blue particle could be selected directly for analysis by use of the adjustable apertures on the microspectrophotometer. VenusandAdonis Pres ntaioni theTemple Madon awithChifd by Titian Figure 6.1 IR transm ittance spectra for blue particles of natural ultramarine obtained from th ree 2340 by Mantegna 2340 by Mantegna fifteenth- and Sixteenth-century Italian paintings (Venus and Adonis by Titian, J. Paul Getty Muse u m , Los Angeles; Presentation in the Temple by Mantegna, Staatliches Musee n , Berl i n ; and Madonna with Child by Mantegna, Accademia Carrara, Bergamo, Italy) . Each spectrum exhibits an absorption band at 2340 cm- 1 that is not due to carbon dioxide. 4000 3000 2000 Wavenumber (cm- 1 ) 1 500 1 000 1 36 Chapter 6 Analysis For this example ( and all following case studies, except as noted), each particle was placed on a barium fluoride ( BaF2 ) window, flattened with a metal roller, then analyzed with transmitted radiation. A Spectra-Tech IRj.LS microprobe was used for the IR analysis ( see Suppliers ) . It is equipped with a narrow-band, cryogenically cooled mercury-cadmium­ telluride ( MCT) detector. The spectra are the sum of 200 scans collected from 4000 to 800 cm- t at a resolution of 4 cm- t . The IRJlS and the sample were continually purged with dry, carbon dioxide ( C0 2 )-free air. This factor is important, because the absorption band of interest occurs in the same region as the CO 2 doublet at 2340 cm- t . Results Comparison of the sample spectra with the IR reference spectra for pig­ ments containing cyano stretches ( Prussian blue and bone black) showed that the small absorption band in the natural ultramarine at 2340 cm- t was distinctly different from the cyano stretch that occurs near 2 1 00 cm- t ( Fig. 6.2 ) . A literature search showed that Orna and coworkers, in the analysis of samples from a fourteenth-century Italian manuscript, published a natural ultramarine spectrum that contained the small absorption band near 2340 cm- t ( Orna et al. 1 9 8 9 ) . Subsequent analyses at the Getty Conservation Institute ( GCI) have identified this absorption Blue particle from Pres ntaioni theTemple by Mantegna Natural ultramarine 201 0 Pruss ian blue Figure 6.2 Comparison of IR transmittance spectrum obtained from a blue particle on a 2090 fifteenth-century Italian painting (Presentation in the Temple by Mantegna) 4000 3000 2000 with reference spectra for natural ultrama­ rine, ivory black, and Prussian blue. Wavenumber (cm- 1 ) 1 500 1 000 Case Studies 1 37 band in samples from four other Italian paintings from the fifteenth and sixteenth centuries. Examination of over thirty samples of ultramarine showed an intriguing trend. The absorption band at 2340 cm-1 occurred only in lapis lazuli and natural ultramarine obtained from the Badakhshan mines in Afghanistan. The band did not occur in any synthetic ultramarine samples or in any samples of lapis lazuli and lazurite obtained from known sources in Siberia (former USSR) or Chile ( Fig. 6.3 ) . Thus, it appears that the presence of this particular absorption band in an ultra­ marine sample shows that it is a natural product whose source may be the lapis lazuli mines in Afghanistan. The Badakhshan mines, the most famous source for lapis lazuli, have been worked for over six thousand years (Webster 1 9 8 3 ) . The blue color i n the lapis i s caused b y two minerals, lazurite and hauyne. Geologically, the lapis from the Afghanistan mines contains pre­ dominantly hauyne ( Banerjee and Hager 1 992 ) . Hauyne contains a Lapis lazuli (Badakhshan, Afghanistan) Lapis lazuli (Siberia) Lazurite (Chile) Synthetic ultramarine (Kremer-Pigmente) Figure 6.3 Comparison of IR transm ittance spectra for lapis lazuli samples obtained from Badakhshan, Afghanistan; Siberia; and Chile, with a spectrum for synthetic ultra­ marine blue. Only samples from the m i nes of Badakhshan exhi bit the absorption band at 2340 cm- 1 , 4000 3000 2000 Wavenumber (cm - ' ) 1 500 1 000 1 38 Chapter 6 higher concentration of calcium and sulfur than other types of sodalite minerals, such as lazurite. It is most likely the sulfur, S+ 6 , that produces the unique IR absorption band at 2340 cm- I . While the literature states that the largest European source of lapis was Afghanistan, there are a few small mines of hauynite found in Italy (Taylor 1 96 7 ) . Samples from the Italian mines have not yet been analyzed. Resolution Based on the extensive number of IR spectra collected of natural ultra­ marine samples, it was concluded that the blue particles in the fifteenth­ century paint samples were natural ultramarine. Furthermore, it is possible that the natural ultramarine in these samples came from the Badakhshan mines. This finding is consistent with known supplies and trade routes for that time period. Case Study 2: Creosote lac resin Prior to the analysis of an unknown material, a logical sequence is to obtain information both on the history of the obj ect and on the sus­ pected composition of the sample( s ) . The second step is to locate refer­ ence samples or spectra that correspond as closely as possible to that projected set of materials. The following example shows a sample that would have been difficult to identify without the contextual information about the obj ect and without the correct reference materials ( all provided at the time of the analysis request by Holcomb and Dean 1 9 9 3 ) . Background Native Americans in the southwestern United States used a variety of natural materials as adhesives and coatings on their pots, baskets, and other vessels . These include pitch or sap from several pines, j unipers, and brittlebush; animal fats and glues made from horns, skin, or bone from deer or mountain sheep; and resin from creosote bush lac scale insect (Sutton 1 99 0 ) . Another source also states that "holes or cracks in pottery were repaired with creosote bush lac or pitch" ( Felger and Moser 1 9 8 5 ) . The creosote bush grows i n the deserts o f California, Arizona, New Mexico, Baja California, and northern Mexico. The resin is found on the outside of branches on infected plants and can be easily removed by twisting it off the branch. The resin is hard and brittle, but it is thermoplastic and becomes workable when heated; thus it must have been applied hot. It hardens on cooling to form a strong bond. Records show that its was used to adhere stone arrowheads in their shafts and to mend broken bowls ( Coville 1 8 92 ) . Found on the branches o f the creosote bush, this insect resin is sometimes incorrectly labeled as creosote gum, when in actuality, it is a secretion produced from the female creosote lac scale insect. Lac scale insects compose a small family of species that exude a resinous substance known as lac. Shellac is the most common commercial product, but exu­ dations from these insects are also used to produce medicines and dyes. In the eastern Mojave Desert, several previously undiscovered Native American artifacts were recovered by cultural resource specialists 1 39 Case Studies of the U.S. Bureau of Land Management. A reddish-brown material was found on the exterior surface of one ceramic pot, near a small crack. The repair, on an otherwise intact pot, must have been done when the pot was in use. Thus, it was important to identify the adhesive in order to increase understanding of the culture, technology, materials usage, and perhaps even trade patterns of the native inhabitants in the area. Analysis question What is this adhesive material, and does it correspond to any materials indigenous to the region ? Method IR microanalysis was used for this study because of convenience and availability. Sufficient sample sizes-almost a milligram of sample and a gram of reference material-were provided for analysis, so other IR analysis methods, such as potassium bromide (KBr) pellets or DRIFTS could have been used if needed. The preparation of small fragments of the samples on BaF2 windows for microanalysis can be readily followed with selective solvent extraction on the same substrate, since BaF2 is inert to most solvents. Analysis The instrument parameters and analysis conditions were the same as those specified in Case Study 1 . Results IR spectra were collected on a small sample of the adhesive from the object. Figure 6.4 shows the spectrum obtained from the sample, as well as reference spectra for creosote lac, j uniper pine resin, and pinon pine resin. After the bulk sample was analyzed, solvent extraction tests were done to check the solubility of the sample and to separate any impurities. A small drop of ethyl acetate was placed on the sample and an additional spectrum obtained from the soluble portion of the resin that collected in a ring around the sample ( Fig. 6 . 5 ) . A parallel reference spectrum col­ lected for the ethyl acetate-soluble portion of creosote lac is also shown. The solubility test and IR spectra show that the extracted residue of the sample corresponds well to the extracted residue of creosote lac. The extraction step is often necessary for the identification of aged, natural products. These materials may contain extraneous materi­ als, such as dirt and insect and animal residues, as well as some insoluble fractions of the material that have chemically altered over time (i.e., oxi­ dized) . Separation of the soluble fractions aids in the interpretation of a mixture of materials, as well as provides solubility information. Resolution The IR spectra indicated that the adhesive used on the Native American ceramic pot did indeed correspond well to creosote lac. The subsequent analysis of the solvent-soluble portions of both samples confirmed the identification. Without the submission of the reference creosote resin for 1 40 Chapter 6 Pinon pine resin Figure 6.4 IR transm ittance spectra for bulk adhesive samples obtained from a Native American ceramic pot, along with reference spectra 4000 3000 2000 1 500 1 000 for creosote lac, j u niper pine resi n , and Wavenumber (cm- 1 ) pinon pine resin . Ethyl acetate extraction of pot repair material (,) OJ c co .� Ethyl acetate extraction of creosote lac rn c co � � Figure 6.5 I R transm ittance spectra of the ethyl acetate-soluble portions of the adhesive 4000 3000 2000 from the ceramic pot and the creosote lac res i n . The two spectra correspond well. Wavenumber (cm- 1 ) 1 500 1 000 141 Case Studies direct comparison, this analysis would only have been able to classify the sample as a natural resin. IR reference spectra for natural products, such as creosote resin, are rarely contained in commercial IR libraries. Case Study 3: Chumash Indian paints IR spectroscopy functions well as a screening tool to characterize and compare many types of materials. This screening can be applied to divide large sample sets into similar compositional groups, as well as to supply a basis for the selection of secondary analysis methods. As shown in this example, IR is used to determine a sample's component classes ( oil, pro­ tein, carbohydrate, etc . ) prior to further specific identification. Background The south-central region of the California coast was inhabited by the Chumash Indians for over a thousand years. The Chumash were skillful artisans, and their rock art is well known. Most often found in the Santa Barbara and Ventura County mountains, some of these paintings reach sizes as large as 40 feet in length and have polychrome designs of six col­ ors ( Grant 1 99 3 ) . Some of the motifs are detailed, showing lizardlike creatures and other animals. Ethnographic information suggests that the Chumash and other Indian groups of central and southern California may have used the paintings as part of a ritualistic procedure and that the paintings may have been related to astronomical observations. Early investigators were struck by the durability of the paintings and were curious as to the tech­ niques used to make them. In 1 8 8 3 , Garrick Mallery was the first person to record and examine Chumash rock art sites; he looked at two sites near Santa Barbara. The first set of samples analyzed was from a group of seven black pigment cakes collected from excavations of Chumash Indian sites in the nineteenth century. The pigment cakes submitted for analysis were obtained from the American Museum of Natural History, New York ( Scott 1 9 94). The pigments had been prepared by mixing them with a binder; the mixture was then formed into small cakes for convenience. Harrington describes the black paints as being prepared from soot mixed with deer marrow and made into a dough (Harrington 1 942 ) . A n additional sample came from the Painted Rock site near Santa Barbara, which is often described as one of the most important Chumash pictograph sites. The site is in the Carrizo Plain area near Soda Lake, a stopping point for migratory birds, and is adj acent to large forests of Digger pines, both sources of food for the Chumash. Historically, it was also home to considerable populations of deer and antelope. By comparing the images currently at the site to historic pho­ tographs, Grant showed that the site has suffered from extensive exfolia­ tion and vandalism-including graffiti, gunshot damage, and modern paint ( Grant 1 99 3 ; Scott and Hyder 1 99 3 ) . The sample, possibly paint, was obtained from a black deposit in a painted region along a vertical crevice in the rock; the black material has previously been described as a tarry organic deposit, as bird droppings, or as a natural vein in the rock. 142 Chapter 6 Analysis questions Sample set 1 . What are the binders in the seven samples cakes? Are they the same ? Sample 2. Does this sample contain any organic materials that may correspond to a paint binder ? Method IR microanalysis was used for the first set of samples because of conve­ nience, availability, and potential for use of selective solvent-extraction techniques. Additionally, while sufficient sample was available, it was important to retain as much sample as possible for future analytical stud­ ies. IR microanalysis was required for the second sample because of the minimal sample size-it contained only a few, barely visible black particles. Analysis The instrument parameters and analysis conditions were the same as those specified in Case Study 1 . Results-sample set 1 Of the seven paint cakes, the IR spectra showed that two clearly con­ tained proteinaceous binders, while the other five appeared to contain oil-and-resin binders. As an example, the IR spectrum for paint cake sample T 1 74 8 2 is shown in Figure 6 . 6 , along with a reference spectrum for dried blood of unspecified origin. Proteins are readily recognizable by a distinct pair of absorption bands for secondary ami des that occur near 1 650 and 1 5 50 cm- t • The presence of protein is confirmed by the sharp, triangular N-H stretching band near 3 3 5 0 cm- t . While the sample spec­ trum corresponds well to the reference spectrum of blood, IR analysis cannot differentiate between various proteinaceous media, such as blood, gelatin, or albumin. The similarity in the two spectra, with the exception of the hydrocarbon stretches at 2 8 00-3 000 cm- I , indicates that the pro­ tein is the primary IR absorbing compound present in the sample. The hydrocarbon stretches imply that there may be a small amount of fat or oil present in the sample. However, within the detection limit of the method, no indications were found that the sample contains resinous or bituminous compounds. This finding was further confirmed by a negative result for the extraction of chloroform and ethyl acetate-soluble compo­ nents. Additionally, no water-soluble components were found in the sample, indicating that the protein is probably not a gelatin (glue ) . Resolution-sample set 1 Based on the IR analysis that classified sample T 1 7482 as a protein, GC was used to identify the specific concentrations of amino acids. The GC results showed that the ratio of amino acids present was in close agree­ ment with a reference standard for blood of unspecified origin ( Scott et al. 1 99 6 ) . Now that the binder in the sample was identified as blood, there was great interest in the source animal species. Thus, Scott submitted the sample for immunological analysis. Using crossover electrophoresis, Newman found positive reactions for both pronghorn antelope antiserum 143 Case Studies Pigment cake sample Q)()c:UJro �if!c: ro t:: E Blood (dried) Figu re 6.6 I R transmittance spectra for a C h u mash I n dian pigment cake sample (T17482) along with a reference spectrum of dried blood of un known origi n . 4000 3500 3000 2500 2000 1 750 1 500 1 250 1000 750 Wavenumber (cm- 1 ) and for human antiserum (Newman 1 994). Thus, this example shows the analysis sequence from a general determination to a very specific one. Results-sample 2 In the second case, the bulk sample of the black deposit material from the Painted Rock site was analyzed first, followed by an ethyl acetate extraction of the sample. The IR spectra for the bulk sample and the extraction of the sample are shown in Figure 6.7. Solvent extraction was used selectively to remove components present in this mixture of materi­ als. The spectrum for the bulk sample indicates that it contains some sili­ cates and possibly carbohydrates. The ethyl acetate extraction of the sample revealed that one component of the paint sample is an esterified hydrocarbon (i.e., oils and fats ). Thus, historical references were checked for the use of oil as a binder in rock art paintings. The oil and pulp of the seed of the wild cucumber (Marah macro carpus) has been cited as one type of binder in California rock art (Bishop 1 994; Watchman 1 99 3 ) . This plant, commonly found in southern California, was also used ritualistically as a body paint in a Chumash curing procedure (Walker and Hudson 1 99 3 ) . The pulp of the cucumber seed contains a mixture of components, primarily oils, proteins, and car­ bohydrates. The oil pressed from the seeds produced a spectrum that cor­ responds well with other plant oils and is primarily composed of long-chain hydrocarbon fatty acid esters. Other natural sources of oils or fats, such as deer fat, black walnut oil, or pinon oil, were also native to the region. Thus, for com­ parison, a sample of mule deer fat was obtained. Mule deer fat is often 1 44 Chapter 6 Black paint bulk sample Q).�oc'"Ec'"(J) Black paint ethyl acetate extract � � Figure 6.7 IR transmittance spectrum for a sample of black paint from Painted Rock along with 4000 3000 2000 1 500 1000 the spectrum for the ethyl acetate-soluble Wavenumber (cm- ' ) portion of the sample. cited as another paint binder, although it was probably used for body painting. Figure 6 . 8 shows the full IR spectra for the ethyl acetate extract of the rock art sample, along with un aged reference samples of cucumber oil and mule deer fat. In general, the spectra are very similar, as would be expected for samples from the same chemical family (i.e., long-chain hydrocarbon fatty acid esters ) . Resolution-sample 2 IR spectra provided characterization of the major components in the sample described as a black deposit or paint found in a crevice. Based on its chemical functional groups, the sample was determined to contain some silicates, possibly some carbohydrates, and a long-chain hydrocar­ bon fatty acid ester. Ester compounds in this category are typically fats and oils that may potentially have been used as paint binders. However, before specific identification can be made of the oil in the paint sample, further analytical studies by GC must be done. Case Study 4: Varnish on a desk As in archaeology, the stratigraphy of paint and varnish layers can be a key to the interpretation of an obj ect's treatment history. Thus, it is often important to examine the composition of individual layers. This case study illustrates how IR spectroscopy can be used to reveal additional information by cross section analysis. Background Identification of resins used for furniture finishes is important for art­ historical analysis of an artifact, as well as for an initial material survey in restoration or conservation treatments. The materials and techniques 145 Case Studies Painted Rock black paint sample ethyl acetate extract Cucumber oil Mule deer fat Figure 6.8 I R transm ittance spectra for the ethyl acetate extraction of the black paint sample from Painted Rock, along with reference spectra for cucumber oil and m u le deer fat. 4000 3000 2000 1 500 1 000 Wavenumber (cm- ' ) for furniture surface treatment have, for the most part, been developed empirically throughout the ages. Collections of old recipes provide some insight into the chemistry of varnishes used for furniture surface treat­ ment (Brachert 1 9 78-79 ). Even though the natural resins used for surface finishes (shellac, copal, pine resins, etc . ) may be difficult to analyze because of their complex composition, natural variability, and suscepti­ bility to oxidation, IR micro spectroscopy has proved to be a good method for the characterization of many pure natural resins used in furniture finish recipes (Derrick 1 9 8 9 ) . A n unusual mahogany rolltop desk with hidden drawers and elaborate mechanical devices is in the Decorative Arts collection of the J . Paul Getty Museum ( 72 .DA.47). The desk, although not stamped with a maker's name, is attributed to David Roentgen and is thought to date from around 1 78 5 . It has a highly polished finish and beautiful filigree gilt-bronze mounts. While the finish on the desk is in good condition, conservators questioned whether the desk had been refinished, and if so, whether any of the former finish remained below the new layers. 146 Chapter 6 Previous IR analysis of a sample from the top surface of the German desk had shown that it contained shellac, cellulose nitrate, and wax. However, since this sample had been removed by scraping a small amount of finish from the surface of the piece, in was unclear as to whether these components had been applied as layers or as a single mixture. Analysis questions Are there multiple layers in the finish? If so, what is the composition of each layer? Method A new sample was collected as a cross section from the top of the shelf near a small crack. The cross section was mounted in polyester embed­ ding media, then microtomed with a glass knife to produce a thin section. The thin section was placed directly on a BaF2 window for photo documentation followed by IR analysis. IR microanalysis was selected in order to obtain a clear characterization of each layer in an intact thin section. Analysis The layers of the thin section were characterized by FT-IR microanalysis; the analysis conditions were the same as those specified in Case Study 1 . Each layer was isolated for analysis by a rectangular aperture approxi­ mately 20 x 1 0 0 }lm in size. Results A photomicrograph of this cross section after microtoming is shown in Figure 6 . 9 . Visually the thin section contains a bottom clear yellow area beneath a darkened opaque layer, which then was covered with a clear layer. The top clear layer is very brittle, and small portions from this layer were lost during the microtoming step. IR analysis showed that the bottom yellow layer ( Fig. 6. 1 0, spectrum C) was shellac. Further examination of the spectrum obtained from the middle, opaque layer ( Fig. 6 . 1 0 , spectrum B) indicated that it contained a few additional bands not present in the spectrum from the bottom, clearer region. Subtraction of the spectrum of the bottom, clear region from the spectrum of the middle, opaque layer resulted in a spec­ trum that corresponds to calcium carbonate ( Fig. 6 . 1 0, spectrum D ) . It is possible that the chalk was used in the final polishing stages of the shel­ lac finish and that it became embedded in the shellac. Analysis of the top clear layer ( Fig. 6 . 1 0, spectrum A) showed that it consisted of a mixture of shellac and cellulose nitrate. This was a common commercial water­ proof varnish sold in the 1 930s and 1 940s. Resolution For this sample, IR microanalysis of the thin cross section showed that the desk has been revarnished at least once with a cellulose nitrate and 1 47 Case Studies Figure 6.9 A photomicrograph of a thin -section sample from the Roentgen desk, embed­ ded i n polyester resin and microtomed to �'" 30)Ul1",t}'., a thickness of 10 jJ m . B Fif.Cf)ccu c ()) () c fl E Figure 6 . 1 0 I R transm ittance spectra (2000-700 c m - ' ) for t h e sample shown in Figure 6.9: top layer (cellulose nitrate/shellac), m iddle layer (shel lac/calcium carbonate), bottom layer (shellac). The su btraction (spectrum B - spectrum C) produces a spectrum (D) with absorption bands that correspond to calcium carbonate. - C) D20 0 150 (180 70 Subtraction Wavenumber (cm- ' ) 148 Chapter 6 shellac varnish that was added on top of a thick shellac layer, and that the two layers were separated by a layer containing calcium carbonate. Case Study 5: Reflection versus transmission Cross sections are typically embedded for stratigraphic examinations. However, it is not always possible or easy to microtome thin sections from the embedded sample for IR transmission analysis. Instead, it would be beneficial to perform IR reflection analysis directly on the embedded sample. This case study compares the results obtained from both reflection and transmission IR analysis for an embedded cross section sample. Background Analysis was requested on a paint cross section sample from an eighteenth­ century armchair in the Bayou Bend Collection of the Museum of Fine Arts, Houston ( Shelton 1 994 ) . This highly ornate Neoclassical armchair, or " drawing room chair," is one of a set of eight extant armchairs attrib­ uted to an unknown maker working in Philadelphia in the late 1 790s ( Sands 1 993; Brown and Shelton 1 994). The distinctive decoration of the chair includes extensive use of applied composition ornaments and a high-contrast, water-gilded, and white painted surface. O bservations revealed that the water gilding on the composi­ tion ornaments and frame was broadly executed with a red clay bole bound in glue, and that a lead white pigmented paint was neatly cut in around the gilding ( Shelton 1 99 4 ) . Previous microscopic characterization of the binders with reactive fluorescent dyes and elemental analysis of the pigments supported the possibility of a proteinaceous binder in the white paint layer. Visually, the cross section sample contained a thick gesso layer, a thin red-brown bole layer, and a layer of white cut-in paint directly over the bole layer. Above the white layer were remnants of a clear sealer or coating on the surface, covered with a thin layer of grime and two layers of restoration. Analysis questions What is the composition of each paint layer? Can comparable results be obtained by IR micro reflection spectroscopy of the polished cross section and by IR transmission analysis of a microtomed thin section ? Method The sample, as received, was embedded in a polyester medium. It was microtomed into a thin section for IR analysis in transmission mode. Additionally, IR reflection analysis was done on the portion of the sample that remained in the embedded block. Analysis The layers of the thin section were characterized by FT-IR transmission microanalysis by use of the conditions specified in Case Study 1 . The microtomed surface of the remaining embedded cross section was smooth 1 49 Case Studies and flat. It was lightly polished, then analyzed by IR spectroscopy in reflection mode in a stepwise linear fashion, or line scan. The sample was placed on the motorized stage of the spectrophotometer, and an analysis window of 40 x 80 Jlm was selected. The stage was moved 1 0 0 times in approximately 5 Jlm increments in the x direction, in order to step the analysis window over the sample. One spectrum was collected at each step, such that 1 00 spectra were produced for the line scan ( Fig. 6 . 1 2 ) Results-transmission analysis From the thin section, spectra were collected for the gesso, the bole, the layer above the bole, and the overpaint. These are shown in Figure 6 . 1 l . The IR analysis shows that the primary binder in the gesso and the bole layers is a protein ( see amide I and amide II bands at 1 65 0 and 1 5 50 em-i ) . Carbonate shows up strongly in the gesso layer (to the point of saturation, 2550, 1 8 00, 1 450 and 8 70 em- i ) and can also be seen to a lesser extent as a component in the bole. Since the analysis aperture was wider than the bole layer, spectra may show an overlap of components. Thus, the carbonate seen in the bole layer could be due to the gesso layer. The primary inorganic material in the bole layer is a clay ( silicate: sharp bands near 3 600 cm-i and a broad, strong band at 1 05 0 em- i ) . Oil appears to b e a component i n the layer above the bole ( the white, cut-in paint) and in the overpaint, or restoration layers ( see the carbonyl Layer 2-above bole Q) '".to:if.�'"()E c (f) c Figure 6 . 1 1 I R transmittance spectra collected for four visually distinct layers with I R transmission microspectroscopy on a m icrotomed thin section of paint from an eighteenth­ century chair. 4000 3000 2000 Wavenumber (cm-1) 1 500 1 000 1 50 Chapter 6 Figure 6 . 1 2 I R absorbance spectra collected from a linear step scan using IR reflection microspectroscopy on an embedded paint 5.000 cross section from an eighteenth-century chair. The analysis window was 40 x «0 80 IJ m , and the step size was approxi­ mately 5 IJm. As the composition of the Q) u c (1j .0 4.000 3.000 rn .0 sample changes, so do the corresponding I R spectra. These relative changes for selected bands can be plotted as a line scan, as shown in Figure 6 . 1 3 . I 2400 I 2200 I 2000 I I I 1400 1 600 1 800 Wavenumber (cm- ' ) 1 200 1 000 band at 1 740 cm- I , along with strong hydrocarbon stretches at 2930 and 2 8 6 0 cm- I ) . However, caution must again be used, since the appearance of the oil bands in the layer above the bole may be due to an overlapping aperture with the coating or overpaint layers. The spectrum for the layer above the bole also appears to have absorption bands that correspond to protein and to basic lead carbonate (a broad band at 1 400 cm-I, with a band at 3 600 cm- I ) . Previous elemental analysis had indicated that lead­ based pigments were found in this region. The overpaint layer contains primarily barium sulfate (a band near 1 1 40 cm- I with three tips and a sharp band at 3550 cm- I ) . Results-reflection analysis From the spectra collected in reflection mode ( Fig. 6 . 1 2 ) , line plots were drawn that show the absorbance intensity of a particular absorption band versus its position in the sample ( Fig. 6 . 1 3 ) . The absorbance inten­ sity of a band corresponds to its relative concentration. All spectra were collected on the same sample, so the relative height of a band from one position can be compared to its height at another position. Since the analysis aperture was fairly large, there are no well-defined edges for the beginning and end of each layer. However, the peak maxima for a mate­ rial should correspond well to the center of the layer in which the mate­ rial is found. Also, some voids in the surface of the sample may cause apparent decreases in the concentration that are not, in fact, real. Examination of Figure 6. 1 3 indicates that the band assigned to silicate ( 1 040 cm- I , line profile 1 ) exhibits the highest concentration in the region of the red bole. This finding corresponds to an identification of clay in this layer. The sulfate-assigned band ( 1 143 cm-I, line profile 2 ) also absorbs strongly i n one portion of the overpaint region; this finding corresponds to the transmission results. Since the band selected for sul­ fate overlaps with the silicate absorption bands, the apparent sulfate in the bole region is likely due to the silicate band. The line profile assigned 1 51 Case Studies Figure 6.1 3 Line scans overlaid on a photom icrograph of the embedded paint cross section from an eighteenth-century chai r. The line scans show the intensity of a selected absorption band versus its collection position on the sample. to carbonate ( line profile 3 , 1 45 0 cm- 1 ) is high in the layer directly above the bole. Also, the carbonate band intensity is variable from high to moderate in the gesso. It is possible that the gesso contains a fairly even distribution of carbonate ( calcite) but that the intensity of the absorption varies due to the particles and voids encountered by the beam ( i .e., that the variation is an artifact of the reflection analysis method ) . Line profile 4 ( 1 65 0 cm-1 ) is assigned t o the amide I band, which is likely due to proteins. The profile lines are Autoscaled to the maximum intensity; thus, the strong absorption for the protein at the bottom (right edge) of the gesso layer makes the rest of the sample appear as if it has little protein. Gesso typically has about 1 0-20 % glue; this proportion should correspond to a small but recognizable absorption band, such as is seen in the transmission spectra. However, the line scans do not clearly indicate its presence. The carbonyl band ( line profile 5, 1 73 0 cm- 1-indicative of oil and resin) is consistently low in the gesso and in the layer above the bole. The carbonyl band absorption increases in the region described as a coating on the layer above the bole. This increase could be due to a layer containing oil or a natural resin. A slight increase in the carbonyl intensity in the overpaint area, as opposed to the gesso region, may indicate the presence of oil in the overpaint. This finding would corre­ spond with the transmission results. The increase in the carbonyl band intensity at both edges of the sample is probably due to the polyester embedding media. Resolution Obtained through direct reflection analysis performed on the mounted cross section, the line scans of the sample provide an effective means for examining and reporting the results. This method also provides some hints as to thin layers that may be present in the sample. 1 52 Chapter 6 However, without the information obtained from the initial transmis­ sion spectra collected from the thin section, it would have been difficult to interpret the information in the line scan. Thus, both are important. Comparison of reflection versus transmission methods suggests that the organic components of the sample-such as the proteins and oils-do not reflect the IR beam as well as do the inorganic components. Therefore, the transmission spectral data are a better indicator for the binders in each of the layers. Case Study 6: Painting cross sections Reflection analysis showed some potential for the examination of embed­ ded cross sections in Case Study 5. However, an area scan should provide a better visual image of the components than a linear scan. An area scan would give a total sample depiction identifying each component versus its location, such as is obtained with elemental mapping and, to some extent, with fluorescent staining. An IR reflection map of the entire sample area is illustrated in this case study. Background Andrea Mantegna was an Italian artist of the late fifteenth and early six­ teenth centuries. Many of his paintings have the very characteristic matte appearance of glue ( distemper) paint on a fine-quality linen support, and they were never meant to be varnished ( Rothe 1 992 ) . The distemper technique, called Tiichlein, was popular in the Netherlands and Germany but had not been associated with any other Italian artist. As part of a detailed investigation of Mantegna's techniques by Rothe, over thirty samples from ten paintings in museums in Europe and the United States were submitted for binding media analysis ( Rothe 1 99 1 ) . Multiple methods-FT-IR microscopy, SEM-EDS, GC/mass spectroscopy ( GCIMS), and high performance liquid chromatography (HPLC)-were used to characterize the components in these samples. The primary reason for analysis was to determine the presence of glue-as opposed to egg-in the binder; egg medium was typical for wood-panel paintings in that time period. One sample, from Mantegna's Adoration of the Magi (J. Paul Getty Museum, Los Angeles ) , was selected for in-depth study by several analysis techniques. Initial IR transmission analysis on particles removed from each visually distinct layer indicated that protein was the primary binder. HPLC analysis of the amino acids in the protein showed that it contained significant amounts of hydroxyproline, thus indicating that animal glue is present in the sample. GCIMS analysis confirmed this finding and also noted the presence of a wax and the absence of choles­ terol in the sample. Analysis question Can IR mapping microspectroscopy be used to identify and locate sample components? Of particular interest is the distribution of the wax that was identified by GCIMS. 1 53 Case Studies Method Initial IR transmission microanalysis was done on particles removed from each visually discrete layer as a control. Then, computer-controlled x-y mapping of a sample in the reflection mode was selected to characterize the components in a sample and to detect components or layers that may not be visually apparent in an optical microscope. Analysis Instrument parameters for both transmission and reflection methods were the same as conditions specified in Case Study 1 . For the area map, a portion of the sample, a four-layer cross x section, was embedded and polished, then placed in the IR spectropho­ tometer, and an analysis grid of 1 0 1 5 points was selected. An array of spectra were collected by reflection of the IR radiation off the surface of the sample at each grid point. The effective resolution of the components x in the sample was determined by the size of the analysis aperture and by the density of the grid. The size of the aperture for this analysis was 20 40 fLm. The selection of size involved a trade-off between resolution and energy throughput. The step size was approximately 20 fLm. The overlap of the windows in the x direction provided an effective increase in the res­ olution of the components in that direction. Each spectrum was the sum of 50 scans and took approximately 1 minute for collection and processing. Results An array of IR spectra were collected and contour maps produced that provide information on the concentration and location of compounds in the sample. This procedure was done by the selection of a wavelength of interest, such as a hydrocarbon band; then its intensity versus its position in the grid where it was collected was plotted. A total sample contour map was prepared by connecting lines for the band intensities of similar value. In these plots, variations in line thickness are used to represent changes in band intensity. The thickest lines correspond to the areas of strongest band intensity-that is, to the highest concentration of the material. The intensities are relative to one another, and the background intensity may not be zero, because of other absorptions in the region. In this particular sample, because previous extensive analyses had been done to determine its components, the selected IR absorption band and corresponding functional group could be related specifically to compo­ nents in the sample. On other samples, it would be precarious to identify a material based on only one IR absorption band. Figure 6 . 1 4 shows a photomicrograph of the Mantegna sample, and Figure 6 . 1 5 shows four IR reflectance maps. Map A is a plot for the carbonyl band at 1 730 cm- i . The highest intensities of the carbonyl band are due to the polyester embedding media surrounding the sample; they provide a general indication of the area analyzed. The absence of a carbonyl band in the region of the sample corresponds to previous analyses, which determined that the binder did not contain egg or oil. Map B is a plot of the intensities of the carbonate band at 1 54 Chapter 6 Figure 6.14 A photomicrograph of a painting cross section sample from the Adoration of the Magi by Mantegna. 1 4 1 6 cm- 1 . This map shows that the entire sample contains carbonate, with the exception of the surrounding embedding media and a central point in the second layer where the sample contains a large particle. Map C plots the intensity of the band at 1 092 em-I, which may correspond to sulfates or silicates, or to both. The highest concentration of this mate­ rial ( s ) is in the third layer of the sample. Map D is a plot of the intensity of the hydrocarbon band at 2 9 1 9 cm- 1 . The highest concentrations occur in the ground ( bottom) layer and correspond to wax. Resolution With the aid of the results from IR transmission studies, many of the Figure 6.1 5 (opposite page) components in each layer could be identified by the IR maps. Of most IR reflectance contour maps for painting significance was that the wax, which was previously found in the sample cross section sample shown i n Figure 6 . 1 4 . by GCIMS bulk analysis, can now be designated according to its location T h e thickest lines correspond t o the in the sample. Two potential sources for the ground-layer wax are, first, highest-intensity absorptions. Absorption that it could have been included in the original mixture of components in bands mapped are (A) a carbonyl band at the ground layer or, second, it could have come from the wax lining. 1 73 0 cm - 1 ; the high intensities represent However, since the IR map shows a fairly even distribution of wax the embedding media; (8) a band assigned throughout the lower layer, it is more likely that wax was an original to carbonate at 1 4 1 6 cm - 1 ; this map component in the ground layer. Additionally, there is no treatment his­ shows a u n iform distribution with the tory indicating that this painting has been relined. exception of lower levels in one region of the m iddle layer and the surrounding Limitations to mapping embedding media; (C) a band assigned to The method of IR reflection mapping shows potential for the determina­ su lfate/silicate absorptions at 1 092 cm- 1 ; tion of materials and their locations within a cross section sample. The this map shows a higher intensity in the technique is complementary to elemental mapping with an electron middle layer; and (D) a hydrocarbon band microscope and may be done on the same sample. At this point, the IR at 2 9 1 9 cm- 1 ; this band has the strongest mapping method has two major limitations. The first limitation is the use intensities in the bottom layer. of specular reflection as an analysis method; this method requires an 1 55 Case Studies Carbonyl band ( 1 730 cm-1 ) Carbonate band ( 1 4 1 6 cm-1 ) 8709 73 0.1 ", B 870.9 37 77992562 ��3" 77995226 � 7 9 0. 1 >>-�77789850.0.51 O� 778850.5 0. 7 778924 0:,] �" J 778924 7 3 9543973 9 1 40.1 40.29 40. 7406 40.85410.3 412 41 0.4159 417841964215 7 39e;;;� �§40.1 40.2940. 7 406 40.85410.3412 41 0.4159 417841964215 5 4 3 9 7 3 9 1 o 7952 c 8770995273 ��/.:§�� 7E:E>- 7992061 7�>- 79920.61 778850.5 77885D5 � 1I 778924 7 3 9543973 9 1 40.1 40.2940. 740.6 40.85410.3 412 41 0.4159 417841964215 7 3 9�543973 9 1 40.1 40.2940. 740.6 40.85410.3 412 41 0.4159 417841964215 x 0.9 A � X (�m) X (�m) Sulfate/sil icate band ( 1 092 cm-1 ) Hydrocarbon band (29 1 9 r � :::: �1Ii X (�m ) cm-1) �.�I X (�m) analysis window with a minimum size of 20 20 pm, because of energy restrictions. Specular reflection can also result in band distortions and shifts for which it is difficult to compensate. The second limitation is that a component cannot be reliably identified based on one IR absorption band. Thus, additional analyses are required to supplement the map and provide interpretation. Future computer programs should allow a map to be created based on the selection of multiple absorption bands that can help identify specific compounds. Case Study 7: Vikane Vapor-phase depletion measurements have been commonly used to study catalyst and pollutant reactions ( Grosjean 1 9 8 5 ) . Normally these mea- 1 56 Chapter 6 surements are made by periodic sampling of the gas in a chamber and analysis of it by a thermal or ionic detector. In this study, IR spec­ troscopy was used as an in situ detector to determine the decrease in concentration of a gas-phase fumigant, Vikane ( sulfuryl fluoride), in the presence of various materials. Background Vikane was developed by Dow Chemical Company in the 1 950s, specifically for the control of drywood termites typically found in warm climates, such as the southern United States (Dow Chemical Co. 1 9 8 2 ) . It has since been widely used as a structural fumigant against a variety of destructive pests in homes, buildings, construction materials, furnishings, and vehicles. Studies conducted on Vikane show that it has several advantages; they include easy dispersal into a structure, rapid penetration into materials, formation of almost no residues, and ready dissipation after aeration (Meikle and Stewart 1 9 62). This study was a part of a j oint investigation by the GCI, the Canadian Conservation Institute, and the Conservation Analytical Laboratory of the Smithsonian Institution, to examine the extent of interaction of Vikane with a wide variety of materials under controlled conditions. Final studies showed minimal measurable changes in most materials with Vikane ( Baker et al. 1 99 0 ) . Analysis question Can IR analysis be used to determine which materials are susceptible to interaction with Vikane ? Method Vapor-phase depletion measurements can be used as a fundamental method to determine the interaction of a solid material with a gas. The theory of this method is that when a gas is placed in a closed chamber with a test material, the only decrease in the gas concentration will occur by ( 1 ) leakage or penetration through seals or gaps in the chamber, ( 2 ) absorption or reaction with the chamber walls, and/or ( 3 ) absorption or reaction with the test substrate surface. Under con­ trolled experimental conditions, the first two parameters should remain constant from run to run. Thus, the test substrate may be varied, and several materials may be compared for their specific absorption of and reactivity to the gas. Since the absorptions will be proportional to the surface area, deposition or uptake of the gas can be normalized for the surface area of each sample, so that any real differences in sample reac­ tivity may be determined. For these experiments, the concentration of Vikane was mea­ sured in situ with IR spectroscopy. This measurement was performed by placing a substrate in an IR gas cell, out of the path of the beam ( Fig. 6 . 1 6 ) , introducing Vikane, and then monitoring the concentration of the fumigant in the cell for several hours. 1 57 Case Studies Analysis IR spectra were obtained at 4 cm-I resolution on a Digilab 1 5 -E FT-IR spectrophotometer ( see Suppliers ) e quipped with a Motorola 3200 computer and a dry nitrogen purge . A wide-range, cryogenically cooled MeT detector was used to examine the mid-IR region from 4000 to 500 cm- I . Each spectrum represents an accumulation of 500 scans. The computer was programmed to run automatically, collecting a spectrum every 5 minutes for the first 5 spectra, then every 10 minutes for 2 5 spectra, then every 2 0 minutes for the remaining 2 0 spectra. F o r the 0% relative humidity ( RH ) runs, the test material was placed inside the cell, then the cell was flushed with pure, dry nitrogen and placed in the instrument. A spectrum was taken of the purged cell after it was placed in the instrument to ensure that the cell was clean; this spectrum was then Figure 6.1 6 used as a background. Then, 2-3 ml of 1 00 % Vikane was injected into x An IR gas cell for depletion studies. The the gas cell, and the automated IR collection program was initiated. The sample is placed in the bottom of the air­ test materials had an exterior dimension of 2 . 5 tight cel l , and Vikane is injected; the con­ After each run, the cell was rep urged with nitrogen. A t this point and centration of Vikane over time is then 8 hours later, spectra were taken to determine whether the test materials mon itored by the collection of I R spectra were desorbing Vikane. 5 . 0 cm ( 1 x 2 in. ) . of the gas in the cell over a 1 0 hour diameter of 5 cm. The windows in the cell Results The gas-phase spectrum of sulfuryl fluoride produces strong vibrational are zinc sele nide. bands that are well resolved at 4 cm- I . The intensity of IR absorbance period . The cell is 10 cm long and has a 1 58 Chapter 6 bands is proportional to the concentration of that species within the lin­ ear range of the detector. Comparison of several blank runs showed that the precision of the measurements for four runs with an empty cell ( blank) taken over a period of four weeks was ±2 %. Each of the curves is linear and horizontal and represents a relatively constant concentration for the 12 hours . Figure 6 . 1 7 shows depletion curves for several materials tested at 0% RH. For the blank cell, the Vikane concentration decreases slightly in the first hour, then remains essentially constant for the next 12 hours. Similar results were seen for metals; initial slight decreases in concentration may be related to the additional deposition surface area in the cell. Vikane depletion is slightly greater ( 5 % ) for the cotton sample, but it still exhibits the same general pattern of an initial drop, then a leveling. In comparison to the other materials that were tested, the proteins showed drastic changes. Silk-showing a 3 7 % decrease-is an exacerbated version of the pattern noticed with proteins. In these experiments, samples analyzed at 0% RH were placed in a cell that was purged with dry nitrogen. However, since the lack of oxygen and water may inhibit some reactions with Vikane-par­ ticularly the corrosion of metals-additional studies were done with dry air humidified to 6 5 % RH (with oxygen present) . At 6 5 % RH, the curves for each metal sample exhibited a rapid initial drop, followed by a leveling. In each case, the curves were lower than on the comparable graph obtained in a dry nitrogen atmos­ phere ( an example for brass is shown in Fig. 6 . 1 8 ) . The depletion at 6 5 % R H ranged from 1 5 % ( copper) t o 6 % ( aluminum and silver ) , while at 0% RH, the depletions ranged from 1 % to 3 % . The presence of moisture or oxygen seems necessary for Vikane absorption or reaction with met­ g als. Even with the depletion of the Vikane, no corrosion or tarnishin was visible on any of the metals after 24 hours of exposure. Interestingly, the organic materials, such as cotton and silk, showed much less Vikane 1.10 .. ____---1 1 .00 1"':::_ :-- _________________Blank OJ Figure 6.1 7 A plot of the IR absorption band of Vikane at 1 492 cm-1 versus collection time. The .D<{'"ococu Cotton 0.90 0.80 th ree lines show experimental results for a blan k cel l , a piece of cotton , and a piece 0.70 of silk. The cell containing a piece of cot­ ton exh ibited a 5% decrease, and the cell with silk showed a 3 7 % decrease i n V i kane concentration. Silk ______ ______ _______ ___ 3 9 6 0.60 L- o --L --1 .l...- ---1 Time (hours) 1 59 Case Studies r- 1 .02 1 .00 Figure 6.1 8 at 1 492 cm- 1 versus collection time. The first run involved a sample of brass placed in the cell with a dry nitrogen atmosphere; there was a 2 % decrease in Vi kane con ­ centratio n . T h e second sample o f brass was placed in the cell with 65 % RH. That run showed a decrease of 8% in Vikane H ____________ ____�O�%�R� __ .0<t:UJ0'" ---f- ---I I I I 0.98 A plot of the IR absorption band of Vikane f-�---- Q) u c _J 0.96 0.94 65% RH --- - 0.92 0.90 2 0 concentration . 4 Time (hours) -- - -- - - 6 - 8 10 depletion in the presence of the higher humidities and oxygen than had been found in the nitrogen atmosphere studies. Resolution In summary, depletion studies showed that IR spectroscopy is a useful tool for monitoring changes in the gaseous environment in an IR cell. While it is not possible to determine from these experiments whether the Vikane was reacting with the materials, the results did give useful infor­ mation as to the types of conditions for which reactions are most likely. Results also showed that humidity does have an effect on Vikane's inter­ actions with materials. Case Study 8: Parylene Artificial aging is used to hasten the degradation of materials. In the fol­ lowing study, IR spectroscopy is used to evaluate the chemical oxidation changes that occur as samples of Parylene are exposed to filtered UVNis radiation. Background Parylene, a generic name for polymers based on para-xylylene, is a con­ formal, vapor-deposited coating that was considered for use in the con­ servation field in the early 1 9 80s (Humphrey 1 9 84, 1 9 8 6 ) . The polymer has been used for the last-chance consolidation of friable, otherwise irreparable artifacts and other objects, such as ancient pinecones and feathers (Abbey Newsletter 1 9 8 8 ) . The polymer was found to have good thermal stability ( Grattan and Bilz 1 9 9 1 ) . Nowlin and coworkers have shown that an uptake of oxygen by three types of Parylene relates to a decrease in tensile strength during thermal oxidation studies at 120 °C to 200 °C (Nowlin, Smith, and Cieloszyk 1 9 8 0 ) . The oxidation kinetics were obtained by both neutron activation analysis and IR spectroscopy. Comparing these two methods, 1 60 Chapter 6 Nowlin showed that the oxygen concentrations determined by neutron activation are directly proportional to the size of a carbonyl ( C = O ) absorption band a t 1 69 5 cm- 1 i n the I R spectra. Thus, for Parylene oxi­ dation, the formation of the carbonyl band in the IR spectra coincides with a reduction in tensile strength, while also providing specific infor­ mation on chemical alterations. An initial experiment indicated that color changes occurred in free films of Parylene-C following exposure to a xenon light source filtered through nominal cutoff filters of 305, 345, 3 8 5 , and 400 nm ( Hansen and Ginell 1 9 8 9 ) . Yellowing occurred progressively, with both increasing time of exposure and wavelength minima for 500 hours expo­ sure. However, since the color-change kinetics did not provide specific information on the chemical modifications or other physical properties (e.g., tensile strength) , IR spectroscopy was used to provide information on the chemical degradation products in the Parylene. Analysis questions Can the chemical degradation products of Parylene be monitored with IR spectroscopy ? What types of radiation exposure cause measurable degradative changes ? Method Attenuated total reflectance (ATR) was chosen for this study, since it selectively analyzes the surface of the sample that is held in optical con­ tact with the crystal. Since photo oxidative degradation products are more abundant on the surface of a film, where the oxygen supply is plen­ tiful, the sensitivity of the IR measurement to deterioration is increased by use of the surface technique. Analysis Parylene-C ( dichloro-para-xylylene; see Suppliers, Union Carbide Corp . ) free films ( 1 2 p m thick ) were irradiated i n a Hereaus Sun-Test chamber equipped with a xenon arc lamp filtered to yield a simulated solar spec­ trum. A water-cooled support plate in the chamber maintained the exposure temperature at 30 °C ( ± 1 0q, which was determined by a thermocouple placed on a sample surface. Long-band-pass optical filters with nominal cutoffs of 305, 345, 3 8 5, 400, and 420 nm were inserted between the xenon lamp and the Parylene-C films to determine the wave­ length threshold for photooxidation. Films were removed for IR and color measurements at intervals during the initial 500 hour exposure. Because the 420 nm minimum filter was excluded prior to completion of the 500 hour exposure, a second exposure experiment was conducted under similar conditions to 750 hours, for verification of the test results. IR measurements were made on a Digilab 1 5 - 8 0 FT-IR spec­ trophotometer ( see Suppliers) with a Harrick x4 beam condenser in the ATR mode ( see Suppliers ) . The instrument was continually purged with dry, CO 2 -free air from a Balston clean-air unit ( see Suppliers, Whatman, Balston Div. ) , to eliminate any atmospheric-induced interference bands. A cryogenically cooled MCT detector was used for maximum spectral 1 61 Case Studies sensitivity. Each spectrum represents the accumulation of 200 scans at a resolution of 4 cm-1. For the ATR measurements in this study, a KRS-5 (thallium bromoiodide) crystal was used at a 45° angle of reflection. This provides an approximate beam penetration of 5 /-Lm. A sample ( approximately 5 x 50 mm) was cut from the film, placed on one side of the crystal, and reproducibly pressed against the crystal surface with a torque wrench set at 2 . 8 gm-m ( 4 oz.-in . ) . Care was taken to ensure that the surface next to the crystal was the surface of the sample that faced the xenon lamp. Results Figure 6 . 1 9 shows a spectral series of Parylene-C exposed under several cutoff filters (345, 3 8 5 , 400, 420 nm) for 750 hours, along with an unex­ posed control. The main changes in the IR absorption spectra detected during the photolysis of Parylene-C are ( 1 ) an increase in band intensities in the carbonyl region ( 1 750-1 670 cm- 1 ) , due to the uptake of oxygen; ( 2 ) an increase in intensity of the hydroxyl absorptions (a broad band at -r- 1 .2 )\ 1 .0 345 nm filter 0.8 <D15.0«Uc(f) 0.6 (; 0.4 Figure 6 . 1 9 0.2 I R absorbance spectra for Parylene-C films after 750 hours of simulated sunl ight exposure with UV cutoff filters (345, 385, 400, and 420 nm), along with the spec­ trum of an unexposed control. The car­ bonyl band at 1 695 cm-1 is an ind icator of ph otodegradation . 0.0 3500 2500 1 400 Wavenumber (cm- 1 ) 1 000 600 1 62 Chapter 6 3400 cm- I ) , due to an increase in the number of alcohols and acids; and ( 3 ) a decrease in the hydrocarbon stretching and bending frequencies ( sharp bands at 3 1 00-2 8 00 cm- I ) , which indicates a loss of carbon­ hydrogen bonds due to oxidation. Overall, this spectral series shows that with an increasing amount of UV in the light, the quantity and number of oxidation products increases. A closer examination of the carbonyl region shows that the appearance and growth in the band at 1 6 95 cm- I ( shown by the arrow in Fig. 6 . 1 9 ) is the first easily recognizable indicator of the Parylene-C oxidation process. Nowlin and coworkers found that this band corresponded directly to the oxygen uptake by parylenes in their thermal degradation studies (Nowlin, Smith, and Cieloszyk 1 9 8 0 ) . Table 6 . 1 lists the total area under the carbonyl stretching band region from 1 720 to 1 660 cm-I for each sample in the exposure matrix. Since the sample size was not uniform for every spectral mea­ surement, the areas of the carbonyl bands were normalized to an internal reference band. Chosen for this purpose was a small band at 1 8 8 0 cm-I ( C-H wag on the aromatic ring), because it would be a relatively stable indicator of the amount of polymer analyzed. This was also the band that Nowlin and coworkers used for normalization in their study (Nowlin, Smith, and Cieloszyk 1 9 8 0 ) . Table 6 . 1 shows that there is a corresponding increase i n the size of the carbonyl band versus the amount of UV light received by the sample. Additionally, there is an increase in the size of the carbonyl band with increasing time of exposure from 0 to 750 hours. Two exceptions to these trends occur for the 500 hour exposures of the unfiltered sample and the 305 nm filter sample; these have lower measurements than the sample exposed under a 345 nm filter. For the unfiltered sample, the measurement at 500 hours is lower than the measurement at 1 5 5 hours. These lower results are due to further degradation of the oxidation prod­ ucts. The samples for both of these measurements were extremely brittle and difficult to analyze. In fact, after the 750 hour exposure, the corre­ sponding samples ( unfiltered and with a 305 nm filter) were deteriorated to the point that they could not be analyzed. Since the growth of the carbonyl band (presented in Table 6 . 1 ) is an early indication of the photo degradation of the polymer, it is significant to note that the area under the carbonyl band for the sample Table 6.1 The total area u nder the carbonyl band Time (hr) (integrated from 1 720 to 1 660 cm-1) for Parylene-C samples exposed to filtered Cutoff filter (nm) none 305 39.8 1 2 .0 0 xenon light. Each spectrum was normal- 35' ized with the intensity of the absorption 1 55' band at 1 880 cm- 1 at 1 .0. 500' 750 average of 6 controls 1 81 83 . 8 91 .0 1 42 2 " Not measured. ' Exposure study 2Exposure study 345 21 (up to 500 hours). (up to 750 hours). 5 . 42 24.8 - 0 . 78 400 420 2 .43 2 . 68 3 .08 9.17 6.71 5.41 385 == 0.49 / 277 12.1 7.61 442 34.1 8 . 74 5 . 98 1 63 Case Studies filtered with a 420 nm filter increased with exposure time. The cutoff filters theoretically allow zero throughput of light from wavelengths shorter than the number on the filter (i.e., higher energies ) , while allow­ ing 1 0 0 % transmission of the light at wavelengths above the filter num­ ber (i.e., lower energies ) . In reality, the cutoff lines are not sharp but are, instead, approximations. In this study, a radiometer was used to deter­ mine the exact photodistribution characteristics of each filter. The spec­ tral distribution obtained for the xenon lamp through the 420 nm cutoff filter indicates that some radiation from 3 9 5 nm to 420 nm was present. This small portion of higher-energy radiation may be responsible for the photooxidation of the material. Comparison of the physical changes (yellowing) with the chemical changes ( formation of the carbonyl band in the IR spectra) indi­ cated that oxidative changes in the IR spectra were apparent earlier (i.e., at lower radiation levels) than were the color changes. This finding was consistent with the formation of a colorless mono benzoyl prior to the formation of deep yellow dibenzoyl. Resolution This example used ATR IR spectroscopy to monitor the minor changes in the chemical composition of Parylene-C film surfaces exposed to light. Two significant points in this study were ( 1 ) that oxidation of Parylene-C occurred in light filtered to the visible region, and ( 2 ) that this oxidation was measurable prior to visual discoloration, or yellowing, of the films. When a 400 nm cutoff filter (typically found in museum environments) was used, a carbonyl band indicating oxidation was readily apparent after an exposure of 1 5 5 hours. Filtering of the violet portion of the spec­ trum with a wavelength minima of 420 nm still resulted in a measurable amount of chemical change in Parylene-C. Case Study 9: Cellulose nitrate sculptures IR analysis is often used to study degradation products, as well as to examine materials during different phases of degradation. While any analysis technique can only identify the materials currently present in a sample, information about the materials, their history, and their cur­ rent condition can sometimes be used to gain insight into the degra­ dation process. Background Cellulose esters, the modern plastics of the early 1 900s, furnished a light­ weight material that could be transformed into a myriad of shapes and colors. Because of this versatility, the plastic found many uses in every­ day products ( buttons, billiard balls, cosmetic cases) , in new products ( movie film), and in works of art ( sculptures). However, it was eventually discovered that plastic products based on cellulose nitrate were inherently unstable. This polymer initially undergoes a very slow, spontaneous decom­ position, at normal room conditions, that can progress to faster, autocat­ alytic degradation in the presence of high humidity, high temperature, or radiation (for a detailed explanation of this chemistry, see Selwitz 1 9 8 8 ) . UV 1 64 Chapter 6 The Museum of Modern Art (MoMA) in New York has three early polymer sculptures created in the 1 920s by Naum Gabo and Antoine Pevsner; the artworks exemplify the Constructivist style. These sculptures were shown by IR spectroscopy to be composed of cellulose nitrate. Examination showed that they exhibit varying degrees of deterio­ ration and range from very good to poor in overall condition. The types of deterioration include crazing, cracking, and discoloration of the cellu­ lose nitrate, as well as corrosion of some metal components that are in contact with the plastic. When two of the pieces began exhibiting drops of clear-to-light-brown liquid on the surface, MoMA and the GCI began an examination of these cellulose nitrate sculptures, in order to obtain a better understanding of the relation between various deterioration mecha­ nisms and the material composition (Derrick, Stulik and Ordonez 1 99 3 ) . Analysis questions What is the composition of the droplets? Are they due to cellulose nitrate degradation ? Method Samples were obtained from the cellulose nitrate sculptures at MoMA and from other collections. When possible, multiple samples were taken from several areas of each sculpture. The samples were acquired as bro­ ken fragments or removed as scrapings, cross sections, and exudates. They were analyzed by IR microspectroscopy at the GCI and by SEM-EDS, XRD, and optical microscopy at MoMA, to identify additives in the polymer, as well as to identify the principal component of the plastic . The application presented below will be limited to the IR microanalysis. Analysis The samples were characterized by FT-IR microanalysis; the analysis conditions were the same as those specified in Case Study 1 . Results IR analysis of the liquid exudate, or " sweat, " showed that it contained an inorganic nitrate. Elemental analysis by energy dispersive spec­ troscopy showed that the exudate contained zinc. Crystals formed when the liquid was placed in a sealed container and liquefied again upon exposure to air. This behavior corresponds to that of reference samples of nitrate salts-for example, calcium and zinc-which are hygroscopic and become hydrated to form a liquid at room conditions. In cellulose nitrate, the nitrate salts can be formed by the reaction of nitric acid (a degradation product) with fillers, stabilizers, or colorants in the piece. Zinc oxide was commonly used as a filler and opacifier. It also acts as a stabilizer by rapidly consuming nitric acid to form zinc nitrate. The samples primarily contained camphor as a plasticizing agent, in addition to an unidentified oil. The presence of camphor was (1/4 confirmed by isolating it from the sample. This was accomplished by placing a tiny sample in the center of a 0.6 cm in. ) diameter glass 1 65 Case Studies tube 1 0 cm (4 in.) long. The area of the sample was gently heated with a flame until droplet condensation was noted on the cooler portion of the tube. The tube was then quickly broken open, and a droplet was trans­ ferred to a BaF2 pellet for analysis by IR microspectroscopy. It was imperative to work fast, since the camphor volatilized quickly. An alter­ nate method for the analysis of a volatile liquid such as camphor would be to place the sample in a micro liquid cell or between two salt pellets. Figure 6.20 shows IR transmittance spectra of three samples of cellulose nitrate: one in good condition, one in moderate condition, and one in poor condition; also shown are spectra of the camphor and liquid nitrate salt. Noticeable in the spectra of the more degraded samples is the increase in the intensity of the band at 1 340 cm- I , due to the presence of nitrate salts in the sample. There is also a corresponding decrease in the intensity of the carbonyl band at 1 73 5 cm- I that is due to decreasing amounts of camphor. The rate of deterioration of cellulose nitrate is dependent on the availability of oxygen and water and on exposure to UV radiation. This fact makes the surface of the polymer the most vulnerable area. In order to obtain a depth profile of the degradation, a cross section sample obtained from broken fragments of the sculpture was analyzed. The sample was embedded in a polyester resin and then polished to a flat, shiny surface. IR spectra were collected in reflection mode. Figure 6.21 shows three IR absorbance spectra in the region of 1 900- 1 5 00 cm- I ; the first was collected at the surface of the cellulose nitrate sample, while the second and third were collected 1 and 2 mm, respectively, deeper into the sample. All three spectra were normalized to the height of the band at 1 650 cm-I, which corresponds to the nitrate ester groups in the cellulose nitrate. The spectra show that the surface of the sculpture contains cellulose nitrate with a diminished amount of camphor ( based on carbonyl at 1 740 cm- I ) compared t o the composition a t a depth o f 2 m m into the sample. The diminished amounts of camphor in the deteriorated areas of the plastic can be due to sublimation. Since the deteriorated surfaces often have cracks, more area is exposed, which may allow more camphor to sublime. Conversely, the loss of camphor may have a degenerative effect on the plastic. Camphor was preferred as a plasticizer because it stabilized the cellulose nitrate as well as made it less brittle ( for more information on cellulose nitrate, see Reilly 1 9 9 1 and Edge et al. 1 99 0 ) . Resolution IR microspectroscopy, along with other analysis methods, was used to increase understanding of the various types and degrees of degradation exhibited by each sculpture. The droplets were determined to be a hydrated nitrate salt resulting from deterioration of cellulose nitrate. At present, there are no established treatments for reversing some of the degradation processes that these obj ects have undergone. Since the deteri­ oration of the polymer is caused by heat, light, acid impurities, and high humidities, preventive conservation practices may minimize further degradation by direct control of the environment. 1 66 Chapter 6 Camphor No evident degradation CD::=()c'""'c'" t!=ifE Slight yellowing Very yellow and brittle Figure 6.20 IR transmittance spectra for camphor (top) Liquid n itrate salt and a liquid nitrate salt (bottom) , along with spectra for three samples of cellulose n itrate (plasticized with camphor) that visually exhibit varyi n g degrees of 3998 3332 2666 2000 1 741 1 482 1 223 964 705 Wavenumber (cm- 1 ) degradation. Case Study In 1 9 8 8 the 1G0e: l Dead Sea Scrolls began an evaluation of the optimum storage and display conditions for the Dead Sea Scrolls. After the determination that control of the environment is critical to the stabilization of severely degraded 1 67 Case Studies 2 Q) ()«.QIf)o c ro .Q Figure 6 . 2 1 An expanded view of IR absorbance spec­ mm inside 1 mm inside Outside surface tra for a cellulose nitrate cross section sample measu red at the outer surface, 1 mm inside, and 2 mm inside. The cam­ phor is depleted near the surface. The spectra are normalized to the height of 1 800 1 750 1 700 1 650 1 600 1 550 Wavenumber (cm- 1 ) the nitrate ester band at 1 650 cm-1 . parchment samples (Hansen 1 9 9 3 ) , several methods were used to evalu­ ate the state of degradation of the scroll fragments . These included XRD, liquid chromatography, and IR spectroscopy. Background The collective group of documents known as the Dead Sea Scrolls were written on parchment, papyrus, and copper scrolls. The parchment scrolls were prepared from the skin of sheep and goats about two thou­ sand years ago. Ancient preparation techniques for parchment involved abrasive dehairing of the skin and/or use of a vegetable matter and enzy­ matic dehairing bath. After removal from the baths, the skins were stretched tightly on a frame, and the water was removed from the skins by scraping with a half-moon knife. When dry, the skins were smoothed by abrasion, usually with pumice stones. Additionally, there is some evi­ dence that the parchment surface was treated with small amounts of vegetable tannage or cedar oil ( Poole and Reed 1 962 ) . Collagen, a protein, i s the primary component o f parchment and can be irreversibly converted to gelatin. The tropocollagen molecule is held in a triple-helical structure by hydrogen bonds that, upon the addition of water and/or heat, can become structurally disorganized, or gelatinized (Weiner et al. 1 9 8 0 ) . Additionally, the protein polypeptide chain may degrade through hydrolysis or oxidation. Collagen denatura­ tion to gelatin has been characterized by IR spectrophotometry by Brodsky-Doyle, Bendit, and Blout ( 1 975 ) ; Susi, Ard, and Carroll ( 1 97 5 ) ; a n d Warren, Smith, a n d Tillman ( 1 96 9 ) , who have shown that the most noticeable change in an IR spectrum during denaturation is an amide II band position shift from 1 5 50 to 1 5 3 0 cm-1 when the collagen structure is converted to the disordered form found in gelatin. Analysis question What is the state of degradation for nine Dead Sea Scroll parchment samples? These samples consist of fragments removed from intact scrolls, along with fragments that cannot be assigned to any specific scroll. 1 68 Chapter 6 Method Initially ATR analysis was used to characterize the front and back surface composition of each of the samples. Later, because it was important to determine the depth of degradation, some of the samples were prepared as thin sections for linear step-scan analysis by IR microspectroscopy. Analysis ATR IR analysis was used to examine front and back surface degradation on nonembedded scroll fragments and for comparison to three modern reference parchment samples. The analysis conditions for ATR measure­ ments are given in Case Study 8 . Thin sections o f the samples were characterized by FT-IR microanalysis; the analysis conditions were the same as those specified in Case Study 1 . A linear spectral map of the Cave IV 9A3 scroll sample was collected with an analysis window of 20 x 1 00 !-Lm stepped across the width of the sample in 15 !-Lm increments. Results The surface degradation of the samples was examined by ATR by use of the method presented. With the use of Brodsky-Doyle's method, the results of the ATR analysis of this set of samples compared the relative differences in position of the amide I and II bands in the spectra to the changes in height for the two bands ( Fig. 6.22; Brodsky-Doyle, Bendit, and Blout 1 975 ) . These changes in position and height indicate the degree of denatu­ ration of the collagen to gelatin. All of the scroll samples exhibit greater degrees of denaturation than do the modern parchment reference samples. Examination of the spectra collected across the width of sev­ eral thin sections (e.g., Fig. 6.23 ) shows that the shift in amide II band position, in addition to the change in relative intensities of both amide I and II bands, is localized in the exterior portions of the samples. Thus, any denaturation and hydrolysis of the collagen is primarily in the outer 20-5 0 pm, depending on the condition of the sample. In general, the skin side of the parchment (with a smooth upper surface) exhibited degrada­ tion to a greater depth than did the flesh side (the reverse ) . Photomicrographs presented i n Figure 6.24, taken i n normal and cross-polarized light, show that the inorganic compounds in the sample exist only near the edges, and that the inorganic material appears to be embedded in the parchment rather than being j ust a surface encrus­ tation. IR absorption bands corresponding to nonproteinaceous materials or additives were found in the spectra of the surface areas of all of the scroll samples. None were detected in the interior of the samples. Three types of compounds-carbonates, silicates (pumice, talc, or dirt) , and alum ( aluminum ammonium sulfate )-were found as mixtures or individ­ ual components in the samples. Alum, which is used in tawing parch­ ment, was found in two samples. Silicates, possibly from pumice used as an abrasive, were found in the exterior surfaces of all the scroll pieces. Carbonates, possibly used to fill pores or as an abrasive, were present in large amounts in one sample and in very small or nondetectable amounts 1 69 Case Studies 1 .8 n�====================��____ e n�a� a� t� t io� ____�D�� u r� ____________ , _, 1 .6 Cave IV 9A3 Temple �.n(f) « .• o OJ o c (1j � 1 .2 • •• • �- Figure 6.22 The difference i n absorption band position Scroll fragments Reference parchment 1 .0 (amide I: 1 650 cm- 1 ; amide I I : 1 550 cm-1) versus the ratio of their intensities (amide I/amide I I ) . All scroll fragments exhibited more degradation of the collagen than did 0.8 1 00 90 Band posit ion difference (amide I 80 the reference parch ment samples. 1 10 amide II [cm- 'll 1 20 in the remaining scroll samples. There could be other nonproteinaceous compounds, such as organic tanning agents, present in the samples in amounts too small to be detected by IR spectroscopy. Resolution Microanalysis showed that the samples were nonhomogeneous and that the spectral results varied from area to area within a sample. Thus, 2.5 2 1 .5 C ::J OJ o c (1j .n 0.5 Figure 6.23 A linear IR absorption band spectral map 1 2.0 of the Dead Sea Scroll cross section sample shown in Figure 6.24. The analysis win­ dow was 2 0 .�o .n«(f) x 1 00 IJm; the step size was 1 5 IJ m . The window was stepped from the flesh side of the parch ment (scan 1 ) to the skin side of the parchment (scan 1 2) . The relative i ntensities of the amide I and amide II bands change; this change indi­ cates that the su rfaces of the sample are more denatured than are the interior. 3500 3000 2500 2000 Wavenumber (cm-1) 1 500 1 70 Chapter 6 Figure 6.24 Photomicrographs of a thin section of a sample from a Dead Sea Scroll (cave IV 9A3) at x250. Normal illumi nation was used for the top photo; the bottom photo was taken in cross-polarized light. while the results themselves were reproducible (as determined by repli­ cate analysis) and were characteristic of the area analyzed, they were not necessarily representative of the entire scroll from which the sample was taken. However, since several samples covering a wide range of types were analyzed, the total set of the IR results on the pieces were exemplary of many areas on the scrolls. In addition, since some areas of the scrolls were shown to be severely degraded, the recommended stor­ age conditions should be based on the worst-that is, the most gela­ tinized scroll. 1 71 Case Studies Summary The characterization of materials is one of the most important functions of IR spectroscopy in the art conservation field. It is often used as the first analytical method for classifying the maj or components in a sample submitted for analysis . Almost any type or form of sample, except for metals, can be analyzed. In most cases, it is necessary to remove small, barely visible particles from the obj ect. Examples in this chapter illustrate the potential for strati­ graphic microanalysis of multilayered materials. The optimal sample form is a thin section prepared by microtoming an embedded cross sec­ tion. Also explored has been the use of IR reflection techniques for the analysis of polished cross sections for the production of molecular maps. Currently the reflection techniques are most useful when supplemental analyses by other methods are available. In addition to its use in the identification of materials, IR spectroscopy can be used to evaluate the condition of a material and to monitor chemical reactions. Both of these functions are significant to the evaluation and monitoring of deterioration. IR analysis is a very practical method for comparative studies of chemical changes in relation to time and conditions. Appendix I Selected I nfrared Spectra Collections and Digitized libraries All instrument manufacturers sell similar collections of digitized spectral libraries that work with their search software. However, to minimize repe­ tition, only a few were selected for this appendix. Please see the Suppliers list for the names and addresses of other instrument manufacturers. Aldrich Library of Infrared Spectra, C. J. Pouchert, ed. Aldrich Chemical Co., 1 0 0 1 W. St. Paul Ave . , Milwaukee, WI 5 3 2 3 3 Classical hard-copy reference of IR grating spectra for pure chemicals. Also includes polymers, organometallics, and carboxylic acid salts. Aldrich-Nicolet Digitized Libraries Nicolet Instrument Corp. , 5 2 2 5 - 1 Verona Road, Madison, WI 5 3 7 1 1 Digitized versions o f the classical Aldrich collection, along with digitized spectra for chemicals sold by Sigma Chemical. Aldrich-Nicolet collection; Sigma-Nicolet collection. Bio-Rad Sadder Div.-see Sadder Research Laboratories. Coblentz Society, Inc., P.O. Box 9952, Kirkwood, MO 63 1 22 Special collection books of high-quality grating spectra contributed by government and industrial labs. Books are edited by Clara Craver and contain text sections with good information on sample preparation and spectral interpretation. The Desk Book of Infrared Spectra; regulated and major industrial chemicals; gases and vapors; halogenated hydro­ carbons; plasticizers and other additives. Galactic Industries Corp., 395 Main St., Salem, NH 03079 Search, data conversion, and data processing spectroscopic software (Spectra Calc) ; data acquisition and processing for data generated by spectroscopy and chromatography instruments ( Lab Calc ) ; designed to integrate laboratory data from several types of instruments. Infrared Data Committee of Japan (IRDC), Sanyo Shupp an Boeki Co., Hoyu Bldg., 8, 2-Chrome, Takaru-cho, Chuo-ku, Tokyo, Japan Search software based on wavenumbers and intensities; possibly chang­ ing to fully digitized spectra ( 1 4,000 spectra ). Selected Infrared Spectra Collections and Digitized libraries 1 73 National Chemical Laboratory for Industry ( NCLI) collection, Japan An integrated system with a digitized collection of electron spin reso­ nance, nuclear magnetic resonance, IR, and mass spectra. This database is available online in Japan; it is described in O. Yamamoto, K. Someno, N. Wasada, J. Hiraishi, K. Hayamizu, K. Tanabe, T. Tamura, and M . Yanagisawa, " An Integrated Spectral Database System including IR, MS, proton-NMR, carbon- 1 3 -NMR, ESR, and Raman Spectra," Analytical Sciences 4 ( 1 9 8 8 } :23 3-3 9 . Sadder Research Laboratories, Bio-Rad Sadder Div., 3 3 1 6 Spring Garden St., Philadelphia, PA Search software ( IR Mentor) ; hard-copy and digitized versions of spectral libraries ( libraries contain FT-IR and grating IR spectra ) . Condensed­ phase and vapor-phase standards; adhesives and sealants; attenuated total reflectance of polymers; coating chemicals; automobile paint chips; commonly abused drugs; controlled pyrolysates of polymers; dyes, pig­ ments, and stains; fats, waxes, and derivatives; fiber and textile chemi­ cals; flame retardants; flavors and fragrances; food additives; inorganics; lubricants; manufacturing starting materials and intermediates; minerals and clays; monomers and polymers; organometallics; pesticides and agricultural chemicals; petroleum chemicals; pharmaceuticals; plasticiz­ ers; polymer additives; prepared and prescription drugs; priority pollu­ tants; rubber chemicals; solvents; steroids; surface-active agents; water-treatment chemicals. Also suppliers for automobile paint chips database; Canadian Forensic Package Library; enhanced EPA Vapor-Phase Package Library; Georgia State Crime Lab Package Library; Merck/Sadder Library; Hummel/Sadder Polymer Library; Sadder/Scholl Polymer Processing Library; University Package Library of Pure Compounds. Sprouse Scientific Systems, Inc., 1 8 0 1 Crossbeam Dr., Charlotte, NC 282 1 7 Search software (Micro-search ), hard-copy and digitized versions o f spec­ tral libraries ( libraries contain FT-IR spectra; books are edited by D. L. Hansen ) . Polymers; Solvents (Transmission Spectra); Solvents (CIRCLE Cell Spectra); Surface-Active Agents, Solvents: Condensed-Phase, Vapor­ Phase, and Mass Spectra. In addition to these four collections, digitized IR spectral libraries on the following topics are available: the Canada Collection: coal, shale, and clay minerals; coatings and resins; environ­ mental toxins; EPA vapor-phase (corrected); epoxy resins, curing agents, and additives; fragrances and essential oils; fibers by IR microscope; gas­ phase IR of environmental chemicals; small-molecule gases and environ­ mental pollutants; general chemical compounds; Georgia State Crime Lab forensic library; Georgia State Crime Lab automotive paint; inorganics on KBr beam splitter; inorganics on CsI beam splitter; lubricants, addi­ tives, and raw materials; minerals, U.S. Geological Survey collection; polymers by transmission; polymers by attenuated total reflectance; poly­ mer additives; general organic compounds; solvents; solvents by cylindri­ cal internal reflectance; solvents, vapor-phase; surface-active agents. 1 74 Appendix I Other Coll ections Afremow, L. c., and J . T. Vandeberg 1 9 66. High resolution spectra of inorganic pigments and extenders in the mid­ infrared region from 1 5 0 0 cm-I to 200 em - I . Journal of Painting Technology 38 (495 ) : 1 69-202. ( 7 8 spectra of pigments with known composition. ) American Society for Testing Materials 1 9 69. ASTM- Wyandotte Index: Alphabetical List of Compound Names, Formulas and References to Published Infrared Spectra; an Index to 92,000 Published Infrared Spectra. Philadelphia: ASTM. (Previous versions: ASTM special publications 1 3 1 [ 1 962], 1 3 1 -A [ I 963].) Association of Official Analytical Chemists 1 9 75. Infrared and Ultraviolet Spectra of Some Compounds of Pharmaceutical Interest. Rev. ed. Washington, D.C.:' Association of Official Analytical Chemists. Bel lamy, L. J . 1 9 75. Advances in Infrared Group Frequencies. London: Chapman and Hall. 1 9 80. The Infrared Spectra of Complex Molecules. 2d ed. London: Chapman and Hall. Bell anto, J . , and A. H idalgo 1 97 1 . Infrared Analysis of Essential Oils. London: Heyden and Sons. Boldyrev, A. I . 1 9 76. Infrared Spectra of Minerals. Moscow: Nedra. B ritish Pharmacopoeia Commission 1 9 80. Infrared Reference Spectra. ( First supplement 1 9 8 1 , second supplement 1 9 82, third supplement 1 9 84. ) London: H.M. Stationery Office. Cai n , D. S., and S. S. Sti m ler 1 9 67. Infrared Spectra of Plastics and Resins. Part 3. Naval Research Laboratory, Report 65 03, Feb. 2 8. Washington, D.C.: U.S. Department of Commerce. Carro l l , G. R., W. C. lalonde, B. D. Gaudette, S. L. Hawley, and H ubert 1 9 8 8 . A computerized database for forensic textile fibres. Journal of the Canadian Society of Forensic Scientists 2 1 : 1 . Chicago Society for Coating Technol ogy 1 9 80. An Infrared Spectroscopy Atlas for the Coatings Industry. Philadelphia: Federation of Societies for Paint Technology. ( 1 433 spectra. ) Coates, J . P. , and L. C. Setti 1 9 83. Oils, Lubricants, and Petroleum Products-a Library Containing Spectra from Fuels, Lubricants, Additives and Related Materials. Norwalk, Conn.: Perkin­ Elmer Corp. Colthup, N. B . , L. H. Daly, and S. E. Wiberley 1 9 75. Introduction to Infrared and Raman Spectroscopy. 2d ed. New York: Academic Press. (About 600 spectra . ) Dobriner, K., E . R. Katzenell enbogen, a n d R. N . Jones 1 953. Infrared Absorption Spectra of Steroids-an Atlas. Vol. 1. New York: Wiley-Interscience. Dolphin, D., and A. E. Wick 1 9 77. Tabulation of Infrared Spectral Data. New York: Wiley. E l l iott, A. 1 9 69. Infrared Spectra and Structure of Organic Long-Chain Polymers. London: Arnold. Selected Infrared Spectra Col lections and Digitized Libraries 1 75 Farmer, V. c . , ed. 1 974. The Infrared Spectra of Minerals. Mineralogical Society Monograph 4. Surrey, U.K. : Adlard and Son. ( Contains detailed information on the relationship of mineral structures to their infrared spectra.) Fl ett, M . 1 96 9 . Characteristic Frequencies of Chemical Groups in the Infrared. New York: American Elsevier. Fox, R. H . , and H. I. Schuetzman 1 9 6 8 . The infrared identification of microscopic samples of man-made fibers. Journal of Forensic Science 1 3 (3 ) : 3 97-406. ( Contains 1 3 spectra of synthetic fibers.) Gadsen, J . A. 1 975. Infrared Spectra of Minerals and Related Inorganic Compounds. London: Butterworth. Gore, R. c., R. W. Hannah, S. C. Pattacini, and T. J . Porro 1 9 7 1 . Infrared and ultraviolet spectra of seventy-six pesticides. Journal of the Association of Official Analytical Chemists 54( 5 ) : 1 028-40. Hershenson, H . H. 1 959, 1 964. Infrared Absorption Spectra Index. New York: Academic Press. (Two volumes cover 1 945-6 2 . ) H u mmel, D . 0., F. and Scholl 1 9 8 1 . Atlas of Polymer and Plastics Analysis. ( Vol. 1, Polymers: Structures and Spectra; vol. 2, Plastics, Fibres, Rubbers, Resins; vol. 3, Additives and Processing Aids . ) New York: Verlag Chemie International. ( O ver 7000 spectra.) I nfrared Users' Group (lRUG) 1 99 5 . Art and Conservation Materials Infrared Spectral Library. (Vol. 1, Natural and Synthetic Products; vol. 2, Colorants [limited distribution] . ) Marina del Rey, Calif. : Scientific Program of the Getty Conservation Institute. Jakes, K. A., L. R. S i bley, and R. Yerkes 1 994. A comparative collection for the study of fibres used in prehistoric textiles from eastern North America. Journal of Archaeological Science 2 1 :641-50. Kagarise, R. E., and L. A. Wein berger 1 954. Infrared Spectra of Plastics and Resins. Part 1 . U.S. Naval Research Lab report #4369, Washington, D.C.: U.S. Department of Commerce. Karcher, W. , ed. 1 98 3 , 1 9 8 8 . Spectra Atlas of Polycyclic Aromatic Compounds. Vols. 1 , 2. Boston: Kluwer Academic Publishers. Keller, R. J . 1 9 8 6 . The Sigma Library of FT-IR Spectra. Vols. 1 , 2 . St. Louis, Mo.: Sigma Chemical Collection. Langenhei m, J . H . , and C. W. Beck 1 96 8 . Catalogue of infrared spectra of fossil resins (ambers). I. North and South America. Botanical Museum Leaflets 22( 3 ):65-120. (45 spectra.) McCl ure, A., J. Thomson, and J. Tan nah i l l 1 96 8 . Infrared spectra o f ninety-six organic pigments. Journal o f Oil and Colour Chemists' Association 5 1 :580. Merck, E., ed. 1 9 8 8 . Merck IR Atlas-A Collection of FT-IR Spectra. New York: VCH Publishers. M i l ler, F. A., and C. H. Wilkins 1 952. Infrared spectra and characteristic frequencies of inorganic ions. Analytical Chemistry 24: 1253-94. 1 76 Appendix I M i n i stry of Aviation Technical Information and Library Services 1 960. An Index of Published Infrared Spectra. Vols. 1 , 2. London: Her Majesty's Stationery Office. Mitzner, B. M . , E. T. Theimer, and S. K. Freeman 1 9 65. The infrared spectra of monoterpenes and related compounds. Applied Spectroscopy 1 9 ( 6 ) : 1 69-85. Morris, W. W. 1 973. High resolution infrared spectra of fragrance and flavor compounds. Journal of the Association of Official Analytical Chemists 56: 1 027. Nakamoto, K. 1 97 8 . Infrared and Raman Spectra of Inorganic and Coordination Compounds. 3d ed. New York: John Wiley and Sons. Nyquist, R. A., and R. O. Kagel 1 9 7 1 . Infrared Spectra of Inorganic Compounds. New York: Academic Press. ( 8 92 spectra. ) Plyusni na, I. I . 1 9 77. Infrared Spectra of Minerals. Moscow: Izd. Mosk. Univ. Polchlopek, S. E., and R. L. Harris 1 963. ATR Spectra of Surface Coatings. Stamford, Conn.: Barnes Engineering Co. Pouchert, C. J . , ed . 1 9 8 1 . The Aldrich Library of Infrared Spectra. 3d ed. Milwaukee, Wis.: Aldrich Chemical Co. (About 1 1 ,000 spectra. ) 1 9 85-89. The Aldrich Library of FT-IR Spectra. (Vol. 1, 1 9 8 5 ; vol. 2, 1 9 8 8 ; vol. 3, 1 9 8 9 . ) Milwaukee, Wis.: Aldrich Chemical Co. Price, B . , and J. Carlson Forthcoming. Infrared Spectra of Naturally Occurring Minerals. Newark, N.].: University of Delaware. Rouen, R. A., and V. C. Reeve 1 9 70. A comparison and evaluation of techniques for identification of synthetic fibers. Journal of Forensic Science 1 5( 3 ) :4 1 0-32. ( Contains 20 spectra of synthetic fibers.) Siesler, H . W., and K. Holland-Moritz 1 9 80. Infrared and Raman Spectroscopy of Polymers. New York: Marcel Dekker. Snodgrass, A . , and B. Price 1 993. Infrared Spectra of the Gettens Collection. Cambridge, Mass.: Harvard Art Museums. Sti m ler, S. S . , and R. E. Kagarise 1 966. Infrared Spectra of Plastics and Resins 2: Materials Developed since 1 954. U.S. Naval Research Lab, #6392, Washington, D.C. : U.S. Department of Commerce. Szymanski, H. A., and R. E. Erickson 1 970. Infrared Band Handbook. Rev. 2d ed. ( 2 vols. ). New York: Plenum. Thermodynamics Research Center Hydrocarbon Project 1 9 90. Selected Infrared Spectral Data. College Station, Tex. : Thermodynamics Research Center, Texas Agricultural and Mechanical University. Thompson, B . 1 9 74. Hazardous Gases and Vapors: Infrared Spectra and Physical Constants. Technical Report no. 595 (August). Fullerton, Calif.: Beckman Instruments. Tipson, R. S . 1 96 8 . Infrared Spectroscopy of Carbohydrates. Washington, D.C.: National Bureau of Standards. Selected Infrared Spectra Collections and Digitized Libraries 1 77 Tungol, M. W., E. G. Bartick, and A. Montaser 1 990a. The development of a spectral data base for the identification of fibers by infrared microscopy. Applied Spectroscopy 44(4):543-49. (Describes the development of a reference library for polymer fibers . ) 1 9 90b. Spectral data base for fibers by infrared microscopy. Spectrochimica Acta 46B: 1 535E. Van der Marel, H . W., and H . Beutelspacher 1 976. Atlas of Infrared Spectroscopy of Clay Minerals and Their Admixtures. New York: Elsevier. Welti, D . 1 9 70. Infrared Vapour Spectra. New York: Heyden and Sons. Wenni nger, J . A., and R. L. Yates 1 967. High resolution infrared spectra of some naturally occurring sesquiterpene hydrocarbons, part 1. Journal of the Association of Official Analytical Chemists 50 ( 6 ) : 1 3 1 3-45. 1 9 70. High resolution infrared spectra of some naturally occurring sesquiterpene hydrocarbons, 2: Second series. Journal of the Association of Official Analytical Chemists 5 3 ( 5 ) : 949-6 1 . White, R. G . 1 964. Handbook of Industrial Infrared Analysis. New York: Plenum Press. Wilks, P. A., and M. R. Iszard 1 964. The Identification of Fibers and Fabrics by Internal Reflection Spectroscopy. Presented at the 1 5th Mid-America Spectroscopy Symposium, Chicago. South Norwalk, Conn.: Wilks Scientific Corp. ( Contains 47 spectra of fiber s . ) Yamaguchi, K . 1 96 8 . Spectral Data of Natural Products. Vols. 1 , 2. New York: Elsevier. Zeller, M. V., and M. R. Grabowski 1 9 78. A Collection of Reference Spectra for Flame Retardant Reagents. Perkin-Elmer Infrared Bulletin no. 66. Norwalk, Conn. : Perkin-Elmer Corp. ( Contains 30 spectra of flame retardants for fabrics. ) Zeller, M. V., and M. P. J uszli 1 9 75. Reference Spectra of Minerals. Norwalk, Conn. : Perkin-Elmer Corp. Zeller, M. V., and S. C. Pattacini 1 9 73. The Infrared Grating Spectra of Polymers. Perkin-Elmer Infrared Applications Study no. 1 3. Norwalk, Conn. : Perkin-Elmer Corp. ( Contains spectra for 29 polymers along with a flowchart to aid in the identification of polymers.) Appendix I Infrared Reference Spectra An important factor for IR spectral identification is access to reference spectra corresponding to appropriate materials. While Appendix I sup­ plied numerous commercial and literature sources for spectra, this appen­ dix gives a few examples of spectra for art and conservation materials, because commercial libraries often do not include materials encountered in cultural artifacts. The spectra are organized by their material classifications. For example, gelatin and casein are both classified as proteins. Materials in the same classification have similar chemical compositions and thus similar spectra. The spectra sheets also provide physical data about the sample, as well as its analysis conditions. Accompanying descriptions supply information about the material and its use in art and conserva­ tion. An alphabetical listing of the materials is given below. Alphabetical Listing of IR Reference Spectra Acryloid B-72, p. 1 9 1 Linseed stand oil, p. 1 8 5 Barium sulfate, p. 1 9 6 Madder, p. 200 Beeswax, crude, p. 1 84 Malachite, p . 1 99 BEVA 3 7 1 , p. 1 92 Mastic, p. 1 8 9 Carnauba wax, p. 1 8 4 Microcrystalline wax, p . 1 8 3 Casein, p. 1 82 Phthalocyanine blue, p. 1 97 Cellulose nitrate, p. 1 90 Pine resin, p. 1 8 7 Chalk, p. 1 94 Plaster, p . 1 95 Copal, Manila, p. 1 8 7 Poly( vinyl acetate ) (PVAC), p. 1 92 Dammar, p . 1 8 8 Polyamide, p. 1 93 Dragon's blood, p . 200 Polycyclohexanone, p. 1 93 Egg yolk, hen, p. 1 8 3 Polyester 1 2 F, p. 1 9 1 Elemi, p. 1 8 8 Poppyseed oil, p . 1 8 5 Gelatin, p . 1 82 Prussian blue, p. 1 9 8 Gum arabic, p. 1 79 Rice starch, p. 1 8 0 Gum tragacanth, p. 1 79 Rosin, p. 1 8 6 Gypsum, p. 1 94 Sandarac, p . 1 8 9 Hide glue, p. 1 8 1 Shellac, p . 1 90 Honey, clover, p . 1 8 0 Silica, p. 1 96 Indigo, natural, p. 1 9 7 Ultramarine, p. 1 9 8 Isinglass, p. 1 8 1 Verdigris, p . 1 9 9 Kaolin, p . 1 95 Walnut oil, p . 1 8 6 1 79 I n frared Reference Spectra G u m Arabic G u m Arabic PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Los Angeles County Museum of Art; RBG, 66.1 848 Sudan Amber color, transparent, chunks 3600-3200 cm" 3000-2800 cm ' O-H C-H stretching band stretching bands 1 650 cm" O-H bending band 1 480-1300 cm" 1 300-900 cm" C-H COO bending band stretching bands Gum arabic is the most commonly used gum in preparation of paints. It is a dried, amorphous exudate from the stem of several species of Acacia trees (Acacia senegal) in tropical and subtropical areas of the world. Most of the current output of gum arabic is from the sub-Sahara region in Africa. The gum is sold in the form of colorless, round lumps, as granules, as thin flakes, or as a powder; all of these may be white or slightly yellowish. Gum arabic is completely soluble in hot and cold water, yielding a viscous solution. It is insoluble in alcohol. Gum arabic is used in watercolor, paints, and inks and for textile sizing. The earliest known inks consisted of gum arabic and lamp black. SYNONYMS: Kordofan, picked turkey, white Sennar, Senegal gum, Ghezineh gum, gomme blonde, gomme blanche, gum acacia, East India gum, kami. IR ANALYSIS LAB Loyola Marymount University, 7/6/89 IR ANALYSIS CONDITIONS poE 1 700 = 1 20 = 4000-700 cm-' Microscope Cast from solvent on BaF, Resolution 4 cm-' Scans Range 600 40 2000 40 = Gum Arabic G u m Tragacanth PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS / G u m Sugar (Astragalus gummifer) Los Angeles County Museum of Art; RBG , 66. 1 848 Western Persia Brown, opaque, sheets 3600-3200 cm ' O-H 3000-2800 cm" C-H 1 750-1 600 cm" c=o stretching band stretching bands Gum Tragacanth Gum tragacanth is an exudate from several species of shrubs of the genus Astragalus found in the dry regions of Iran, Syria, and Turkey. It is available in the form of dull white, translucent plates or as a yellowish powder. It is insoluble in alcohol but soluble i n alkaline solutions and solutions of hydrogen peroxide. A soluble fraction, tragacanthin, dissolves when added to water, whereas an insoluble fraction, bassorin (60-70% by wt.) swells to a gel-like state. A solution is prepared by wetting the powder with alcohol, then adding water and shaking. Gum tragacanth is used for textile sizing and printing, pastel crayon production, leather curing, and furniture polishes. SYNONYMS: Gum tragacanth, gum dragon, gomme adragante, Smyrna tragacanth, Anatolian tragacanth, Persian tragacanth. stretching band 1 650 cm" O-H bending band 1 480-1300 cm" C-H bending bands 1 300-900 cm" COO stretching bands IR ANALYSIS LAB Loyola Marymount University, 7/1 1/89 IR ANALYSIS CONDITIONS poE 1 700 Microscope = 1 20 Range = 4000-700 cm-' Cast from solvent on BaF, Resolution Scans 40 Gum Tragacanth 2000 = 4 cm-' 60 40 / G u m Sugar 1 80 Appendix I I Rice Starch Starch PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS U.S. Customs Lab, Long Beach, Calif. Unknown White, opaque, powder 3600-3200 cm" O-H stretching band 3000-2800 cm" 1 650 cm" C-H stretching bands 1 480-1300 cm" 1 300-900 cm" O-H bending band C-H C-O bending bands stretching bands Starches occur as granules of varying size in the rools, bulbs, and seeds of mosl planls. Chemically, starch is a carbohydrate in the same family as cellulose, gums, and sugars. Starch contains about 20% of water soluble amylose and 80% of a water-insoluble fraction called amylopectin. Both fractions correspond to different carbohydrates of high molecular weight and formula (C,H"O,)o' Starch turns iodine blue. Starch is a fairly poor adhesive but has been used in some cases for lining paintings. As a paint binder, it was most popular for fingerpaints and cheap house paints. VARIETIES: Wheat, corn, rice, dextrin, dextran, British gum, mucilage, sorghum, potato, tapioca, arrowroot, sago palm. IR ANALYSIS LAB Getty Conservation Institute, 1/19/93 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' = 200 = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution Scans Range 80 60 40 40 / Starch G u m Sugar Honey, Clover Honey PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS J. Paul Getty Museum Antiquities Conservation USA A sweet, viscous fluid produced b y bees from the nectar of flowers. Honey i s a mixture of fructose, glucose, dextrose, and water (-20%), with trace amounts of enzymes and oils. Its composition varies slightly depending on the source of nectar. Honey was used since early times as a plasticizing additive to watercolors, tempera, size, and glair. Golden-yellow, highly viscous, liquid 3600-3200 cm" O-H stretching band 3000-2800 em" C-H stretching bands 1650 cm" O-H bending band 1 480-1300 cm" C-H bending bands 1 300-900 cm" C-O stretching bands IR ANALYSIS LAB Getty Conservation Institute, 9/21/84 IR ANALYSIS CONDITIONS Digilab I SE/80 = 4 cm-' = 200 Range = 4000-800 cm-' KBr pellet Ground with KBr Resolution Scans 40 360 Honey 20 180 160 140 120 10 80 60 40 / G u m Sugar 1 81 Infrared Reference Spectra Hide Glue (pearls) Animal Glue PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS J. & Paul Getty Museum Decoralive Arts Conservation; Gieck Co. USA Ughl amber, Iranslucent, chunks 3400-3200 cm·' N-H 31 00-2800 cm·' 1 660-1 600 cm·' C-H stretching bands C=O stretching band stretching band 1 565-1 500 em·' C-N-H 1 480-1300 cm·' C-H bending band bending band Animal glue is an adhesive consisting primarily of gelatin and other protein residues of collagen, keratin, or elastin. Glues may be made from bones, skins, hides, and intestines of animals (fish, goats, sheep, cattle, horses, etc.). These agglutinating materials are removed by extraction with hot water, then cooled and dried to produce gelatin or glue. Animal glues are available in the form of sheets, droplets, chips, granules, cubes, and powder. They occur in a wide variety of colors ranging from transparent to opaque and white to brown. Glue is soaked in cool water to form a turbid jelly that will become clear and thinner upon heating to 40 'C. Glue will decompose and darken when it is boiled. Animal glues are strong adhesives that have been used in furniture manufacture, gilding, gessoes, and paint binders. VARIETIES: Animal glue, glue, gelatin, size, isinglass, fish glue, rabbit-skin glue, bone glue, hide glue, parchment glue, calfskin glue, skin glue, Nikawa, sturgeon glue, sturgeon's glue, deerskin glue. IR ANALYSIS LAB Getty Conservation Institute, 9/1 4/84 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 KBr pellet = 4 cm-' Ground with KBr = 4000-£00 cm-' Resolution Scans = 200 Range 40 360 320 280 240 2000 180 160 140 120 10 80 60 40 Animal Glue Isinglass Protein (sheets) Fish Glue PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Zecchi Russia White, opaque, sheets 3400-3200 cm·' N-H stretching band 31 00-2800 cm·' C-H stretching bands 1 660-1600 cm·' C=O stretching band 1 565-1500 cm·' C-N-H bending band C-H bending band 1 480-1300 cm·' Fish glue is made from unsorted fish waste and is an adhesive consisting primarily of gelatin and other protein residues of collagen, keratin, or elastin. These agglutinating agents are removed by extraction with hot water, then cooled and dried to produce gelatin or glue. Varied production techniques can produce poor-quality fish glue. The highest quality is made from the bladders of sturgeons. It is clear, bluish white, and very flexible. It is solidified into flat disks that are usually broken into smaller bits for sale. Isinglass is a particularly fine glue made from a specific type of sturgeon. It is generally sold in narrow, soft, translucent strips. Isinglass is very expensive. Glue is to be soaked in cool water to form a turbid jelly that will become clear and thinner upon heating to 40'C. Glue will decompose and darken when it is boiled. High-quality fish glues are used for paintings and gilding. VARIETIES: Gelatin, size, isinglass, fish glue, sturgeon glue, sturgeon's glue, ichthycoll. IR ANALYSIS LAB Getty Conservation Institute, 1 /28/94 IR ANALYSIS CONDITIONS Spectra-Tech IR!!S = Microscope Bulk sample on BaF, 4 cm-' Resolution Scans = 50 Range = 4000-700 cm-' 40 360 320 280 240 20 180 Fish Glue 10 80 60 40 Protei n 1 82 Appendix II Gelatin Gelatin PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Knox Gelatine, Inc. USA Light yellow or white, opaque, powder 3400-3200 cm" N-H 31 00-2800 cm" C-H 1 660-1600 cm" 1 565-1 500 cm" C�O stretching band C-N-H bending band 1 480-1300 cm" C-H stretching band stretching bands Gelatin is a mixture of proteins prepared by hydrolyzing, via boiling, collagen obtained from skin, ligaments, and tendons. Its production differs from that of animal glue in that raw materials are selected, cleaned, and treated with special care, so that the product is cleaner and purer than glue. Gelatin is strongly hydrophilic and can absorb up to ten times its weight of water. It is sold as colorless sheets or as a fine powder and is more elastic than most animal glues. Gelatin is used for photographic film emulsions, sizing, adhesive, ink, encapsulation, and food products. SYNONYMS: Gelatin, gelatine, size. bendi ng band IR ANALYSIS LAB Getty Conservation Institute, 1 /28/94 IR ANALYSIS CONDITIONS Spectra-Tech IR!,S Microscope � 50 Bulk sample on BaF, Resolution � 4 cm-' Scans Range � 4000-700 cm-' 4000 360 320 280 240 20 180 & 60 40 Gelatin Protein Casein PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Harvard Art Museums; Eimer Amend USA Light beige, opaque, powder N-H stretching band 3 1 00-2800 cm" C-H stretching bands 1 660-1600 cm" C�O stretching band 1 565-1500 em" 1 480-1300 cm" C-N-H 3400-3200 em" C-H Casein Casein has been used a s a glue and binder since earliest recorded periods. It is a proteinaceous, dried precipitate produced from milk. It contains sulfur and phosphorus. Casein can be prepared in different ways, but it is best used when fresh. One preparation method is to add dilute hydrochloric acid to hot skim milk. The precipitate is then collected, washed, and dried. It is a white to yellowish powder that is insoluble in water and alcohol but is soluble in carbonates and other alkaline solutions. For use, casein is soaked overnight and a weak alkali (lime, borax) is added to increase solubility. Casein provides strong adhesion and is insoluble in water when dried. SYNONYMS: Casein, caseinate, whey glue, Casco glue, milk acid powder, Kasein. bending band bending band IR ANALYSIS LAB Loyola Marymount University, 1 0/4/90 IR ANALYSIS CONDITIONS P- E 1 700 Microscope � 1 20 � 4000-700 cm-' Dissolved in 01 H,O, dried on BaF, Resolution � 4 cm-' Scans Range 40 360 320 280 240 2000 180 Casei n 60 40 Protein 1 83 Infrared Reference Spectra Egg Yolk, Hen (dried fil m on glass) Egg PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. Parker, Getty Conservation Institute USA Yellowish , oily, powder 3400-3200 cm·' N-H 31 00-2800 cm·' 1 750-1600 cm·' C-H stretching bands C=O stretching bands stretching band 1 565-1500 cm·' C-N-H 1 480-1300 cm·' C-H The whole egg, yolk, or white may be used as a lempera medium. The egg yolk is a stable emulsion of an aqueous liquid with an oily, proteinaceous medium Ihal dries quickly into a hard, insoluble film. It is the traditional tempera medium and may be mixed with oil andlor resin for painting. The white of the egg, or glair, has been used as a medium for illuminated manuscripts. It is also used as a size for attaching gold leaf. Albumen is the adhesive substance of egg white. As a pure film, albumen is clear, brittle, and water soluble. Water solubility can be decreased by heating or adding tannin. VARIETIES: Egg, yolk, whole egg, egg white, glair, egg tempera, hen, duck, chicken, goose, pheasant, pigeon, quail, albumen, albumine. bending band bending band IR ANALYSIS LAB Loyola Marymount University, 5/1 7/89 IR ANALYSIS CONDITIONS poE 1 700 = 4 cm-' Microscope Dried film on KBr = 4000-700 cm-' Resolution Scans = 1 20 Range 60 40 240 20 & Egg Protei n Microcrysta l l i ne Wax PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter Mineral Wax Co. Mineral waxes are relatively pure materials that consist of a hydrocarbon series with little to none of the alcohols or esters found in plant waxes and beeswax. Mineral waxes are generally obtained from the fractional distillation of shale oil, lignite, or petroleum. They are soluble in mineral oil, chloroform, naphtha, benzene, and ether. Mineral waxes are very stable and nonreactive. Paraffin and microcrystalline waxes are white, translucent materials. England White, opaque, chunks 3000-2800 cm·' C-H 1 480-1300 cm·' C-H bending bands C-H torsion bands 750-700 cm·' VARIETIES: Mineral wax, paraffin, ozokerite, ceresin, ceresine, microcrystalline wax, earth wax, cerin, cerosin, ozocerite. stretching bands IR ANALYSIS LAB Getty Conservation Institute, 6/1 5/84 IR ANALYSIS CONDITIONS Digilab 1 5E/80 = 4 cm-' = 4000-600 cm-' KBr pellet Ground with KBr Resolution Scans = 200 Range 40 360 320 280 240 2000 1800 160 140 120 1000 80 60 40 M i neral Wax Wax 1 84 Appendix II Beeswax, Crude Beeswax PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter & Co. England Brownish yellow, opaque, chunks 3600-3200 cm"' O-H stretching band 3000-2800 cm"' C-H stretching bands 1 780-1700 cm"' C=O stretching band 1 480-1300 cm"' C-H bending bands 1 300-900 cm"' 750-700 cm"' C-O stretching bands C-H torsion bands Beeswax is produced by many species of bees; the most common is Apis me/lifica. It is secreted from the organs on the underside of the abdomen of the worker bees and is used in forming the cells of the honeycomb. Wax may be obtained by melting the combs in hot water and straining to remove impurities that may contain resins, sugars, and other plant materials. The waxes from different localities vary considerably in color and texture and chemical composition. The color ranges from light yellow to dark brown. The darker varieties are often bleached by exposure to light and air or with ozone or hydrogen peroxide. Beeswax contains about 1 0% hydrocarbons in addition to alcohols, acids, and ester. Punic wax is refined beeswax. VARIETIES: Beeswax, punic wax, crude beeswax, bleached beeswax, yellow beeswax, white beeswax, virgin beeswax. IR ANALYSIS LAB Getty Conservation Institute, 6/1 4/84 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 = 4 cm-' = 200 Range = 4000--600 cm-' KBr pellet Ground with KBr Resolution Scans 40 360 320 2800 240 20 180 160 140 120 10 BO 600 40 & Beeswax Wax Carnauba Wax Vegetable Wax PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter Co. Northern Brazil Yellow, opaque, chunks 3600-3200 cm"' O-H stretching band 3000-2800 cm"' C-H stretching bands 1 780-1 700 cm"' C=O stretching band 1 480-1 300 cm"' C-H 1 300-900 cm"' C-O stretching bands C-H torsion bands 750-700 cm"' Vegetable waxes are low-melting mixtures of long-chain hydrocarbon compounds found in or on plants. Their properties range widely from the soft white of Japan wax to the hard yellow of carnauba wax to the brownish black of bitumen wax. The hard waxes, such as carnauba, are often added to softer waxes, such as beeswax, for stiffening. Vegetable waxes generally contain fatty acids or alcohols along with the hydrocarbon series. Carnauba, one the hardest waxes, is obtained from the leaves of the wax palm, Copernicia cerifera, in Brazil. VARIETIES: Vegetable wax, bitumen wax, montan wax, candelilla wax, candilla wax, carnauba wax, Japan wax, rice wax, Brazil wax. bending bands IR ANALYSIS LAB Getty Conservation Institute, 6/1 5/84 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 = 4 cm-' = 200 Range = 4000--600 cm-' KBr pellet Ground with KBr Resolution Scans 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Vegetable Wax Wax 1 85 Infrared Reference Spectra Linseed Stand Oil Linseed Oil PROVENANCE Ashley's Art; Grumbacher SOURCE USA Yellow, transparent, liquid APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS 3600-3200 cm·' O-H stretching band 3000-2800 cm·' C-H stretching bands 1 750-1730 cm·' C=O stretching band 1 480-1300 cm·' C-H bending bands 1 300-900 cm·' C-O stretching bands 750-700 cm·' C-H torsion band Linseed oil is obtained from the seeds of the flax (Unum usitatissimum) plant. It is the most important drying oil in artists' media. The oil is commercially extracted from the crushed seed by hot water and steam. Cold pressing is a less efficient method for extraction, but it produces a higher-quality artist paint. Many types of aging, refining, and bleaching procedures have been used to purify the oil and make it dry faster. In the past, one method to refine linseed oil was to let it stand over time. Any mucilage or impurities settled out so that a clarified oil was produced. Modern stand oil is prepared by steam treatment, in the absence of oxygen, to produce a thicker and glossier oil. VARIETI ES: Linseed oil, raw, cold-pressed, refined, stand oil, blown, bodied, boiled, sun -refined, sun-bleached, flaxseed oil. IR ANALYSIS LAB Loyola Marymount University, 5/3/89 IR ANALYSIS CONDITIONS P-E 1 700 = 4 cm-' Microscope Dried film on KBr = 4000-700 cm-' Resolution Scans = 1 20 Range 40 360 320 280 240 20 1800 160 140 120 10 80 600 40 Linseed Oil Oil Poppyseed Oil (med i u m/slow d rying) Poppyseed Oil PROVENANCE SOURCE APPEARANCE Ashley's Art; Grumbacher USA Very light yellow, transparent, liquid Poppy oil is a naturally colorless transparent oil obtained from the seed of the opium poppy (Papaver somniferum). It comes primarily from India, Russia, France, and Asia Minor. Poppy oil dries slower than linseed oil and yellows less, so it was sometimes used with white pigments. It produced a soft, rubbery paint film with a long wet-in-wet work time that was popular with Impressionist painters. Thick layers of poppy oil paint films tend to wrinkle and crack upon aging. SYNONYMS: Poppyseed oil, poppy oil. CHARACTERISTIC IR ABSORPTION BANDS 3600-3200 cm·' O-H 3000-2800 cm·' C- H stretching bands C=O stretching band 1 750-1730 cm·' 1 480-1300 cm·' stretching band bending bands 1 300-900 cm·' C-H C-O stretching bands 750-700 cm·' C-H torsion band IR ANALYSIS LAB Loyola Marymount University, 4/26/89 IR ANALYSIS CONDITIONS P-E 1 700 Microscope Dried film on KBr Resolution = 4 cm-' Scans = 1 20 Range = 4000-700 cm-' 40 360 320 280 240 20 180 1600 1400 120 10 800 60 40 Poppyseed Oil Oil 1 86 Appendix I I Walnut Oil Walnut Oil PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Spectrum Naturals USA Walnut oil, pressed from the seeds of a walnut tree (Juglans regia), is pale in color and dries slower than does linseed oil. It also yellows and cracks less than linseed oil and dries faster than poppyseed oil. Nut oil was popular in Italy, the Netherlands, and Germany. Perhaps the reason that it has now fallen into disuse is its high cost and its tendency to turn rancid and putrid on storage. Slightly yellow, transparent, liquid SYNONYMS: Walnut oil, nut oil. 3600-3200 cm·' 3000-2800 cm·' 1 750-1730 cm·' 1480-1300 cm·' 1 300-900 cm·' 750-700 cm·' O-H stretching band C-H stretching bands C=O stretching band C-H CoO bending bands stretching bands C-H torsion band IR ANALYSIS LAB Loyola Marymount University, 6/28/89 IR ANALYSIS CONDITIONS poE 1700 Microscope 4 cm-' = 120 Range = 4000-700 cm-' Dried film on KBr Resolution = Scans 40 360 3200 280 240 2000 180 160 140 120 10 80 60 40 & Walnut Oil Rosin Oil (colopho ny) Balsam PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter Balsam is a general term used to designate the resinous exudate from Coniferae trees. These softer resins generally contain a large amount of Co. England Golden-yellow, transparent, chunks 3600-3200 cm·' 3100-2800 cm·' 1740-1640 cm·' 1650-1600 cm·' 1480-1300 cm·' 1300-900 em·' O-H C-H stretching band stretching bands C=O stretching bands C-C stretching band C-H bending bands CoO stretching bands essential oils that come from trees that grow in sandy soil near the sea. Balsam is a soft semiliquid consisting of terpenes of resinous character. Upon distillation, a liquid portion called turpentine and a solid residue called colo phony, or rosin, are produced. Balsams are often used in varnishes or as paint media; however, they deteriorate easily unless a harder resin is mixed with them. Rosin is often used in recipes for oil varnishes. VARIETIES: Balsam, colophony, rosin, Greek pitch, Venice turpentine, Strasbourg turpentine, Canada balsam, copaiba balsam, pine resin, larch balsam, larch turpentine, tolu balsam, natural balsam, oleoresin, ester gum, Bordeaux turpentine, Burgundy pitch, Burgundy resin, gum thus, olio d'Abezzo, Jura turpentine, copaiva balsam, silver fir turpentine. IR ANALYSIS LAB Getty Conservation Institute, 3/22/85 IR ANALYSIS CONDITIONS Digilab 15E/80 0.8 mg ground with KBr Resolution = 4 cm-' Scans = 200 Range = 400 00 cm-' KBr pellet 0-6 40 360 320 280 240 2000 180 160 140 120 10 80 60 400 Balsam Natural Resin 1 87 Infrared Reference Spectra Pine Resi n PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS (Pinus edulis, pinon) U.S. National Park Service, Colorado Las Animas County, Colorado, USA Yellow tears, sticky 3600-3200 cm" O-H stretching band 31 00-2800 cm" 1 740-1640 cm" C-H stretching bands 1 650-1 600 cm" C-C stretching bands 1 480-1300 cm" C-H bending bands 1 300-900 cm" CoO stretching bands C=O stretching band Balsam Balsam is a general term used to designate the resinous exudate from Coniferae trees. These softer resins generally contain a large amount of essential oils that come from trees that grow in sandy soil near the sea. Balsam is a soft semiliquid consisting of terpenes of resinous character. Upon distillation, a liquid portion called turpentine and a solid residue called colophony, or rosin, are produced. Balsams are often used in varnishes or as paint media; however, they deteriorate easily unless a harder resin is mixed with them. The United States, France, and Spain are the largest producers of balsams. VARIETIES: Balsam, colophony, rosin, Greek pitch, Venice turpentine, Strasbourg turpentine, Canada balsam, copaiba balsam, pine resin, larch balsam, larch turpentine, tolu balsam, natural balsam, oleoresin, ester gum, Bordeaux turpentine, Burgundy pitch, Burgundy resin, gum thus, olio d'Abezzo, Jura turpentine, copaiva balsam, silver fir turpentine, pine resin. IR ANALYSIS LAB Getty Conservation Institute, 7/24/90 IR ANALYSIS CONDITIONS Digilab 1 5EtSO KBr micropellet Ground with KBr Resolution = 4 cm-' Scans = 200 Range = 4000-600 cm-' 240 20 180 160 140 120 10 80 600 40 Balsam Natu ral Resin Copal, Manila Copal PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Unknown Light amber, opaque, chunks 31 00-2800 cm" O-H stretching band C-H stretching bands 1 740-1 640 cm" C=O stretchi ng band 3600-3200 cm" 1 650-1 600 cm" C-C 1 480-1 300 cm" C-H stretching band bending bands 1 300-900 cm" CoO stretching bands Copal is a term given to a large variety of hard natural resins obtained directly from trees or as fossil resins. They have a large range of solubility and color (from colorless to a bright yellow-brown). The hardest copal resin is Zanzibar; Sierra Leone, kauri, and Congo are of medium hardness; Manila and Borneo are soft copals. The oldest resins are the hardest. Copal resins may be purchased as large lumps or small tears. Congo copal is often used in commercial spirit varnish manufacture today. Co pal resins have also been used as oil varnishes. They tend to darken and become insoluble with age. VARIETIES: Zanzibar, Demerara, Benguela, Sierra Leone, Mozambique, red Angola, white Angola, Congo, kauri, Manila, Pontianak, Madagascar, Accra, Loango, Gaboon, bastard Angola, Borneo, Singapore, South American, Cochin, Brazilian, Benin, swamp gum, kauri gum, bush gum, Manila nubs, old bold Pontianak. IR ANALYSIS LAB Getty Conservation Institute, 1 /28/94 IR ANALYSIS CONDITIONS Spectra-Tech IR�S Microscope Bulk sample on BaF, Resolution = 4 cm-' Scans = 50 Range = 4000-700 cm-' 60 40 Copal Natural Res i n 1 88 Appendix I I Dammar Dammar PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Unknown Beige, translucent, chunks 3600-3200 cm" 31 00-2BOO cm" 1 740-1640 cm" 1 650-1 600 cm" O-H C-H stretching band stretching bands C=O stretching band C-C stretching band 1 4BO-1300 cm" C-H bending bands 1 300-900 cm" CoO stretching bands Dammar, the palest natural resin, is obtained from Dipterocarpaceae (genus Shorea or Hopea) trees growing in Malaysia and Indonesia. The soft, viscous, highly aromatic resin oozes readily from incisions in the bark and dries to become transparent, brittle, odorless lumps that are sorted into the following grades: pale (A), yellow (B), amber (C), and dust. To prepare as a varnish, dam mar pieces are placed in a cheesecloth bag partially submersed in turpentine. After a few hours, the dammar is dissolved and any residual material remaining in the bag is thrown out. This produces a high-quality, clear varnish for paintings. SYNONYMS: Damar, Malay dammar, Mata Kuching, cat's eye dammar, penak, gum batu, hitam, Batavian dam mar, Singapore dammar, Borneo dam mar, Pontianak dam mar, black dam mar, Pedong, East India dam mar, grade A Batavia, no.l Singapore, Bata gum. IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Digilab 1 5E/BO KBr pellet Ground with KBr Resolution = 4 cm-' Scans = 200 Range = 4000-600 cm-' 40 360 320 280 240 20 180 160 140 120 10 80 600 40 Dammar Natu ral Resin Elemi Elemi PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Unknown Light yellow, opaque, paste 3600-3200 cm" O-H stretching band 31 00-2BOO cm" C-H stretching bands 1 740-1 640 em" C=O stretching band 1 650-1 600 cm" C-C stretching band 1 4BO-1300 cm" C-H bending bands 1 300-900 cm" CoO stretching bands Elemi is a resin derived from trees of the family Burseraceae. Because of the high oil content of the elemis, the term was used to describe oleoresins in the seventeenth and eighteenth centuries. Now the term usually describes Manila elemi, which originates in the Philippines and is gathered from Canarium communis. This resin is extremely soft and has a very pungent odor. Elemi has been used in varnishes, but the components responsible for its initial malleability (mono- and sesquiterpenoids) evaporate, and it eventually hardens. Elemi has been used in printing inks, textile coatings, paper coatings, perfume bases, and waterproofing. SYNONYMS: Elemi gum, Luzon, Manila elemi, Nauli elemi, Canarium. IR ANALYSIS LAB Getty Conservation Institute, 1 /28/94 IR ANALYSIS CONDITIONS Spectra-Tech IR I lS Microscope = 4 cm-' Bulk sample on BaF, = 4000-700 cm-' Resolution Scans = 50 Range 60 40 Elemi Natu ral Resin 1 89 Infrared Reference Spectra Mastic Mastic PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter & Co. Chios, Greece Hard, pale yellow, tears 3600-3200 cm·' 31 00-2800 cm·' O-H C-H stretching band stretching bands 1 740-1640 cm·' C=O stretching band 1 650-1600 cm·' C-C 1 480-1300 cm·' C-H bending bands 1300-900 cm·' CoO stretching bands Mastic is produced by a Pistacia lentiscus tree, which grows in southern Europe and northern Africa. The resin collected from the island of Chios has a reputation for highest quality. Mastic is sold commercially in small, transparent "tears" of a pale straw color. The resin is soluble in alcohol but insoluble in petroleum ethers. It is used as a varnish for oil paintings and as an additive in an oil medium called megilp. As with dammar, mastic varnish is prepared by placing the resin bits in a gauze bag suspended in solvent. Mastic varnishes yellow and become insoluble with time. SYNONYMS: Chios mastic, Indian mastic, khinjak, Turkish mastic, pistacia galls, Bombay mastic. stretching band IR ANALYSIS LAB Getty Conservation Institute, 1 1 /5/90 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 KBr pellet = Inside portion ground with KBr 4 cm-' Resolution Scans = 200 Range = 4000--600 cm-' 40 360 320 280 240 20 180 160 140 120 10 800 600 40 & Mastic Natu ral Resi n Sandarac Sandarac PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter Co. Sandarac comes from Callitris quadrivalvis, a small tree that grows in northern Africa and Australia. The resin comes in pale yellow lumps or sticks that are hard, brittle, and powdery on the surface because of oxidation. It is soluble in alcohol and hot turpentine and forms a hard white film that becomes darker and redder with age. Sandarac spirit varnishes are often sold as retouching varnishes because they dry very quickly. Northern Africa Hard, yellow, lumps with powdery surface 3600-3200 cm·' O-H stretching band 31 00-2800 cm·' C-H stretching bands 1 740-1640 cm·' C=O stretching band C-C stretching band 1 650-1 600 cm·' 1 480-1300 cm·' C-H bending bands 1 300-900 cm·' CoO stretching bands SYNONYMS: Sandarac, Berenice, Mogador, gum sandarac, gum juniper, white gum, Cyprus pine, Australian pine gum. IR ANALYSIS LAB Getty Conservation Institute, 3/22/85 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 KBr micropellet = 200 Ground with KBr Resolution = 4 cm-' Scans Range = 4000--600 cm-' 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Sandarac Natu ral Resin 1 90 Appendix I I Shel lac (med i u m , flake-button) Shellac PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS J. Paul Getty Museum Paintings Conservation N/A Amber, transparent, flakes 3600-3200 cm" O-H 31 00-2800 cm" C-H stretching bands C=O stretching band 1 740-1640 cm" stretching band 1 650-1600 cm" C-C 1 480-1300 cm" C-H bending bands 1 300-900 cm" C-O stretching bands Shellac is the resinous secretion of the lac insect Tachardia /acca. The insect feeds on a plant and converts the plant juice into the resin and red dye exudate. It comes almost entirely from India. The crude lac, seed lac, is gathered from the trees and crushed as !lraded. The lac is then washed, heated, and drawn into thin sheets. When cool, the sheets are broken into fragments for sale as flake shellac. Shellac colors range from a deep red to a pale gold. Shellac is soluble in alcohol and is used to obtain the high gloss on French polished furniture. VARIETIES: Shellac, baisakhi, jethwi, seed lac, stick lac, button lac, black button lac, kiri, garnet lac, orange flakes, lemon flakes, bleached shellac, refined shellac. stretching band IR ANALYSIS LAB Getty Conservation I nstitute IR ANALYSIS CONDITIONS Digilab 1 5E/80 KBr pellet = 4 cm-' Ground with KBr = 4000-500 cm-' Resolution Scans = 200 Range 240 20 Shel lac Natural Resin Cel lulose Nitrate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS ( 1 . 8% N) Lawrence Livermore Labs USA Colorless, transparent 3600-3200 cm" O-H stretching band 31 00-2800 cm" C-H stretching bands 1 660-1625 em" N-O stretching band 1 285-1 270 cm" N-O stretching band 1 480-1 300 cm" 1 300-900 cm" C-H C-O bending bands bending bands 890-800 cm" N-O bending band Cellulose Nitrate Some of the earliest synthetic resins were made from cellulose fibers. Cellulose nitrate was first made as a substitute for ivory and later was used for photographic film and as clear lacquers, adhesives, and high-gloss paints. Celluloid is a proprietary product of cellulose nitrate mixed with camphor as a plasticizer. Cellulose nitrate is inherently unstable and slowly decomposes at room temperature. UV light, heat, andlor high humidities can hasten its decomposition. Cellulose nitrate is still commercially available and is used as adhesives and coatings. VARIETIES: Celluloid, pyroxylin, airplane wing dope, nitrocellulose, guncotton , collodion, Duco, celloidin, celluidine, photoxylin. IR ANALYSIS LAB Getty Conservation Institute, 2/23/87 IR ANALYSIS CONDITIONS Digilab 1 5E/80 KBr micropellet Ground with KBr Resolution = 4 cm-' Scans = 200 Range = 4000-600 cm-' 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Cellulose Nitrate Synthetic Resin 1 91 I nfrared Reference Spectra Acryloid PROVENANCE 8-& 72: SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS methyl acrylate/ethyl methacrylate copolymer Acrylic Conservation Materials Ltd.; Rohm Haas USA Transparent, colorless, pellets 31 00-2BOO cm·' C-H 1 740-1640 cm·' C=O stretching band 1 4BO-1300 cm·' C-H stretching bands bending bands 1 300-900 cm·' C-O stretching bands Acrylic resins are a commercially important family of polymers that were first made in 1 901 and sold by Rohm Haas and Du Pont in the United States since the 1 930s. Acrylics have many popular uses. They are sold in solid form as glass substitutes under the names of Plexiglas and Lucite; they are also used as adhesives, varnishes, and paint media (Acryloid F- l 0, Lucite 44, Acryloid B-72). Bocour Artists Colors began selling Magna acrylic-based artist paints in 1 949. While the resins are generally soluble in mineral spirits and turpentine, they may also be dispersed in water to form acrylic emulsions such as Rhoplex AC-234. Uquitex, an acrylic emulsion paint, was first marketed in 1 954. & VARIETIES: Plexiglas, Lucite, Acryloid, Paraloid, Rhoplex, Uquitex. IR ANALYSIS LAB Getty Conservation Institute, 4/30/90 IR ANALYSIS CONDtTIONS Digilab 1 5 E/BO KBr pellet Ground with KBr Resolution = 4 cm-' Scans = 200 Range = 4000-500 cm-' 40 3600 320 280 240 20 180 160 140 120 1000 80 60 40 Acrylic Polyester PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Synthetic Resin 12F Polyester American Hoechst Corp. USA White, translucent, fibers 31 00-2BOO cm·' C-H stretching bands 1 740-1640 cm·' C=O stretching band 1 620-1420 cm·' aromatic bands 1 4BO-1300 cm·' C-H C-O 1 300-900 cm·' Polyester resins are a special type of alkyd resins. When catalyzed, they can harden at room temperature and pressure with very little shrinkage to produce a clear, colorless filament, block, or film. They are often used for encapsulating and embedding samples and objects. One type of polyester, polyethylene terephthalate, is used to make Mylar and other strong, moisture-resistant films, as well as to make Dacron, an important textile fiber. SYNONYMS: Polyester, Dacron, Mylar, Bio-Plastic, Caroplastic, Castolite, Vestopal, Terelene, Cronar. bending bands stretching bands IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Spectra-Tech IR�S Microscope = 1 00 = 4000-700 cm-' Bulk sample on BaF, Resolution = 4 cm-' Scans Range 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Polyester Synthetic Resin 1 92 Appendix I I Poly(vinyl acetate)(PVAC) Poly(vinyl acetate) PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Conservation Materials Ltd_ USA Transparent, colorless, pellets 1 750-1 650 cm·' C-H stretching bands C=O stretching band 1 480-1300 cm-' C-H 1 300-900 cm·' CoO stretching bands C-H torsion band 3 1 00-2800 cm·' 750-700 cm·' Poly(vinyl acetate) (PVAC) was first produced in 1 9 1 2 and was used as an artists' medium in 1 938. Water-based emulsions, or latex, paints have been used as house paints as well as artists' media. Vinyl polymer resins produce clear, hard films and are also used as coatings, hot melts, and adhesives. Other types of vinyl polymers include polyvinyl butyral, polyvinyl chloride, polyvinylidene chloride, and polyvinyl alcohol. VARIETIES: Poly(vinyl acetate), Vinylite, Vinylac, Elmer's glue, Vinamul, Mowilith, AYAT. bending bands IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Digilab 1 5 E/80 KBr pellet Ground with KBr Resolution = 4 cm-' Scans = 200 Range = 4000-500 cm-' 40 360 320 280 240 20 180 160 140 120 10 80 60 40 371: 371 Poly(vi nyl acetate) B EVA Synthetic Resin ethylene/vi nyl acetate copolymer mixed with polycyclohexanone BEVA PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Australian Museum; Adam Chemical Co. Australia White, opaque gel, dried to film 31 00-2800 cm·' C-H 1 750-1 650 cm·' C=O stretching band stretching bands 1 480-1 300 cm·' C-H 1 300-900 cm·' CoO stretching bands C-H torsion band 750-700 cm·' BEVA 371 is a thermoplastic, elastomeric polymer mixture. It is composed of Elvax (ethylenelvinyl acetate [EVA] copolymer), Ketone Resin N (polycyclohexarione), A-C copolymer (EVA), Cellolyn 21 (phthalate ester of hydroabietyl alcohol), and paraffin. It is an opaque gel at room temperature and has a melting point of 50-55 °C. It is soluble in naphtha, toluene, acetone, and alcohol. BEVA produces a matte, waxy finish and is used as a consolidant for paintings and textiles. bending bands IR ANALYSIS LAB Getty Conservation Institute, 4/30/90 IR ANALYSIS CONDITIONS Digilab 1 5E/80 Attenuated total reflectance (ATR) Free film = 4000-500 cm-' Resolution = 4 cm-' Scans = 200 Range 40 360 320 280 240 20 180 160 140 120 10 80 60 40 B EVA 371 SynthetiC Resin 1 93 I nfrared Reference Spectra Polycyclohexanone Polycyclohexanone PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS H . Lanke Unknown Polycyclohexanone resins are important because they are soluble in turpentine. This allows them to be mixed with or used instead of natural resins as varnishes. They resemble dammar closely but are harder and remain practically colorless. Some studies have shown, however, that solubility may be lost over time. White, translucent, chunks OTHER VARIETIES: AW-2, MS2A, ketone N, BASF N, Laropal K-80. 3600-3200 cm" O-H stretching band 31 00-2800 cm" C-H stretching bands 1 750-1650 cm" C=O stretching band 1 480-1300 cm" C-H bending bands 1 30D-900 cm" C-O stretching bands 75D-700 cm" C-H torsion band IR ANALYSIS LAB Getty Conservation Institute, 1 0/8/84 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 KBr pellet Ground with KBr = 4000-600 cm-' Resolution = 4 cm-' Scans = 200 Range 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Polycyclohexanone Synthetic Resin Polyamide Polyamide PROVENANCE SOURCE APPEARANCE Scientific Polymer Products, Inc. (catalog no. 385) USA Polyamides can be thought of as synthetic proteins because they are made by the polymerization of amino acids or lactams. Polyamides are thermoplastic resins that are characterized by their high degree of toughness, strength, and durability, along with their resistance to chemicals and heat. They are manufactured as bristles, libers, molding powders, sutures, adhesives, and coatings. The most important examples polyamides are the various kinds of nylon. 01 White, powder VARIETIES: Nylon, Versamid, Nylon-6, soluble nylon. CHARACTERISTIC IR ABSORPTION BANDS 3400-3250 cm" N-H 31 00-2800 cm" C-H stretching bands C=O stretching band 1 700-1630 cm" 1 620-1550 cm" 1 480-1300 cm" N- H C-H stretching band bending band bending bands IR ANALYSIS LAB Getty Conservation Institute, 1 0/1/84 IR ANALYSIS CONDITIONS Digilab 1 5 E/80 = 4 cm-' = 200 Range = 4000-600 cm-' KBr pellet Ground with KBr Resolution Scans 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Polyamide Synthetic Resin 1 94 Appendix II Chalk: calcium carbonate, GaG0 3 Calcium Carbonate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Calcium carbonate is found in many natural forms such as chalk, limestone, marble, and seashells. It can be found worldwide and ranges in color (because of impurities) from white to gray to yellow. The pigment is prepared by grinding the stone or shell with water and by levigating to separate the coarser material. Artificial chalk is known as precipitated chalk and is whiter and more homogeneous than natural chalk. Pearl white is made from calcined oyster shells. Calcium carbonate reacts with acids to evolve carbon dioxide. France White, opaque, powder 1490-1370 cm·' 910-850 cm"' CO;O-C-O stretching band bending band SYNONYMS: Calcium carbonate, chalk, pearl white, oystershell white, marble, limestone, whiting, lime white, aragonite, calcite, marl, travertine, CI Pigment White 18. IR ANALYSIS LAB Getty Conservation I nstitute, 10/15/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S �4 � 200 Range � 4000-800 cm-' Microscope Bulk sample on BaF, cm-' Resolution Scans Comment: baseline corrected 40 360 320 280 240 20 180 10 80 60 40 Calcium Carbonate Gypsu m : White calciu m sulfate, dihydrate, GaS04 '2H 20 Calcium Sulfate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Unknown VARIETIES: Calcium sulfate, anhydrite, gypsum, plaster, terra alba, alabaster, hydrated calcium sulfate, mineral white, stucco, Keene's cement, Martin's cement, Mack's cement. White, powder 1 140-1080 cm"' -620 cm"' 3700-3200 cm·' Calcium sulfate can be commonly found in three forms: anhydrous (anhydrite), dihydrate (gypsum), and hemihydrate (plaster of Paris). Anhydrite is a colorless, inert pigment that is often a component in gesso grosso, while pure calcium sulfate dihydrate is found in gesso sottile. Gypsum is also used as a filler and as a base for lake pigments. asymmetric SO.'" stretching band SO.'" bending band (not shown) antisymmetric and symmetric O-H stretching bands IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Digilab 15E/80 � 4 cm-' � 200 � 4000-500 cm-' KBr pellet Ground with KBr Resolution Scans Range 10 80 60 40 Calcium Sulfate White 1 95 I nfrared Reference Spectra Plaster: calcium sulfate, hemihydrate, CaS04 °1/2H 20 Calcium Sulfate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Germany VARIETIES: Calcium sulfate, anhydrite, gypsum, plaster, terra alba, alabaster, hydrated calcium sulfate, mineral white, stucco, Keene's cement, Martin's cement, Mack's cement. White 1 1 40-1080 cm" Calcium sulfate can be commonly found in three forms: anhydrous (anhydrite), dihydrate (gypsum), and hemihydrate (plaster of Paris). Anhydrite is a colorless, inert pigment that is often a component in gesso grosso, while pure calcium sulfate dihydrate is found in gesso sottile. Gypsum is also used as a filler and as a base for lake pigments. asymmetric SO." stretching band -620 cm" SO;- bending band (not shown) 3700-3200 cm" antisymmetric and symmetric O- H stretching bands IR ANALYSIS LAB Getty Conservation Institute, 10/15/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution Scans Comment: baseline corrected 40 360 3200 280 240 2000 180 160 140 120 10 80 600 40 Calcium Sulfate Wh ite Clay PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Germany White O-H stretching bands 3700-3200 cm" 1 1 00-1000 cm" asymmetric Si-O-Si stretching bands 9 1 0-830 cm" Si-O stretching bands Many types o f clay naturally occur around t h e world. They are prinCipally composed of hydrated aluminum silicate. Small amounts of other minerals can change the color (white, yellow, brown, or red) and texture of the clays. Clay is usually formed by the weathering of aluminum-bearing rocks, such as granite. When pure, china clay (kaolin) is a fine, white, amorphous powder that becomes very plastic when water is added. When heated to high temperatures, clays became hard because of the loss of water and are used to make pottery, porcelain, and bricks. Clay is also used as a filler and whiting in paints and grounds. VARIETIES: China clay, kaolin, modeling clay, porcelain clay, Tonerde, fuller's earth, white bole, bolus alba, terra alba, pipe clay, Bouvigal white, Rouen white, Spanish white, feldspar, ball clay, bentonite, stoneware clay, kaolinite, illite, montmorillonite, halloysite, argilla. IR ANALYSIS LAB Getty Conservation Institute, 10/15/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution Scans Comment: baseline corrected 40 360 3200 280 2400 20 180 160 140 Clay 600 40 Wh ite 1 96 Appendix II Silica : Si0 2 Silica PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Silica is widely available because it makes up one of the largest portions of the earth's crust. In its purest form, silica, or silicon dioxide, occurs as quartz. The more common, but less pure, forms are quartzite, sandstone, and sand. The fossil form of silica is diatomaceous earth. All forms of silica are inert, unaffected by heat, insoluble in strong acids (except hydrofluoric), and slowly attacked by strong alkalis. Silica is not commonly used as a pigment; however, it is found in grounds, primers, and wood fillers. Silica is used in the manufacture of glass, ceramics, and enamelware. USA White 1 1 00-1000 cm" asymmetric Si-O-Si stretching band VARIETIES: Silica, silicon dioxide, quartz, silex, diatomaceous earth, sand, flint, chalcedony, opal, agate, diatomite. IR ANALYSIS LAB Getty Conservation Institute, 1 0/1 6/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' = 200 = Microscope Bulk sample on BaF, Resolution Scans Range 4000-800 cm-' Comment: baseline corrected 60 40 40 360 320 280 240 20 180 Sil ica Wh ite Barium Sulfate : BaS04 Barium Sulfate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Barium white is obtained naturally from t h e mineral barite. I t c a n also b e made artificially by a process discovered in the late nineteenth century. The artificially prepared barium sulfate is called blanc fixe. It is a white, opaque pigment composed of zinc sulfide and barium sulfate. The mixture of the two components is so intimate that it is hard to distinguish microscopically. It is an inert, transparent pigment that is often used as a filler or as a base for lake pigments. Germany White sot 1 200-1050 cm" asymmetric 3700-3200 cm" O-H stretching bands stretching bands SYNONYMS: Barium sulfate, baryte, barite, terra ponderosa, blanc fixe, permanent white, silver white, Albilith, Becton white, Orr's white, Permalba, baryta white, Constant white, Schwerspatweiss, heavy spar, CI Pigment White 22. IR ANALYSIS LAB Getty Conservation Institute, 1 0/1 5/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S Microscope = 4 cm-' = 200 Range = 4000-800 cm-' Bulk sample on BaF, Resolution Scans Comment: baseline corrected, contains carbonate ( 1 450 cm-') and hydrocarbon (3000-2800 cm-') impurities 40 360 320 280 240 20 180 160 140 Bari um Sulfate 60 40 White 1 97 I nfrared Reference Spectra Indigo PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Indigo is a natural, dark blue dye obtained from the Indigofera tinc/oria plants native to India, Java, and other tropical areas. Synthetic indigo, first produced in 1 880, has almost entirely replaced the natural dyestuff. The natural material is collected as a precipitate from a fermented solution of the plant. It is a fine powder that may be used directly as a pigment in oil, tempera, or watercolor media, but it is more commonly used as a textile dye. The exposed material can fade rapidly in strong sunlight. H. Schweppe Java Blue, powder 3400-3200 cm" 31 00-2800 cm" 1 700-1 550 cm" 1 620-1420 cm" N-H C-H c=o stretching band stretching bands SYNONYMS: Indigo carmine, intense blue, indico, indican, anil, anneill, blue ynde, CI 73000. stretching band aromatic bands IR ANALYSIS LAB Getty Conservation Institute, 4/29/93 IR ANALYSIS CONDITIONS Spectra-Tech IR�S Microscope = 200 Bulk sample on BaF, 4 cm-' == Resolution Scans Range 4000-800 cm-' Comment: baseline corrected 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Indigo Blue Phthalocyanine Blue (royal blue PB1 53) Phthalocyanine Blue PROVENANCE SOURCE Kremer-Pigmente Copper phthalocyanine (phthalocyanine blue) is a synthetic organic pigment that was first introduced in 1 935. It is usually adsorbed on an aluminum hydrate base to form a deep blue color. Other colors are achieved by varying the formulation-i.e., chlorinated copper phthalocyanine produces a green colorant. Phthalocyanine colors are important commercial pigments because of their light and chemical stability. They are used in enamels, automotive paints, plastics, and inks. Germany APPEARANCE Blue, powder CHARACTERISTIC IR ABSORPTION BANDS 31 00-2800 cm" C-H stretching bands 1 700-1 550 cm" C=N stretching band 1 620-1420 cm" aromatic bands 1 480-1300 cm" C-H bending bands 1 330-1 1 00 cm" CoN stretching bands SYNONYMS: Heliogen blue, Monastral blue, phthalocyanine green, Winsor blue, CI Pigment Blue 1 5. IR ANALYSIS LAB Getty Conservation Institute, 1 0/1 3/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' Microscope Bulk sample on BaF, Resolution Scans = 200 Range = 4000-800 cm-' Comment: baseline corrected 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Phthalocyanine Blue Blue 1 98 Appendix I I Prussian Blue PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Germany SYNONYMS: Prussian blue, Turnbull's blue, Paris blue, Saxon blue, Milori blue, Chinese blue, bronze blue, Berlin blue, American blue, Antwerp blue, steel blue, mineral blue, iron blue. Blue -2100 cm ' Prussian blue, synthetically produced ferric ferrocyanide, was discovered in 1 704. Its finely divided particles are a deep blue. It is transparent, has high tinting strength, and is stable to light and high temperatures; but it turns brown in the presence of alkalis. It is used in paints and printing inks. [Fe(C=N),J'" ion stretching band IR ANALYSIS LAB Getty Conservation Institute, 1 0/1 3/92 IR ANALYSIS CONDITIONS Spectra-Tech IRIlS = = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, 4 cm-' Resolution Scans Comment: baseline corrected 40 360 320 2800 240 2000 1800 160 140 120 1000 80 60 40 Prussian Blue Blue Ultramarine PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Unknown Blue, opaque, powder 1 1 50-950 cm" overlapping stretching bands for Si-O-Si, 2340 cm" and Si-O-AI sulfur ion stretching band that occurs in some natural ultramarines The pigment ultramarine can be prepared from a natural semiprecious stone, lapis lazuli. The pigment is composed of silicon, aluminum, sodium, sulfur, and oxygen. A commercial process for synthetic ultramarine, developed in the 1 820s, produces a very pure, deep, fine-particle material. Variations in the process give a wide range of shades of blues, violets, and reds. The pigment is stable to light but is affected by acids. SYNONYMS: Lapis lazuli blue, lazurite, ultramarine blue, bleu d'azur, ultramarine ash, French ultramarine, ultramarine red, ultramarine violet, ultramarine green, French blue, new blue, permanent blue, oriental blue, Gmelin's blue, Guimet's blue. IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Spectra-Tech IRIlS = 4 cm-' = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution Scans 40 3600 320 2800 240 20 180 160 140 Ultramarine 600 40 B l ue 1 99 Infrared Reference Spectra Malachite : basic copper carbonate, CuC03 ·Cu(OH) 2 Basic Copper Carbonate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Forbes Collection Basic copper carbonate naturally occurs in two mineral forms, azurite (blue: 2CuCO,·Cu(OH),) and malachite (green: CuCO,·Cu(OH),). The two minerals usually occur together. Pigments are prepared by careful selection, grinding, washing, and levigation. Both are sensitive to acids. The synthetic pigment is called green verditer and is a pale greenish blue. Unknown Green, opaque, powder 1530-1350 cm·' 900--650 cm·' 3700-3100 cm·' 1100-1000 cm·' CO,'· o-co SYNONYMS: Basic copper carbonate, azurite, mountain blue, malachite, mountain green, blue verditer, blue bice, green verditer, green bice, mineral green. stretching bands bending bands O-H stretching bands O-H bending bands IR ANALYSIS LAB Analytical Answers, Inc., 1 2/96 IR ANALYSIS CONDITIONS Bio- Rad FTS 40 = 4 cm-' = 50 = 4000-750 cm-' Microscope Bulk sample on BaF, Resolution Scans Range 40 360 320 280 240 20 1800 1600 60 40 Basic Copper Carbonate G reen Copper Acetate PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS Kremer-Pigmente Germany Green 1660-1550,1450-1400,-1050,-1020,-925 cm·' acetate ion stretching and bending bands 3550-3200 cm·' antisymmetric and symmetric O-H Basic copper acetate i s a greenish blue crystalline powder that i s called verdigris. Its preparation, known since ancient times, involves exposing copper to vapors of fermenting solutions. The crystals are soluble in water and acids and are toxic. The pigment is unstable and can leave a black residue upon decomposition. When combined with terpenoid resins, such as Venice turpentine, verdigris forms copper resinate. Verdigris is used as a pigment and a textile dye. SYNONYMS: Copper acetate, verdigris, copper resinate, crystals of Venus, cupric acetate. stretching bands IR ANALYSIS LAB Getty Conservation Institute, 1 0/14/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S =4 = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution cm-' Scans 400 3600 320 280 240 20 180 Copper Acetate 60 40 G reen 200 Appendix I I Madder (CI Natu ral Red PROVENANCE SOURCE APPEARANCE 8) H. Schweppe Madder Madder is a natural red dye obtained from the root of the Rubia /inc/orium plant, which is cultivated in Europe and Asia Minor. The dye contains three principal colorants: alizarin (red), purpurin (red), and xanthine (yellow). The dye is extracted from the dried, powdered root as a precipitate when it is boiled in water. Alum lakes of madder, madder lake, and rose madder were used as artists' pigments. Madder was commonly used to dye textiles until synthetic alizarin was developed in 1 868. Germany Red, powder SYNONYMS: Madder lake, alizarin (natural), CI Pigment Red 83. CHARACTERISTIC IR ABSORPTION BANDS 3600-3200 cm"' O-H stretching band 31 00-2800 cm"' C-H stretching bands 1 740-1 640 cm"' C=O 1 620-1420 cm"' 1 480-1300 cm"' aromatic bands 1 300-900 cm"' CoO stretching bands C-H stretching bands bending bands IR ANALYSIS LAB Getty Conservation Institute, 2/24/92 IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' Microscope Bulk sample on BaF, = Resolution Scans = 200 Range 4000-800 cm-' Comment: baseline corrected 40 360 320 60 40 Madder Red Dragon's Blood Dragon's Blood PROVENANCE SOURCE APPEARANCE CHARACTERISTIC IR ABSORPTION BANDS A. F. Suter & Co. Unknown Dragon's blood is a transparent, red, resinous exudation from the rattan cane palm, Calamus draco, that grows in eastern Asia. It is soluble in alcohol but insoluble in water. The color is fugitive when exposed to air but remains when protected by a resin film. It is used in stain varnishes, marble coloring, paints, and lithography. Red, resinous, powder SYNONYMS: Called 3600-3200 cm"' O-H stretching band 31 00-2800 cm"' C- H stretching bands 1 740-1 640 cm"' 1 650-1600 cm"' C=O stretching band C=C stretching band 1 620-1420 cm"' aromatic bands 1 480-1300 cm"' C-H bending bands 1 300-900 cm"' CoO stretching bands cinnabaris by the ancients and by Pliny. IR ANALYSIS LAB Getty Conservation Institute IR ANALYSIS CONDITIONS Spectra-Tech IR�S = 4 cm-' = 200 Range = 4000-800 cm-' Microscope Bulk sample on BaF, Resolution Scans 40 360 320 280 240 20 180 160 140 120 10 80 60 40 Dragon's Blood Red G l ossary absorbance The amount of light absorbed by the sample at any specific wavelength. The intensity of a ' band in absorbance u n its is d i rectly proportional to the concentration of sample responsible for the absorption band at that wave length. I t is useful to plot the y-axis of I R spectra in absorbance u n its (absorption bands ascending, or peaks) for q u antitative analysis meth­ ods, spectral searching, and su btraction routines. absorption The absorption of specific wavelengths of energy by an atom or molecu le that results in an el ectron ic, vibrational, translational, or rotational motion. absorption bands (or peaks) A spectral absorption recorded as a band (transmittance u n its) or as a peak (absorbance u n its) . ampl itude attenuated total reflection (ATR) The i ntensity, vol u m e , o r magnitude o f a wave. An older, although sti l l - used , name for i nternal reflection spectroscopy. See i nternal reflecti o n . baseline The position of a spectral c u rve when the sam ple is n o t absorbing a n y radiatio n . U nder optimized conditions, the baseline occurs at 1 00 % transmittance, or 0 . 0 absorbance. blackbody radiation A radiator that e m its a conti nuous spectrum of wavelengths with no missing freq uencies. The term is based on the thermodynamic principle that any material that emits all wave­ lengths when it is hot m ust absorb all wavelengths when it is cold. The color of a totally absorbing material is black, and thus the perfect emitter was given the name blackbody (Crooks 1 978) . combi nation band A weak absorption band that is the product of the com b i n.ation of two, or even three, strong vibrational q uanta. The frequency of the band is equal to the sum of the freq u e n ­ c i e s of the originating b a n d s . A combi nation b a n d f o r a strong absorption b a n d at 1 600 c m - 1 and one at 1 2 50 c m - 1 would occ u r at 2 850 c m - 1 . computer search routine A comp uterized li brary search program typically based on the comparison of peak position and intensity of an u n known spectrum versus those i n thousands of reference spectra. Conne's advantage An advantage of FT- I R spectroscopy over dispersive I R , due to FT- I R ' s wavelength accu racy. Because in FT- I R a laser is used to cal ibrate the wavelengths in the spectru m , accu racy is ensured without a n y external calibrati o n . T h i s accu racy is i m portant f o r the comparison of spectra to one another, as is done in l i b rary searc h i n g and spectral sub­ traction routines. correlation chart A chart showing most common IR group freq ue ncies and their positions, ranges, and rela­ tive intensities. 202 Glossary deconvol ution A mathematical routine that operates on two or more overlapping bands, reducing the l i n e width of i ndivid ual components, thereby i m p roving the spectral resolutio n . degrees of freedom Allowed molecular motions-translational, rotati onal, a n d vibrational-with i n a molecule. The degrees of freedom depend on the n u m ber of atoms i n a molecule and its symm etry. detector diffraction An instrument or cell capable of converting rad iant energy i nto an electrical signal. A physical phenomenon i n w h ich radiation is dispersed or scattered when it passes by a sharp edge. I n IR m icrospectroscopy, diffraction may occ u r when the beam passes through the apertures. diffuse reflection (DRIFTS) A n IR analysis tec h n i q u e i n which the IR beam is diffusely reflected from the su rface of a sam ple. It may be used with rough or porous samples, such as samples collected on silicon carbide paper. d ispersion electromagnetic spectrum Separation of rad iant ene rgy into d iscrete wavelengths. The total range of electromagnetic radiatio n . The IR region is one small part of the elec­ tromagnetic spectru m . electronic transition A change i n the energy levels o r spin d i rections of electrons with the absorption o r emis­ sion of energy. far infrared (far- I R or F I R) The region of the electromagnetic spectrum (500-20 cm- 1 ; 20-500 I-l-m) that falls between the m i d - I R and the m icrowave region . The far- I R region is well suited to the study of organometal lic or i norganic compounds and is useful in the identification and dif­ ferentiation of many m i nerals and colorants. Fourier transform frequency (v) A complex mathematical function that converts an i nterferogram into a spectru m . The n u m be r o f oscillations, or waves, p e r u n i t time-i . e . , cycles p e r seco n d . T h e term i s also used t o deSignate t h e specific wave n u mber o f an absorption band. functional group A group of two or more atoms with i n a molecule that i m part a given characteristic to that molecule ( e . g . , hydroxyl, carbonyl). Most functional groups absorb I R radiation at repro­ ducible freq ue ncies, known as group freq uencies. fundamental The frequency correspon d i n g to a first-order vibration of the molecule. The fundamental vibration will produce the strongest absorption band for a given transition of a functional gro u p . group freq uency A freq uency that is associated w i t h a particular functional group ( i . e . , carbo nyl, C=O) and is c o m m o n t o all molecules contained i n that gro u p . G r o u p freq uencies are used t o deter­ m i n e the chemical class of a material. i nterferogram A plot of intensity versus d isplacement of an optical light path . This plot is the measured result of radiation that has passed through an interferometer; it may be converted to a spectrum using a Fourier transform mathematical process. interferometer An apparatus with a moving m i rror and a fixed m i rror that can modulate a spectrum into an interferogram, thus allow i n g all freq ue ncies to be measured at one time. internal reflection spectroscopy (I RS) An IR analysis tec h n i q u e i n which the sam ple is placed i n optical contact with a high­ refractive - i ndex element. When an IR beam is passed through the eleme nt, a slight pene­ tration of the beam i nto the sam ple occurs. This tech n i q u e is usefu l for su rface analysis. G lossary microspectrophotometer 2 03 An I R m icroscope coupled to an I R spectrometer, to compose a system capable of acq u i r­ i n g IR spectra of m icroscopic size samples. m i d-infrared ( m i d - I R or M I R) The region in which most fundame ntal vi brations for organic molecules occu r (4000-500 cm- 1 ; 2 . 5-20 f.Lm ) . T h i s region can b e subd ivided i nto t h e group frequency region (4000-1 300 c m -1 ; 2 . 5-8.0 f.Lm) and the fingerprint region ( 1 300-500 c m - 1 ; 8 . 0-20 f.Lm). modulate To change a wave fo rm . An i nterferometer modulates, or changes, the wave form of light from a s i n e pattern to an interferogram pattern . monochromator A device that separates light i nto its spectrum of freq uencies. I n dispersive I R spectrom­ eters, a monochromator i s used to disperse the rad iation prior to passi n g each wavelength through the sam ple. m u ltiplex advantage (Fel lgett's advantage) The major advantage of FT- I R spectrometers over d ispersive spectrometers. FT- I Rs mea­ sure all wavelengths of IR rad iation s i m u ltaneously, w h i l e dispersive spectrophotometers measure one resolution element at a time. Thus, an FT- I R can acq u i re a whole spectrum i n t h e time i t takes a d i spersive spectrometer t o collect o n e resolution element. near i nfrared (near- I R or N I R ) The IR region from 1 4,000 to 4000 c m - 1 (0.7-2 . 5 f.L m ) . Spectra gene rated i n the near- I R region consist entirely o f overto nes, combi nations, and combi nations o f overtones of fundamental vi bration modes from the m i d - I R region. n o i se Small, rapid fluctuations usually observed i n the baseline of the spectru m . Noise is associ­ ated with i nstrument conditions rather than being specific to a sample. overtone A weak vi brational transition occurri n g at approximately twice the freq uency of a strong fundamental absorption frequency. A n overtone band for a strong absorption band at 1 700 c m - 1 would occur at 3400 c m - 1 . path length The thickness of a measured medi u m . The absorption i ntensity is proportional to the path length of measurement. This relationship is often observed when a sam ple i s too thick and thus absorbs too strongly, p roducing satu rated absorption bands. qual itative quantitative reflectance Analysis used to determine what kind of material i s present. Analysis used to determine how m uch of a material is present. The amount of rad iation reflected from a sam ple. A n IR spectrum plotted in reflectance u n its can usually be converted to appear as a transmittance spectrum with the Kubelka­ M u n k or Kramers - K ro n i g transformations for diffuse reflection and specular reflection, respectively. reflection Radiation that bounces off the su rface of a material after contact. refraction The change in angle of a light path as it passes from one medium i nto another with a dif­ ferent refractive i n dex. resolution The abil ity of an i n strument to separate two closely occurring absorpti ons. T h i s abil ity i s a function of i nstrumental and spectral parameters such as detector sensitivity, absorption intensity, absorption freq uency, interferometer scan distance, and signal-to-noise ratio . rotational transition T h e rotation o f a molecule around its center o f mass with t h e absorption or emission of en ergy. 204 Glossary selection rule A rule that determ ines whether a given vibration w i l l be seen in the spectru m , based on the symmetry of the molecule. The primary selection rule, or req u i rement, for active IR absorptions is that the vibration m u st result i n a change i n the dipole moment of the molecule. signal-to-noise ratio source spectral l i n e The i n tensity of the recorded absorption band versus the inten sity of noise. A high-temperature body used to gene rate rad iant energy. Absorption related specifically to a q u antu m energy change. This absorption is never actu­ ally seen as a l i n e but rather as a band or peak . spectrophotometer An i nstrument for record i n g the i n tensity and frequency of spectral absorptions. Also sometimes referred to as a spectrometer. spectroscopy The study of the interaction of l i ght and matter. The term is also used to specify the tech­ n i q u e of record i n g and studying spectra. spectrum ( p I . , spectra) A recorded tracing of the amount of radiation absorbed at each frequency over a given spectral range of i n terest. specular reflection (external reflection) A type of reflection in which the reflection angle of a beam is eq ual to the i ncident angle, as i n a m i rror. s u btraction A mathematical routine for compari ng two spectra by su btracti n g the absorption bands of one from the other. It is useful for e l ucidating small changes between two similar spectra that may otherwise be overlooked. throughput advantage (Jacq u i not's advantage) An advantage of FT- I R over dispersive instru ments. A greater amount of rad iation reaches an FT- I R detector than reaches a detector for a dispersive i nstru ment, because of the lim itations of the monochromator slit. This greater energy throughput gives FT- I R more sen sitivity, which is often needed for reflection tech niques. translational tran sition The movement of an entire molecule to a new position i n space d u e to the absorption or em ission of energy. transmission transm ittance The passage of radiation through a material without its being absorbed or reflected. The amount of radiation transm itted through a sam ple. Transm ittance is equ ivalent to the logarithmic reCiprocal of absorbance. IR spectra are often pl otted with the y-axis givi n g percent transm ittance (absorption bands desce ndi ng) t o i nc rease the size of smaller absorption bands i n relation to more i n tense absorption band s . vibrational tran sitions The change i n b o n d angles or bond lengths w i t h i n a molecule d u e t o t h e absorption or em ission of energy. Molecular vibrations account for the strongest absorption bands i n an IR spectru m . wavelength wave n u mber (( 11A.)) The distance between two successive maxima or m i n i m a of a wave-i . e . , the length of one wave. The n u m ber of waves per u n i t length . Wave n u m ber u n its are commonly used in IR spec­ troscopy and are ex pressed i n cm -' . Suppliers Becton Dickinson, Acute Care, 1 Becton Dr., Franklin Lakes, NJ 074 1 7; ( 20 1 ) 8476 8 00. Sells Beaver blades and other microsurgical tools. Bio-Rad, Digilab Div., 237 Putnam Ave., Cambridge, MA 02 1 39; ( 6 1 7) 8 6 8 -4330. Sells FT-IR spectrophotometers, microscopes and other accessories, thermal and chro­ matographic IR attachments. Bomem International, 7800 Quincy St., Willowbrook, IL 6052 1 ; ( 7 0 8 ) 9 8 6 - 1 090. Sells dispersive and FT-IR spectrophotometers along with many accessories, including microscopes. Bruker Instruments, Inc., 19 Fortune Dr., Billerica, MA 0 1 82 1 ; ( 5 0 8 ) 6 6 7-9580. Sells dispersive and FT-IR spectrophotometers along with many accessories, including microscopes. Buck Scientific, Inc., 58 Fort Point St., East Norwalk, CT 06855-1 097; (203) 8 5 39444. Sells dispersive and FT-IR spectrophotometers along with many accessories. Carolina Biological Supply Co., 2700 York Road, Burlington, NC 2 72 1 5; ( 8 00) 334555 1 . Sells Caroplastic polyester for embedding. Castolite Co., P. O. Box 39 1 , Woodstock, IL 60098; ( 8 1 5 ) 338-4670. Sells Castolite polyester for embedding. Conservation Materials, 1 2 75 Kleppe Lane, Suite 10, Sparks, NV 89431 ; ( 702) 331 0582. Sells conservation products, including Rhoplex AC-33. Digilab-see Bio-Rad. Ernest E. Fullam, Inc., 900 Albany Shaker Road, Dept. AL, Latham, NY 1 2 1 1 0- 1 4 9 1 ; ( 5 1 8 ) 78 5-5533. Sells microanalysis tools and containers, silicone molds for preparing cross sections. Galactic Industries Corp., 395 Main St., Salem, NH 03079; ( 603) 8 9 8 -7600. Sells spectral conversion and search software, data processing routines, including three­ dimensional spectral processing routines. Graseby Specac, 301 Commerce Dr. , Fairfield, CT 06430; ( 8 00) 447-2558. Sells acces­ sories for IR spectrometers, gas cells, optical crystals, sample preparation equipment. Harrick Scientific, 8 8 Broadway, P. O. Box 1 2 8 8 , Ossining, NY 1 0562; ( 9 1 4 ) 7620020. Sells accessories for IR spectrometers, optical crystals, sample preparation equipment, custom accessories (such as ATR and DRIFTS units). High Pressure Diamond Optics, 231 Gianconda Way, Suite 1 03, Tucson, AZ; ( 520) 544-9338. Sells high- and low-pressure diamond anvil cells; diamond microtoming knives. International Crystal Laboratories, 1 1 Erie St., Garfield, NJ 07026; ( 20 1 ) 478-8944. Sells accessories for IR spectrometers, optical crystals, sample preparation equipment. lASCO, 8 649 Commerce Dr., Easton, MD 2 1 60 1 ; ( 8 00) 333-5272. Sells dispersive and FT-IR spectrophotometers, accessories including microscopes. 206 Suppliers KVBIAnalect, 1 7 8 1 9 Gillette Ave., Irvine, CA 92 714; ( 7 1 4 ) 660-8 8 0 1 . Sells dispersive and FT-IR spectrophotometers, accessories including microscopes. Ladd Research Industries, Inc., 1 3 Dorset Lane, Williston, VT 05495; ( 802) 658496 1 . Sells general microscope supplies a n d acrylic, epoxy, a n d wax materials for embedding. Mattson Instruments, 1 00 1 Fourier Dr., Madison, WI 5 3 7 1 7; ( 6 0 8 ) 8 3 1 -5 5 1 5 . Sells dispersive and FT-IR spectrophotometers, accessories including microscopes. McCarthy Scientific Co., P. O. Box 5332, Fullerton, CA 92635; ( 7 1 4 ) 526-2742. Sells optical crystals, sample preparation equipment. Midac Corp., 1 79 1 1 Fitch Ave. , Irvine, CA 92714; ( 7 1 4 ) 660-855 8 . Sells FT-IR sys­ tems, portable IR air-monitoring systems. Minitools, 634 University Ave., Los Gatos, CA 95030; (408) 3 9 5 - 1 5 8 5 . Sells micro­ tools, micromanipulation devices, microdrills. Nicolet Instrument Corp., 5225-5 Verona Road, Madison, WI 5 3 7 1 1 ; ( 6 0 8 ) 276- 6 1 00 . Sells FT-IR spectrophotometers, accessories including microscopes. Perkin-Elmer Corp., 7 6 1 Main Ave., Norwalk, CT 06859; ( 8 00) 762-4000. Sells dis­ persive and FT-IR spectrophotometers, accessories including microscopes, other types of analytical instrumentation. Photometrics, Inc., 1 5 8 0 1 Graham St., Huntington Beach, CA 92649; ( 7 1 4 ) 8 95- 4465. Provides searches of numerous commercial IR libraries. Pike Technologies, 29 1 9 Commerce Park Dr., Madison, WI 5 3 7 1 9; ( 6 0 8 ) 274-272 1 . Sells IR accessories, microscope computer-controlled mapping stages. Shimadzu Scientific Instruments, Inc., 7 1 02 Riverwood Dr. , Columbia, MD 2 1 046; ( 8 00) 477-1 227. Sells dispersive and FT-IR spectrophotometers, accessories including microscopes, other types of analytical instrumentation. Spectra-Tech ( Spectra Technology), Inc., 2 Research Dr., Shelton, CT 06484-0849; (203 ) 926-8998. Develops and sells innovative IR accessories, including microscopes, IRj.LS microspectrophotometers, compression cells that use salt plates or diamond win­ dows, roller knives. Also sells 3M disposable IR cards containing thin polymer films for sample preparation. Structure Probe, Inc., P. O. Box 656, West Chester, PA 1 93 8 1 ; ( 2 1 5 ) 43 6-5400. Sells microanalysis tools and containers, silicone molds for preparing cross sections. Ted Pella, Inc., P. O. Box 23 1 8, Redding, CA 96099; ( 9 1 6 ) 243-2200. Sells acrylic, epoxy, and wax materials for embedding, along with several types of Peko silicone embedding molds. Union Carbide, 39 Old Ridgebury Rd., Danbury, CT 068 1 7; (203 ) 794-5300. Manufactures and sells Parylene. Ward's Natural Science, P. O. Box 92912, Rochester, NY; ( 800) 962-2660. Sells Bio­ Plastic polyester for embedding. Whatman, Balston Div., 1 00 Ames Pond Dr., Tewksbury, MA 0 1 8 76; ( 800) 343-4048 . Sells Balston dry air systems to purge I R spectrometers. Wig-L-Bug, Crescent Dental Manufacturing Co., 7750 47th St., Lyons, IL 60534; (708) 447-8050. References Abbey Newsl etter 1 9 8 8 . Parylene made available for conservation. Abbey Newsletter 1 2 ( 6 ) : 1 0 8 . Abd EI- Hady, M . M . [ 1 9 8 8] . Infra-red investigations o n monumental limestone samples. I n 6th International Congress on Deterioration and Conservation of Stone, vol. 1, compo J. Ciabach, 3 8 7-94. Torun, Poland: Nicholas Copernicus University Press Department. l. c . , 5., 5., Afremow, and J. T. Vandeberg 1 966. High resolution spectra of inorganic pigments and extenders in the mid­ infrared region from 1500 cm-I to 200 cm-I . Journal of Painting Technology 3 8 (495 ) : 1 69-202. Aldrich, D. and M . A. S m ith 1 995. Pharmaceutical applications of infrared microspectroscopy. In Practical Guide to Infrared Microspectroscopy, ed. H. Humecki, 323-76. New York: Marcel Dekker. American Society for Testing Materi als (ASTM) 1 9 8 1 . Standard Practices for Internal Reflection Spectroscopy. ASTM E 573-8 1 . Philadelphia: ASTM. Baer, N. and N. Ind ictor 1 976. Linseed oil-metal acetylacetonate systems 3: Infrared spectroscopic observation of the drying film. Journal of Coatings Technology 4 8 : 5 8-62. Baker, M., D. von Endt, W. Hopwood, and D. Erhardt 1 9 8 8 . FTIR microspectrometry: A powerful conservation analysis tool. In Preprints of Papers Presented at the Sixteenth Annual Meeting of the AIC, New Orleans, Louisiana, June 1 -5, 1 988, 1 - 1 3 . Washington, D . C . : American Institute for Conservation of Historic and Artistic Works. Baker, M. T. , H. D. B u rgess, N. E. B i nnie, M. R. Derrick, and J . R. Druzik 1 990. Laboratory investigation of the fumigant Vikane. In ICOM Committee for Conservation Preprints, 9th Triennial Meeting, Dresden. Paris: ICOM Committee for Conservation. Banerjee, A., and T. Hager 1 992. On some crystals of lapis lazuli. Zeitschrift fur Naturforschung 4 7 : 1 094. Barclay, R. l. 1 98 9 . An improved method for solvent extraction of oil from a whale bone sculpture. Journal of the International Institute for Conservation-Canadian Group 1 4 : 1 8-22. Barer, R., A. R. Cole, and H . W. Thompson 1 949. Infra-red spectroscopy with the reflecting microscope in physics, chemistry and biology. Nature 1 6 3 : 1 9 8-20 3 . 208 References Bartick, E. G . 1 9 8 7. Considerations for fiber sampling with infrared microspectroscopy. In The Design, Sample Handling, and Applications of Infrared Microscopes: A Symposium, ed. P. B. Roush. ASTM Special Technical Publication 949. Philadelphia: American Society for Testing Materials. Bartick, E. G . , J . C. Corbett, and G. L. McClure 1 9 82. Computerized quantitative analysis of copolymers by IR spectroscopy. In Computer Applications in Applied Polymer Science, 1 8 5-96. Washington D.C.: American Chemical Society. Bartick, E. G . , M. W. Tungol, and J . A. Reffner 1 9 94. A new approach to forensic analysis with infrared microscopy: Internal reflection spectroscopy. Analytica Chimica Acta 2 8 8 : 35-42. Beck, C. W. 1 9 72. Aus der Bernstein-Forschung (Amber research). Die Naturwissenschaften 5 9 ( 7):294-9 8 . Beck, C . W., A. B . Adams, G . C . Southard, a n d C . Fellows 1 97 1 . Determination of the origin of Greek amber artifacts by computer-classification of infrared spectra. In Science and Archaeology, ed. R. H. Brill, 235-40. Cambridge, Mass: MIT Press. Beck, C. W., J . Green l ie, M. Diamond, A. Macch iarulo, A. Hannen berg, and M. Hauck 1 9 7 8 . The chemical identification of Baltic amber at the Celtic Oppidum Stare Hradisko in Moravia. Journal of Archaeological Science 5: 343-54. Beck, C. W., C. J. Smart, and D. J . Ossenkop 1 9 8 9. Residues and linings in ancient Mediterranean transport amphoras. In Archaeological Chemistry. Washington D.C.: American Chemistry Society. Beck, C. W. , E. Wilbur, and S. Meret 1 964. Infrared spectra and the origin of amber. Nature (London) 2 0 1 ( 4 9 1 6 ):256-57. Beck, C. W., E. Wilbur, S . Meret, D. Kossove, and K. Kermani 1 965. The infrared analysis of amber and the identification of Baltic amber. Archaeometry 9:96- 1 09. Bellamy, L. J . 1 9 80. The Infrared Spectra o f Complex Molecules. 2 d ed. London: Chapman and Hall. Berni, R. J . , and N. M. Morris 1 9 84. Infrared spectroscopy. In Analytical Methods for a Textile Laboratory, ed. J. W. Weaver, 265-92. Research Triangle Park, N.C.: American Association of Textile Chemists and Colorists. Besan i nou, D. 1 9 84. Cire et cires: E tude sur la composition, l'alteration, la restauration, la conservation des oeuvres ceroplastiques. Paris: Institut fran\ais de restauration des oeuvres d'art. Bettembourg, J. M. 1 9 8 8 . Examen et analyse des processus de corrosion vitraux anciens (Examination and analyses of corrosion processes of ancient stained glass windows). In 2nd International Conference on Non-Destructive Testing: Microanalytical Methods and Environment Evaluation for Study and Conservation of Works of Art, Perugia, 1 7-20 April 1 988, 1 . 1- 1 . 1 5. Rome: Comas Grafica. B i l l m eyer, F. W. , J r., and M. Saltzman 1 9 66. Principles of Color Technology. New York: John Wiley and Sons. B i rstein, V. J . 1 975. O n the technology o f central Asian wall paintings: The problem o f binding media. Studies in Conservation 20:8-1 9. 209 References 1 97 8 . Infra-red spectroscopic investigation of grounds and pigments of central Asian wall paintings. Khudozestvennoe nasledie 434:5-22. B i rstein, V. J . , and V. M . Tu l ' Chinskii 1 977. Ob identifikatsii vesestv pokrovnogo sloia egiptskikh kamennikh stel ( On the identification of substance of covering layers of Egyptian stone tombs). Khudozestvennoe nasledie 3 3 3 : 8- 1 1 . 1 979. Identifikatsiia nekotor'ikh materialov zivopisi ikon'i 'mucenik i mucenitsa' metodom ik-spektroskopii. Khudozestvennoe nasledie 5 3 5 : 1 9 8-20 1 . 1 9 8 1 . IR-spectroscopic analysis of aged gelatins. In ICOM Committee for Conservation 6th Triennial Meeting, Ottawa, 2 1 -2 5 September 1 98 1 , Preprints, 9 . 1 -9 . 8 . Paris: ICOM Committee for Conservation. B iscontin, G . , and S. Vol p i n 1 9 8 9 . Indagine sulle patine a d ossalato mediante FT-IR ( FT-IR investigations on calcium oxalate films). In Le pellicole ad ossalati: Origine e significato nella conser­ vazione delle opere d'arte ( Oxalate films: Origin and meaning in the conservation of works of art), 1 5 1-6 3 . Milan: Centro del C.N.R. " Gino Bozza. " B i shop, M . 1 994. Conversation with author, Getty Conservation Institute, Marina del Rey, Calif. Blanco, M. T., F. Puertas, A. Palomo, and F. Accion 1 99 1 . Infrared spectroscopy as a complementary technique to identify inorganic salts in ancient deteriorated mortars, grouts and plasters. In Science, Technology, and European Cultural Heritage: Proceedings of the European Symposium, Bologna, Italy, 1 3-1 6 June 1 989, ed. N. S. Baer, C. Sabbioni, and A. Sors, 60 1-6. Oxford and Boston: Butterworth-Heinemann. B lasius, E . , H. Wagner, H. B raun, R. Krumbholz, and B. Schwartz 1 9 8 3 . Tile fragments as characteristic evidence for ancient Roman settlements: Scientific investigations. Archaeometry 25(2 } : 1 65-7 8 . B leck, R.-D., and R . Ziessler i 967. Chemische Untersuchungen an der Kirche in Thorey, Kreis Arnstadt ( Chemical investigations at the church in Thorey near Arnstadt). Neue Museumskunde 1 0( 1 } . . Bockoff, F. J . , K. - M Guo, G. E. Richards, and E. Bockoff 1 984. Infrared studies of the kinetics of insolubilization of soluble nylon. In Adhesives and Consolidants: Preprints of the Contributions to the lIC Paris Congress, 2-8 September 1 984, ed. N. S. Brommelle, E. M. Pye, P. Smith, and G. Thomson. London: International Institute for Conservation of Historic and Artistic Works. B rachert, T. 1 9 78-79. Historic transparent varnishes and furniture polishes. Translated by R. Mussey. Parts 1-5. Maltechnik-Restauro 1 ( 1 97 8 } :56; 2 ( 1 978 } : 1 20; 3 ( 1 97 8 } : 1 85; 4 ( 1 978}:263; 2 ( 1 979 } : 1 3 1 . Bradley, S . 1 987. Techniques for the analysis of salts. Conservation News 34:24-25. Brodsky-Doyle, B., E . G . Bendit, and E . R. Blout 1 975. Infrared spectroscopy of collagen and collagen-like peptides. Biopolymers 14:937-45. Brown, M . K., and C. A. Shelton 1 994. Bayou Bend's latest acquisition: Old World inspiration for a New World mas­ terpiece. In 42nd Annual Theta Charity Antiques Show, Houston, Texas, September 22-25, 1 994. Exhibition catalogue. Houston: Theta Charity Antiques Show. B u rnstock, A., and T. Learner 1 992. Changes in the surface characteristics of artificially aged mastic varnishes after cleaning using alkaline reagents. Studies in Conservation 3 7 ( 3 } : 1 65-84. 210 References Butler, S. A. 1 9 8 8 . The Ageing of Paraloid B-72 Based Adhesives 1 : Solubility and Infrared and UV- Visible Spectroscopy Studies. London: British Museum, Department of Conservation, Conservation Research Section. Butz, W. H . 1 960. Infrared absorption analysis o f powdered samples. I n Beckman Application Data Sheet. Application note IR- 8 0 63, Feb. 1 960. Fullerton, Calif. : Beckman Instruments. Cai n , C. E . , and V. F. Kalasinsky 1 9 8 5 . Characterization of eighteenth- and nineteenth-century paper using Fourier transform infrared spectroscopy and thin-layer chromatography. In Application of Science in Examination of Works of Art: Proceedings of the Seminar, September 7-9, 1 983, ed. P. A. England and L. van Zelst, 55-5 8 . Boston: Research Laboratory, Museum of Fine Arts. Camaiti, M., R. Ingoglia, G. Moggi, A. Pasetti, and A. Scala 1 9 9 1 . Controllo della reversibilita di trattamenti protettivi effettuati con polimeri fluorurati su materiali lapidei ( Controlling the reversibility of protective treatments using fluoropolymers on stone materials). In Le pietre nell'architettura, struttura e superfici: Atti del convegno di studi, Bressanone, 25-28 giugno 1 99 1 , ed. Guido Biscontin and Daniela Mietto, 267-76. Padua, Italy: Libreria Progetto Editore. Cardamone, J eanette M . 1 9 8 8 . Fourier transform infrared reflectance absorbance spectroscopy (IRAS) for non­ destructive evaluation of textiles. In 2nd International Conference on Non-Destructive Testing: Microanalytical Methods and Environment Evaluation for Study and Conservation of Works of Art, Perugia, 1 7-20 April 1 988. Rome: Comas Grafica. Carriveau, G. W. 1 9 84. Technical examination of oriental lacquer. In Archaeological Chemistry 3, e d . J . B . Lambert, 395-402. Advances in Chemistry series 205. Washington, D.C.: American Chemical Society. Cartwright, L. J . , N . S . Cartwright, and P. G . Rodgers 1 977. A microtome technique for sectioning multilayer paint samples for micro­ analysis. Journal of the Canadian Society for Forensic Science 1 0: 1 0-12. Cen n i n i , C. 1 960. I1 libro dell'arte. In The Craftsman's Handbook, ed. and trans. D. V. Thompson Jr. New York: Dover Publications. Chess, C. A. 1 995. Applications of reflectance microspectroscopy in the electronics industry. In Practical Guide to Infrared Microspectroscopy, ed. H. Humecki. New York: Marcel Dekker. Chicago Society for Coating Technology 1 98 0 . An Infrared Spectroscopy Atlas for the Coatings Industry. Philadelphia: Federation of Societies for Paint Technology. Clark, R. J . H . 1 964. The application o f diffuse reflectance spectroscopy to inorganic chemistry. Journal of Chemical Education 4 1 (9}:489. Coblentz, W. W. 1 905. Investigation of Infrared Spectra. Carnegie Institute Publications no. 35. Washington, D.C.: Carnegie Institute. Cole, A. R. H . , and R. N. J ones 1 952. A reflecting microscope for infrared spectroscopy. Journal of the Optical Society of America 42:348. 211 References Connor, M., and F. G i rardet 1 992. Etude du mode de fixation du soufre sur un gres calcareux (Study of sulfur fixation modes on a calcareous sandstone). In Proceedings of the 7th International Congress on Deterioration and Conservation of Stone, Held in Lisbon, Portugal, 1 5-1 8 June 1 992, ed. ]. D. Rodrigues, Henriques, and Jeremias, 407- 1 6 . F. F. T. Lisbon: Laborat6rio Nacional d e Engenharia Civil. Cook, R., and M. D. Paterson 1 9 7 8 . New techniques for the identification o f microscopic samples o f textile fibers by infrared spectroscopy. Forensic Science International 1 2:237-43. Cooley, J. W., and J . W. Tukey 1 965. An algorithm for the machine calculation of complex Fourier series. Mathematics of Computation 1 9:297-3 0 1 . Cov i l le, F. V. 1 8 92. The Panamint Indians of California. American Anthropologist 5 : 3 5 1 -6 1 . Crooks, J . E. 1 9 7 8 . The Spectrum in Chemistry. London: Academic Press. Dau p h i n , Y. 1 993. Potential of the diffuse reflectance infrared Fourier transform (DRIFT) method in paleontological studies of bones. Applied Spectroscopy 47( 1 ): 52. de Keijzer, M., and M . F. S . Karreman 1 9 8 9 . Een vroeg-twintigste-eeuwse pigmentcollectie: De pigmentcollectie van het Missiemuseum te Steyl-Tegelen (An early 20th-century pigment collection: The pigment collection in the Missiemuseum at Steyl-Tegelen). Mededelingenblad (IlC Nederland) 6 ( 2 ) : 7-24. Delbourgo, S . 1 972. L a technique d e l a fresque d e Cennino Cennini a Botticelli: Etude physico­ chimique ( Fresco technique from Cennino Cennini to Botticelli: Physico-chemical study) . Annales du laboratoire de recherche des Musees de France, 4-1 5. Delbourgo, S., and M. C. Gay 1 96 8 . La physico-chimie au service de l'archeologie-examen d'une serie d'echantil­ Ions provenant de fouilles effectuees au Soudan (Physico-chemistry at the service of archaeology-examination of a series of samples from excavations done in Sudan). Bulletin du laboratoire du Musee du Louvre 1 2:20-25. Demm ler, K. 1 9 8 0. The determination of residual active oxygen in parts of unsaturated polyester resins and its influence on post curing and yellowing by light. Kunstoffe 70:78 6-92. Derrick, M . R. 1 9 8 9 . Fourier transform infrared spectral analysis of natural resins used in furniture finishes. Journal of the American Institute for Conservation 2 8 ( 1 ):43-56. 1 9 9 1 . Evaluation of the state of degradation of Dead Sea Scroll samples using FT-IR spectroscopy. In Book and Paper Annual, 49-6 5 . Washington, D.e.: Ale. 1 995. Infrared microspectroscopy in the analysis of cultural artifacts. In Practical Guide to Infrared Microspectroscopy, ed. H. Humecki, 2 8 7-322. New York: Marcel Dekker. Derrick, M. R., E. Doehne, A. Parker, and D. Stu l i k 1 994. Some new analytical techniques for use i n conservation. Journal o f the American Institute for Conservation 3 3 ( 3 ): 1 7 1-84. Derrick, M . R., C. Druzik, and F. Preusser 1 9 8 8 . FTIR analysis of authentic and simulated black lacquer finishes on eighteenth­ century furniture. In Urushi: Proceedings of the Urushi Study Group, June 1 0-27, 1 985, Tokyo, ed. N. S. Brommelle and P. Smith, 227-34. Marina del Rey, Calif.: Getty Conservation Institute. 212 References Derrick, M. R., J . M. Land ry, and D. C. Stu l i k 1 9 9 1 . Methods i n Scientific Examination o f Works o f Art: Infrared Microspectroscopy. Marina del Rey, Calif. : Getty Conservation Institute. Derrick, M. R., l. Souza, T. Kieslich, D. Stu l i k, and H. Florsheim 1 994. Embedding paint cross-section samples in polyester resin: Problems and solutions. Journal of the American Institute for Conservation 3 3 ( 3 ):227-45. Derrick, M . R., D. C. Stu l i k, J. M . Land ry, and S. P. Bouffard 1 992. Furniture finish layer identification by infrared linear mapping microspec­ troscopy. Journal of the American Institute for Conservation 3 1 ( 2 ) :225-3 6 . Derrick, M . R . , D . C . Stu l i k, a n d E. Ordonez 1 99 3 . Deterioration of cellulose nitrate sculptures made by Gabo and Pevsner. In Symposium '9 1 : Saving the Twentieth Century-the Degradation and Conservation of Modern Materials, Abstracts, 1 69-82. Ottawa: Canadian Conservation Institute. Domaslowski, W., and M. Kesy-Lewandowska 1 9 8 8 . Identification of deposits on stone historical objects. In 2a conferenza inter­ nazionale sulle prove non distruttive metodi microanalitici e indagini ambientali per studio e la conservazione delle opere d'arte . . . Perugia, 1 7-20 aprile 1 988. Vol. 1 . 10 Rome: Istituto Centrale per il Restauro. Dow Chemical Co. 1 982. Vikane Fumigation Manual. Indianapolis: Dow Agro Sciences. D u raiswamy, D . , K. Ramaswamy, and R. Venkatachalapathy 1 992. Infrared spectroscopic studies of archaeological materials: Determination of firing temperature. In Role of Chemistry in Archaeology: 1 st International Colloquium Held in Hyderabad (India), 1 5-1 8 November 1 99 1 , ed. M. C. Ganorkar and N. Rama Rao, 47-54. Hyderabad, India: Birla Institute of Scientific Research. Eastes, J . W., and J . W. Salisbury 1 9 86. Spectral properties of sulfated limestone and marble: Implications for in situ assessment of atmospheric pollution damage to carbonate rock building materials. Applied Spectroscopy 40(7):954-59. Edge, M., N. S . Allen, M. Hayes, P. N. K . Riley, C. V. Horie, and J. Luc-Gardette 1 990. Mechanisms of deterioration in cellulose nitrate base archival cinematograph film. European Polymer Journal 26(6) :623-30. Erhardt, D . , W. Hopwood, M . Baker, and D . von Endt 1 9 8 8 . A systematic approach to the instrumental analysis of natural finishes and binding media. In Preprints of Papers Presented at the Sixteenth Annual Meeting of the AIC, New Orleans, Louisiana, June 1 -5, 1 988, 67-84. Washington, D. C. : American Institute for Conservation of Historic and Artistic Works. Fah renfort, J . 1 962. Attenuated total reflection-A new principle for production of useful infrared reflection spectra of organic compounds, molecular spectroscopy. In Proceedings of the 4th International Meeting on Molecular Spectroscopy, Bologna, 1 959, vol. 2, ed. A. Mangini. London: Pergammon. Faraone, G . 1 9 87. L a spettroscopia i n reflettanza diffusa: Un efficace metodo d i indagine delle superfici di materiali lapidei (Diffuse reflectance spectroscopy: An effective method for investigating stone material surfaces). Restauro e citta 7 : 1 56-57. Felger, R. S., and M . B . Moser 1 9 8 5 . People of the Desert and Sea: Ethnobotany of the Seri Indians. Tucson: University of Arizona Press. Fell er, R. l. 1 954. Dammar and mastic infrared analysis. Science 1 2 0( 3 1 30 ) : 1 069-70. 1 959. Identification and analysis of resins and spirit varnishes. In Application of Science in Examination of Works of Art-Proceedings of the Seminar, September 1 5-1 8, 1 958. Boston: Museum of Fine Arts. 213 References Feller, R . L . , ed. 1 98 6 . Artists' Pigments: A Handbook of Their History and Characteristics. Vol. 1 . Cambridge: Cambridge University Press; Washington, D.C.: National Gallery of Art. ( Contains articles with IR spectra on Indian yellow; cobalt yellow; barium sulfate; cadmium yellows, oranges, and reds; red lead and mini urn; green earth; zinc white; chrome yellow and other chromate pigments; lead antimonate yellow; carmine. ) Fellgett, P. 1 970. The origins and logic of multiplex, Fourier and interferometric methods in spectrometry. In Proceedings for Aspen International Conference on Fourier Spectroscopy, ed. G. A. Vanasse, A. T. Stair, and D. J. Baker, 1 3 9-42. U.S. Air Force document no. AFCRL-71 -00 1 9. Bedford, Mass.: Air Force Cambridge Research Laboratories. Ferraro, J . R., and L. J . Basile 1 979. The diamond anvil cell as a sampling device in IR. American Laboratory 1 1 : 3 1-36. Ferrus, R., R. Pages, and C. Diez 1 9 8 1 . Analisis cuantitativo de estucados caolin-caseina mediante espectroscopia de infrarrojos 0 reflexion ( Quantitative analysis of kaolin-casein coatings by means of infra-red reflection spectroscopy ). Investigaci6n y tecnica de! papeI 1 8 ( 6 7 ) : 8 0-9 1 . Fischer, G . , and M . Bader 1 994. Melt film technique for IR spectroscopy. American Laboratory ( November ):32c. Fol lette, T. 1 9 8 5 . Amber in goldworking. Archaeology 3 8 (2):64-65 . Francis, S . A . , a n d A. H . E l l ison 1 9 5 9 . Infrared spectra of monolayers on metal mirrors. Journal of the Optical Society of America 49( 1 ) : 1 3 1-3 8 . Fred ian i , P. , and U . Matteol i 1 97 8 . A methodological approach to the study of the deterioration o f the statues in the Boboli's garden ( Pitti Palace, Florence) 3: Rapid determination of gypsum on marble by infrared spectroscopy. In ICOM Committee for Conservation 5th Triennial Meeting, Zagreb, 1 -8 October 1 978, Preprints. Paris: International Council of Museums. Freeman, K. L. 1 979. Techniques used in the analysis of polymers. ICCM Bulletin 5 ( 2 ) : 1 2-27. Fromageot, D. 1 9 9 0 . Photovieillissement de revetements de consolidation a base de polyamides solubles ( Light aging of consolidation coatings based on soluble polyamides). In Technologie industrielle. Conservation, restauration du patrimoine culture!. Colloque AFTPV/SFIIC. Nice, 1 9-22 septembre 1 989, 2 8-33. Puteaux, France: Erec. Fromageot, D . , and J . Lemaire 1 99 1 . The prediction of the long-term photo-aging of soluble polyamides used in conservation. Studies in Conservation 3 6 ( 1 ) : 1-8. Fuchs, D . R., H . Rom ich, a n d H . Sch m idt 1 9 90. Glass-sensors: Assessment of complex corrosive stresses in conservation research. In Materials Issues in Art and Archaeology 2: Symposium Held April 1 7-2 1 , 1 990, San Francisco, California, USA, ed. P. B. Vandiver, J . Druzik, and G . S. Wheeler, 23 9-5 1 . Pittsburgh: Materials Research Society. Fujinaga, T. , T. Takenaka, and T. M u roga 1 976. Origin of foreign and Japanese ambers studied by elemental analyses and infrared spectroscopy. Bunseki Kagaku 25 ( 1 1 ) :795-99. Full er, M . P. , and P. R. Griffiths 1 97 8 a. Diffuse reflectance measurements by infrared Fourier transform spectrometry. Analytical Chemistry 50 ( 1 3 ) : 1 906- 1 0 . 214 References 1978b. Infrared analysis by diffuse reflectance spectrometry. American Laboratory 1 0( 1 0) :69-80. 1980. Infrared microsampling by diffuse reflectance Fourier transform spectrometry. Applied Spectroscopy 34(5):53 3-39. Fuoco, R . , K. H . Shafer, and P. R. Griffiths 1 9 8 6 . Capillary gas chromatography/Fourier transform infrared microspectrometry at sub ambient temperature. Analytical Chemistry 5 8 : 3 249-54. Garrido, J. M . C. 1 969. El Azul Maya. Madrid: Instituto de Conservaci6n y Restauraci6n de Obras de Arte, Arqueologfa y Etnologia. Gettens, R. J . 1 932. A microsectioner for paint films. Technical Studies in the Field of the Fine Arts 1 :20. 1 9 3 6. The cross-sectioning of paint films. Technical Studies in the Field of the Fine Arts 5 : 1 8 . 1 952. Science in the art museum. Scientific American 1 87( 1 ) :22-27. 1 959. The identification of pigments and inerts on paintings and other museum objects. In Application of Science in Examination of Works of Art: Proceedings of the Seminar, September 1 5-1 8, 1 958, 3 1 -49. Boston: Museum of Fine Arts. Gettens, R. J . , and G. L. Stout 1 966. Painting Materials: A Short Encyclopaedia. New York: Dover Publications. Gettens, R. J . , and E. West-FitzHugh 1 974. Malachite and green verditer. Studies in Conservation 1 9 ( 1 ) :2-2 3 . Gettens, R. J . , E. West-FitzHugh, a n d R. L. Fel ler 1 974. Calcium carbonate whites. Studies in Conservation 1 9 ( 3 ) : 1 57-84. Giangrande, C. 1 9 8 8 . Identification of bronze corrosion products by infrared absorption spec­ troscopy. In Recent Advances in the Conservation and Analysis of Artifacts: Jubilee Conservation Conference, London, 6-1 0 July 1 987, compo James Black, 1 35-4 8 . London: University o f London, Institute of Archaeology, Summer Schools Press. Gianno, R., D. W. von Endt, D. Erhardt, K. M. Koch u m men, and W. Hopwood 1 9 8 7 . The identification of insular southeast Asian resins and other plant exudates for archaeological and ethnological application. In Recent Advances in the Conser­ vation and Analysis of Artifacts: Jubilee Conservation Conference, London, 6-1 0 July 1 98 7, compo James Black, 229-3 8 . London: University of London, Institute of Archaeology, Summer Schools Press. G i l lard, R . , S. Hardman, R. Thomas, and D. Wilki n son 1 994. The detection o f dyes by FTIR microscopy. Studies in Conservation 3 9 : 1 8 7-92. G lauert, Audrey M. 1 972. Fixation, dehydration, and embedding of biological sections. In Practical Methods in Electron Microscopy. Amsterdam: North-Holland Publishing Co. Godla, J . 1 990. The use o f wax finishes o n pre-industrial American furniture. Master's thesis, Antioch University, West Townsend, Mass. Goos, F., and H . Hanchen 1 947. Ein neuer und fundamentaler Versuch zur Totalreflexion. Ann. Physik 1 :3 3 3 . Gorgo n i , c . , o. F. F. T. L . Lazzarini, and Salvadori 1 992. Minero-geochemical transformations induced by lichens in the biocalcarenite of the Selinuntine monuments. In Proceedings of the 7th International Congress on Deterioration and Conservation of Stone, Held in Lisbon, Portugal, 1 5-1 8 June 1 992, ed. J. D. Rodrigues, Henriques, and Jeremias, 5 3 1 -3 9 . Lisbon: Laborat6rio Nacional de Engenharia Civil. 215 References Grant, C. 1 99 3 . The Rock Painting of the Chumash: A Study of a California Indian Culture. Santa Barbara, Calif.: Santa Barbara Museum of Natural History. G rattan, D. W., and M. B i l z 1 9 9 1 . The thermal aging of Parylene a n d the effect of antioxidant. Studies in Conservation 3 6( 1 ) :44-52. Griffiths, P. R., and J. A. de Haseth 1 98 6 . Fourier Transform Infrared Spectrometry. New York: Wiley-Interscience. Griffiths, P. R., and M. P. Ful ler 1 9 82. Mid Infrared Spectrometry of Powdered Samples. Vol. 9 of Advances in Infrared and Raman Spectroscopy, ed. R. J. H. Clark and R. E. Hester. London: Heyden. Grimaldi, D. 1 99 3 . The care and study of fossiliferous amber. Curator 3 6 ( 1 ) :3 1 -49. Grosjean, D . 1 98 5 . Wall loss o f gaseous pollutants i n outdoor Teflon chambers. Environmental Science and Technology 1 9( 1 1 ) : 1 059-65. G u i neau, B . a 1 9 8 3 . Applications d e l a spectrometrie (rayons x , infra - rouge, raman) l a mise e n evidence d e lazurite e t d e bleu d e Prusse dans des poudres minerales ( Applications of spectrometry [x-ray, infrared, raman] for revealing azurite and Prussian blue in min­ eral powders). In La peinture funeraire, caracterisation, datation, technique de la peinture antique (Funerary painting: Characterization, dating, technique of ancient painting), 75-90. Valbonne, France: Apdca. G u ralnik, D. B . , ed. 1 9 84. Webster's New World Dictionary. 2d college ed., s.v. "infrared. " Hadzi, D . , and F. Cvek 1 97 8 . Smolni Kit in Premaz za Zare ( Resinous putty and paint on urns). Arheoloski vestnik, 1 28-3 3 . Hansen, E . F. 1 9 9 3 . The effects of relative humidity on some physical properties of modern vellum: Implications for the optimum relative humidity for the display and storage of parch­ ment. Journal of the American Institute for Conservation 3 1 ( 3 ):325. Hansen, E. F . , M . R. Derrick, M . R. Sch i l l ing, a n d R. Garcia 1 99 1 . The effects of solution application on some mechanical and physical properties of thermoplastic amorphous polymers used in conservation: Poly(vinyl acetate )s. Journal of the American Institute for Conservation 30(2) :203- 1 3 . Hansen, E. F, and W. S . G i nell 1 9 8 9 . The conservation of silk with Parylene-C. In Historic Textile and Paper Materials: Conservation and Characterization, ed. H. L. Needles and H. S. Zeronian, 1 0 8-33 . Advances in Chemistry series 2 12. Washington, D.C.: American Chemical Society. Hansen, E. F., R. Lowinger, and E. Sadoff 1 994. Consolidation of porous paint in a vapor saturated atmosphere: A technique for minimizing changes in the appearance of powdering, matte paint. Journal of the American Institute for Conservation 32( 1 ): 1-14. Hansen, E. F . , A. Wallert, a n d M . Derrick 1 995. An organic colorant used in painted ancient Maya architectural sculpture at Nakbe, Peten, Guatemala. Internal report, Getty Conservation Institute, Marina del Rey, Calif. Harrick, N. J . 1 95 9 . Reflection o f infrared radiation from a germanium-mercury interface. Journal of the Optical Society of America 49:376. 216 References 1 9 7 1 . Determination of refractive index and film thickness from interference fringes. Applied Optics 1 0 ( 1 0) :2344-49. 1 979. Internal Reflection Spectroscopy. Ossining, N.Y.: Harrick Scientific Corp. Harrick Scientific Corp. 1 987. Optical Spectroscopy: Sampling Techniques Manual. Ossining, N.Y.: Harrick Scientific Corp. Harrington, J . P. 1 942. Culture element distributions 1 9 : Central California coast. University of California Anthropological Records 7( 1 ) : 1-42. Harthcock, M . A., and S . C. Atkin 1 9 8 8 . Infrared microspectroscopy: Development and applications of imaging capabilities. In Infrared Microspectroscopy: Theory and Applications, ed. R. G. Messerschmidt and M. A. Harthcock. New York: Marcel Dekker. Hedl ey, G . , M. Odlyha, A. B u rnstock, J . Ti l l i nghast, and C. Husband 1 990. A study of the mechanical and surface properties of oil paint films treated with organic solvents and water. In Cleaning, Retouching and Coatings-Technology and Practice for Easel Paintings and Polychrome Sculpture: Preprints of the Contributions to the Brussels Congress, 3-7 September 1 990, ed. J. S. Mills and P. Smith. London: International Institute for Conservation of Historic and Artistic Works. Hergert, H . L. 1 9 7 1 . Infrared spectra. In Lignins: Occurrence, Formation, Structure and Reactions, ed. K. V. Sarkanen and C. H. Ludwig, 267-95. New York: Wiley-Interscience. Herschel, w. 1 800. Experiments on the refrangibility of the invisible rays of the sun. Philosophical Transactions of the Royal Society 90:284-92. Hexter, M . R., and W. R. Hopwood 1 992. Investigation of decorative coating on Kongo ceramics using u.v. light and FTIR analysis. In Materials Issues in Art and Archaeology 3: Symposium Held 2 7 April-1 May 1 992, San Francisco, ed. P. B. Vandiver, J . R . Druzik, G . S. Wheeler, and C. Freestone, 2 9 1 -3 0 7. Pittsburgh: Materials Research Society. 1. H i l l , H. E . 1 98 3-84. Chemical analysis o f pottery residues. Bulletin of the Experimental Firing Group 2: 86-89. Hill, J . 1 98 9 . Micro-scalpel. Western Association for Art Conservators Newsletter 1 1 ( 1 ) : 7-8. 1 99 3 . Conversation with author, Getty Conservation Institute, Marina del Rey, Calif., summer. Hodson, J . , and J. A. Lander 1 987. The analysis of cured paint media and a study of the weathering of alkyd paints by Fourier transform infra-red/photoacoustic spectroscopy. Polymer 2 8 ( 2 ) : 25 1-56. Holcomb, T., and C. Dean 1 99 3 . Letter to author, including samples, November. Hon, D. N. S . 1 989. Fourier transform IR spectroscopy and electron spectroscopy for chemical analysis: Use in the study of paper documents. In Historic Textile and Paper Materials: Conservation and Characterization, ed. H. L. Needles and H. S. Zeronian, 349-6 1 . Advances in Chemistry series 2 1 2 . Washington, D.C.: American Chemical Society. H umecki, H . J . 1 9 8 8 . Polymers and contaminants b y infrared microspectroscopy. I n Infrared Microspectroscopy, ed. R. G. Messerschmidt and M. A. Harthcock, 5 1 -72. New York: Marcel Dekker. 217 References 1 9 95a. Microsample preparation techniques. In Practical Guide to Infrared Microspectroscopy, ed. H. Humecki. New York: Marcel Dekker. H u m ecki, H., ed. 1 995b. Practical Guide to Infrared Microspectroscopy. New York: Marcel Dekker. H u m ph rey, B . 1 9 84. The application of Parylene conformal coating technology t o archival and artifact conservation. Studies in Conservation 2 9 ( 3) : 1 1 7. 1 9 8 6. Vapor phase consolidation o f books with the Parylene polymers. Journal o f the American Institute for Conservation 25( 1 ): 1 5-29. Ito, M., and M. Takahashi 1 9 8 5 . IR reflection-absorption spectroscopic study of benzotriazole on copper. Surface Science 1 5 8 ( 1-3):609- 1 5 . Jacq u i not, P. 1 954. 1 7e Congres du GAMS, Paris. J akes, K. A., and J . H. Howard I I I 1 96 8 . Formation o f textile fabric pseudomorphs. I n Proceedings o f the 24th International Archaeometry Symposium, ed. J. S. Olin and M. J. Blackman, 1 65-77. Washington, D.C.: Smithsonian Institution Press. J akes, K. A., J . E. Katon , and P. A. Martogl io 1 990. Identification of dyes and characterization of fibers by infrared and visible microspectroscopy: Application to Paracas textiles. In Archaeometry '90: Proceedings of the 2 7th Annual Archaeometry Symposium, ed. E. Pernicka and G. Wagner, 305- 1 5 . Basel, Switzerland: Birkhauser Verlag. Jakes, K. A., l. R. Sibley, and R. Yerkes 1 9 94. A comparative collection for the study of fibres used in prehistoric textiles from eastern North America. Journal of Archaeological Science 2 1 :641-50. J ayme, G., and G. Traser 1 9 7 1 . Infrarotspektroskopische Untersuchungen an gestrichenen Papieren: Die IR­ Spektren der Rohstoffe fur Streichmassen (Infrared spectroscopic investigations on coated papers: IR-spectra of raw materials used for paper coatings). Das Papier 25(7): 356-66. J ohnson, M., and E. Packard 1 9 7 1 . Methods used for the identification of binding media in Italian paintings of the fifteenth and sixteenth centuries. Studies in Conservation 1 6: 1 45-64. Karreman, M. F. S . 1 9 8 9. Toepassing van enkele analytische technieken ten behoeve van preventieve conservering en van incidentele vraagstellingen (Application of analytical techniques in solving problems in conservation science and some incidental questions). In Mogelijkheden en grenzen van natuurwetenschappelijk onderzoek aan en ten behoeve van voorwerpen van kunst en wetenschap, ed. W. G. T. Roelofs and J. A. Mosk. 65-72. Amsterdam: Centraal Laboratorium voor Onderzoek van Voorwerpen van Kunst en Wetenschap. Katon, J. E., and A. J . Sommers 1 9 92. IR microspectroscopy: Routine IR sampling methods extended to the micro­ scopic domain. Analytical Chemistry 64( 1 9 ) : 9 3 1 A-940A. Katon, J . E., A. J . Sommers, and P. l. Lang 1 9 8 9-90. Infrared microspectroscopy. Applied Spectroscopy Reviews 2 5 ( 3/4): 1 73-2 1 1 . Kauppinen, J . K., D . J . Moffatt, H . Mantsch, and D . G . Cameron 1 9 8 1 . Fourier self-deconvolution: A method for resolving intrinsically overlapped bands. Applied Spectroscopy 35(3):27 1 -76. 218 References Kenjo, T. 1 976. Effect of pH on the hardening of Japanese lacquer films. Science for Conservation 1 5 : 1-8. 1 97 8 . Studies o n the analysis o f lacquer, 2: Infrared spectrometry o f lacquer films. Kobunkazai no Kagaku (Scientific Papers on Japanese Antiques and Art Crafts) 23( 1 1 ): 32-39. K i rby, J . , and R. White 1 996. The identification of red lake pigment dyestuffs and a discussion of their use. National Gallery Technical Bulletin 1 7:56-74. Kiril lov, A. L., and E. A. Mikolajchuk 1990. Quantitative estimation of archaeological wood degradation degree by infra­ red Fourier transform spectroscopy. In ICOM Committee for Conservation 9th Triennial Meeting, Dresden, German Democratic Republic, 2 6-3 1 August 1 990, Preprints, ed. K. Grimstad, 239-40. Paris: ICOM Committee for Conservation. Kobus, H . J . 1 9 87. The use of Fourier transform infra-red spectroscopy and energy dispersive X­ ray microanalysis techniques for the analysis of small paint samples. ICCM Bulletin 1 3 ( 3/4 ) : 9- 1 6 . Koenig, Jack L . 1 992. Spectroscopy o f Polymers. Washington, D.C.: American Chemical Society. Koestler, R. J . 1 99 3 . Insect eradication using controlled atmospheres and FTIR measurement for insect activity. In ICOM Committee for Conservation 1 0th Triennial Meeting, Washington, D . C. , USA, 22-27 August 1 993, Preprints, ed. J. Bridgland, vol. 2, 8 82-86 . Paris: ICOM Committee for Conservation. Koltai, O. 1 984. Romai kori hagymafejes exust fibula restauralasa ( Restoration of a bulbiform silver fibula of the Roman Age). Muzeumi Mutargyvedelem 1 3 :275-84. Korte, E. H., and H . Staat 1 98 9 . Regular-reflection IR spectroscopy of historical varnishes. Proceedings of SPIE (International Society for Optical Engineering) 1 145 :296-97. Kortu m, G. 1 9 6 9 . Reflectance Spectroscopy. New York: Springer-Verlag. Kosek, J . , and L. R. Green 1 992. A survey of oil paintings and sketches on paper in the collection in the British Museum: An assessment of stability. In The Institute of Paper Conservation: Conference Papers, Manchester 1 992, ed. S. Fairbrass, 96-1 02. Worcester, U.K.: Institute of Paper Conservation. Kosik, M . , V. Luzakova, and V. Reiser 1 972. Study of the thermal degradation of cellulose and its derivatives. Cellulose Chemistry and Technology 6(5):5 89-97. Krishnan, K., J. R. Powel l , and S . L. H i l l 1 995. Infrared microimaging. I n Practical Guide t o Infrared Microspectroscopy. ed. H. Humecki. New York: Marcel Dekker. Kubel ka, P. 1 94 8 . New contributions to the optics of intensely light-scattering materials: Part l . Journal of the Optical Society of America 3 8 ( 5 ):448-57. Kuhn, H . 1 960. Detection and identification o f waxes, including punic wax b y infrared spectrography. Studies in Conservation 5 ( 2 ) : 1-79 . 1 970. Verdigris and copper resinate. Studies in Conservation 1 5( 1 ) : 1 2-36. 219 References Lang, P. L . , J . E. Katon, and A. S. Bonanno 1 9 8 8 . Identification o f dust particles by molecular microspectroscopy. Applied Spectroscopy 42: 3 1 3-17. Lang, P. L., J . E . Katon , J . F. O ' Keefe, a n d D. W . Schiering 1 98 6 . The identification of fibers by infrared and raman microspectroscopy. Microchemical Journal 34: 3 1 9-3 1 . Lang, P. L., M . V. Orna, L. J . Richwine, T. F. Mathews, and R . S . Nelson 1992. The visible and infrared microspectroscopic characterization o f organic red pig­ ments removed from three medieval Byzantine manuscripts. Microchemical Journal 46:234-48 . Langenheim, J . H., and C. W. Beck 1 965. Infrared spectra as a means of determining botanical source of amber. Science 149:52-55. 1 96 8 . Catalogue of infrared spectra of fossil resins (ambers), 1: North and South America. Botanical Museum Leaflets, Harvard University 22(3 ):65-120. Launer, P. J. 1 962. Perkin-Elmer Instrumentation News 1 3 ( 3 ) : 1 0. Laurie, A. P. 1 9 14. The Pigments and Mediums of the Old Masters. London: Macmillan. Laver, M. E., and R. S. Will iams 1 9 7 8 . The use o f a diamond cell microsampling device for infrared spectrophotomet­ ric analyses of art and archaeological materials. Journal of the IIC-Canadian Group 3 ( 2 ) :34-3 9. Lear, J . B . 1 9 8 1 . Analysis of paint films. Journal of Coatings Technology 5 3 ( 6 75 ) : 63-65. Lee, G . K. 1 9 9 1 . Analytical chemistry tracks poachers. Analytical Chemistry 6 3 ( 9 ) : 5 1 3A-5 1 5A. Leyden, D. E., and R. S . Murthy 1 9 86. Surface selective sampling techniques in Fourier transform infrared spec­ troscopy. Spectroscopy 2(2) :27. Leyshon, W. E., and R. N. Roberts 1 9 8 3 . Contaminated aerosol dusters. Abbey Newsletter 7(2):26. Liang, C. Y. 1 972. Infrared spectroscopy and physical properties of cellulose. In Instrumental Analysis of Cotton Cellulose and Modified Cotton Cellulose, ed. R. T. Conner. New York: Marcel Dekker. Lippincott, E. R., C. E. Weir, A. van Valkenburg, and E. N . B u nting 1 960. Studies of infrared absorption spectra of solids at high pressures. Spectrochimica Acta 1 6: 5 8-73 . Low, M. J. D . , and N. S. Baer 1 977. Application of infrared Fourier transform spectroscopy to problems in conser­ vation. Studies in Conservation 22: 1 1 6-28 . 1 978. Advances in the infrared spectroscopic examination o f pigments. In ICOM Committee for Conservation 5th Triennial Meeting, Zagreb, 1 -8 October 1 978, Preprints. Paris: International Council of Museums. Lubec, G., G. Nauer, K. Seifert, E. Strouhal, H. Porteder, J. Szilvassy, and M. Teschler 1 987. Structural stability of hair over three thousand years. Journal of Archaeological Science 14(2 ) : 1 1 3-20. Ludwig, F. J. 1 965. Analysis o f microcrystalline and paraffin waxes b y means o f infrared spectra in the molten state. Analytical Chemistry 3 7: 1 73 7-4 1 . 220 References Majors, R. E. 1 9 92. Nomenclature for sampling in analytical chemistry. LC·CC: Magazine of Liquid and Cas Chromatography 1 0 ( 7 ) : 500-506. Mal i s, T. F. , and D . Steele 1 9 9 0 . Ultramicrotomy for materials science. Materials Research Society Symposium Proceedings 1 99:3-42. Maniatis, Y., A. Katsanos, and M . E. Caskey 1 9 82. Technological examination of low-fired terracotta statues from Ayia Irini, Kea. Archaeometry 24(2 ) : 1 9 1-98. Marti n, G . 1 9 8 8. The identification of modern polymer systems using ET.I.R. In Preprints of Contributions to the Modern Organic Materials Meeting, Edinburgh, 1 4-1 5 April 1 988, 47-56. Edinburgh: Scottish Society for Conservation and Restoration. Martoglio, P. A., S. P. Bouffard, A. J . Sommer, J . E. Katon, and K. A. Jakes 1 990. Unlocking the secrets of the past: The analysis of archaeological textiles and dyes. Analytical Chemistry 62( 2 1 ) : 1 1 23A-1 1 28A. Masschelei n - K leiner, L., and J. B . Heylen 1 96 8 . Analysis of ancient red lacquers. Studies in Conservation 1 3 ( 2 ) : 8 7-97. Masschelei n - K leiner, L., J. Heylen, and F. Tricot-Marckx 1 96 8 . Contribution a l'analyse des liants, adhesifs et vernis anciens. Studies in Conservation 1 3: 1 05-2 1 . Masschelei n - K leiner, L . , a n d L . Maes 1 9 7 8 . Ancient dyeing techniques in eastern Mediterranean regions. In ICOM Committee for Conservation 5th Triennial Meeting, Zagreb, 1 -8 October 1 9 78, Preprints. Paris: International Council of Museums. Masschelei n - K leiner, L., and F. Tricot-Marckx 1 96 5 . La detection de polysaccharides dans les materiaux constitutifs des oeuvres d'art. Institut royal de patrimoine artistique-Bulletin 8 : 1 80-9 1 . Matsuda, Y. 1 9 8 6 . Dyeing behaviour and photofading of berberine as a dyestuff. Scientific Papers on Japanese Antiques and Art Crafts 31 :24-31 Matsuda, Y. , and T. Miyoshi 1 9 8 9 . Non-destructive analysis of Japanese ancient fabrics. Scientific Papers on Japanese Antiques and Art Crafts 34: 1 - 8 . Mattei n i , M . , A. Moles, a n d S. Giovannoni 1 9 94. Calcium oxalate as a protective mineral system for wall paintings: Methodology and analyses. In La conservazione dei monumenti nel bacino del Mediterraneo: atti del 3 ° simposio internazionale, Venezia, 22-25 giugno 1 994 (The conservation of monuments in the Mediterranean basin: Proceedings of the 3rd international symposium), ed. V. Fassina, H. Ott, and E Zezza, 1 5 5-62. Venice: Soprintendenza ai Beni Artistici e Storici di Venezia. Mattiel lo, J . 1 94 1 . Raw Materials for Varnishes and Vehicles. Vol. 1 o f Protective and Decorative Coatings: Paints, Varnishes, Lacquers, and Inks. New York: J. Wiley. McCawley, J. C. 1 9 75. Diamond cell infrared spectroscopy in the analysis of paints and pigments. In ICOM Committee for Conservation 4th Triennial Meeting, Venice, 1 3-1 8 October, Preprints, 5-1 1. Paris: International Council of Museums. McClure, A., J . Thomson, and J. Tannah i l l 1 9 6 8 . Infrared spectra o f ninety-six organic pigments. Journal of the Oil and Colour Chemists' Association 5 1 ( 7 ) : 580-635. 221 References McCormick-Goodhart, Mark 1 98 9 . Research on collodion glass plate negatives: Coating thickness and FTIR identification of varnishes. In Topics in Photographic Preservation, compo R. E. Siegel. Vol. 3. Washington, D . C . : Photographic Materials Group of the American Institute for Conservation of Historic and Artistic Works. McCrone, W. C. 1 982. The microscopical identification of pigments. Journal of the IIC-Canadian Group 7( 112 ) : 1 1-34. McCrone, W. c., and J. G . Deily 1 973. The Particle Atlas. 2d ed. Vol. 1. Ann Arbor, Mich.: Ann Arbor Science Publishers. McDonald, R. S., and P. A. W i l ks 1 9 8 8 . ]CAMP.DX: A standard form for exchange of infrared spectra in computer readable form. Applied Spectroscopy 42( 1 ): 1 5 1-62. McGovern, P. E., and R. H . M i chel 1 990. Royal purple dye: Its identification by complementary physicochemical tech­ niques. MASCA Research Papers in Science and Archaeology 7:69-76. Meikle, R. W., and D. Stewart 1962. The residue potential of sulfuryl fluoride, methyl bromide and methane­ sulfonyl fluoride in structural fumigations. Journal of Agricultural and Food Chemistry 1 0( 5 ) : 393-97. Mei l u nas, R. J . 1 98 6 . The application o f diffuse reflectance infrared Fourier transform spectroscopy to the analysis of paint surfaces. Bachelor's thesis, Massachusetts Institute of Technology, Boston. Mei l u nas, R. J . , J. G. Bentsen, and A. Stein berg 1 990. Analysis of aged paint binders by FTIR spectroscopy. Studies in Conservation 35:33-5 1 . Messerschm idt, R . G . 1 9 8 8 . Photometric considerations in the design and use o f infrared microscope acces­ sories. In Infrared Microspectroscopy: Theory and Applications, ed. R. G. Messerschmidt and M. A. Harthcock. New York: Marcel Dekker. Messerschmidt, R. G . , and M. A. Harthcock, eds. 1 9 8 8 . Infrared Microspectroscopy: Theory and Applications. New York: Marcel Dekker. Michelson, A. A. 1 89 1 . Visibility of interference-fringes in the focus of a telescope. Philosophical Magazine 5 ( 3 1 ) :256-59. 1 902. Light Waves and Their Uses. Chicago: University of Chicago Press. Mikolajchuk, E. A., N. G. Gerassi m ova, A. A. leonovich, A. V. Obolenskaya, I. Y. levd ik, and S. Y. Kazanskaya 1 987. Examination of waterlogged archaeological oak wood. In Conservation of Wet Wood and Metal: Proceedings of the ICOM Conservation Working Groups on Wet Organic Archaeological Materials and Metals, ed. I. D. MacLeod, 95-107. Paris: International Council of Museums. M i l l er, J . , E. Moffatt, and J. S i rois 1 990. CCI Native Materials Project: Final Report. Ottawa: Canadian Conservation Institute, Analytical Research Services. Mills, J . S . , and R. White 1 977. Natural resins of art and archaeology: Their sources, chemistry and identification. Studies in Conservation 22: 1 2-3 1 . 1 994. The Organic Chemistry of Museum Objects. 2 d ed. London: Butterworth­ Heineman. 222 References Morris, N. M. 1 9 9 1 . Comparison of sampling techniques for the characterization of cotton textiles by infrared spectroscopy. Textile Chemist and Colorist 2 3 (4 ) : 1 9-22. Moser, F. H . 1 973. Ultramarine pigments. I n Pigment Handbook, ed. T. C . Patton. Vol. 1 . New York: Wiley. Newman, G. A., and G. W. W. Stevens 1 977. Identification of an early microphotographic emulsion by means of infrared spectroscopy. Laboratory Practice 2 6 ( 1 0 ):78 1-82. Newman, M . 1 994. Immunological analysis of a paint fragment from a Chumash site, Santa Barbara County, California. Analysis report to David Scott, Getty Conservation Institute, Los Angeles. Newman, R. 1 9 8 0 . Some applications of infrared spectroscopy in the examination of painting materials. Journal of the American Institute for Conservation 1 9 ( 1 ) :42-62. 1 99 6 . Conversation with author, Museum of Fine Arts, Boston, fall. Newman, R., C. Weston , and E. Farrell 1 9 80. Analysis of watercolor pigments in a box owned by Winslow Homer. Journal of the American Institute for Conservation 1 9 : 1 03-4. Nowl i n , T. E., D. F. S m ith, and G. S. Cieloszyk 1 98 0 . Thermal oxidative stability of poly p-xylylenes. Journal of Polymer Science 1 8 : 2 1 03- 1 9 . Nyquist, Richard A. 1 96 8 . Factors affecting infrared group frequencies: Carbonyl stretching absorption bends. Applied Spectroscopy 4 0 ( 3 ) : 3 3 6-39 . O l i n , J . S. 1 9 6 6 . The use of infrared spectrophotometry i n the examination o f paintings and ancient artifacts. Instrument News 1 7: 1 . O l i n , J . S., M . E . Salmon, and C. H . O l i n 1 969. Investigations o f historical objects utilizing spectroscopy and other optical methods. Applied Optics 8 ( 1 ) :29-39. Omecinsky, D . , a n d G . W. Carriveau 1 9 82. IR investigation of resinous and synthetic varnishes. In Preprints of Papers Presented at the 1 0th Annual Meeting, Milwaukee, Wisconsin, 20-30 May 1 982, 1 41 -49. Washington, D.C. : American Institute for Conservation of Historic and Artistic Works. Oosterbroek, M . , R. J . Lammers, L. G. J . van der Ven, and D. Y. Perera 1 9 9 1 . Crack formation and stress development in an organic coating. JCT: Journal of Coatings Technology 6 3 ( 797):55-60. Orna, M . V. , P. L. Lang, J. E . Katon, T. F. Mathews, and R. L. Nelson 1 98 9 . Applications of infrared microspectroscopy to art historical questions regarding medieval manuscripts. In Archaeological Chemistry 4, ed. R. Allen, 265- 8 8 . Washington, D.C. : American Chemical Society. Palenik, S . 1 992. Modern microscopy o n the light side: The FTIR microscope. Microscopy Today 7:4-5. Paralusz, C. 1 974. Internal reflection spectroscopy applied to the analysis of adhesive tapes. Journal of Colloid and Interface Science 47( 3 ) : 7 1 9-46. References 223 Parra, E., a n d A. Serrano 1 990. Chemical analysis of wax seals and dyed textile attachments born parchment documents: Preliminary investigations. In ICOM Committee for Conservation 9th Triennial Meeting, Dresden, German Democratic Republic, 2 6-3 1 August 1 990, Preprints, ed. K. Grimstad, 62-67. Paris: ICOM Committee for Conservation. Payne, K. J . , and A. Veis 1 9 8 8 . Fourier transform IR spectroscopy of collagen and gelatin solutions-deconvo­ lution of the amide I band for conformational studies. Biopolymers 27: 1 749-60. Pecina, H., and R. Kommert 1 9 8 5 . Badania spektroskopowe w podczerwieni drewna z roznych epok historycznych (Infra-red spectral studies of wood from different historical periods). Folia forestalia polonica, b (drzewnictwo) 1 6:3 1-4 3 . Perron, J . 1 98 9 . The use o f FTIR i n the study o f photographic materials. I n Topics in Photographic Preservation, compo R. E. Siegel. Vol. 3. Washington, D.C.: Photographic Materials Group of the American Institute for Conservation of Historic and Artistic Works. Pey, E. B. F. 1 987. The Hafkenscheid Collection: A collection of pigments and painting materials dating from the first half of the 1 9th century. Maltechnik-Restauro 93(2 ):23-3 3 . Pl ahter, L . E . , E . Skug, and U . Plahter 1 974. Gothic painted altar frontals from the church of Tingelstad: Materials, tech­ nique, restoration. Mediaeval Art in Norway. Vol. 1 . Oslo: Universitetsforlaget. Pl esters, J . 1 954. The preparation and study o f paint cross-sections. Museums Journal 54(4):97. 1 95 6 . Cross-sections and chemical analysis of paint samples. Studies in Conservation 2 ( 3 ) : 1 1 0-57. Poole, J. B., and R. Reed 1 962. The preparation of leather and parchment by the Dead Sea Scrolls community. Technology and Culture (winter ) : 1-26. Poslusny, M., and K . E. Daugh erty 1 98 8 . Nondestructive adhesive analysis on stamps by Fourier transform infrared spectroscopy. Applied Spectroscopy 42( 8 ) : 1 466-6 9 . Pratt, E . 1 9 9 1 . A n investigation into a cast resin sculpture by Jean Dubuffet. I n Selected Student Papers of the Seventeenth Annual Conservation Training Programs Conference, April 2 5-2 7, 1 99 1 . Buffalo: Department of Conservation, State University of New York at Buffalo. Pretzel, B . 1 994. Silicon carbide sampling for FT-IR. Presentation a t Infrared User's Group meet­ ing, Philadelphia Museum of Art, Philadelphia. Rao, G. B . 1 982. Effect o f atmospheric pollutants ( SO/ NO/ Cll/ H2S) o n marble. Birla Archaeological and Cultural Research Institute Technical Bulletin 4 : 1 1-2 1 . 1 984. The effect of product of relative humidity and concentration o f sulfur dioxide on marble. Journal of Archaeological Chemistry 2:39-40. Rayleigh, Lord 1 89 1 . On the interference bands of approximately homogeneous light: In a letter to Prof. A. Michelson. Philosophical Magazine 5(34 ):407-1 1 . Reedy, T. J . , and C . L . Reedy 1 9 8 8 . Statistical Analysis in Art Conservation Research. Los Angeles: J. Paul Getty Trust. 224 References Reffner, J . A. 1 9 89. Infrared spectral mapping of polymers by FT-IR microscopy. In Microbeam Analysis-1 089, ed. P. E. Russell, 1 6 7-76. San Francisco: San Francisco Press. 1 993. The commercial development of FT-IR microspectroscopy. Microscopy Today 93-3:6. Reffner, J. A., and P. A. Martogl io 1 995. Uniting microscopy and spectroscopy. In Practical Guide to Infrared Microspectroscopy. ed. H. Humecki, 41-84. New York: Marcel Dekker. Reffner, J . A., W. T. W i h lborg, and S . W. Strand 1 9 9 1 . Chemical microscopy of surfaces by grazing angle and internal reflection FTIR microscopy. American Laboratory 23(April):46-50. Reid, N. 1 9 72. Ultramicrotomy (part 2). In Practical Methods in E lectron Microscopy. Amsterdam: North-Holland Publishing Co. Rei l l y, J . A. 1 9 9 1 . Celluloid objects: Their chemistry and preservation. Journal of the American Institute for Conservation 30( 2 ) : 1 45-62. Riederer, J . 1 9 69. Infrarotspektrographische Untersuchung der gel ben und roten Eisenoxidpigmente. Deutsche Farben-Zeitschrift 23( 1 2 ): 5 69-77. 1 9 74. Recently identified Egyptian pigments. Archaeometry 1 6 ( 1 ) : 1 02-9. 1 9 77. Technik und Farbstoffe der fruhmittelalterlichen Wandmalereien Ostturkistans (Technique and materials of early medieval mural paintings from East Turkistan). In Beitraege zur Indienforschung-Ernst Waldschmidt zum 80 Geburtstag gewidmet ( Contributions to Indian research in honour of Ernst Waldschmidt's 8 0th birthday). Veroeffentlichen des Museums fiir Indische Kunst Berlin 4. Berlin: Museum fiir Indische Kunst. Robinson, N . , R. P. Evershed, W. J. Higgs, K. Jerman, and G. Egl i nton 1 9 87. Proof of a pine wood origin for pitch from Tudor (Mary Rose) and Etruscan shipwrecks: Application of analytical organic chemistry in archaeology. Analyst 1 1 2:637-44. Roelofs, W. G . T. [ 1 9 8 9]. Het onderzoek naar vernissen, bindmiddelen en organische kleurstoffen op voorwerpen van kunst en wetenschap (Identification of varnishes, media, and organic dyestuffs occurring on objects of art and science ). In Mogelijkheden en grenzen van natuurwetenschappelijk onderzoek aan en ten behoeve van voorwerpen van kunst en wetenschap, ed. W. G. T. Roelofs and J. A. Mosk, 24-33. Amsterdam: Centraal Laboratorium voor Onderzoek van Voorwerpen van Kunst en Wetenschap. Roelofs, W. G. T., P. B. Hall ebeek, J . H. Hofenk De G raaff, and R. F. S. Karreman 1 9 8 7. The analysis of natural dyestuffs and organic pigments: A comparative study into the possibilities and limits of various methods. In ICOM Committee for Conservation 8th Triennial Meeting, Sydney, Australia, 6-1 1 September 1 987, Preprints, ed. K. Grimstad, vol. 2, 709-17. Marina del Rey, Calif.: Getty Conservation Institute. Rogers, P. G . , R. Cameron, N. S. Cartwright, W. H. Clark, J . S. Deak, and E. W. W. Norman 1 9 76. The classification of automotive paint by diamond window infrared spec­ trophotometry, part 1: Binders and pigments. Journal of the Canadian Society for Forensic Science 9: 1-14. Rothe, A. 1 9 9 1 . Analysis request form, Getty Conservation Institute, Marina del Rey, Calif., spring. 1 9 92. Mantegna's paintings in distemper. In Andrea Mantegna, ed. J. Martineau. London: Royal Academy of Arts; New York: Metropolitan Museum of Art. References 225 Roush, P. B . , ed. 1 987. The Design, Sample Handling, and Applications of Infrared Microscopes: A Symposium. ASTM Special Technical Publication 949. Philadelphia: American Society for Testing Materials. Roy, A., ed. 1 99 3 . Artists ' Pigments: A Handbook of Their History and Characteristics. Vol. 2. Washington, D.C. : National Gallery of Art. ( Contains articles with IR spectra on azu­ rite and blue verditer; ultramarine blue; lead white; lead-tin yellow; smaIt; verdigris and copper resinate; vermilion and cinnabar; malachite and green verditer; and cal­ cium carbonate whites.) Ryland, S. G . 1 995. Infrared microspectroscopy of forensic paint evidence. I n Practical Guide to Infrared Microspectroscopy, ed. H. Humecki. New York: Marcel Dekker. Saltzman, M . 1 992. Identifying dyes i n textiles. American Scientist 80:474-8 1 . Saltzman, M . , and A. Keay 1 972. Colorant identification. In Fundamentals and Problems of Color. Philadelphia: Federation of Societies for Paint Technology. Saltzman, M., A. Keay, and J . Ch ristensen 1 96 3 . Identification of colorants in ancient textiles. Dyestuffs 44( 8 ) :24 1 -5 1 . Sands, J . 1 993. "An effect which far exceeds any conception . . . " Colonial Williamsburg: The Journal of the Colonial Williamsburg Foundation (spring):72-73 . Schreiner, M . , and M. Grasserbauer 1 98 5 . Microanalysis of art objects: Obj ectives, methods and results. Fresenius' Journal of Analytical Chemistry 322: 1 8 1 -9 3 . Schrenk, J . l. 17-21, 19 0, 1 9 9 1 . Corrosion and past " protective" treatments o f the Benin "bronzes" i n the National Museum of African Art. In Materials Issues in Art and Archaeology 2 : Symposium Held April San Francisco, California, USA, ed. P. B. Vandiver, ]. Druzik, and G. S. Wheeler, 805-12. Pittsburgh: Materials Research Society. Sch u lz, H . , and B. Kropp 1 99 3 . Microspectroscopy FTIR reflectance examination of paint binders on ground chalk. Fresenius' Journal of Analytical Chemistry 346 : 1 14-22. Schweppe, H. 1 979. Identification of dyes on old textiles. Journal of the American Institute for Conservation 1 9( 1 ) : 1 4-23 . 1 9 8 9 . Identification o f red madder insect dyes b y thin layer chromatography. In Historic Textile and Paper Materials: Conservation and Characterization, ed. H. L. Needles and H. S. Zeronian, 1 5 3-74. Advances in Chemistry series 212. Washington, D.C.: American Chemical Society. Schwochau, K., T. E. Haevernick, and D. Ankner 1 963. Zur infraotspecktrosckopischen Herkunftsbestimmung von Bernstein ( Using infra-red spectroscopy to determine origins of amber). Jahrbuch des Romisch­ Germanischen Zentrals-Museums Mainz 1 0 . Scott, D. A. 1 994. Analysis request form, Getty Conservation Institute, Marina del Rey, Calif., March. Scott, D. A., and W. D. Hyder 1 99 3 . A study of some California Indian rock art pigments. Studies in Conservation 3 8 : 1 55-73. 226 References Scott, D. A., M. Newman, M. Sch i l l i ng, M. Derrick, and H. Khanjian 1 996. Blood as a binding medium in a Chumash Indian pigment cake. Archaeometry 3 8 ( 1 ) : 1 03-12. Selwitz, C . 1 9 8 8 . Cellulose Nitrate in Conservation. Research i n Conservation 2 . Marina del Rey, Calif.: Getty Conservation Institute. Sharpless, T. W. 1 98 0 . Corrosion: The problem of storage. The Numismatist ( October) : 2450-54. Shearer, G. 1 98 7 . Use of diffuse reflectance Fourier transform infrared spectroscopy in art and archaeological conservation. In Recent Advances in the Conservation and Analysis of A'fifacts: Jubilee Conservation Conference, London, 6-1 0 July 1 987, compo James Black, 253-5 6 . London: University of London, Institute of Archaeology, Summer Schools Press. Shearer, G. L., and S. Doyal 1 9 9 1 . Use of FT-IR in the conservation of twentieth-century objects. In Materials Issues in Art and Archaeology 2: Symposium Held April 1 7-2 1 , 1 990, San Francisco, California, USA, ed. P. B. Vandiver, J. Druzik, and G. S. Wheeler, 8 1 3-2 3 . Pittsburgh: Materials Research Society. Shearer, J . C, D. C. Peters, G. Hoepfner, and T. Newton 1 9 8 3 . FTIR in the service of art conservation. Analytical Chemistry 5 5 ( 8 ) : 8 74-76, 8 78-80. Shelton, C. 1 994. Letter to author, including samples, November. Shoeib, A. S. A., M. Roznerska, and K. Boryk-Jozefowicz 1 9 9 0 . Weathering effects on an ancient Egyptian limestone, which has been affected by salt. In The Conservation of Monuments in the Mediterranean Basin-The Influence of Coastal Environment and Salt Spray on Limestone and Marble: Proceedings of the 1 st International Symposium, Bari, 7-1 0 June 1 989/La conser­ vazione dei monumenti nel bacino Mediterraneo: Influenza dell ambiente costiero e dello spray marino sulla pietra calcareo e sui marmo. Atti del l Simposio inter­ nazionale, Bari, 7-1 0 giugno 1 989, ed. Zezza, 203-8. Brescia, Italy: Grafo Edizioni. F. Sh reve, O. D . , M. R. Heether, H. B. Knight, and D. Sween 1 950. Infrared absorption spectra: Some long chain fatty acid esters and alcohols. Analytical Chemistry 22: 14 9 8-1 5 0 1 . Siesmayer, B . , A . G iebelhausen, J . Zam be l l i , and J . Riederer 1 975. Application of infrared spectroscopy to the examination of mineral pigments of historical works of art in comparison with recent European deposits. Fresenius' Journal of Analytical Chemistry 277( 3 ) : 1 93-96. S m ith, A. L. 1 979. Applied Infrared Spectroscopy: Fundamentals, Techniques and Analytical Problem Solving. Chemical Analysis series, vol. 54. New York: John Wiley and Sons. Sommer, A. J . , and J. E. Katon 1 98 8 . In Proceedings of the 23rd Annual Conference of the Microbeam Analysis Society, ed. D. E. Newbury, 207-14. San Francisco: San Francisco Press. Souza, L., and M. Derrick 1 995. The use of FT-IR spectrometry for the identification and characterization of gesso-glue grounds in wooden polychromed sculptures and panel paintings. In Materials Issues in Art and Archaeology 4: Symposium Held May 1 6-2 1 , 1 994, Cancun, Mexico, ed. P. B. Vandiver, J. R. Druzik, J. L. G. Madrid, I. C. Freestone, and G. S. Wheeler. Pittsburgh: Materials Research Society. References 227 Sramek, J . 1 97 8 . The non-destructive investigation o f chemical alterations i n the surface of stones. In Alteration et protection des monuments en pierre: Colloque international, Paris, 5-9 juin 1 9781Deterioration and Protection of Stone Monuments: International Symposium, June 5-9, 1 978. Paris: n.p. Staats, H . , E. H. Korte, and o. Kolev 1 98 9 . Infrared reflection studies of historical varnishes. In Recent Developments in Molecular Spectroscopy, ed. R. Jordanov, 64-74. Teaneck, N.J. : World Scientific Publishing Co. Sti mson, M. M . , and M. J . O'Oonnell 1 952. Journal of the American Chemical Society 74: 1 805. Stodulski, L . 1 994. Telephone conversation with author, summer. Strauss, I. 1 98 4 . Uebersicht ueber synthetisch organische Kuenstlerpigmente u n d Moeglichkeiten ihrer Identifizierung (A survey of synthetic organic artists' pigments and their possible identification). Maltechnik-Restauro 90(4):29-44. Stringari, c., Q. and E. Pratt 1 99 3 . The identification and characterization of acrylic emulsion paint media. In Symposium '9 1 : Saving the Twentieth Century-the Degradation and Conservation of Modern Materials, Abstracts, 4 1 1-40. Ottawa: Canadian Conservation Institute. Susi, H . , J. S. Ard, and R. J . Carro l l 1 975. Hydration a n d denaturation of collagen as observed by infrared spectroscopy. Journal of the American Leather Chemists Association 66( 1 1 ) : 5 0 8-1 9. Sutton, M. 1 990. Notes on creosote lac scale insect resin as a mastic and sealant in the south­ western Great Basin. Journal of California and Great Basin Anthropology 1 2 ( 2 ) :262-6 8 . Taylor, O . 1 967. The sodalite group o f minerals. Contributions to Mineralogy and Petrology 1 6 : 1 72 . Teetsov, A. S . 1 977. Techniques for small particle manipulation. The Microscope 2 5 : 1 03-1 3 . 1 995. Techniques for nanogram samples. I n Practical Guide t o Infrared Microspectroscopy. ed. H. Humecki. New York: Marcel Dekker. Tennent, N. H . , and K. M. Antonio 1 9 8 1 . Bronze disease: Synthesis and characterisation of botallackite, paratacamite and atacamite by infra-red spectroscopy. In ICOM Committee for Conservation 6th Triennial Meeting, Ottawa, 2 1 -25 September 1 98 1 , Preprints, 3-1 1 . Paris: ICOM Committee for Conservation. Tennent, N. H . , and T. Baird 1 98 5 . The deterioration of Mollusca collections: Identification of shell efflorescence. Studies in Conservation 30(2) :73-85 . Tobe, H . , N . Morito, K. Monma, a n d W. Suetaka 1 974. Spectrographic investigation of the corrosion inhibition of copper by benzimi­ dazole. Journal of the Japan Institute of Metals 3 8 ( 8 ) : 770-76. Todd, J. M., M. H . E i chel, C. W. Beck, and A. Macch iaru lo 1 976. Bronze and iron age amber artifacts in Croatia and Bosnia-Herzegovina. Journal of Field Archaeology 3 ( 3 ) : 3 1 3-27. Tranter, G . C. 1 976. Patination of lead: An infra-red spectroscopic study. British Corrosion Journal 1 1 (4) :222-24. 228 References Tsang, J . , and R. Cunn ingham 1 9 9 1 . Some improvements in the study of cross-sections. Journal of the American Institute for Conservation 30(2): 1 63-77. Tungol, M . W., E . G . Bartick, and A. Montaser 1 9 9 1 . Analysis of single polymer fibers by Fourier transform infrared microscopy: The results of case studies. Journal of Forensic Sciences 36(4) : 1 027-4 3 . 1 995. Forensic examination o f synthetic textile fibers b y microscopic infrared spec­ trometry. In Practical Guide to Infrared Microspectroscopy, ed. H. Humecki. New York: Marcel Dekker. Twi l l ey, J . 1 984. The analysis o f exudate plant gums in their artistic applications: An interim report. In Archaeological Chemistry 3, ed. J. B. Lambert, 357-94. Advances in Chemistry series 205. Washington, D.C.: American Chemical Society. van der Loeff, L. S . , and K. Groen 1 993. The restoration and technical examination of Gerard Dou's The Young Mother in the Mauritshuis. In ICOM Committee for Conservation 1 0th Triennial Meeting, Washington, D . C., USA, 22-27 August 1 993, Preprints, ed. J. Bridgland, 98-103. Paris: ICOM Committee for Conservation. van't H u l - Ehrnreich, E. H . 1 970. Infrared microspectroscopy for the analysis of old painting materials. Studies in Conservation 1 5 : 1 75-82. van Zelst, L., D. W. von Endt, and M . Baker 1 9 8 8 . Non-destructive and micro-sample FTIR spectrometric analysis of organic materials in art objects. In 2nd international conference on non-destructive testing, microanalytical methods and environment evaluation for study and conservation of works of art, Perugia, 1 7-20 April 1 9 88, 3 0 . 1-30. 1 7. Rome: Istituto Centrale per il Restauro-Associazione Italiana Prove Non Distruttive. Venkataraman, K., ed. 1 977. Analytical Chemistry of Synthetic Dyes. New York: John Wiley and Sons. Vincent, R. K., and G. R. H u nt 1 96 8 . Infrared reflectance from matte surfaces. Applied Optics 7 ( 1 ) : 5 3 . Walker, P. L., a n d T. Hudson 1 993. Chumash Healing: Changing Medical Practices in an American Indian Society. Banning, Calif.: Malki Museum Press. Wannemacher, R. 1 9 80. IR spectrophotometry: Valuable tools for textile chemists. American Dye Stuff Reporter 69:26-28 , 3 5 . Ward's Natural Science 1 990. Embedding in Bio-Plastic. 6th ed. Ward's Curriculum Aid no. 246-0005. Rochester, N.Y.: Ward's Natural Science. Warren, J. R., W. E. Smith, and W. J . Ti l l man 1 969. Internal reflectance spectroscopy and the determination of the degree of denat­ uration of insoluble collagen. Journal of the American Leather Chemists Association 64:4-1 1 . Watchman, A. 1 99 3 . Perspectives and potentials for absolute dating prehistoric rock paintings. Antiquity 67:5 8-65. Webster, R . 1 9 8 3 . Gems: Their Sources, Descriptions and Identification 4th e d . London: Butterworths. Weiner, S., Z. Kusanovich, E. G i l -Av, and W. Traub 1 9 80. Dead Sea Scrolls parchments: Unfolding of the collagen molecules and race­ mization of aspartic acid. Nature 2 8 : 820-23. 229 References Weir, C. E., E. R. Lippincott, A. van Val ken burg, and E. N. B u nting 1 9 6 0 . Infrared studies in the 1- to i s-micron region to 30,000 atmospheres. Journal of Research of the National Bureau of Standards-A, Physics and Chemistry 6 3 ( 1 ):55-62. West-FitzHugh, E., ed. 1 997. Artists' Pigments. Vol. 3 . Washington, D.C.: National Gallery of Art. ( Contains articles with IR spectra on Egyptian blue, orpiment and realgar, indigo and woad, madder and alizarin, gamboge, Vandyke brown, Prussian blue, emerald green and Scheele's green, chromium oxide greens, and titanium dioxide whites. ) White, J . 1 964. New method for measuring diffuse reflectance in the infrared. Journal of the Optical Society of America 54( 1 1 ) : 1 33 2 . Wh ite, R. L., a n d J . Ai 1 992. Variable-temperature diffuse reflectance infrared studies of calcium oxalate monohydrate. Applied Spectroscopy 46( 1 ) :93-99. Wilks, P. A., J r. 1 967. Applications of internal reflection spectroscopy: Identification of gas chro­ matographic fractions, pyrolysis, and skin analysis. In Modern Aspects of Reflectance Spectroscopy, Proceedings Symposium, 1 92-206. New York: Plenum Press. Wilks, P. A., J r. , and M. R. Iszard 1 965. The identification of fibers and fabrics by internal reflection spectroscopy. In Developments in Applied Spectroscopy, vol. 1 4 , ed. E. N. Davis, 1 4 1-49. New York: Plenum Press. Wil l iams, R. 5., J . B. Waddington, and J. Fenn 1 990. Infrared spectroscopic analysis of Central and South American amber exposed to air pollutants, biocides, light and moisture. Collection Forum 6(2):65-75. Wolbers, R. 1 9 84. Developing Fourier transform infrared spectroscopy ( FTIR) as an aid in the detection of asphalt-containing paint films. In Art Conservation Training Programs Conference, May 1 -3, 1 983, Postprints, 1 03-22. Cooperstown, New York: Department of Conservation of Historic and Artistic Works, State University of New York at Buffalo. Wright, N., and L. W. Hersher 1 947. Journal of the Optical Society of America 37:2 1 l . Zappia, G., C . Sabbion i , M . G . Pauri, and G . Gobbi 1 992. Effects of SOl-enriched atmosphere on ancient and modern building materials. Materials Engineering 3 ( 3 ) :445-5 8 . Zolotovich, G . , and A . Popov 1 969. Cosmetics from a Thracian tomb in Bulgaria ( 1 st century Cosmet. 42(6):425-32. A.D. ) Soap, Perfum. Zuber, G . E., R. J. Warren, P. P. Begosh, and E. L. O'Donnell 1 984. Direct analysis of thin-layer chromatography spots by diffuse reflectance Fourier transform infrared spectrometry. Analytical Chemistry 5 6 ( 1 4 ) :2935. Index Amides, absorption band frequencies of, Note: Italicized letters ( and t following page numbers indicate figures and tables, respectively, 46-47, 48t, 49( Amplitude, of radiation waves, 5 , 6( Anhydrides, absorption band frequencies of, A 96-97, 98( Anhydrite, absorption bands for, 1 1 7 Animal glue, reference spectrum for, 1 8 1 ( Anionic groups, absorption bands for, 1 1 6t, Absorbance mode, for spectral display, 84(, 85 Absorbance ratio method, 1 2 3-124 Absorption in IR experiments, 1 3 theory of, 6-1 2 Absorption bands for anionic groups, 1 1 6t, 1 1 6-1 1 8 correlation charts for, 99, 99( frequency of, 82-83 for selected functional groups, 95t, 1 1 6-1 1 8 Aperture(s), i n I R microspectroscopy, 95-98 96-97, 98( 34t, 36, 36( for infiltration prevention, 37 IR transmittance spectrum of, 1 1 0(, 1 9 1 ( Acryloid B-72 IR spectra for, 43, 44(, 1 1 0( with expanded carbonyl region, 6 1 ( reference spectrum for, 1 9 1( Adhesive tape, for fiber collection, 32 Adhesives, chemical analysis methods for, 1 8t Adoration o( the Magi (Mantegna), infrared analysis of, 1 52-154, 1 5 3( Air pollutants, chemical analysis methods for, 1 8 t Alcohols, absorption band frequencies of, 96, 97( Aldehydes, absorption band frequencies of, 96-97, 98( Alkali halide pellets, in IR microspec­ troscopy, 71( Aluminum foil, for sample storage, 22, Aluminum mirrors, in reflection­ absorption, 63 Amber, spectral identification of, 1 04 26 71, 72, 76 in infrared spectrum, 1 1 attributes of, 82-83 intensity of, 83 and concentration of absorbing mole­ cules, 85, 122-123 and dipole moment, 122 in quantitative analysis, 1 2 1 for polyester, 37 shapes of, 8 3 for water vapor, 9( Accelerated aging studies, 1 3 3 Acetone, a s solvent, 3 0 Acids, absorption band frequencies of, Acrylic, 1 9 1 for embedding of paint cross sections, infrared transmission characteristics of, 95t, 97-98, 98( and cross section analysis, 76-77, 77( and diffraction effects, 73-74, 75( effects of varying area of, 72-73, 74( selection of, 72( Arabic gum, reference spectrum for, 1 79( Archaeological objects, infrared analysis of, 1 3 1 Chumash Indian paints, 1 4 1 - 1 44, 143(, 1 44(, 145( Dead Sea Scrolls, 1 66-170, 1 69(, 1 70( Area mapping microspectroscopy, '77, 78( Art objects infrared analysis of, 1 3 0- 1 3 1 cellulose nitrate sculptures, 1 63-165, 1 66(, 1 67( paintings of Italian masters cross sections in, 1 52-1 5 5 ultramarine pigments in, 1 34-1 3 8, 1 3 5(, 1 3 6( inorganic substances in, 1 7 organic substances in, 1 7- 1 8 Artist's brush, 2 0 , 2 1 ( for cross section sampling, 3 3 in microtoming, 4 1 Artists' Pigments handbook series, 1 1 3 ATR objective, 79, 80( Attenuated total reflection (ATR), 60, 65, See also Internal reflection spectroscopy case studies using, 1 60-163, 1 6 8 IR spectra of Acryloid B-72 collected by, Barium sulfate mid-IR absorption band regions for, 1 1 9t reference spectrum for, 1 96( Baseline, spectrum as quality check, 8 8 , 8 8 t sloping, 8 8 , 8 9 ( Basic copper carbonate, reference spectrum for, 1 99( Beam condensers, 52, 54( in internal reflection spectroscopy, 67 Beer's law, 85, 122-123 Beeswax, IR transmittance spectrum for, 1 0 1 (, 1 84( Bending vibration, 1 1 Benzene, a s solvent, 29( BEVA 3 7 1 , reference spectrum for, 1 92( Binders in California rock paintings, 142-144 chemical analysis methods for, 1 8 t, 34 IR analysis of paints and, 120 Black pigments mid-IR absorption band regions for, 1 1 9t Blood as binder in Chumash Indian paints, 142-143 dried, IR transmittance spectrum for, 143( Blue pigments mid-IR absorption band regions for, 1 1 9t reference spectra for, 1 97(-1 98( ultramarine pigments, infrared analysis of, 1 34-1 3 8, 1 3 5(, 1 3 6( Bohr, Niels, atomic model of, 7, 7( Brown, mid-IR absorption band regions for, 1 1 9 t C B Calcite (calcium carbonate) absorption bands for, 1 1 6, 1 1 6t and rabbit-skin glue, IR transmittance spectra for mixture of, 1 2 1 ( infrared transmittance spectrum of, 1 1 5( reference spectrum for, 194( Calcium fluoride, infrared transmission char­ acteristics of, 4 8t Calcium oxalate, as weathering product, studies of, 1 3 3-1 3 4 Calcium sulfate, reference spectra for, Badakhshan mines, Afghanistan, lapis lazuli from, 1 3 7(, 1 37-138 Balsam, reference spectra for, 1 8 6(-1 8 7( Barite absorption bands for, 1 1 7 I R transmittance spectrum for, 1 1 5( Barium fluoride for elimination of interference fringes, 76 Calibration curve, 1 2 3 Capillary tubes for liquid sampling, 2 6 in solvent extraction, 3 1 Carbon dioxide, extraneous bands produced by, 8 8t, 90-91 Carbon disulfide, as diluent, 5 1 44(, 6 1 ( microspectroscopy, 7 9 Autoscale subtraction computer routine, 124 Azurite, absorption bands for, 1 1 6, 1 1 6t, 1 1 7 1 94(, 1 95( 231 Index Carbon double bond region in polymer identification, 1 1 2 in spectral interpretation, 94 Carbon tetrachloride, as diluent, 5 1 Carbonates, absorption bands for, 1 1 6t, 1 1 6-1 1 7 Carbonyls, absorption band frequencies of, 95t, 96-98, 98f Carnauba wax, reference spectrum for, 1 84f Case studies cellulose nitrate sculptures, 1 6 3-165, 1 66f, 1 67f Chumash Indian paints, 141-144, 143f, 144f, 145f creosote lac resin, 1 38-1 4 1 , 140f Dead Sea Scrolls, 1 66-170, 1 69f, 1 70f furniture surface treatments, 144-148, 147f mapping microspectroscopy, 152-155 Parylene oxidation, 1 5 9-163, 1 6 1f, 1 62t reflection versus transmission analysis, 148-152 ultramarine pigments, 1 34-1 38, 1 35f, 1 3 6f Vikane interaction with solid materials, 1 55-159, 158f, 1 5 9f Casein, reference spectrum for, 1 82f Cassegrain reflective optics objective, 80f Cat-hair brush, 20, 21f in microtoming, 41 Cellulose nitrate, 163, 190 reference spectrum for, 1 90f sculptures, infrared analysis of, 1 63-165, 1 66f, 1 67f Cellulosic IR transmittance spectrum for, 11 Of spectral identification of, 109 Cennini, Cennino, 1 3 4 Ceramics chemical analysis methods for, 1 8t Native American, infrared analysis of, 1 38-14 1 , 1 40f Cerussite, absorption bands for, 1 1 6, 1 1 6t Cesium bromide, infrared transmission char­ acteristics of, 48t Cesium iodide, infrared transmission charac­ teristics of, 48t C-H stretching region in polymer identification, 1 1 1 in spectral interpretation, 94 Chalk IR transmittance spectrum for, 1 1 5f, 1 94f mid-IR absorption band regions for, 1 1 9t Chemical analysis techniques combining, 1 8-1 9 comparison of, 1 7t order of application, 1 8 t Chloroform, a s solvent, 29f, 3 0 Chromatography, 1 7t, 1 2 1 Chumash Indian paints, infrared analysis of, 141-144, 1 43f, 144f, 145f Clay, 195 IR transmittance spectrum of, 1 15f, 1 95f mid-IR absorption band regions for, 1 1 9t thermal transformations in lattice structure of, 1 1 8 Cloth-lap procedure, 48 Coatings chemical analysis methods for, 1 8t IR analysis methods for, 45t Coblentz, William W., 1 Collagen, in parchment, 1 6 7 Colorants. See also Pigments chemical analysis methods for, 1 8t infrared analysis of, 132 spectral identification of, 1 1 3-120 Combination bands, 1 1 Commercial liquid cells, 5 1 Compression cells, 71f, 75-76 interference fringes produced by, 76 Computer libraries search programs, for spec­ tral interpretation, 92-93 Computer spectral subtraction methods, 124-125 Concentration, sample, determination of, 123 Consolidants, chemical analysis methods for, 1 8t Container storage, of samples, 22 Contamination of sample, avoidance of, 23 Contour mapping microspectroscopy, 78, 79f Convolution, 125-126 Cooley, James, 2 Copal, IR transmittance spectrum for, 1 06f, 1 8 7f Copper acetate, reference spectrum for, 1 9 9f Copper carbonate, basic, reference spectrum for, 1 99f Corrosion products chemical analysis methods for, 1 8t infrared analysis of, 132 Creosote lac resin, infrared analysis of, 1 38-14 1 , 140f Cross section samples collection and preparation procedures, 25t, 33-41 embedded, reflection versus transmission analysis of, 148-152 embedding of, 34-37 microspectropic analysis of, 72f, 76-77, 77f microtoming of, 37-41 o Dammar, reference spectrum for, 188f Dead Sea Scrolls, infrared analysis of, 1 66-170, 1 69f, 1 70f Deconvolution, 125-127, 1 28f Degrees of freedom, 8-10 for triatomic molecule, 1 0f Depletion measurements, vapor-phase, 1 55-1 5 9 Derivative spectroscopy, 1 2 5 , 127f Detector response, 12f, 12-13 Deterioration studies, infrared spectroscopy in, 1 3 3-134 cellulose nitrate sculptures, 1 63-165 Dead Sea Scrolls, 166- 1 70 Diamond cells, 58-59, 59f interference fringes produced by, 76 Diamond, IR transmission characteristics of, 48t, 59 Diamond knives, for rotary microtomes, 37-38, 38f Die, pellet, 53f, 54-55 Difference spectra, 125 Diffraction, apertures and, 73-74, 75f Diffuse reflection, 60f Diffuse reflection spectroscopy (DRIFTS), 60, 63-65 accessory for, 64f introduction of, 60 IR spectra of Acryloid B-72 collected by, 44f, 61f for liquid analysis, 51 spectral alterations due to, 6 1 t Digilab, 2 Dipole moment change in, as selection rule, 1 1 intensity of absorption bands and, 122 Direct measurement method, 123 Dispersive spectrophotometer, grating-type, 85-86 Disposable infrared cards, 56 Documentation, sample, 2 1 -22, 24, 7 1 Dragon's blood, reference spectrum for, 200f DRIFTS. See Diffuse reflection spectroscopy Dyes. See Colorants E EDS. See Energy dispersive spectroscopy Egg yolk, reference spectrum for, 1 83f Electromagnetic radiation absorption theory of, 6-12 spectral regions of, 4, 5f types of, 4 wave theory of, 4-6, 6f Electronic transition, 8 Electrons, in Bohr's atomic model, 7 Elemi, reference spectrum for, 188f Embedding, of cross section samples, 34t, 34-37, 3 6f, 37f infiltration during, 35-37 and microspectroscopic analysis, 76 molds and embedding media blocks used for, 35f optimal for microtoming, 35, 39, 39f with polyester resin, 34-35 trimming to produce trapezoid tip, 39, 40f Energy dispersive spectroscopy (EDS), 1 7t Epoxy, for embedding and microtoming of paint cross sections, 34t Eppendorf GELoader, polypropylene tips for, 3 1 Esters, absorption band frequencies of, 96-97, 98f Ethanol, as solvent, 30 Ethnographic materials, infrared analysis of, 1 3 1 case study, 1 38-141 Ethyl acetate IR transmittance spectra for, 140f as solvent, 29f, 30 External reflection, 60, 60f reflection-absorption, 63 specular, 62-63 External reflection accessory, variable­ angle, 62f Eye blades, 2 1 Eyelash brush, 2 0 , 21f in microtoming, 4 1 F Far-infrared (FIR) region, 14 Fast Fourier transform (FFT) algorithm, discovery of, 2 Fellgett, Peter, 1-2 Fibers chemical analysis methods for, 1 8 t contaminants, 23 flattening of, 32-33, 58, 75-76 advantages to, 60 infrared analysis methods for, 45t microspectroscopic analysis of, 72f, 72-74 reflection analysis of, 67 sample collection and preparation proce­ dures, 25t, 32-33 scattering caused by, 56 transmission analysis of, 59-60 Fillers (inorganic), chemical analysis methods for, 1 8 t Films on diamond cells, 58-59, 59f infrared analysis methods for, 45t preparation of, 56-57 reflection analysis of, 67 thickness of, calculating, 56, 57 232 transmission analysis of, 56-59 on transparent supports, 56-58 unsupported, 56 and interference fringes, 56, 57{ Fingerprint region, 14 and identification of material, 83 in polymer identification, 1 1 2-1 1 3 i n spectral interpretation, 94 Finishes, chemical analysis methods for, 1 8t FIR region. See Far-infrared region First-order vibration. See Fundamental vibration Fish glue, reference spectrum for, 1 8 1{ Flattening of sample, 32-33, 58 advantages to, 60 methods for, 75-76 Flourinated oil (Fluorolube), mixture of particles with, 57 Forceps, in IR microspectroscopy, 71 Fourier self-deconvolution, 125-127, 1 28{ Fourier transform infrared (FT-IR) spectrometers, 1-2 attachment of microscopes to, 68 and plotting formats, 85 resolution on, 86 Frequency of absorption bands, 82-83 of radiation waves, S ad vantages of using, 6 FT-IR spectrometers. See Fourier transform infrared spectrometers Functional group(s), 1 1-12 absorption band qualities and information about, 82, 83 correlation charts for, 99, 99{ selected, absorption band frequencies of, 95t, 95-98 in spectral interpretation, 93-95 Functional group imaging. See Molecular mapping Fundamental transition, 9 Fundamental vibration, 1 1 Furniture surface treatments, infrared analysis of, 144-152 G Gamma radiation, 4, 5{ Gas(es) interaction of solid material with, vapor­ phase depletion measurements for, 1 54-158 IR analysis methods for, 45t rotational absorption bands of, 9{, 50 sample collection and preparation procedures, 24-25, 25t transmission analysis of, 50 Gas cell, 50, 50{ for depletion studies, 1 57{ Gas chromatography (GC), 1 7t application of, 142 GC-IR interface, 50 Gelatin collagen denaturation to, 1 6 7 I R transmittance spectrum for, 98{, 1 82{ Gems, chemical analysis methods for, 1 8 t Germanium, a s IRS element, 66 Gettens Collection, 92, 1 09 Glass absorption bands for, 1 17 chemical analysis methods for, 1 8t infrared transmission characteristics of, 46, 48t, 49{ Glass containers, for sample storage, 22 Glass depression slide, 22{, 22-23 Index Glass knives, for rotary microtomes, 38, 38{, 39{ Gold mirrored surface in reflection-absorption, 63 in solvent extraction, 30 Grazing-angle spectroscopy, 63, 79 Green pigments mid-IR absorption band regions for, 1 1 9t reference spectra for, 1 99{ Grinding of sample, 54 anomalies produced by, 55 Group frequencies, 12 Gum(s) IR transmittance spectra for, 1 0 1{, 1 79{-1 80{ spectral identification of, 108 Gypsum absorption bands for, 1 1 7 mid-IR absorption band regions for, 1 1 9t reference spectrum for, 1 94{ H Hair samples, collection of, 32 Herschel, William, 1 Hexane, as solvent, 29{ Hide glue, IR transmittance spectrum for, 1 0 1 {, 1 8 1{ High performance liquid chromatography (HPLC), 1 7t Honey, 1 80 IR transmittance spectrum of, 97{, 1 8 0{ HPLC. See High performance liquid chromatography Hydrocarbon stretching region in polymer identification, 1 1 1 in spectral interpretation, 94 Hydrocarbons aliphatic, absorption band frequencies of, 95t, 95-96, 96{ aromatic, absorption band frequencies of, 95t, 96, 97{ Hydrocerussite, absorption bands for, 1 1 7 Hydrogen Bohr's atomic model for, 7{ emission spectrum of, 7 Hydroxyl, absorption band frequencies of, 95t, 96 Hypodermic needle, for cross section removal, 33 Indigo, reference spectrum for, 1 97{ Inductive coupled plasma (ICP), 1 7t Infiltration, of paint cross section samples, 35-37 prevention methods, 37 Infrared radiation definition of, 1 discovery of, 1 molecular transitions affected by, 8 Infrared spectra, 5{, 83 absorption bands observed in, 1 1 attributes of, 82-83 detector response, 12{, 12-13 good-quality, requirements for, 87-9 1 , 88t interpretation of. See Spectral interpretation plotting formats for, 84{, 84-86 reference collections of, 9 1 -92 regions in, 1 3-14 Infrared spectroscopy applications of, 1 3 0-1 34, 1 7 1 . See also Case studies compared with other analysis techniques, 1 7t history of, 1-2, 3{ methods of, 43-80 microspectroscopy, 43, 68-79 optimal sample thickness for, 41 reflection analysis, 43, 60-68 transmission analysis, 43, 45-60 units used in, 6 vibrational transitions in, 1 0 Inorganic substances in art objects, 1 7 chemical analysis methods for, 1 8t contaminants, 23 separation of organic substances from, 31 Instrument configuration, 86-87 Intensity of absorption bands, 83 and concentration of absorbing mole­ cules, 85, 122-123 and dipole moment, 122 in quantitative analysis, 1 2 1 o f spectrum, a s quality check, 88t, 89-90 Interference fringes compression/diamond cells and, 76 free film samples and, 56, 57{ Internal reflection, 60{, 65 Internal reflection spectroscopy (IRS), 60, 65-68, 66{. See also Attenuated total reflection applications of, 65-66 elements for, 66 introduction of, 60 for liquid analysis, 51 sample preparation for, 67, 67{ spectral alterations due to, 6 1 t IR. See Infrared Iron oxide pigments, mid-IR absorption band regions for, 1 1 9t IRS. See Internal reflection spectroscopy IRIlS microspectrophotometer, 69, 70{, 136 Isinglass, reference spectrum for, 1 8 1{ Italian masters binders used by, infrared analysis of, 152-155 ultramarine pigments used by, infrared analysis of, 1 34-138, 1 35{, 1 36{ Ivory black, IR transmittance spectrum for, 1 3 6{ Ivory, spectral identification of, 1 0 8 J. Paul Getty Museum, Roentgen desk at, infrared analysis of varnish on, 144-148, 147{ ]acquinot, P., 2 ]CAMP.DX format, 93 K Kaolin, IR transmittance spectrum for, 1 1 5{, 1 95{ Ketones, absorption band frequencies for, 96-97, 98{ Klucel F IR transmittance spectrum for, 1 1 O{ spectral identification of, 109 Kramers-Kronig transformation, 63 KRS-5 infrared transmission characteristics of, 48t as IRS element, 66 Kubelka-Munk function, in diffuse reflection analysis, 63, 65 l Lab-Calc, 93 Lacquers accelerated aging studies of, 1 3 3 chemical analysis methods for, 1 8t spectral identification of, 1 04 233 Index Lapis lazuli, 1 3 4 IR transmittance spectra for, 1 3 7( sources of, 1 37-1 3 8 Lattice structure, o f pigments, 1 1 4 Linear mapping microspectroscopy, 77, 77( Linseed oil, IR transmittance spectrum for, 1 0 1 (, 1 85( Liquid(s) IR analysis methods for, 45t reflection analysis of diffuse, 64 internal, 67 sample collection and preparation proce­ dures for, 25 t, 25-26 transmission analysis of, 50-51 Liquid cells, 5 1 , 5 1 ( Liquid nitrogen, adding t o sample before grinding, 54 Liquid water, vibrational transitions of, 9( M Madder, reference spectrum for, 200( (Mantegna), ultramarine particles in, infrared analysis of, 1 3 5(, 1 35-1 3 8 Malachite absorption bands for, 1 1 6, 1 1 6t, 1 1 7 I R transmittance spectrum for, Madonna with Child 1 1 5(, 1 99( mid-IR absorption band regions for, 1 1 9t Mallery, Garrick, 1 4 1 Mantegna, Andrea, 1 5 2 binders used by, infrared analysis of, 1 52-1 5 5 ultramarine particles in paintings of, infrared analysis of, 1 35(, 37-41 and micro spectroscopic analysis, 76 oblique sectioning, 40-4 1 , 4 1 ( optimal embedment for, 35, 3 9 , 39( orientation of sample, 39-40, 40( problem solving, 4 1 trapezoid tip for, 3 9 , 40( Microwave radiation, 4, 5( Mid-infrared (MIR) region, 1 3-14 of pigments, 1 1 9t Mineral oil, mixture of particles with, 57 Mineral wax, reference spectrum for, 1 8 3( MIR region. See Mid-infrared region Mixture(s) resolution enhancement methods for, 125 separation of by pyrolysis, 3 1-32, 32( by solvent extractions, 29-3 1 , 30(, 3 1( spectral identification of, 120-1 2 1 , 1 2 1 ( Molar absorptivity, 1 2 2 Molecular mapping, 77(, 77-79, 78(, 79( Molecular transitions, 8 prediction of, degrees of freedom and, 8-10 MoMA. See Museum of Modern Art, New York Mortars, chemical analysis methods for, 1 8t Muggli, Robert 2 Multiplex advantage, discovery of, 2 Museum of Fine Arts, Houston, Neoclassical armchair at, infrared analysis of paint on, 1 4 8-152, 149( Museum of Modern Art, New York, cellulose nitrate sculptures at, deteriora­ tion studies of, 1 64-165 Z., 1 35-1 3 8 Mapping microspectroscopy, 77-79 applications of, 1 3 2 area, 7 7 , 78( case study of, 152-155 contour, 78, 79( limitations of, 79, 1 54-155 linear, 77, 77( Masonry, chemical analysis methods for, Mastic, 1 8 9 I R absorbance spectrum for, 105( IR transmittance spectrum for, 1 0 1 (, mapping, 77(, 77-79, 78(, 79( applications of, 1 32 case study of, 152-155 particle analysis, 70-72, 72( resolution limit achievable in, 74 sample thickness and, 74-75, 75( Microtoming, of cross section samples, 1 8t 1 06(, 1 8 9( Mathematical manipulations of spectra, 1 24-127 resolution enhancement methods, 1 25-1 27 subtraction techniques, 124-125 Mercury-cadmium-telluride (MCT) detectors, 69, 8 6 , 1 3 6 Metals, chemical analysis methods for, 1 8 t Michelson, Albert, 1 Microcrystalline wax, reference spectrum for, 1 83( Micropellet(s), 52 preparation of, 55 Micropellet die and holder, 53( Microscopes, coupling with IR spectropho­ tometer, 2, 6 8 , 6 9 Microspectrophotometer, 6 8 accessories for, 79 capabilities of, 69-70 design of, 69 IRpS, 69, 70(, 1 3 6 Microspectroscopy, 43, 68-79 aperture selection in, 7 1 , 72, 72(, 76 applications of, 68-69 cross section analysis, 72(, 76-79, 77( diffraction in, 73-74, 75( fiber analysis, 72(, 72-74 N Native American ceramic pots, creosote lac resin used in, infrared analysis of, 1 3 8-1 4 1 , 140( Natural materials. See Organic substances Near-infrared (NIR) region, 1 3 Neoclassical armchair (Museum o f Fine Arts, Houston), infrared analysis of paint on, 1 4 8-152, 149( Newton, Isaac, and internal reflection, 65 NIR region. See Near-infrared region Nitric acid, as solvent, 30 Nitrogen, liquid, adding to sample before grinding, 54 Noise, spectrum as quality check, 8 8 t, 8 8-89 smoothing methods for, 8 9 , 90( Nujol, mixture of particles with, 5 7 Nylon IR transmittance spectrum of, 1 1 O( spectral identification of, 1 0 9 o OH-NH region in polymer identification, 1 1 1 in spectral interpretation, 9 3 Oil(s) IR transmittance spectra for, 1 0 1 (, 1 85(-1 8 6( spectral identification of, 1 02-103 Oil mull, dispersion of particles in, 57 Olin, Jacqueline, 130 Optical microscope, coupling with IR spectrometer, 2 Organic substances in art objects, 1 7-1 8 chemical analysis methods for, 1 8t contaminants, 23 separation from inorganic matrix, 3 1 spectral identification of, 1 00-108, 102( Overtones, 9, 1 1 p Paint(s) chemical analysis methods for, 1 8t, 1 8-1 9 Chumash Indian, infrared analysis of, 1 4 1 - 1 44, 143(, 1 44(, 145( cross section samples of, 33-34 embedding of, 34t, 34-37, 36(, 37( infiltration of, 35-37 microtoming of, 37-41 reflection versus transmission analysis of, 1 4 8-152 infrared analysis of, 120, 1 22(, 1 30-1 3 1 of Italian masters, infrared analysis of, 1 34-1 3 8 , 1 35(, 1 36( on Neoclassical armchair, infrared analysis of, 1 4 8-1 52, 1 49(, 1 50(, 1 5 1( Paraffin for embedding and microtoming of paint cross sections, 34t IR transmittance spectrum of, 96( Parchment, ancient preparation techniques for, 1 6 7 Particle, IR microspectroscopic analysis of, 70-72, 72( Parylene, oxidation of, infrared analysis of, 1 59-1 63, 1 6 1(, 1 62t Patinas chemical analysis methods for, 1 8 t infrared analysis of, 1 32 Pelco silicone rubber molds, for embedding, 35 Pellet(s) in infrared transmission analysis, 52-54 numbered grid scratched into, 7 1 , 71 ( preparation of, 54-55 Pellet die, 53(, 54-55 Pellet holder, 53( Percent transmittance, 12, 12( Photomicrographs, 24 Phthalocyanine blue, reference spectrum for, 1 9 7( Pigments. See also specific pigment chemical analysis methods for, 1 8 t infrared analysis of, case study, 1 34-1 3 8 , 1 35(, 1 36( infrared transmittance spectra for, 1 1 5(, 1 94(-200( mid-IR absorption band regions for, 1 1 9 t in paint analysis, 1 2 0 spectral identification of, 1 1 3-120 Pine resin, reference spectrum for, 1 8 7( Plaster absorption bands for, 1 1 7 chemical analysis methods for, 1 8 t I R transmittance spectrum of, 1 1 5(, 1 95( Plastic containers, for sample storage, 22 Plastics chemical analysis methods for, 1 8 t infrared analysis of, 1 63-165 Plotting formats, 84(, 84-86 Polarized light microscopy (PLM), 1 7t Polishing of infrared windows, 47-48 of IRS elements, 66 Polyamide, 1 9 3 IR transmittance spectrum of, 1 1 0(, 1 93( Index 234 Polycyclohexanone, 193 IR transmittance spectrum of, 1 1 0(, 1 93( spectral identification of, 1 0 9 Polyester, 1 9 1 absorption bands for, 3 7 embedding with, 34-35 for paint cross sections, 34t, 36, 37( IR transmittance spectrum of, 98 (, 1 9 1( Polyethylene infrared transmission characteristics of, 48t infrared transmittance spectrum of, 1 1 0( spectral identification of, 1 0 9 Polymer(s) characterization process for, 1 1 0-1 1 3 chemical analysis methods for, 1 8t reference spectra for, 1 9 0(-1 93( spectral identification of, 1 0 9- 1 1 3 , 1 1 1( Polystyrene free film of, interference fringe pattern obtained from, 57( IR transmittance spectrum for, 97( Polyvinyl acetate (PVAC), reference spectrum for, 1 92( Poppyseed oil, reference spectrum for, 1 85( Potassium bromide for elimination of interference fringes, 76 infrared transmission characteristics of, importance of, 1 2 8 and visual pattern recognition procedure, 9 1 -92 Reflection, 46( types of, 60( Reflection analysis, 43, 60-68 comparison of methods, 44(, 6 1 t, 6 1 ( diffuse reflection spectroscopy (DRIFTS), 60, 63-65 internal reflection spectroscopy (IRS), IR microspectrophotometer and, 70 reflection-absorption (R-A), 63 spectral alterations due to, 61 t specular reflection, 62-63 of stone deterioration, 1 3 3 versus transmission analysis, case study of, 1 4 8-1 52 Reflection-absorption (R-A), 63 spectral alterations due to, 6 1 t Refraction, 46( Refractive index values, 4 8 t Residues, chemical analysis methods for, 1 8t Resin(s) accelerated aging studies of, 1 3 3 i n furniture surface treatment, infrared analysis of, 144-148, 1 4 7( infrared analysis of, case study, 1 3 8-1 4 1 , 140( 46, 48t, 49( for pellet pressing, 54 Potassium chloride, infrared transmission characteristics of, 4 8 t Powder samples internal reflection analysis of, 67 preparation of, 64 Presentation in the Temple (Mantegna), ultramarine particles in, infrared analysis of, 1 3 5(, IR absorbance spectra for, 1 05( IR transmittance spectra for, 1 0 1 (, spectral identification of, 1 03-107, 1 07( Resolution enhancement methods, 125-127 Reststrahlen bands, 62 Rice starch, reference spectrum for, 1 80( Rock art, Chumash Indian, infrared analysis of, 1 4 1 - 1 44, 143(, 1 44(, 145( 71 Roentgen, David, 145 Roentgen desk (J. Paul Getty Museum), infrared analysis of varnish on, 1 0 1 (, 143(, Rosin, IR transmittance spectrum for, Pressed-pellet technique for IR analysis, 52-55 144-148, 147( 106(, 1 86( 1 8 1(-1 8 3( spectral identification of, 1 0 8 , 142 Prussian blue IR transmittance spectrum for, 1 3 6(, mid-IR absorption band regions for, 1 1 9t Pulverizing of samples, 54 PVAC. See Polyvinyl acetate Pyrolysis, mixture separation by, 3 1 -32, Q R 1 06(, 1 8 6(-1 90( 1 35-1 3 8 , 1 36( Probe, in IR microspectroscopy, Proteins IR transmittance spectra for, 60, 65-68 1 98( Rotary microtomes, 37-38, 3 8(, 39( Rotational transitions, 8 degrees of freedom corresponding to, 9, 1 0(, l O t energy transition levels for, of water vapor, 9( Rutherford, Ernest, 7 9( 32( S Qualitative analysis, 87-99 determination of spectral quality, 8 7-9 1 , 8 8 t Quantitative analysis, 1 2 1 -124 Quartz, infrared transmission characteristics of, 48t Salts chemical analysis methods for, 1 8 t for elimination of interference fringes, 76 Sample blank, 23 Sample(s)/sampling. See also specific type background information, 1 9 collection and preparation procedures, 24-4 1 , 25t R-A. See Reflection-absorption Radiation. See Electromagnetic radiation Radio frequency radiation, 4, 5( Rayleigh, Lord, 1 Razor blade, microscalpel made from, 2 1 , 2 1 ( Red pigments mid-IR absorption band regions for, 1 1 9t reference spectra for, 200( Reference spectra, 1 78-200 on artists' colorants, 1 1 3 collections of, 9 1 -92, 1 09, 1 72-177 computer libraries search programs for, 92-93 concentration of, determination of, 1 2 3 contamination of, avoidance of, definition of, 1 6 design, 1 7- 1 9 documentation, 2 1 -22, 2 4 , 7 1 flattening of, 32-33, 5 8 , 75-76 freestanding, 56 grinding/pulverizing of, 54 implementation, 20-23 location, 1 9-20 representative, 20 storage, 22-23 with swabs, 26-27, 27( 23 thickness of, effects in IR microspec­ troscopy, 74-75, 75( tools for, 20-2 1 , 2 1 ( Sandarac, 1 8 9 I R absorbance spectrum for, 105( IR transmittance spectrum for, 106(, 1 8 9( Sapphire, infrared transmission characteristics of, 4 8 t Scaled absorbance subtraction, 1 2 4 Scalpels, 2 1 , 2 1 ( for cross section removal, 3 3 for liquid sampling, 2 6 proper use of, 2 8 , 2 8 ( Scattering, reduction of, 56 Selection rules, for IR absorptions, 1 1 Semiquantitative analysis, 1 2 1-122 Shellac, 1 07, 138, 1 9 0 I R absorbance spectrum for, 1 05( IR transmittance spectrum for, 1 0 1 (, 1 06(, 1 90( Signal-to-noise ratio, of spectrum, 8 8-89 Silica/silicates absorption bands for, 1 1 5(, 1 1 6t, 1 1 7-1 1 8 I R transmittance spectrum for, 1 1 5(, 1 96( Silicon, as IRS element, 66 Silicon carbide paper, for sample collection, 64 Silver chloride infrared windows, 47, 4 8t as IRS element, 6 6 Skeletal (torsional) vibration, 1 0-1 1 Slide sandwich, 22(, 22-23 Smoothing methods, to decrease spectrum noise, 89, 90( Sodium chloride for elimination of interference fringes, 76 infrared transmission characteristics of, 46, 4 8t Sodium hydroxide, as solvent, 30 Solids cross section. See Cross section samples fibrous. See Fibers IR analysis methods for, 45t reflection analysis of diffuse, 64-65 internal, 67 sample collection and preparation proce­ dures, 25t, 28-41 solvent-soluble, 29-3 1 transmission analysis of, 52-60 film techniques, 56-59 pressed-pellet technique, 52-55 Solubility schematic, 29( Solution(s) diffuse reflection analysis of, 64 film preparation from, 56-57 internal reflection analysis of, 67 Solution spectroscopy, 50-51 Solvent(s), chemical analysis methods for, 1 8t Solvent extractions, mixture separation by, 29-3 1 , 30(, 3 1(, 1 20 Spectral identification, 87, 87( of inorganic materials, 1 1 3-120 of mixtures, 120-1 2 1 , 1 2 1 ( of organic materials, 100-108, 1 02( of synthetic resins (polymers), 1 09-1 1 3, 1 1 1 ( Spectral interpretation absorption band attributes and, 82-83 computer libraries search programs and, 92-93 correlation charts and, 99, 99( functional groups in, 93-95 identification scheme for, 87( instrument configuration, 86-87 mathematical manipulations in, 124-127 235 Index plotting formats and, 84(, 84-86 qualitative analysis and, 87-99 quantitative analysis and, 1 21-124 spectra-structure correlations in, 95-98 visual comparison and, 9 1 -92 Spectral quality, determination of, 87-9 1, 88t Spectral subtraction, 124-125, 126( Spectra-Tech, 2 IRIlS microprobe, 1 3 6 Spectroscopy definition of, 4 infrared. See Infrared spectroscopy Spectrum (spectra), 7 electromagnetic, 4, 5 ( infrared. See Infrared spectra quality of, determination of, 87-9 1 , 88t Specular reflection, 62-63 as distortion in reflection-absorption experiment, 63 IR spectra of Acryloid B-72 collected by, 44(, 6 1 ( mapping studies and, 7 9 spectral alterations due to, 6 1 t Starch, reference spectrum for, 180( Steel knives, for rotary microtomes, 37, 38( Stereo microscope, in IR microspectroscopic analysis, 70-7 1 , 76 Stone(s) chemical analysis methods for, 1 8t weathering of, infrared analysis of, 1 3 3 Storage of infrared windows, 49 of samples, 22-23 Stretching vibration, 1 0 Subtraction techniques, for spectral analysis, 1 24-125, 126( Sugars, reference spectra for, 1 79(-1 80( Sulfates, absorption bands for, 1 1 5(, 1 1 6t, 117 Sulfuric acid, as solvent, 30 Sulfuryl fluoride (Vikane), infrared analysis of, 1 55-1 59, 1 5 7( Swabs, sampling with, 26-27, 27( Synthetic resins (polymers) infrared analysis of, 1 3 1 reference spectra for, 1 90(-1 93( spectral identification of, 1 09-1 13, 1 1 1 ( T Teflon, infrared transmission characteristics of, 48t Thallium iodide bromide, infrared transmission characteristics of, 48t Thin-layer chromatography (TLC), 1 7t Torque wrench, 67( Torsional (skeletal) vibration, 1 0-1 1 Tragacanth, spectral identification of, 1 08, 1 79( Translational transition, 8 degrees of freedom corresponding to, 9, 1 0(, lOt Transmission, 46( in IR experiments, 1 3 Transmission analysis, 4 3 , 45-60 acceptance of, 80 advantages of, 45 film techniques for, 56-59 of gases, 50 IR spectra of Acryloid B-72 collected by, 44(, 6 1 ( o f liquids, 50-51 microspectroscopy and, 71 possible spectral anomalies with, 47t pressed-pellet technique for, 52-55 versus reflection analysis, case study of, 148-152 of solids, 52-60 support materials used in, 46-49, 48t Transmittance mode, for spectral display, 84(, 85 Tukey, John, 2 Tungsten knives, for rotary microtomes, 37, 38( Tungsten needle, 20, 2 1 ( U Ultramarine mid-IR absorption band regions for, 1 1 9t pigments, infrared analysis of, 134-1 38, 135(, 1 36( reference spectrum for, 1 98( Ultraviolet radiation, 4, 5( Ultraviolet spectroscopy, units used in, 6 Unknown material, spectral identification of. See Spectral identification Urushi ( oriental lacquer), spectral identification of, 1 04 UV. See Ultraviolet V Vapor-phase depletion measurements, 155-159 Variable-angle external reflection accessory, 62( Vegetable wax, reference spectrum for, 1 84( Venus and Adonis (Titian), ultramarine parti­ cles in, infrared analysis of, 1 34-138, 1 35( Verdigris, reference spectrum for, 1 99( Vibrational transitions, 8 degrees of freedom corresponding to, 9-10, 1 0(, lOt energy transition levels for, 9( in IR spectroscopy, 10 of lattice structure, 1 14 of liquid water, 9( types of, 1 0-1 1 Vikane (sulfuryl fluoride), interaction with solid materials, infrared analy­ sis of, 1 55-1 59, 1 5 8(, 1 59( Visible radiation, 4, 5( Visible spectroscopy, units used in, 6 Visual pattern recognition procedure, 91-92 W Walnut oil, reference spectrum for, 1 86( Water as solvent, 29(, 30 vibrational transitions of, 9( Water of hydration, absorption bands for, 1 1 6, 1 1 6t Water vapor extraneous bands produced by, 88t, 90-91 rotational absorption bands for, 9( Wave theory, of electromagnetic radiation, 4-6, 6( Wavelength, 5, 6( disadvantages of using, 6 Wavenumber, 5-6 advantages of using, 6 Wax(es) IR transmittance spectra for, 101(, 1 83(-1 84( spectral identification of, 1 00-102 White pigments mid-IR absorption band regions for, 1 1 9t reference spectra for, 1 94(-1 95( Wick-Stick, 55 Window region in polymer identification, 1 1 1-1 1 2 i n spectral interpretation, 9 4 Windows, infrared, 46-49 film analysis on, 56-58 materials for, 46-47, 48t polishing of, 47-48 storage of, 49 thickness of, 47 Wood, chemical analysis methods for, 1 8t x yZ X rays, 4, 5( X-ray diffraction (XRD), 1 7t X-ray fluorescence (XRF), 1 7t Yellow, mid-IR absorption band regions for, 1 1 9t Zinc selenide infrared transmission characteristics of, 48t as IRS element, 66 About the Authors Michele R. Derrick is a chemist and conservation scientist with more than twenty years' experience analyzing and characterizing materials. She graduated from Oklahoma State University in 1 9 7 9 with an M.S. degree in analytical chemistry, then worked at the University of Arizona Analytical Center. She next worked for twelve years as a conservation scientist at the Getty Conservation Institute. Derrick currently has a dual role as a consultant for the Museum of Fine Arts, Boston, and as a chemist at a commercial analytical laboratory. Derrick has published more than thirty articles in j ournals and proceedings. In 1 99 5 she received the Kress Foundation conservation publication fellowship that funded this volume. She currently holds a grant from the National Center for Preservation Technology and Training to compile a database on materials used in the production and conservation of historic and artistic obj ects and sites. Dusan Stulik graduated from Charles University in Prague with B.S. and M.S. degrees in chemistry. He subsequently obtained a Ph.D. degree in physics from the Czechoslovakia Academy of Sciences. He is currently a senior scientist in the Scientific Program at the Getty Conservation Institute, where his research focuses on the application of modern sci­ entific methods to conservation science. James M. Landry is a professor of chemistry and director of the Natural Science Program at Loyola Maiymount University in Los Angeles. He received his B.S. and M.S. degrees in chemistry from Xavier University in Cincinnati. He then obtained his Ph.D. degree in inorganic chemistry from Miami University of Ohio, specializing in molecular spectroscopy. His research interests include projects in IR microspectroscopy and gas chromatography-mass spectrometry. He has recently been involved in developing a formulation and application process for a novel coating that blocks the transmission of heat through a variety of materials. He has been involved in the Los Angeles Collaborative for Teacher Excellence ( LACTE) , an association of ten colleges funded by the National Science Foundation that works to improve the preparation of future K-1 2 science and math teachers. ISBN 0 - 89236-469-6 V i e w p u b l i c a t i o n s t a t s